US20010051250A1 - Honeycomb structure and method of manufacturing honeycomb structures - Google Patents

Honeycomb structure and method of manufacturing honeycomb structures Download PDF

Info

Publication number
US20010051250A1
US20010051250A1 US09/316,779 US31677999A US2001051250A1 US 20010051250 A1 US20010051250 A1 US 20010051250A1 US 31677999 A US31677999 A US 31677999A US 2001051250 A1 US2001051250 A1 US 2001051250A1
Authority
US
United States
Prior art keywords
foils
honeycomb structure
separating layer
bonding
stack
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
US09/316,779
Other versions
US6383601B2 (en
Inventor
Menno W.J. Prins
Petrus W.J. Linders
Johannes C. Jans
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
US Philips Corp
Original Assignee
US Philips Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by US Philips Corp filed Critical US Philips Corp
Assigned to U.S. PHILIPS CORPORATION reassignment U.S. PHILIPS CORPORATION ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: JANS, JOHANNES C., LINDERS, PETRUS W.J., PRINS, MENNO W.J.
Priority to US09/858,726 priority Critical patent/US6440527B2/en
Publication of US20010051250A1 publication Critical patent/US20010051250A1/en
Application granted granted Critical
Publication of US6383601B2 publication Critical patent/US6383601B2/en
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

The invention relates to a method of manufacturing honeycomb structures in which multiple foils are welded together by means of thermal compression and the multiple foils form the honeycomb structure in the expanded condition. The bonding locations, where the foils are fused together, are defined by inserting a structured layer between the foils.

