US20010052660A1 - Method for reducing dilation balloon cone stiffness - Google Patents
Method for reducing dilation balloon cone stiffness Download PDFInfo
- Publication number
- US20010052660A1 US20010052660A1 US09/907,989 US90798901A US2001052660A1 US 20010052660 A1 US20010052660 A1 US 20010052660A1 US 90798901 A US90798901 A US 90798901A US 2001052660 A1 US2001052660 A1 US 2001052660A1
- Authority
- US
- United States
- Prior art keywords
- mold
- balloon
- parison
- stretch
- polymeric composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
- I. Field of the Invention
- The present invention relates to dilatation balloon catheters of the type employed in percutaneous transluminal angioplasty procedures, and more particularly to a method of molding such balloons to reduce their cone stiffness and thereby improve the maneuverability in smaller and more tortious passages of the vascular system.
- II. Discussion of the Prior Art
- Dilatation balloon catheters are well known for their utility in treating the build-up of plaque and other occlusions in blood vessels. Typically, a catheter is used to carry a dilatation balloon to a treatment site, where fluid under pressure is supplied to the balloon, to expand the balloon against a stenotic lesion.
- The dilatation balloon is affixed to an elongated flexible tubular catheter proximate its distal end region. When the balloon is expanded, its working length, i.e., its medial section, exhibits a diameter substantially larger than that of the catheter body on which it is mounted. The proximal and distal shafts or stems of the balloon have diameters substantially equal to the diameter of the catheter body. Proximal and distal tapered sections, referred to herein as “cones”, join the medial section to the proximal and distal shafts, respectively. Each cone diverges in the direction toward the medial section. Fusion bonds between the proximal and distal balloon shafts and the catheter form a fluid-tight seal to facilitate dilation of the balloon when a fluid under pressure is introduced into it, via an inflation port formed through the wall of the catheter and in fluid communication with the inflation lumen of the catheter.
- Along with body tissue compatibility, primary attributes considered in the design and fabrication of dilation balloons are their strength and pliability. A higher hoop strength or burst pressure reduces the risk of accidental rupture of the balloon during dilation. Pliability refers to formability into different shapes, rather than elasticity. In particular, when delivered by the catheter, the dilatation balloon is evacuated, flattened and generally wrapped circumferentially about the catheter in its distal region. Thin, pliable dilatation balloon walls facilitate a tighter wrap that minimizes the combined diameter of the catheter and the balloon during delivery. Furthermore, pliable balloon walls enhance the catheter “trackability” in the distal region, i.e., the ability of the catheter to bend in conforming to the curvature in vascular passages through which it must be routed in reaching a particular treatment site.
- One method of forming strong, pliable dilatation balloons of polyethylene terrathalate (PET) is disclosed in U.S. Pat. No. RE. 33,561 (Levy). A tubular parison of PET is heated at least to its second order transition temperature, then drawn to at least triple its original length to axially orient the tubing. The axially expanded tubing is then radially expanded within a heated mold to a diameter about triple the original diameter of the tubing. The form of the mold defines the aforementioned medial section, shafts and cones, and the resulting balloon has a burst pressure greater than 200 psi.
- Such balloons generally have a gradient in wall thickness along the cones. In particular, larger dilatation balloons, e.g., 3.0-4.0 mm diameter (expanded) tend to have a wall thickness in the working length in the range of from 0.010 to 0.020 mm. Near the transition of the cones with the working length or medial section, the cones have approximately the same wall thickness. However, the wall thickness diverges in the direction away from the working length, until the wall thickness near the proximal and distal shafts is in the range of 0.025 to 0.040 mm near the associated shaft or stem.
- The increased wall thickness near the stems does not contribute to balloon hoop strength, which is determined by the wall thickness along the balloon medial region. Thicker walls near the stems are found to reduce maneuverability of the balloon and catheter through a tortious path. Moreover, the dilatation balloon cannot be as tightly wrapped about the catheter shaft, meaning its delivery profile is larger and limiting the capacity of the catheter and balloon for treating occlusions in smaller blood vessels.
- U.S. Pat. No. 4,963,133 (Noddin) discloses an alternative approach to forming a PET dilation balloon, in which a length of PET tubing comprising the parison is heated locally at opposite ends and subjected to axial drawing to form two “necked-down” portions, which eventually become the opposite ends of the completed balloon. The necked-down tubing is then simultaneously axially drawn and radially expanded with a gas. The degree to which the tubing ends had been necked-down is said to provide control over the ultimate wall thickness along the walls defining the cones. However, it is believed that the use of the Noddin method results in balloons exhibiting a comparatively low burst pressure.
