US20020166844A1 - Room-temperature surface weld repair of nickel-base superalloys having a nil-ductility range - Google Patents
Room-temperature surface weld repair of nickel-base superalloys having a nil-ductility range Download PDFInfo
- Publication number
- US20020166844A1 US20020166844A1 US09/850,895 US85089501A US2002166844A1 US 20020166844 A1 US20020166844 A1 US 20020166844A1 US 85089501 A US85089501 A US 85089501A US 2002166844 A1 US2002166844 A1 US 2002166844A1
- Authority
- US
- United States
- Prior art keywords
- percent
- article
- maximum
- nickel
- cobalt
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
- The invention herein described was made in the course of or under a contract or subcontract thereunder (or grant) with the Department of the Navy.
- This invention relates to the weld repair of surface defects in alloys, and more particularly to such repairs conducted on cast nickel-base superalloys having a nil-ductility range.
- Nickel-base alloys contain more nickel than any other element, plus alloying elements that are added to improve the mechanical and physical properties of the alloy. Nickel-base superalloys are nickel-base alloys that are strengthened by precipitation of gamma prime and/or a related phase. These materials are used in aircraft gas turbine components and other applications which require good strength, creep resistance, fracture toughness, and other mechanical properties at elevated temperatures such as 1500° F. and higher for extended periods of time.
- The selection of the types and amounts of alloying elements present in the alloy, in combination with the thermal processing, determines to a large degree the properties of the alloy. In some cases, the nickel-base superalloy is moderately strong and moderately ductile, even at high temperatures. In other cases, the combination of alloying elements causes the material to be very strong but of limited ductility even at temperatures approaching the melting point, a temperature at which many alloys become highly ductile.
- In one class of nickel-base superalloys, the alloy has very small, substantially no (nil), ductility in the temperature range between the solidus (freezing) temperature of the alloy and a temperature about 600° F. below the solidus temperature. This behavior plays a significant role in the properties of the alloy, because as the alloy is cooled through this range, or is processed or operated while in this range, the material is highly susceptible to the formation of cracks and other defects which remain in the structure upon cooling to room temperature and during service. Such cracks can also occur later in the processing, as for example in the formation of hot tears during welding and post-weld heat treatments. Examples of such nickel-base superalloys having a “nil-ductility range” are Rene 108 and Mar-M246.
- Articles made of nickel-base superalloys are usually cast from the melt into a mold, with investment casting being the most popular approach, and then further processed. The as-cast articles sometimes have near-surface defects such as hot tears, surface-connected porosity due to shrinkage defects, and near-surface inclusions, which are acute problems for the alloys having a nil-ductility range. These near-surface defects are deleterious to the properties of the article, either directly or by preventing the closure of interior porosity and shrinkage cavities during subsequent processing.
- If the surface defects are not too severe, as is often the case, they may be repaired. However, earlier repair techniques involving welding procedures are not fully successful in removing the near-surface defects, particularly for the nickel-base superalloys with a nil-ductility range. It is often the case that the repair procedure itself leads to even further defects, which in turn must be repaired. The repair procedures are accordingly very labor intensive, time consuming, and expensive. They also result in products which may have reduced properties at the location of the repair.
- An important advance in welding repair procedures was disclosed in U.S. Pat. No. 5,897,801. In this approach, the weld repair is performed with the article heated to an elevated temperature and in a controlled atmosphere. The approach works quite well for many applications. If the article is large in size, the required controlled-atmosphere heating oven is also quite large and involves a large capital expenditure. The repair cost for each article is relatively high, due to the use of the controlled-atmosphere heating oven, the long cycle time for each article, and the skill required.
- There is accordingly a need for an improved technique for repairing near-surface defects in articles made of nickel-base superalloys having a nil-ductility range at elevated temperature, which achieves good results yet is less expensive than the approach of the '801 patent. The present invention fulfills this need, and further provides related advantages.
- The present invention provides a method for weld repairing a nickel-base superalloy article having a nil-ductility range. It is suitable for repairing relatively small near-surface defects, such as small surface cracks, small near-surface pits, and near-surface inclusions such as small ceramic particles. These small near-surface defects are often the cause of the rejection of castings of nil-ductility-range nickel-base superalloys. The present approach allows the repair of these smaller defects at room temperature and without generally heating the body of the article to elevated temperature, so that the repair operation may proceed much more rapidly than does the approach of the '801 patent. The approach of the '801 remains the preferred technique for repairing larger defects and for joining articles made of the nil-ductility-range nickel-base superalloys.
