US20030114831A1 - Catheter having improved curve retention and method of manufacture - Google Patents
Catheter having improved curve retention and method of manufacture Download PDFInfo
- Publication number
- US20030114831A1 US20030114831A1 US10/020,521 US2052101A US2003114831A1 US 20030114831 A1 US20030114831 A1 US 20030114831A1 US 2052101 A US2052101 A US 2052101A US 2003114831 A1 US2003114831 A1 US 2003114831A1
- Authority
- US
- United States
- Prior art keywords
- catheter shaft
- catheter
- nucleating agent
- tubular member
- polymeric material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
The present invention provides a polymeric treatment for curved regions in shaft assemblies that increases curve retention without affecting the flexibility within these regions. More specifically, the present invention modifies the underlying crystalline morphology of a polymer in order to decrease crystal fracturing. In particular, the present invention treats polymeric materials suitable for catheter construction with a nucleating agent.
Description
- The present invention relates generally to the field of catheter devices having a pre-formed flexible curve along the length of the catheter body. More specifically, the present invention relates to the use of certain polymeric materials, and the treatment of those polymeric materials, to manufacture pre-formed curves that are more flexible and have a greater curve retention.
- This invention resides in the construction and use of catheters for interventional procedures in such fields as cardiology, neurology, urology and gastroenterology. Design features are incorporated in these catheters to facilitate their use in: (1) the advancement of the catheter through a patient's bodily passages to reach specific sites in vessels or chambers of interest; (2) correct placement of the catheter's distal tip at a targeted site within the patient, and finally (3) holding the catheter at a targeted site while procedures with other devices are completed including while the site moves in response to normal bodily functions such as breathing or a heart beat.
- Guide catheters are one type of catheter utilized in these procedures. Guide catheters are relatively large lumen catheters used to guide smaller diameter catheters such as therapeutic, diagnostic or imaging catheters into bodily passages that are curved or branched. More specifically, guide catheters provide a conduit for at least a portion of the path followed by these additional catheters to desired target sites within a patient's vasculature or other body lumen or organ. In order for the catheter to be effective, however, the catheter must be able to traverse the tortuous pathways of a patient's vasculature or other anatomy in a manner as atraumatic as possible.
- In order to function efficiently, guide catheters generally have a relatively stiff main body portion and a relatively soft distal portion. The stiff main body portion gives the guide catheter sufficient pushability and torqueability to allow the guide catheter to be inserted percutaneously into an artery, moved and rotated in the vasculature to position the distal end of the catheter at the desired site. However, the distal portion should have sufficient flexibility so that it can track over a guide wire and be maneuvered through a tortuous path to the treatment site. In addition, a soft distal tip at the very end of the catheter should be used to minimize the risk of causing trauma to a blood vessel while the guide catheter is being moved through the vasculature to the proper position.
- Thus, to limit insertion time and discomfort to a patient, a catheter must be stiff enough to resist the formation of kinks, while at the same time, the catheter must possess flexibility to be responsive to maneuvering forces when guiding the catheter through the vascular system. In addition to these features, catheters must be designed to reach a targeted site and maintain the position at that site throughout the procedure. Guide catheters typically have pre-formed bends formed along their distal portion to facilitate both the placement of the distal end of the guide catheter and to the ostium of a particular coronary artery of a patient and to remain stable once in position. Likewise, angiographic catheters, which are used in evaluating the progress of coronary artery disease in patients, generally have a desired distal end curvature configuration to facilitate both the steering of the catheter to a particular artery to be examined and to provide a stable positioning of the catheter's distal portion.
- As stated above, improved stabilization of a catheter's position is often achieved through curves or bends imparted to the catheter by the manufacturer. Some of these pre-formed curves function by anchoring the catheter against an opposing wall within a patient's vasculature or other anatomy. Proper anchoring is often achieved by matching the predisposed shape of the catheter with the general shape of the targeted site. Often a curve is imparted to the distal end of a catheter with the intention of placing the catheter's distal opening at a desired location in the vessel, or alternatively, on the vessel wall. A guide catheter especially designed for a procedure in a coronary artery, for example, is shaped such that when the guide catheter is inserted into the femoral artery and through the aorta of a patient, the curvature of the catheter will place its distal tip inside one of the coronary ostia. Thus, a guide catheter for the right coronary artery is shaped differently than one for the left coronary artery. A guide catheter designed to provide access to a carotid artery is again shaped differently. Likewise, guide catheters of still other shapes are designed for other bodily passages and regions of interest. Further, there are differences between patients' body structures which require varying sizes of each curve type.