Description

  • The invention relates to a method of manufacturing honeycomb structures which includes the following steps: [0001]
  • connecting a plurality of foils to one another so as to realize a stack of interconnected foils which form a honeycomb structure in the expanded condition, the foils being fused at various bonding locations, and [0002]
  • expanding the plurality of foils in a direction transversely of the surface of the foils in order to form the honeycomb structure. [0003]
  • The invention also relates to a honeycomb structure which includes a plurality of foils which are interconnected in different bonding locations by welding. [0004]
  • The method and the honeycomb structure of the described kind are known from international patent application WO 93/01048. Because of their low weight and unique structural properties, honeycomb structures are universally used in industrial applications. [0005]
  • Honeycomb structures made of comparatively thin foils are widely used because of their low weight and ability to withstand high compression loads. Such honeycomb structures are used, for example in aircraft components and running shoes. [0006]
  • Honeycomb structures are also used in, for example an X-ray examination apparatus. Such an X-ray examination apparatus then includes an adjustable X-ray filter. The adjustable X-ray filter includes a bundle of capillary tubes which are formed by the honeycomb structure. The capillary tubes may be completely or partly filled with an X-ray absorbing liquid. Furthermore, one end of the capillary tubes is connected to a reservoir containing an X-ray absorbing liquid. An electric voltage is applied across the tubes and the X-ray absorbing liquid in order to fill the capillary tubes. This enables adjustment of a two-dimensional intensity profile of an X-ray beam traversing the X-ray filter. Honeycomb structures are also used as light diffusers in luminaries. [0007]
  • The known method realizes the honeycomb structure by expansion of interconnected foils. A stack of foils is formed by successively arranging first and second foils against one another and by heating the bonding locations via the second foil, so that the first and second foils start to melt. When the desired melting depth has been reached in the first foil, heating is terminated and the foils are cooled. Subsequently, a next foil is placed on the stack. The described process steps are repeated until the stack contains a number of foils which suffices to realize a honeycomb structure comprising the desired number of channels. After the plurality of foils has been interconnected in this manner, the stack of foils is expanded by pulling in order to form the honeycomb structure. [0008]
  • It is a drawback of the known process that it is difficult to apply the appropriate amount of heat to the bonding locations on the second foils so as to achieve the desired melting depth and to prevent the foils from being completely connected to one another. [0009]
  • It is an object of the invention to provide a method where the amount of heat to be applied is not critical and the foils are not completely connected to one another. To achieve this, the method according to the invention is characterized in that it includes a step for providing a structured separating layer on at least one side of the foil in order to realize the bonding locations on the foil. Other attractive versions of the method according to the invention are disclosed in the dependent claims. The separating layer is structured in such a manner that it comprises openings which constitute the bonding locations. Neighboring foils to both sides of the relevant separating layer can contact one another via the openings. When pressure is exerted on the stack of foils with the separating layers inserted between individual foils, the neighboring foils are bonded together at the areas where they contact one another at the bonding locations in the separating layers. The separating layers prevent the bonding of neighboring foils outside the bonding locations. For example, the bonding locations are formed by narrow strips which form the bonding seams along which the neighboring foils are fused by thermal compression so that they are bonded together along said bonding seams. The insertion of the structured separating layer also offers the advantage that the process of bonding the foils in the stack can be accelerated. Furthermore, the structured layer can be provided, for example by providing a metal layer on the foil and by locally removing material of the metal layer so as to define the bonding locations. A further advantage resides in the fact that the foils to be used may be thin. For example, use is made of foils having a thickness of approximately 5 μm. Furthermore, it is advantageous to use foils having a high mechanical strength. It has been found that polypropylene sulphon (PPS) is a suitable material for the foils; polyethyleneterephthalate (PETP), polyethylene and polyesters are also suitable materials for forming the foils. [0010]
  • The stacked foils are preferably expanded by clamping the foils transversely of the plane of the foils. As a result, neighboring foils locally move away from one another at the areas where they are not interconnected. The expanded, stacked foils can be maintained in the expanded condition by keeping them mechanically clamped. The stacked foils can also be maintained in the expanded condition by drastically reducing the elasticity of the foils, after clamping, by temporary heating or irradiation by means of X-rays or ultraviolet radiation. The pattern of cross-sections of the channels in the honeycomb is determined by the degree of expansion of the stack of foils transversely of the foil surface, the spacing of the bonding seams in the direction parallel to the surface of the foils, the seams along which the foils are attached to one another, and the width of said bonding seams. If the width of the bonding seams in a regular pattern between adjoining foils is approximately three times smaller than their spacing and if the stack of foils is expanded only slightly, a more or less eye-shaped pattern will be obtained; if the stack is expanded further, a hexagonal honeycomb pattern arises and if the stack is expanded even further, a pattern of rectangles having slightly rounded corners is obtained. Using a honeycomb pattern it is achieved notably that the mechanical strength of the expanded stack of foils is very high. When the width of the bonding seams in a regular pattern between adjoining foils is approximately two times smaller than their spacing, a rhombic pattern (with slightly rounded corners) or a pattern of eyes will be obtained, depending on whether the stack of foils is expanded more or less. When the bonding seams are much narrower than their spacing and the stack of foils is expanded only slightly, an eye-shaped pattern of channel cross-sections is formed. The directions of the channels in the expanded foils are dependent on the directions of the bonding seams relative to one another in the expanded foils. For example, when straight or curved, mutually parallel bonding seams are used, straight and curved channels, respectively, are formed and when the bonding seams are made to converge towards one another, tapered channels are formed. Furthermore, it is also possible to use bonding seams which are parallel in pairs while individual pairs of bonding seams enclose a small angle relative to one another. This yields filter elements in the form of channels; individual channels then enclose an angle relative to one another. It is also possible to realize other shapes by non-parallel expansion of the outermost foils. [0011]
  • A special version of the invention is characterized in that the step for realizing the structured separating layer comprises two sub-steps: a first sub-step for providing a separating layer on the at least one side of the foil, and a second sub-step for providing structures in the separating layer by the removal of material from the separating layer in order to realize the bonding locations. The bonding locations on the foils are thus defined. Material can be removed from the separating layer, for example by laser ablation. [0012]
  • A further method according to the invention is characterized in that it includes two sub-steps: stacking the plurality of foils and heating the stack to a temperature beyond the melting point of the foils. The process for realizing the stack of bonded foils can thus be substantially accelerated, because first all foils are stacked on one another and subsequently the entire stack of foils is heated to a temperature beyond the melting point of the foils in a single further step. Due to the presence of the structured separating layer, the material of the foils melts only in the bond locations defined by the structured separating layer. [0013]