- Copending application Ser. No. 08/582,371, filed Jan. 11, 1996, describes a method for reducing cone stiffness by using a laser to ablate and remove polymeric material from the cone areas after the balloon is blown. It is preferable that the desired result be obtained during the balloon molding operations obviating the need for additional post molding operations.
- Therefore, it is an object of the present invention to provide a method for stretch blow molding dilatation balloon having a high burst pressure and hoop strength, but with reduced material mass in the balloon cones, thus reducing cone stiffness and improving the trackability, crossing profile, stenosis recross and balloon retrieval, via a guiding catheter.
- To achieve these and other objects of the invention, there is provided a method of making dilatation balloons with reduced cone stiffness. The method comprises the steps of first providing a mold having a cavity including a cylindrical center segment defining a working length of a dilatation balloon body where the center segment is of a predetermined diameter. The mold cavity also includes two opposed end segments, each having an arcuate cone shape tapering from the predetermined diameter of the center segment to a smaller desired balloon shaft diameter. The side edges of the mold are dimensioned to be within about 0.05 in. of the termination point of the arcuate cone at the smaller desired balloon shaft diameter.
- Next, a tubular polymeric parison of a predetermined diameter and wall thickness is placed with a mold and the parison has the opposed ends thereof extending beyond the side edges of the mold, the opposed ends being clamped in a tensioning fixture. The mold is heated to bring the temperature of the parison near or above the glass transition temperature of the polymeric material comprising the parison. The tensioning fixture is then longitudinally displaced relative to the mold to initially longitudinally stretch the parison by a predetermined amount to introduce a degree of longitudinal orientation and to neck down the tubular parison to a lesser diameter.
- Following this initial longitudinal stretch, a second longitudinal stretching operation is initiated and as the tensioning fixture is being moved to achieve a second stretch, a gas is injected into the tubular parison to radially expand the parison to a limit defined by the mold cavity. At this point, the wall thickness in the working length of the balloon and in its cones is a function of the degree of longitudinal and radial stretching as well as the gas pressure applied to effect the radial expansion.
- Following inflation of the balloon within the mold, a third longitudinal stretch is performed by further displacing the tensioning fixtures relative to the mold. It is the third stretch within the above-described mold that is found to remove material from the cone area as the tubing is drawn down to a desired size for a catheter shaft. Removal of material from the cone area renders them more pliable than balloons prepared in the same way but not subjected to longitudinal stretching following the radial expansion of the balloon within the mold. The third stretch also creates an increased number of nucleation sites for crystallization to occur.
- After the third stretch operation is terminated, the temperature of the mold is increased such that the biaxially oriented balloon reaches its crystallizing temperature for effectively locking the molecular structure in place.
- Following crystallization, the mold is cooled below the glass transition temperature of the polymer so that the crystallization structure of the balloon is not lost. Once the mold has sufficiently cooled, it can be opened and the balloon removed.
- FIG. 1 is a top elevational schematic view of the equipment used in carrying out the method of the present invention;
- FIG. 2 is an enlarged view of one of the jaws of the mold showing the desired profile of the mold cavity used in preparing dilatation balloons having reduced cone stiffness;
- FIG. 3 is a drawing helpful in understanding the manner in which the mold cavity shape is arrived at; and
- FIG. 4 is a flow chart of the steps employed in preparing dilatation balloons exhibiting reduced cone stiffness.
