US20030079333A1 - Process for making a metal-polymer composite having an irradiated polymer coating - Google Patents
Process for making a metal-polymer composite having an irradiated polymer coating Download PDFInfo
- Publication number
- US20030079333A1 US20030079333A1 US10/038,266 US3826601A US2003079333A1 US 20030079333 A1 US20030079333 A1 US 20030079333A1 US 3826601 A US3826601 A US 3826601A US 2003079333 A1 US2003079333 A1 US 2003079333A1
- Authority
- US
- United States
- Prior art keywords
- polymer
- coating
- composite
- polymer coating
- polyolefin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
A process for making a metal-polymer composites suitable for shaping into container end panels having improved resistance to feathering and angel hair formation. A polymer coating is applied to a metal sheet. The polymer coating includes at least one polymer selected from polyolefins, anhydride modified polyolefins, epoxies, and phenoxies. The polymer coating on the composite is then irradiated with an electron beam. The metal sheet preferably comprises an aluminum alloy and the polymer coating preferably comprises maleic anhydride modified polyropylene.
Description
- The present invention relates to a process for making a metal-polymer composite suitable for shaping into container bodies and container end panels for food and beverage containers. More specifically, the invention relates to a metal-polymer composite including a polymer coating having improved resistance to feathering and angel hair formation.
- Metal sheet coated with a thermoplastic resin on one or both sides has long been used for shaping into bodies and end panels for food and beverage containers. The coating is applied by a variety of processes including roll coating, reverse roll coating, spraying, electrocoating, powder coating, and lamination. Coatings are applied to the metal sheet in order to improve corrosion resistance, formability, and appearance.
- Coating processes most commonly used commercially at the present time require solvent based systems that generate vapors. In order to provide a more environmentally acceptable coating process not requiring any solvents, extrusion coating of thermoplastic polymers onto metal surfaces has been proposed. Some prior art patents disclosing extrusion coating onto metal include Smith et al. U.S. Pat. No. 5,407,702; Levendusky et al. U.S. Pat. No. 5,919,517; Hitchock et al. U.S. Pat. No. 4,452,374; and Schmid et al. U.S. Pat. Nos. 5,942,285 and 6,153,264.
- Extrusion coated aluminum alloy sheet performs adequately for some purposes. However, the highly ductile nature of thermoplastic polymers leads to problems when the polymer coated sheet is formed into end panels for food and beverage containers. The first problem, called “feathering” or “membraning”, occurs when the thermoplastic coating separates from the metal when a pull tab or stay on tab is opened. A thin sheet of the separated coating is visible, either partially covering the container spout or sticking out from the opened panel. A second problem is called “angel hair”, in which polymer coating pushed into the score line on the end panel forms fine filaments when the end is opened, thereby creating an undesirable appearance. The fine filaments of coating are free to enter the container through the opening or to enter the consumer's mouth. Angel hair sometimes also forms at the peripheral edges of polymer coated metal disk blanks for can bodies and at the top edges of polymer coated can bodies.
- Accordingly, there still remains a need to provide polymer coated metal sheet having improved resistance to feathering and angel hair formation when the coated sheet is shaped into container end panels.
- A principal objective of the present invention is to provide a process for making a metal-polymer composite including a polymer coating having improved resistance to feathering and angel hair formation.
- Some advantages of the invention are that the process is inexpensive, can be performed quickly, and is capable of being operated without generating pollutants.
- Additional objectives and advantages of our invention will become apparent to persons skilled in the art from the following detailed description of some particularly preferred embodiments.
- In accordance with the present invention there is provided a process for making a metal-polymer composite suitable for shaping into container bodies and container end panels for food and beverage containers. The composite includes a metal sheet and a polymer coating. The polymer coating preferably includes only a single layer, but may include 2 or more layers.
- The metal sheet may comprise an aluminum alloy, steel, aluminum alloy-coated steel, or aluminum-coated steel. Aluminum alloy sheet is particularly preferred.
- Aluminum alloys suitable for shaping into container bodies include aluminum-manganese alloys of the AA3000 series and aluminum-magnesium alloys of the AA5000 series. Aluminum alloys suitable for shaping into container end panels include aluminum-magnesium alloys of the AA3000 or AA5000 series and especially the AA5182 and AA5042 alloys.
- Aluminum alloys suitable for container end panels such as AA5182 are provided as an ingot or billet or slab by casting. Before working, the ingot or billet is subjected to elevated temperature homogenization. The alloy stock is then hot rolled to provide an intermediate gauge sheet. For example, the material may be hot rolled at a metal entry temperature of about 700-950° F. to provide an intermediate product having a thickness of about 0.130 inch to about 0.190 inch. This material is cold rolled to provide a sheet ranging in thickness from about 0.007 to 0.014 inch We prefer AA5182 aluminum alloy sheet in either the H19 or H39 temper.