  • The invention also relates to a honeycomb structure which includes a plurality of foils which are bonded to one another at various bonding locations by welding. The honeycomb structure according to the invention is characterized in that the bonding locations are separated from one another by a structured separating layer provided on at least one side of the foil. [0014]
  • A further embodiment of the honeycomb structure according to the invention is characterized in that the structured separating layer contains a metal having a thickness in a range of less than 500 nm. An example of such a metal contains aluminum. [0015]
  • The invention also relates to a diagnostic X-ray apparatus provided with an X-ray filter. The diagnostic X-ray apparatus according to the invention is characterized in that the X-ray filter includes a honeycomb structure as defined in claim 4. [0016]
  • The invention also relates to a luminary provided with a diffuser. The luminary according to the invention is characterized in that the diffuser includes a honeycomb structure as defined in claim 4. [0017]
  • The above and other, more detailed aspects of the invention will be described in detail hereinafter, by way of example, with reference to the drawing.[0018]
  • In the drawing: [0019]
  • FIG. 1 shows a stack of foils, [0020]
  • FIG. 2 shows a honeycomb structure, [0021]
  • FIG. 3 shows the use of a honeycomb structure according to the invention in a luminary, and [0022]
  • FIG. 4 shows the use of a honeycomb structure according to the invention in an X-ray filter.[0023]
  • The method of manufacturing the honeycomb structure will be described in detail hereinafter with reference to the FIGS. 1 and 2. FIG. 1 is a diagrammatic front and side view of an example of a stack of foils used to form the honeycomb structure for use in the X-ray filter. The individual foils [0024] 10 in the stack alternate with structured separating layers 15. The thickness of the foils amounts to, for example approximately 5 μm. Preferably, the separating layers 15 are strips of aluminum having a thickness in a range of from approximately 5 to 500 nm; preferably, aluminum strips having a thickness of approximately 20 nm are used. When the foils are heated under pressure to a temperature beyond the melting point, the neighboring foils are partly fused in bonding locations where no aluminum is present between the neighboring foils. The neighboring foils are locally bonded to one another by way of such a thermal compression treatment. At the areas where a strip of aluminum is present between neighboring foils, the foils are not bonded by the thermal compression treatment. It has been found that foils having a melting point in the range of from 70 to 500° C. are very suitable for carrying out such thermal compression.
  • The [0025] honeycomb structure 30 shown in FIG. 2 has been formed by expanding the stacked foils 10. The stack of foils 10 has been expanded in the direction of the arrows 20. Expansion is realized, for example by pulling one or both rigid plates 11 in the direction of the arrows. Buffer members 12 are provided between the stack of foils 10 and the respective rigid plates 11. The expansion of the stack of foils locally creates spaces between neighboring foils, i.e. at the areas where they are not bonded to one another. When use is made of parallel separating strips, approximately parallel bonding seams along which the neighboring foils are bonded to one another are formed by thermal compression. As a result of such approximately parallel bonding seams, the spaces between the foils are shaped as capillary tubes which extend approximately perpendicularly to the plane of drawing and parallel to the bonding seams. The degree of expansion of the stack of foils determines, in conjunction with the dimensions of the bonding seams and the spacing of the bonding seams, the dimensions of the capillary tubes. As a result of the expansion in the direction transversely of the foils, the buffer members 12 are slightly contracted in the direction parallel to the foils. It is thus achieved that the stack of foils is expanded mainly transversely of the foils and the size of the local spaces between the foils is uniform over the honey comb structure.
  • In order to realize the structured separating layer, on one side of the foils there is provided a metal layer having a thickness of, for example 20 nm. This metal layer can be deposited, for example by way of a vapor deposition process. Subsequently, the metal is removed from the foil at the area of the bonding locations by means of, for example laser ablation. Other possibilities for locally removing the material are, for example, wet chemical etching or the use of a shadow mask vapor deposition method. In order to make the temperature adjustment even less critical during the heating and bonding of the stack of foils, preferably both sides of the foils are provided with the structured separating layer. FIG. 3 shows the use of the [0026] honeycomb structure 30 as a diffuser in a luminary 31. The luminary 31 includes a housing 32, a lamp 33, a reflector 34 and a honeycomb structure 30. The lamp 33 is, for example a fluorescent tube. The reflector 34 is shaped, for example as a parabolic reflector which is arranged in the housing 32 or is integral with the housing. The fluorescent tube 33 is mounted in the housing 32 near a focal line of the parabolic reflector 34. The honeycomb structure 30 is provided in a window of the housing 32 opposite the parabolic reflector 34. The channels 35 of the honeycomb structure 30 are oriented, for example parallel to one another and in the direction of an object to be illuminated (not shown). The length of the channels amounts to, for example 2 mm and their diameter is, for example 1 mm. In order to enhance the efficiency, the inner side of the channels is preferably provided with a diffusely dispersive reflection layer. A high-efficiency diffuser is thus obtained. In addition to the described application, it is also possible to bend the honeycomb structure so that exit openings of the channels, via which light rays emanate from the luminary, are directed towards a focal line or a focal spot.
  • FIG. 4 shows an application of a [0027] honeycomb structure 30 in an X-ray filter 45 of an X-ray examination apparatus 40. Such an X-ray examination apparatus 40 includes an X-ray source 41, an X-ray detector 42, a power supply unit for delivering a voltage for the X-ray source 41, a monitor 48, an X-ray filter 45 and a control unit 47. The object 43 to be examined is arranged between the X-ray source 41 and the X-ray detector 42. The X-ray detector 42 converts an X-ray beam 44 having traversed the object 43 into an electric image signal 49. The image signal 49 is then displayed on a monitor 48. In order to attenuate the X-ray beam 44 locally so as to adjust a two-dimensional intensity profile, an X-ray filter 45 is arranged in the X-ray beam 44 between the X-ray source 41 and the object 43. The X-ray filter 45 comprises a large number of filter elements. A filter element preferably includes a capillary tube. The capillary tubes (not shown in FIG. 4) are formed by the honeycomb structure 30. The length of the capillary tubes amounts to, for example 25 mm and their diameter to, for example 275 μm. The capillary tubes communicate, by way of a first opening, with a reservoir (not shown in FIG. 4) which contains an X-ray absorbing liquid, for example an aqueous solution of a lead salt. The X-ray absorptivity of the X-ray filter 45 can be adjusted via the control unit 47 by applying electric voltages across the inner side of the capillary tubes of the X-ray filter 45 and the X-ray absorbing liquid. This is because the adhesion of the X-ray absorbing liquid to the inner side of the capillary tubes is dependent on the electric voltage applied across the inner side of the capillary tubes and the X-ray absorbing liquid. The capillary tubes are filled with a given quantity of X-ray absorbing liquid in dependence on the electric voltage present across the individual capillary tubes and the X-ray absorbing liquid. Because the capillary tubes extend approximately parallel to the X-ray beam, the X-ray absorptivity of the individual capillary tubes is dependent on the relative quantity of X-ray absorbing liquid present in the capillary tube.
  • Other applications of the honeycomb structure according to the invention are, for example its use as a collimator for X-rays in an X-ray examination apparatus. Another application is, for example its use as an anti-scatter grid in an X-ray examination apparatus. [0028]