- Referring to FIG. 1, there is illustrated schematically the apparatus for stretch blow molding dilatation balloons for later assembly on to catheter body stock in the fabrication of dilatation balloon catheters. The mold itself is indicated generally by
numeral 10 and comprises first and second mold halves 12 and 14 which when abutting one another at aparting line 16 define aninternal mold cavity 18. The mold halves or jaws can be open or spread apart to allow placement of a tubular parison therein. The opposed ends of theparison jaws 26 which are mounted onrails - As those skilled in the art appreciate, the
mold 10 incorporates heating elements (not shown) and appropriately positioned temperature sensors for monitoring the mold temperature and sending temperature information back to a microprocessor-based controller for maintaining precise closed-loop control of the temperature of the mold and of the parison contained in it. Likewise, a suitable linear encoder (not shown) is operatively coupled to the translatable clampingfixtures 26 to provide positional information to the microprocessor-based controller whereby the degree of longitudinal stretch imparted to theparison 20 can be precisely controlled. - The equipment for stretch blow molding shown in FIG. 1 also includes a means for introducing a
gas 32, under pressure, into the lumen of thetubular parison 20 and for monitoring and controlling that pressure again, using closed-loop control. - Except for the
mold cavity 18 formed in the mold halves 12 and 14, the equipment used in carrying out the method of the present invention is altogether conventional. The mold cavity employed is unique, as is the operation whereby the cone segments of the balloons to be formed in it are made to contain less material than in conventional designs. - FIG. 2 is a view looking at the interior of one of the
jaws mold cavity 18. - The portion of the balloon between the dashed construction lines A-A define the working length of a dilatation balloon formed therein and this portion of the balloon is generally cylindrical. The portion of the mold between construction lines A and B form the cones and, as can be seen from FIG. 2, the cones do not have a linear taper. They are slightly arcuate in the zone between the construction lines A and B. The portion of the mold between the construction lines B and C will ultimately comprise the shaft portion of the balloon formed in the
mold cavity 18. - The following table sets out typical mold dimensions in stretch blow-molding a dilatation balloon having a working length of 20 mm and an expanded diameter of 4.0 mm. These dimensions are illustrative only because the various dimensions change depending upon the size of the balloon to be formed.
TABLE I Dimension Magnitude (Inches) A-A .763 B-B 1.532 C-C 1.557 B-C .025 A-B .372 R1 .832 R2 1.010 - With reference to FIG. 3, for any size balloon diameter, the radiused balloon ends of the mold are designed using the following graphical construction technique:
- 1. The
horizontal centerline 32 for the mold is first established. - 2.
Construction lines 34 above and below thehorizontal center line 32 are established to define the desired balloon diameter. - 3.
Construction lines 36 above and below the center line establish the desired balloon shaft diameters for both the proximal and distal ends. - 4. The
vertical center line 38 for the mold is set. - 5.
Lines vertical center line 38. - 6.
Construction lines 42 are created at the points of intersections oflines lines 42 form a desired angle with respect toline 36. An angle of 12° is typical. Each oflines 42 should cross thehorizontal center line 32 of the mold.Construction lines 42 determine the length of the end of the balloon. - 7.
Construction line 44 is created at the intersection oflines Construction line 44 indicates the boundary for the end of the balloon and the transition to the balloon shaft. - 8.
Arcs 46 are next constructed.Arc 46 is a three point arc, and it should pass through the intersection oflines lines arcs 46 should be chosen so that they are tangent to line 34 at the intersection oflines - 9.
Construction lines 42 can now be erased and the portion of thearcs 46 to the left (outside) ofconstruction line 44 can also be erased. - 10. Displace
construction line 44 to the left by 0.025 in. to 0.25 in. establish the left end of the mold which is depicted in FIG. 13 byconstruction line 48. - 11. The
lines 36 to the right (inside) ofconstruction line 44 and to the left (outside) ofconstruction line 48 are trimmed to form the short land of the mold. - 12.
Construction line 44 can now be erased andlines 34 trimmed to the left (outside) ofline 40 of the left half of the mold. - 13. The foregoing construction steps are then repeated for the right side of the mold to form the other balloon end.
- As will be explained in further detail hereinbelow, by providing the arcuate cone segments and the short cylindrical shaft segments (dimension B-C in Table I), it is possible to remove polymeric material from the cone portions of the mold by providing a third stretch to the parison following inflation of the parison to achieve radial orientation.
- Using the mold created using the techniques outlined above in the apparatus of FIG. 1, dilatation balloons exhibiting a reduced cone thickness as compared to prior art stretch blow molding operations can be achieved. Referring to FIG. 4, there is illustrated a flow chart of the steps used to prepare such improved dilatation balloons. In carrying out the method, a precut length of a suitable tubular parison is placed in the mold so as to span the mold cavity in the longitudinal direction. The opposed ends of the parison are clamped by the tensioning
member 26. The mold is partially closed about thetubular parison 20 and a gas at a relatively low pressure is introduced into the lumen of the parison and a slight tension is applied to eliminate sagging of the parison when subsequently heated. - Following this initial setup and pretensioning, the
mold 10 is heated up to a desired temperature which depends upon the thermoplastic material involved. Generally speaking, the mold is heated to a temperature which is above the glass transition temperature. For PET, the mold may typically be heated to 175°. Once this temperature is reached, the molding operation can be begin. - The parison is subjected to a first stretching operation to initiate longitudinal orientation in the plastic. The degree of stretch varies with the tube size (wall thickness) and the tube material. This first stretch which for a PET parison may be in the range of ¼ in. to 1-½ in. at each end thereof, not only results in some longitudinal orientation, but it also necks down the original tubing comprising the parison to a smaller diameter.