- Guide catheters currently available from manufacturers are designed in a variety of shapes specific for different bodily passages and procedures. Those of skill in the art recognize these different shapes by names such as Judkins Right, Judkins Left, Amplatz Right, Amplatz Left, Bentson, Shepherd Hook, Cobra, Headhunter, Sidewinder, Newton, Sones and others, each formed in a different shape. Most of these different shapes are manufactured in gradations of size and/or curvature to accommodate differences among individual patients.
- When a guide catheter is inserted and advanced within a patient, its pre-formed curved shape is often distorted by the tortuous vasculature and connecting passages of a patient's vasculature. The bends must essentially become straight as the catheter is slowly advanced within the anatomy, usually over a guidewire. In order for the pre-formed manufactured curves or bends to be effective in properly seating the guide catheter, however, the imparted curves must be capable of returning their pre-formed shape or at least a predictable variant of the original shape. This is referred to herein as curve retention. Similarly, after the guide catheter is properly seated, the curves of the catheter must retain the catheter's positioning despite the constant movements in response to normal bodily functions such as breathing or a heartbeat or when other devices are passed through the lumen of the positioned catheter.
- Manufacturers, therefore, often add filler material, or alternatively, use stiffer materials in curved regions to increase curve retention. Although adding materials achieves better curve retention upon placement, decreasing the catheter's flexibility in curved regions causes significant alterations in the catheter's overall performance. Specifically, the catheter's trackability is often affected. For guide catheters having curves imparted within the distal regions of the catheter, the effect in trackability performance can be quite significant. Thus, it is a goal of the present invention to create a catheter design having exceptional curve retention without diminishing the catheter's flexibility and overall trackability performance.
- The present invention provides a polymeric treatment for curved regions in shaft assemblies that increases curve retention without significantly affecting the flexibility within these regions. More specifically, the method of the present invention modifies the underlying crystalline morphology of a polymer in order to decrease crystal fracturing. In particular, the present invention treats polymeric materials suitable for catheter construction with a nucleating agent. A nucleating agent is a material that affects the number and size of crystals formed during the nucleation process. Nucleating agents introduce more nuclei into a polymer's nucleation process. Therefore, under similar cooling procedures, a polymer treated with a nucleating agent results in a rise in the number of crystals formed and a reduction in the overall size of each crystal when compared with an untreated polymer.
- The appended claims particularly point out and distinctly claim the subject matter of this invention. The various objects, advantages and novel features of this invention will be more fully apparent from a reading of the following detailed description in conjunction with the accompanying drawings in which like reference numerals refer to like parts, and in which:
- FIG. 1 is a partial plan view of a catheter assembly in accordance with the present invention;
- FIG. 2A is an illustration of the crystal morphology of a polymeric material lacking nucleating agent treatment;
- FIG. 2B is an illustration of the crystal morphology of the same polymeric material as shown in FIG. 2A, having been treated with a nucleating agent; and
- FIG. 3 is partial plan view of a diagnostic catheter assembly in accordance with the present invention.
- The following detailed description should be read with reference to the drawings, in which like elements in different drawings are numbered identically. The drawings, which are not necessarily to scale, depict selected embodiments and are not intended to limit the scope of the invention. Examples of construction, materials, dimensions, and manufacturing processes are provided for selected elements. All other elements employ that which is known to those skilled in the field of the invention. Those skilled in the art will recognize that many of the examples provided have suitable alternatives that may be utilized.