- A method of weld repairing a nickel-base superalloy article having a nil-ductility range from a solidus temperature of the superalloy to about 600° F. below the solidus temperature comprises the steps of furnishing the article of such a composition and having a body with a near-surface defect near a surface thereof, and providing a heat source having a heat source beam with an amperage of no greater than about 5 amperes. The diameter of the heat source beam is preferably no greater than about 0.025 inches. Examples of suitable nickel-base superalloys having a nil-ductility range include R108, Mar M-246, AF2-1DA, Udimet 500, B1900, and Udimet 700. The article may be in any form, but is typically in an as-cast state. The heat source is preferably a plasma welding torch. Examples of near-surface defects are pits, cracks, and solid inclusions such as embedded ceramic particles.
- The method further includes weld repairing the near-surface defect, the step of weld repairing including the steps of locally melting the surface of the article in a region of the near-surface defect using the heat source to form a melted region, while not otherwise heating the body of the article, and thereafter allowing the melted region to solidify. The melted region preferably has a molten pool depth of no greater than about 0.030 inch, more preferably no greater than about 0.020 inch, and most preferably no greater than about 0.010 inch. The melted region is thereafter allowed to solidify.
- The repair may be accomplished either by heating and melting the region of the near-surface defect without the addition of a filler metal, or by adding a filler metal into the melted region. The filler metal, where used, typically has a filler metal composition that is substantially the same as that of the nickel-base superalloy of the article.
- The present approach utilizes a small, narrowly focused, low-power heat source such as a small plasma welding torch or a laser. The heat source melts only a small depth at and below the surface of the article. The portions of the article that are further from the surface are not substantially affected by the welding process. Accordingly, there is reduced concern that hot tears and strain-age cracking in a heat affected zone (HAZ) will affect the body. The present approach has the important advantage that it is accomplished at ambient temperature without heating the body of the article and does not require the use of a special atmosphere. The processing is therefore much faster and uses less capital equipment than required for the approach of the '801 patent, although the present approach is more limited in the types of defects that may be repaired than is the approach of the '801 patent. For example, the present approach is not concerned with blade-tip and other larger-size weld repairs.
- Other features and advantages of the present invention will be apparent from the following more detailed description of the preferred embodiment, taken in conjunction with the accompanying drawings, which illustrate, by way of example, the principles of the invention. The scope of the invention is not, however, limited to this preferred embodiment.
- FIG. 1 is an article made of a cast nickel-base superalloy having a nil-ductility range;
- FIG. 2 is an enlarged sectional view through the casting of FIG. 1 prior to repair, taken on line2-2;
- FIG. 3 is a block diagram of a process for repairing the article of FIG. 1;
- FIG. 4 is a schematic view of a weld repair apparatus having a heat source, in relation to the casting during the repair procedure;
- FIG. 5 is an enlarged detail of FIG. 4 during the repair procedure; and
- FIG. 6 is a view like that of FIG. 2, after weld repair is complete.
- FIG. 1 depicts an
article 20 made of a cast nickel-base superalloy having a nil-ductility range from a solidus temperature of the superalloy to about 600° F. below the solidus temperature. Thearticle 20 is typically a casting in the as-cast form, but the invention is not so limited and may be used on other types hof articles. Examples of castings of interest used in aircraft gas turbine engines include fairings for the GE 414 engine. - As seen in FIG. 2, the
article 20 has abody 22 with at least one near-surface defect 24 therein. The near-surface defect 24 is at or near asurface 26 of thebody 22. Some exemplary near-surface defects 24 illustrated in FIG. 2 include asmall pit 28, asmall crack 30, andsolid inclusions 32 of foreign matter such as small ceramic particles embedded into or slightly below thesurface 26. These near-surface defects 24 result from the casting operation. Although care is taken during the casting operation to minimize the incidence of such near-surface defects, they cannot be completely avoided in any commercial-scale casting plant. - The near-
surface defects 24, if located at critical areas of thearticle 20, may lead to the rejection of the article as unsuitable for its intended purpose. The present invention is concerned with removing the near-surface defects 24 without the necessity of heating thearticle 20 to high temperature as required by the approach of U.S. Pat. No. 5,897,801. - FIG. 3 depicts a preferred approach for practicing the invention. The