- After the prestretch (first stretch), the mold is completely closed and a second longitudinal stretch is initiated. During the time that the second stretch is occurring, the balloon is fully inflated by injected an inert, dry gas, e.g., nitrogen, under relatively high pressure into the lumen of the parison to thereby radially expand the parison to fill the mold. The gas pressure depends on tubing thickness and the desired wall thickness of the resulting balloon but will typically be in the range of from 50 psi to about 400 psi. The wall thickness of the resulting balloon is a function of both the longitudinal stretch and the radial stretch employed. There is also an interaction between the pressure and the degree of longitudinal stretch on the thickness of the resulting balloon wall. Generally speaking, the higher the pressure, the less the wall is thinned by the longitudinal stretching.
- With continued reference to the flow chart of FIG. 4, following inflation of the balloon and while the balloon is still subjected to the pressure of the inflation gas, the parison is longitudinally stretched a third time. Because of the arcuate shape of the mold in the zone thereof defining the end cones and because of the short dimension B-C (FIG. 2 and Table I), the third longitudinal stretch is effective to remove material from the cone area of the balloon and to simultaneously draw the tubing down to a desired size thereby providing a thinner shaft portion for later attachment to the catheter body.
- Defining the stretch ratio as the ratio of the length after the stretch divided by the length prior to the stretch, for a PET polymer the first stretch ratio may be in the range of from 1.005 to 2.0, that for the second stretch in the range of from 1.05 to 3.0 and for the third stretch in the range of from 1.1 to 4.0.
- Following the third stretch operation, the temperature of the mold is increased to the crystallizing temperature of the polymer employed to effectively “freeze” the molecular structure resulting from the longitudinal and radial orientation in place. The crystallizing step takes place with the balloon pressurized to the same inflation pressure earlier applied during the balloon inflation step. This helps to ensure that the balloon walls in the working area will remain at the same thickness after the third longitudinal stretch and subsequent crystallizing.
- The mold can now be cooled down back below the glass transition temperature for the polymer and, following that, the mold can be opened and the clamps released. The portion of the parison outside of the mold is then trimmed off and the balloon is ready to be mounted on a catheter body.
- Comparative tests were run on balloons prepared in accordance with the method of FIG. 4 when using a mold having a profile like that of FIG. 2 with balloons fabricated using a prior art “two stretch” molding process having all of the steps of FIG. 4 except the third stretch following balloon inflation and in a mold that had linear (rather than arcuate) cone profiles. These specific parameters that were compared were derived by advancing a plurality of dilatation catheters having balloons manufactured in accordance with the method of the present invention and balloons manufactured in accordance with the described prior art through a test fixture. The test fixture had a tortuous path and located at differing spots within the tortuous path were a Palmez-Schatz stent and a Wallstent® Endoprosthesis. The purpose of this test was to evaluate the forces required to push the catheter through the fixture and the ability of the catheter to pass through each of the stents without getting caught by the stent's structure. The average force that was required to pass the conventional catheter through the test fixture was 695.9 grams. This is to be compared with 390.5 grams required to be applied to the catheters having balloons made in accordance with the present invention to traverse the same test fixture. This represents approximately a 44 percent reduction in tracking force.
- A further test was conducted to assess the force required to re-cross a stenosis following balloon inflation. Balloons made in accordance with the method of the present invention in the mold cavity made as described herein showed an approximate decrease of 18 percent in the stenosis recross force when compared to balloons molded in the conventional “two stretch” process.
- Testing further revealed that the balloons molded with the “three stretch” process of the present invention required the lowest force to withdraw the balloon catheter through a guiding catheter. The force to withdraw the balloons prepared in the three stretch process was about 28% less than the force necessary to withdraw balloons made using the prior art two stretch process.
- Balloons made in accordance with the three stretch process of the present invention were able to be guided through the stent blocks. The conventional balloons made using the two stretch process were not capable of being pushed through the stents, even with considerable effort.
- The improved performance of dilatation balloons made in accordance with the present invention is believed to be due to the extraction of material from the cone areas of the balloon taking place during the third stretch. The process of the present invention produces a high degree of molecular orientation, yielding balloons with high strength and simultaneously a reduced balloon wall thickness, balloon cone thickness and balloon shaft diameter. This eliminates the need for subsequent balloon processing following the balloon blowing operation.
Claims (11)