- Referring now to the drawings, FIG. 1 is a partial plan view of a catheter in accordance with the present invention. The catheter of the present invention may be used in conjunction with most catheter devices suited for placement within the human anatomy. As such, the catheter assembly may be utilized in cardiology, neurology, urology and gastroenterology, among others. In gastroenterological devices, the catheter of the present invention may be incorporated into the shaft design of an endoscope, or alternatively, into a biliary catheter. Likewise, in vascular devices, the
catheter assembly 10 of the present invention may be incorporated into the shaft design of a guide or diagnostic catheter, or in the alternative, into the vascular catheters used to ultimately treat the maladies requiring the medical procedure. - For illustrative purposes, the
catheter 10 is shown as a guide or diagnostic catheter, which is representative of a catheter that can incorporate the present invention. Other intravascular catheter embodiments are additionally suitable without deviating from the spirit and scope of the present invention. - The
guide catheter 10 includes ashaft assembly 12. Aconventional manifold assembly 14 is connected to the proximal end of theshaft assembly 12. The proximal end of theshaft assembly 12 attaches to astrain relief 16 that further extends into themanifold assembly 14. Thestrain relief 16 is generally made of a polyurethane material that snap-fits into themanifold assembly 14 at one end. The other end of thestrain relief 16 is generally adhesively bonded to theshaft assembly 12, forming a continuous and sealed fluid connection from the proximal end of themanifold assembly 14 to the distal end of theshaft assembly 12. - A
single manifold portion 18 or multiplemanifold ports 18 as shown in FIG. 1 extend from themanifold assembly 14 for attaching and fluidly connecting ancillary apparatus to a lumen extending through the guide catheter. Eachmanifold port 18 includes a lumen terminating into either a common lumen or a dedicated lumen extending within the shaft assembly 12 (e.g., a guidewire lumen). Functionally, themanifold assembly 14 additionally provides a convenient place for a physician to apply longitudinal or rotational forces in order to manipulate the guide catheter during a medical procedure. - The dimensions and materials used in making the
shaft assembly 12 are selected based upon the desired catheter application. For instance, aguide catheter 10 is generally characterized as having a multi-layer tubular member construction. This tubular member includes at least a single lumen extending the length of theshaft assembly 12. The lumen within theguide catheter 10 possesses an inner diameter capable of receiving another catheter, preferably a diagnostic catheter. Since many diagnostic catheters have outer diameters in the range of 5F-10F, a guide catheter must either accommodate the largest diagnostic catheter, or identify those catheter sizes theguide catheter 10 may receive. The dimensions of guide catheters are well known in the art. - Materials used to form the
guide catheter 10 vary depending upon the stiffness desired for theshaft assembly 12. Nylon and similar polyamides such as DURETHAN® (available from Bayer) are particularly suitable for rigid tubular members. Other suitable materials for a rigid tubular member include polyetheretherketone (PEEK), polyimide (PI), and polyetherimide (PEI). Rigidity may additionally be imparted to the tubular member by incorporating a braid on or within the tubular member. Polyether block amide (PEBA), in contrast to the rigid polyamides, is a relatively flexible polymeric material having a durometer of approximately 70D. Finally, the use of a polyamide such as CRISTAMID® (available from Elf Atochem) imparts a slightly less rigid durometer than the rigid polyamides and slightly greater than the flexible PEBA material. - Disposed upon the distal end of the
guide catheter 10 is adistal tip 20. Thedistal tip 20 generally comprises a soft polymeric material that allows theguide catheter 10 to navigate and traverse the tortuous pathways of a patient's vasculature in a manner as atraumatic as possible. Materials suitable for thedistal tip 20 include a polyethylene, polyamide, or block copolymer such as PEBAX® having a lower durometer than the proximal shaft materials. In preferred embodiments, adistal tip 20 comprising a polymeric material having a durometer of about 28D is heat welded or bonded to the distal end of the tubular member. In an alternative embodiment, the last ½ to 1 mm of the tip at its distal end is made of a different material from the tip material to form a tip extension. In particular, the last ½ to 1 mm is made from a material that is more durable relative to the softer tip material. In particular, the more durable material will resist deforming or tearing when in use, such as in tracking the patient's tortuous anatomy. For example, this last ½ mm to 1 mm may be manufactured from Marlex high-density polyethylene having approximately a 63D durometer. Thisdistal tip 20 material selection often improves the integrity of the tip region at its distal-most end. - In yet other embodiments, the
distal tip 20 is molded to aid in catheter navigation, or alternatively, in a manner that more securely engages thedistal tip 20 with a targeted site within the patient's anatomy. Distally tapering adistal tip 20 from a larger outer diameter to a smaller outer diameter enhances navigation ofguide catheter 10. A smallerdistal tip 20 allows theguide catheter 10 to more readily follow passages that are curved or branched. - As described in detail above, the stabilization of a guide catheter's position within a patient's anatomy is often achieved through curves or bends22 imparted into the shaft assembly by the manufacturer. These