article 20 is furnished, numeral 40. The article is made of the nickel-base superalloy having a nil-ductility range from the solidus temperature of the superalloy to about 600° F. below the solidus temperature. Examples of such nickel-base superalloys include, but are not limited to, a composition in weight percent selected from the group consisting of R108, having a nominal composition of 0.07-0.10 percent carbon, 8.0-8.7 percent chromium, 9.0-10.0 percent cobalt, 0.4-0.6 percent molybdenum, 9.3-9.7 percent tungsten, 2.5-3.3 percent tantalum, 0.6-0.9 percent titanium, 5.25-5.75 percent aluminum, 0.01-0.02 percent boron, 1.3-1.7 percent hafnium, 0.1 percent maximum manganese, 0.06 percent maximum silicon, 0.01 percent maximum phosphorus, 0.004 percent maximum sulfur, 0.005-0.02 percent zirconium, 0.1 percent maximum niobium, 0.1 percent maximum vanadium, 0.1 percent maximum copper, 0.2 percent maximum iron, 0.003 percent maximum magnesium, 0.002 percent maximum oxygen, 0.002 percent maximum nitrogen, balance nickel and incidental impurities; Mar M-246, having a nominal composition of 9 percent chromium, 10.0 percent cobalt, 0.7 percent molybdenum, 10.0 percent tungsten, 1.0 percent titanium, 5.5 percent aluminum, 0.5 percent maximum iron, 0.15 percent carbon, 0.015 percent boron, 0.05 percent zirconium, 1.5 percent hafnium, 1.5 percent tantalum, balance nickel and incidental impurities; Mar M-200, having a nominal composition of 0.15 percent carbon, 9 percent chromium, 10 percent cobalt, 1 percent iron, 5 percent aluminum, 0.015 percent boron, 2 percent titanium, 12.5 percent tungsten, 0.05 percent zirconium, 1 percent niobium, balance nickel and incidental impurities; AF2-1DA, having a nominal composition of 0.35 percent carbon, 12 percent chromium, 10 percent cobalt, 3 percent molybdenum, 0.5 percent maximum iron, 4.6 percent aluminum, 0.015 percent boron, 3 percent titanium, 6 percent tungsten, 0.1 percent zirconium, 1.5 percent tantalum, balance nickel and incidental impurities; Udimet 500, having a nominal composition of 0.1 percent carbon, 18 percent chromium, 17 percent cobalt, 4 percent molybdenum, 2 percent iron, 3 percent aluminum, 3 percent titanium, balance nickel and incidental impurities; B 1900, having a nominal composition of 0.1 percent carbon, 8 percent chromium, 10 percent cobalt, 6 percent molybdenum, 6 percent aluminum, 0.015 percent boron, 1 percent titanium, 0.1 percent zirconium, 4 percent tantalum, balance nickel and incidental impurities; Inconel 100, having a nominal composition of 0.18 percent carbon, 9.5 percent chromium, 15 percent cobalt, 3 percent molybdenum, 5.5 percent aluminum, 0.015 percent boron, 4.2 percent titanium, 0.06 percent zirconium, 1 percent vanadium, balance nickel and incidental impurities; Udimet 700, having a nominal composition of 0.1 percent carbon, 15 percent chromium, 18.5 percent cobalt, 5.25 percent molybdenum, 4.25 percent aluminum, 0.03 percent boron, 3.5 percent titanium, balance nickel and incidental impurities; and Rene 80, having a nominal composition of 0.17 percent carbon, 14 percent chromium, 9.5 percent cobalt, 4 percent molybdenum, 3 percent aluminum, 0.015 percent boron, 5 percent titanium, 4 percent tungsten, 0.03 percent zirconium, balance nickel and incidental impurities. - A
heat source 60 is provided to effect the weld repairs, numeral 42. Theheat source 60 produces a highly directed, tightly confined, relatively low-power heating beam. Apreferred heat source 60 is aplasma welder 62 as shown in Figure 4. Theplasma welder 62 includes aplasma welding torch 64 into which a plasma-gas flow 66 of a plasma gas such as argon is introduced. The power for the plasma welding torch is provided by apower supply 68. Theheat source 60 may be of other operable types, such as a laser. - The
heat source 60 is of a relatively low power. Preferably, theheat source 60 has aheat source beam 72 with a power level of no greater than about 5 amperes. The voltage is not critical, but typically is in the range of from about 15 to about 75 volts. Similarly, a diameter DB as it leaves theheat source 60 of theheat source beam 72 is no greater than about 0.025 inch, although thebeam 72 may spread somewhat after it leaves theheat source 60. The result is that, as shown in FIG. 5, a molten pool depth DMP of a meltedregion 74 extending below thesurface 26 of thearticle 20 is no greater than about 0.030 inch, more preferably no greater than about 0.020 inch, and most preferably no greater than about 0.010 inch. The molten pool depth DMP produced during welding may be readily determined after welding is complete by observing the microstructure of the final repaired article. The microstructure in the region that was melted as the meltedregion 74 during weld repair differs from that of the remainder of the article, generally by exhibiting a finer-scale structure resulting from the faster cooling at the end of the weld repair. - The low power level and small diameter of the