Claims (9)

1. A method of manufacturing honeycomb structures which includes the following steps:
connecting a plurality of foils to one another so as to realize a stack of interconnected foils which form a honeycomb structure in the expanded condition, the foils being fused at various bonding locations,
expanding the stack of foils in a direction transversely of the surface of the foils in order to form the honeycomb structure, characterized in that the method includes a step for:
providing a structured separating layer on at least one side of the foil in order to realize bonding locations on the foil.
2. A method as claimed in
claim 1
, characterized in that the step for realizing the structured separating layer comprises two sub-steps for:
providing a separating layer on the at least one side of the foil, and
providing structures in the separating layer by the removal of material from the separating layer in order to realize the bonding locations.
3. A method as claimed in
claim 1
, characterized in that the method for interconnecting the foils includes two sub-steps for:
stacking the plurality of foils, and
heating the stack to a temperature beyond the melting point of the foils.
4. A honeycomb structure which includes a plurality of foils which are fused to one another at various bonding locations, characterized in that the bonding locations are separated from one another by a structured separating layer provided on at least one side of the foil.
5. A honeycomb structure as claimed in
claim 4
, characterized in that neighboring foils are locally connected to one another along bonding seams, the ratio of the width of the individual bonding seams to the distance between neighboring bonding seams being in the range of from 0.1 to 0.4 and preferably amounting to approximately ¼ or ⅓.
6. A honeycomb structure as claimed in
claim 4
, characterized in that the structured separating layer contains a metal having a thickness in a range of less than 500 nm.
7. A honeycomb structure as claimed in
claim 6
, characterized in that the metal contains aluminum.
8. A diagnostic X-ray apparatus provided with an X-ray filter, characterized in that the X-ray filter includes a honeycomb structure as claimed in
claim 4
.
9. A luminary provided with a diffuser, characterized in that the diffuser includes a honeycomb structure as claimed in
claim 4
.
US09/316,779 1998-05-22 1999-05-21 Honeycomb structure and method of manufacturing honeycomb structures Expired - Fee Related US6383601B2 (en)