pre-formed curves 22 act by anchoring a selected portion of theshaft assembly 12 against an opposing wall within a patient's vasculature or other body portion. Proper anchoring is often achieved by matching the predisposed shape of thecurved shaft assembly 12 with the general curved anatomical shape around a targeted site. In vascular procedures involving treatment to one of the coronary arteries, often acurve 22 is imparted to the distal end of ashaft assembly 12 with the intention of placing the catheter'sdistal tip 20 at a desired angle. Aguide catheter 10 especially designed for a procedure in a coronary artery, for example, has ashaft assembly 12 shaped so that when theguide catheter 10 is inserted through the aorta of the patient, the curvature of the catheter'sshaft assembly 12 will place itsdistal tip 20 at an angle that engages one of the coronary ostia. - Guide catheters currently include a variety of shapes specific for different bodily passages and procedures. Those of skill in the art recognize these different shapes by names such as Judkins Right, Judkins Left, Amplatz Right, Amplatz Left, Bentson, Shepherd Hook, Cobra, Headhunter, Sidewinder, Newton, Sones and others, each formed in a different shape. The
guide catheter 10 of FIG. 1 generally depicts a curve. Although one selected curve is shown in detail, additional pre-formed curves and bends, being known in the art, and including those listed above, are also incorporated as within the scope of the present invention. In order to understand how pre-formed curves and bends 22 are imparted to aguide catheter 10, and more specifically, how thosebends 22 retain their shape, it is important to understand the physical characteristics of the polymers forming thecurves 22. - Certain polymeric materials possess a crystalline microstructure. A polymer's flexibility, tensile strength and hardness are all directly related to the makeup of that polymer's crystalline microstructure. In particular, these physical attributes are greatly influenced by how the crystalline microstructure was initially developed, under the nucleation process. Nucleation is the process by which
crystals 28 are formed. The nucleation process starts through the introduction of a foreign substance that acts as anucleus 30 for the developingcrystal 28. Under normal reaction conditions,nuclei 30 used for the nucleation process are generally naturally occurring impurities in the polymeric material itself. The first beginnings of acrystal 28 form on thesenuclei 30. Once started, thesecrystals 28 quickly propagate into larger crystals by accretion. FIG. 2A illustrates thecrystal 28 morphology of a typical polymeric material suitable for the present invention. The Figure depicts numerousindividual crystals 28 each having anucleus 30, and an array offine grain structures 32 radiating from thenucleus 30. - The crystalline morphology of a polymeric catheter tubular member is developed after the tubular member is extruded. The molten polymeric material is shaped into a desired form and then cooled to retain that desired shape. During the cooling process, and more generally during the nucleation process, the
crystals 28 propagate to support the desired shapen framework. The completion of the nucleation and cooling process results in a crystalline microstructure not unlike that depicted in FIG. 2A. - For some polymers, the nucleation process is very fast, and for other polymers, the process is so slow that the polymer generally retains an amorphous morphology. Thus, a key to understanding a polymer's crystalline microstructure, and later in manipulating that microstructure, is through quantifying the polymer's crystal growth rate. The crystal growth rate for any particular polymer is influenced by the polymer's nucleus density, the growth rate of
crystals 28 in the polymer and the degree of cooling of the polymer melt. Materials suitable for forming theshaft assembly 12 of the present invention (PEEK, PI, PEI, PEBA and certain polyamides) all possess crystal growth rates that support a crystalline morphology. Moreover, these materials are quantified as having crystal growth rates that permit their crystalline microstructure to be modified during the nucleation process. - Modification of the crystalline microstructure is desirable in order to overcome some shortcomings in traditional manufacturing processes. Specifically, it is desirable to modify the crystalline microstructure in
guide catheters 10 having pre-formed bends and curves 22. Under typical manufacturing processes,crystals 28 develop large elongatedfine grain structures 32 that radiate from the crystal'snucleus 30. The relative size ofcrystals 28 makes them prone to fracturing along their elongatedfine grain structures 32. Consequently, fracturing of the elongatedfine grain structures 32 cause the polymeric material, as a whole, to lose retention in its imparted shape. Crystal fracturing is a particular problem incurved areas 22 of aguide catheter 10 where curve retention is paramount to stabilizing the guide catheter's position within a patient's anatomy. - When a
guide catheter 10 is inserted and advanced within a patient, its pre-formed curved shape is distorted (essentially straightened) by the tortuous vasculature and connecting passages of a patient's vasculature. Thebends 22 straighten as theguide catheter 10 is slowly advanced within the anatomy. Such unavoidable manipulations to thecurved regions 22 of theguide catheter 10 cause the underlying crystalline microstructure to fracture. Once fractured, theguide catheter 10 is unable to retain its exact pre-formed shape or a predictable final shape. In order for the pre-formed manufacturedcurves 22 to be most effective in properly seating theguide catheter 10, however, the imparted curves 22 must be capable of retaining their pre-formed shape or a predictable final shape. - Current manufacturing processes compensate for the loss of curve retention by adding filler material, or alternatively, by using stiffer materials within the