- Aluminum alloys such as AA5042 are provided as an ingot that is homogenized. This procedure is followed by hot rolling to an intermediate gauge of about 0.125 inch. Typically, the intermediate gauge product is annealed, followed by cold rolling to a final gauge of about 0.007 to 0.014 inch. We prefer AA5042 aluminum alloy sheet in the H2E72 temper.
- The aluminum alloy sheet is generally cleaned with an alkaline surface cleaner to remove any residual lubricant adhering to the surface, and then rinsed with water. Cleaning may be avoided if the residual lubricant content is negligible.
- A conversion coating is next applied to the sheet to assure good adhesion of the polymer coating and to improve corrosion resistance. Both chrome-containing and chrome-free conversion systems are suitable. The chrome conversion coating generally contains a chromate and a phosphate. Some non-chrome conversion coatings are solutions containing zirconate, titanate, molybdate, tungstate, vanadate, and silicate ions, generally in combination with hydrogen fluoride or other fluorides. The conversion coated sheet may be rinsed with water and then dried before a polymer coating is applied.
- The polymer coating applied to the metal sheet is selected from polyolefins, anhydride modified polyolefins, epoxies, and phenoxies, and preferably is an anhydride modified polyolefin. Suitable polyolefins include polypropylene, polyethylene, ethylene-propylene copolymers, propylene-1-hexene copolymers, and mixtures thereof. We prefer polypropylene and copolymers containing propylene and up to about 50 mole percent of a co-monomer. The anhydride modifier may be at least one of maleic anhydride, citraconic anhydride, itaconic anhydride, glutaconic anhydride, 2,3-dimethyl maleic anhydride, and mixtures thereof. The polyolefin is preferably modified with about 0.5-20 weight percent maleic anhydride, more preferably about 0.5-2 weight percent. We especially prefer polyolefins modified with about 1 weight percent maleic anhydride.
- A suitable anhydride modified polypropylene copolymer resin is sold commercially by Basell North American Inc. under the trade designation Pro-fax PF-711. The polymer has a density of about 0.90 g/cm3.
- Optionally, the polymer web may contain certain additives including dyes, pigment particles, anticorrosion agents, antioxidants, adhesion promoters, light stabilizers, lubricants, and mixtures thereof.
- The polymer coating may be applied to the sheet by any of several techniques, including extrusion coating, slot coating, roll coating, powder coating, laminating, spraying, and electrostatic coating. Extrusion coating is particularly preferred. The polymer coating is preferably extruded onto the metal sheet as a single layer. Alternatively, two or more layers may be coextruded onto the sheet including a tie layer adjacent the metal sheet and one or more overlayers coated over the tie layer. Examples of suitable polymers in the tie layer are anhydride modified polyolefins; ethylene/acrylic acid copolymers such as the copolymers sold by The Dow Chemical Company under the trademark PRIMACOR; and adhesive compositions sold by Rohm & Haas under the trademark MORPRIME. The overlayer preferably comprises a polyolefin, more preferably polypropylene, polyethlene, or a propylene-ethylene copolymer. Other suitable polymers in the overlayer include anhydride modified polyolefins, epoxies, and phenoxies.
- Preferably, both sides of an aluminum alloy sheet are extrusion coated with a polymer coating leaving a thickness of about 0.04-0.5 mils (1-13 microns). A polymer coating having a thickness of about 0.4 mils (10 microns) is particularly preferred for can body interiors.
- The polymer coating on the aluminum-polymer composite is irradiated with an electron beam to improve resistance of the polymer coating to feathering and angel hair formation. The radiation dose is about 2-20 megarads, preferably about 5-15 megarads. Electron beam radiation has the advantage of being applied quickly over a wide area in a short time.
- The irradiated composites are shaped into container bodies and container end panels for food and beverage containers. Container bodies for holding carbonated beverages are shaped by a process in which blanks are cupped, wall ironed, bottom domed, necked, and then flanged. Easy open end panels for carbonated beverages are generally shaped by stamping metal blanks between shaping dies. Electron beam radiation is preferably applied to the polymer coated aluminum sheet. Optionally, radiation may be applied after the composites are shaped into container bodies or container end panels.
- FIG. 1 is a flowsheet diagram of a particularly preferred process of the present invention.
- In accordance with the present invention there is provided an AA5182 aluminum alloy sheet in the H19 temper. The sheet thickness is about 7-14 mils (0.18-0.36 mm) and is preferably about 8.6 mils (0.22 mm).
- The sheet is cleaned with an alkaline surface cleaner if necessary to remove residual surface lubricant, and rinsed. The cleaned sheet is then conversion coated with an aqueous solution containing chromate and phosphate ions, rinsed again, and dried.
- An extrusion coating apparatus of the type shown in Smith et al. U.S. Pat. No. 5,407,702 and Levendusky et al. U.S. Pat. No. 5,919,517 is provided to coat both sides of the aluminum alloy sheet with a polymer coating. The disclosures of both patents are incorporated herein by reference, to the extent consistent with our invention. The metal sheet is heated to a temperature of about 177° C. just prior to coating.