heat source beam 72, and the small depth and lateral extent of the meltedregion 74 are important features of the invention. The nickel-base superalloys having a nil-ductility range are susceptible to cracking due to differential thermal strains produced between the surface regions and the deeper regions. They are additionally susceptible to liquation cracking and resulting hot tears at the grain boundaries, in the heat affected zone upon cooling after welding. Both of these damage mechanisms are dependent upon the depth of the meltedregion 74 and the consequent size of the heat affected zone. By restricting the power level and diameter of theheat source beam 72, the depth DMP of the meltedregion 74 is small. The volume change on solidification is typically about 3 percent. For a melted region having a scale of about 0.030 inch, the preferred maximum value of DMP, the length change upon solidification is on the order of 0.0009 inch, which can be accommodated by the heat-affected zone without producing cracking or other defects. Significantly larger melted regions would produce larger length changes that could not be accommodated by the heat-affected zone. A maximum depth DMP of the meltedregion 74 of less than about 0.020 inch is even more preferred, and a maximum depth DMP of the meltedregion 74 of less than about 0.010 inch is most preferred. These smaller values of DMP result in even lower strains and stresses upon cooling, with less residual stress. However, the depth of the meltedregion 74 must be sufficiently great to remove the near-surface defect 24, up to the maximum permitted depth. Larger defects are not repairable by this approach. - The result is that the weld repair of relatively small near-surface defects is accomplished without heating the
body 22 of thearticle 20, except as it may be heated incidentally from theheat source beam 72. Even that incidental heating is relatively small for a large-size article 20, because of the low power level of theheat source beam 72. Thus, if the power level, diameter, and/or depth of the melted region are too large, the present approach will not be operable. - The weld repair may be accomplished strictly by melting a region at the
surface 26 of thearticle 20. The weld repair may optionally include aflow 70 of a filler metal which is introduced into theplasma welding torch 64, at least partially melted in the plasma, and thence fed into the meltedregion 74 that is melted by the plasma. The filler metal may be in powder or wire form, or other physically suitable form. The filler metal, when used, desirably has a filler metal composition that is substantially the same as that of the nickel-base superalloy of the article. - Returning to the discussion of FIG. 3, the near-
surface defect 24 is weld repaired, numeral 44. The step of weld repairing 44 includes locally melting 46 the surface of thearticle 20 in a region of the near-surface defect 24 using theheat source 60 to form the meltedregion 74. Thebody 22 of thearticle 20 is not otherwise heated. Thebody 22 experiences some slight incidental heating due to the heat conducted from the melted region. To effect the local heating without adversely affecting neighboring regions and to prevent the meltedregion 74 from becoming too large, it may be desirable to provide run-outtabs 76 on thesurface 26 at the sides of the intended meltedregion 74 of a material of higher melting point than thearticle 20. The run-outtabs 76 permit the heating by theheat source 60 to be initiated and terminated away from the meltedregion 74. - During the
local melting step 46 as seen in FIG. 5, the meltedregion 74 extends downwardly from the surface 26 a depth of no more than DMP. The depth DMP is greater than the size of the near-surface pits 28 and near-surface cracks 30. Upon melting, the near-surface pits 28 and near-surface cracks 30 are closed by the melted metal. The depth DMP is greater than the depth to which near-surface inclusions 32 extend, so that theinclusions 32 float upwardly through the melted metal to the surface. The effectiveness of the present approach is therefore limited to repairs of near-surface defects 24 that do not extend further into thearticle 20 than the depth DMP. The present approach is therefore not intended to be of general applicability, unlike the approach of U.S. Pat. No. 5,897,801. For example, many blade tip repairs, leading-edge repairs, and trailing-edge repairs for damage to airfoils are not repairable by the present approach because the required melted depth is too large, and the present approach is not suitable for the joining of two separate articles by welding. On the other hand, the present approach is much faster and less expensive when used to repair the near-surface defects to which it is applicable, because the entire article need not be heated to elevated temperature and because it is not necessary to use a controlled-atmosphere chamber to protect the area being repaired. - After the
local melting 46 that effects the weld repair, the meltedregion 74 is allowed to cool and solidify, numeral 48. - FIG. 6 depicts the
article 20 at this point after completion of the weld repair. The near-surface pits 28 and near-surface cracks 30 have been removed from repairedregions 78 through the local melting process, and are now depicted by dashed lines to indicate their prior positions.Ceramic particles 80, which were previously theinclusions 32 below thesurface 26 prior to repair (FIG. 2), have floated to the surface of the melted region and can be easily removed. As discussed earlier, it may be necessary to feed filler material into the molten region in each case during the weld repair, if removal of the near-surface defect 24 would result in too-large of a depression at the repaired surface of the article. - Although a particular embodiment of the invention has been described in detail for purposes of illustration, various modifications and enhancements may be made without departing from the spirit and scope of the invention. Accordingly, the invention is not to be limited except as by the appended claims.
Claims (17)