curved regions 22. Although these modifications increase curve retention, their addition also decreases the flexibility ofguide catheter 10 within thesecurved regions 32. Moreover, a loss in flexibility within thecurved regions 32 of theguide catheter 10 may also significantly alter the overall performance ofguide catheter 10. Specifically, the guide catheter's trackability is often affected. Forguide catheters 10 havingcurves 22 imparted within the distal regions of theguide catheter 10, the effect on trackability performance can be quite significant. The present invention provides a polymeric treatment forcurved regions 20 in shaft assemblies that increases curve retention without affecting the flexibility within these regions. - The present invention modifies the underlying crystalline morphology of a polymer in order to decrease crystal fracturing. In particular, the present invention treats polymeric materials suitable for
guide catheter 10 construction with a nucleating agent. A nucleating agent is a material that affects the number and size of crystals formed during the nucleation process. - FIG. 2B depicts the same polymeric material shown in FIG. 2A. However, the material in FIG. 2B has been treated with a nucleating agent. Nucleating agents introduce more nuclei into a polymer's nucleation process. Therefore, under similar cooling procedures, a polymer treated with a nucleating agent results in an increase in the number of
crystals 28 formed and a reduction in the overall size of eachcrystal 28, when compared with an untreated polymer under the same conditions. The discrepancy incrystal 28 number and size is best illustrated by comparing FIG. 2A (untreated) with FIG. 2B (treated with nucleating agents). - As described above, crystal fracturing occurs along the elongated
fine grain structures 32 of thecrystal 28. With nucleating agent treated polymers, however, thefine grain structures 32 are not highly elongated.Individual crystals 28 are highly crowded in nucleating agent treated polymers. As a result, crystal growth accretion is extremely short before acrystal 28 abuts a neighboringcrystal 28. Thus, the elongatedfine grain structures 32 are also very short. It is these shorterfine grain structures 32 that resist fracturing as a result of stresses applied to the crystalline framework. - Longer elongated fine grain structures32 (seen in FIG. 2A) are more susceptible to fracturing because
individual crystals 28 become weaker with increased size. Shorter elongated fine grain structures 32 (which cannot be fully illustrated due to the compact size of each crystal in FIG. 2B) are unlikely to fracture because of their compact size. This resistance to fracturing makes nucleated polymers particularly useful in the bends and curves of a catheter. In particular, such treated curves and bends fail to deform from their originally imparted configuration when advanced through a patient's anatomy. Moreover, these bends and curves are also more likely to retain their positioning within a patient's anatomy despite constant movements in response to normal bodily functions such as breathing and heartbeat. These attributes instill physician and patient confidence, alike, when using highly predictable guide catheters. The physician may feel comfortable that the angle imparted outside of a patient will be reproduced and be retained when theguide catheter 10 is inserted within the patient at the targeted site. - A number of nucleating agents suitable for
shaft assembly 12 construction are commercially available. In a presently preferred embodiment, inorganic additives, organic additives and polymers are preferred nucleating agents. Examples of inorganic additives include, but are not limited to, talc, silica, kaolin, molybdenum disulfide, iron sulfide, titanium dioxide and sodium phenylphosphonate. Examples of organic additives include, but are not limited, to sodium p-tert-butylbenzoate, monton wax, montanic ester salts, salts of monocarboxylic acids and polycarboxylic acids. Examples of polymers include, but are not limited to, ethylene and acrylic ester copolymers, fumeric acid polymers, ethylene, propylene 1,4-hexadiene and norbornadiene. These nucleating agents possess superior nucleation rates for materials suitable for forming theguide catheter 10. More specifically, these nucleating agents are particularly suitable for polymeric materials used to form the pre-formed bends and curves 22 of particular catheter assembly embodiments. Utilization of additional nucleating agents suitable for the preferred polymeric materials listed above, being known in the art, is also incorporated as within the scope of the present invention. - Nucleating agents are commercially available in a variety of differing material states. For example, specific nucleating agents are commercially available as powders, pastes and liquids. The use of one material state may be more appropriate than another depending upon the manner of manufacturing of the resulting catheter device. Nucleating agents in powder form are particularly suited for incorporation within a polymeric material. The powdered nucleating agent is measured, added and dispersed within the polymeric material to maintain a specified concentration throughout the mixture. The required ratio of nucleating agent to polymer that initiates the desired change in crystalline morphology may vary depending upon the specific polymeric material used. In certain polymeric materials, any further increases in the required concentration ratio fail to further improve the crystalline microstructure of the polymer. In some embodiments, the ratio of nucleating agent to polymer is about 0.5% to about 99.5% by weight. In preferred embodiments, the nucleating agent is present in a concentration of about 0.01% to about 1.0% by weight.