- The extrusion coating apparatus applies to the aluminum sheet a coating of a polypropylene copolymer resin having a thickness of approximately 0.4 mil (10 microns). A particularly preferred polypropylene copolymer is sold by Basell North America under the trade designation Pro-fax PF-711. The copolymer resin has a density of about 0.90 g/cm3.
- The aluminum-polymer composite is cooled (preferably with water) and dried.
- Finally, the polymer coating in the composite is irradiated by an electron beam. A suitable electron beam generator is commercially available from Energy Sciences, Inc. of Wilmingon, Mass. under the trade designation ESI “ELECTROCURE” EB SYSTEM.
- Composite specimens were irradiated by an electron beam so that their Pro-fax PF-711 copolymer coatings received 5, 10 and 15 megarad dosages. All composites exhibited feathering and angel hair formation before irradiation. Angel hair formation was reduced in the 5 and 10 megarad specimens and virtually eliminated in the 15 megarad specimens. Feathering was virtually eliminated by a 10 megarad exposure. For comparison, specimens of the same composite were exposed to various doses of ultraviolet (UV) radiation. The UV radiation did not reduce angel hair formation or feathering at exposures practical for manufacturing purposes.
- Composites made up of AA5182 aluminum alloy sheet coated with polyethylene terephthalate (PET) resin webs were also subjected to 5, 10 and 15 megarad doses of electron beam radiation and various doses of UV radiation. The electron beam radiation had no beneficial effect on feathering or angel hair formation in the aluminum-PET composites at the exposure levels tested. The UV radiation required longer time exposures than practical for manufacturing purposes.
- The foregoing disclosure of our invention has been made with reference to some particularly preferred embodiments. Persons skilled in the art will understand that numerous changes and modifications can be made without departing from the spirit and scope of the following claims.
Claims (18)
1. A process for making a metal-polymer composite suitable for shaping into food and beverage container bodies and container end panels, comprising
a. applying to a metal sheet a polymer coating comprising a polymer selected from the group consisting of polyolefins, anhydride modified polyolefins, epoxies, and phenoxies, thereby to form a metal-polymer composite including a polymer coating, and
b. irradiating the polymer coating on said composite with an electron beam, thereby to improve resistance of said coating to feathering and angel hair formation.
2. The process of claim 1 wherein said metal sheet comprises a metal selected from the group consisting of aluminum alloys, steel, aluminum alloy-coated steel, and aluminum-coated steel.
3. The process of claim 1 wherein said metal sheet comprises an aluminum alloy of the AA3000 or AA5000 series.
4. The process of claim 1 wherein said polymer comprises a polyolefin selected from the group consisting of polypropylene, polyethylene, propylene-ethylene copolymers, propylene-1-hexene copolymers, and mixtures thereof.
5. The process of claim 1 wherein said polymer comprises a polyolefin selected from the group consisting of polypropylene and copolymers comprising propylene and up to about 50 mole percent of a co-monomer.
6. The process of claim 1 wherein said polymer comprises a polyolefin modified with an anhydride selected from the group consisting of maleic anhydride, citraconic anhydride, itaconic anhydride, glutaconic anhydride, 2,3-dimethylmaleic anhydride, and mixtures theeof.
7. The process of claim 1 wherein said polymer comprises a polyolefin modified with about 0.5-20 weight percent maleic anhydride, based on the weight of the polyolefin.
8. The process of claim 1 wherein the step of applying the polymer coating to the metal sheet comprises extrusion coating, roll coating, or laminating.
9. The process of claim 1 wherein the step of irradiating comprises irradiating at a dosage of about 2-20 megarads.
10. The process of claim 1 further comprising
c. shaping said composite into a container body or container end panel.
11. The process of claim 10 wherein step b. is performed before step c.
12. The process of claim 10 wherein step b. is peformed after step c.
13. The process of claim 1 further comprising
d. before step a., conversion coating a surface portion of said metal sheet.
14. A process for making an aluminum-polymer composite suitable for shaping into container end panels having improved resistance to feathering and angel hair formation, comprising
a. applying to an aluminum alloy sheet a polymer coating comprising a maleic anhydride modified polyolefin, said polyolefin being selected from the group consisting of polypropylene and copolymers comprising propylene and up to about 50 mole percent of a co-monomer, thereby to form an aluminum-polymer composite, and
b. irradiating the polymer coating on said composite with an electron beam.
15. An aluminum-polymer composite made by the process of claim 14 .
16. A container end panel shaped from the composite of claim 15 .
17. An aluminum-polymer composite comprising
a. an aluminum alloy sheet having a thickness of about 7-14 mils, and
b. a polymer coating adhered to said sheet, said polymer coating having a thickness of less than about 1 mil, said polymer coating comprising an anhydride modified polyolefin, said polyolefin being selected from the group consisting of polypropylene, polethylene, and copolymers comprising propylene and up to about 50 mole perecent of a co-monomer, said polymer coating being irradiated with an electron beam.
18. A container end panel shaped from the composite of claim 17.