- Once the nucleating agent containing polymer is properly admixed, the polymeric mixture is then fed into an extruder. The extruder then dispenses the admixed polymeric material to form a tubular member, and this member is configured to a desired shape. Nucleating agents in paste and liquid form are additionally suitable for this manufacturing method. Alternatively, the desired shape can be formed in a subsequent heat treatment process wherein a select portion including a curve is melted and recrystallized in a desired configuration.
- As discussed above, the catheter assembly of the present invention may also be incorporated into other catheters. Specifically, the multi-lumen shaft assemblies of
balloon dilatation catheters 40 are suited for the catheter assembly improvement of the present invention. The basic construction and use of multi-lumenballoon dilatation catheters 40 are all well known in the art. An example of an OTW catheter may be found in commonly assigned U.S. Pat. No. 5,047,045 to Arney et al. An example of an SOE catheter is disclosed in commonly assigned U.S. Pat. No. 5,156,594 to Keith. -
Multi-lumen catheter 40 construction generally includes the use of aninner tubular member 42 and anouter tubular member 44. In one embodiment, the spatial orientation of the two tubular members is such that the outertubular member 44 is coaxially displaced over theinner tubular member 42 defining an annular inflation lumen therebetween. This spatial relationship is best illustrated with reference to FIG. 3. - Materials used to form the outer tubular member may vary upon the stiffness desired for the
shaft assembly 12. Nylon and similar polyamides such as DURETHAN® (available from Bayer) are particularly suitable for rigid outertubular member 44. Other suitable materials for a rigid outertubular member 44 include polyetheretherketone (PEEK), polyimide (PI), and polyetherimide (PEI). Polyether block amide (PEBA), in contrast to the rigid polyamides, is a relatively flexible polymeric material having a durometer of approximately 70D. Finally, the use of a polyamide such as CRISTAMID® (available from Elf Atochem) imparts a slightly less rigid durometer than the rigid polyamides and slightly greater than the flexible PEBA material. All of these materials possess crystal growth rates that support a crystalline morphology. Moreover, these materials are quantified as having crystal growth rates that permit their crystalline microstructure to be modified during the nucleation process. - The
inner tubular member 42 defines a guidewire lumen, which provides a passage for aguidewire 46. Theinner tubular member 42 is generally made of polyethylene such as Marlex HDPE. In alternative embodiments, the inner tubular member is made of, or lined with, a lubricious material such as polytetrafluoroethylene (PTFE). Materials suitable for forming theinner tubular member 42 are generally classified as having a rapid crystallization growth rate. In contrast to materials forming the outertubular member 44, materials forming theinner tubular member 42 generally possess such rapid crystal growth rates that they fail to support a crystalline morphology that may be modified using nucleating agents. - The benefits of modifying the outer
tubular member 44 may be transferred to theinner tubular member 42, and thereby, to theballoon dilatation catheter 40 as a whole. Because of the spatial relationship within the multi-lumen catheter assembly, the outertubular member 44 restrains theinner tubular member 42. Therefore, modifying the outer polymeric structure oftubular member 44, in effect, also modifies the performance characteristics experienced by theinner tubular member 42. Nucleating agent modifications to the outertubular member 42 are similar to those with reference to theguide catheter assembly 16 of FIG. 1. - Numerous characteristics and advantages of the invention covered by this document have been set forth in the foregoing description. It will be understood, however, that this disclosure is, in many respects, only illustrative. Changes may be made in details, particularly in matters of shape, size and ordering of steps without exceeding the scope of the invention. The invention's scope is of course defined in the language in which the appended claims are expressed.
Claims (21)
1. A catheter shaft comprising:
a polymeric tubular member having a lumen extending the length therein, wherein the tubular member includes a pre-formed bend along a portion of the length of the tubular member, wherein the polymeric material forming at least a portion of the pre-formed bend includes a sufficient quantity of a nucleating agent dispersed therein.
2. The catheter shaft of claim 1 , wherein the polymeric material is selected from the group consisting of polyamide, polyethylene terephthalate, polyetheretherketone, polyimide, polyetherimide and polyether block amide and mixtures thereof.
3. The catheter shaft of claim 1 , wherein the nucleating agent is selected from the group consisting of talc, silica, kaolin, molybdenum disulfide, iron sulfide, titanium dioxide, sodium phenylphosphanate and mixtures thereof.
4. The catheter shaft of claim 1 , wherein the nucleating agent is selected from the group consisting of sodium p-tert-butylbenzoate, monton wax, montanic ester salts, salts of monocarboxylic acids and polycarboxylic acids and mixtures thereof.
5. The catheter shaft of claim 1 , wherein the nucleating agent is selected from the group consisting of an ethylene and an acrylic ester copolymer, a fumeric acid polymer, ethylene, propylene, 1,4-hexadiene, norbornadiene and mixtures thereof.
6. The catheter shaft of claim 1 , wherein the nucleating agent is present in a concentration of about 0.01% to 1.0% by weight.
7. The catheter shaft of claim 1 , wherein the catheter shaft is a portion of a guide catheter.
8. The catheter shaft of claim 1 , wherein the catheter shaft is a portion of a vascular catheter.
9. The catheter shaft of claim 1 , wherein the catheter shaft is a portion of a biliary catheter.
10. A catheter shaft comprising:
a tubular member having a lumen extending the length therein, wherein the tubular member further comprises at least two segments having differing rigidities, wherein at least one of the segments of the tubular member has a pre-formed bend extending over at least a portion of the length thereof which includes a polymer in a portion of said pre-formed bend having a sufficient quantity of a nucleating agent dispersed therein.
11. The catheter shaft of claim 10 , wherein the polymeric material is selected from the group consisting of polyamide, polyethylene terephthalate, polyetheretherketone, polyimide, polyetherimide and polyether block amide and mixtures thereof.
12. The catheter shaft of claim 10 , wherein the nucleating agent is selected from the group consisting of talc, silica, kaolin, molybdenum disulfide, iron sulfide, titanium dioxide, sodium phenyl phosphanate and mixtures thereof.
13. The catheter shaft of claim 10 , wherein the nucleating agent is selected form the group consisting of sodium p-tert-butyl benzoate, monton wax, montanic ester salts, salts of monocarboxylic acids and polycarboxylic acids and mixtures thereof.
14. The catheter shaft of claim 10 , wherein the nucleating agent is selected from the group consisting of an ethylene and an acrylic ester copolymer, a fumeric acid polymer, ethylene, propylene, 1,4-hexadiene, norbornadiene and mixtures thereof.
15. The catheter shaft of claim 10 , wherein the nucleating agent is present in a concentration of about 0.01% to about 1.0% by weight.
16. The catheter shaft of claim 10 , wherein the catheter shaft is a portion of a guide catheter.
17. The catheter shaft of claim 10 , wherein the catheter shaft is a portion of a vascular catheter.
18. The catheter shaft of claim 10 , wherein the catheter shaft is a portion of a biliary catheter.
19. A process for improving curve retention in catheters having a pre-formed curve, the process comprising:
providing a polymeric material;
providing a nucleating agent;
admixing the nucleating agent with the polymeric material; and
extruding the admixed polymeric material and forming a catheter shaft having a pre-formed curve along a portion of the catheter shaft's length.
20. The process of claim 19 , wherein the pre-formed curve is formed prior to cooling the extruded polymeric material, followed by cooling the pre-formed curve.
21. The process of claim 19 , wherein the pre-formed curve is formed subsequent to cooling the extruded polymeric material in a further step comprising heating a portion of the catheter shaft and forming the pre-formed curve, followed by cooling.