TWI713651B - Liquid crystal composition and liquid crystal display element - Google Patents

Abstract

The present invention provides a liquid crystal composition capable of achieving vertical alignment of liquid crystal molecules through the action of a polar compound and a polymer, and a liquid crystal display element containing the composition. The present invention is a nematic liquid crystal composition that contains a polar compound as a first additive and a polymerizable compound having at least three polymerizable groups as a second additive, and has negative dielectric anisotropy. The material may also contain a specific liquid crystal compound with large negative dielectric anisotropy as the first component, and a specific liquid crystal compound with a high upper limit temperature or a small viscosity as the second component, and the present invention is a kind of The composition of the liquid crystal display element.

Description

Liquid crystal composition and liquid crystal display element

The present invention relates to a liquid crystal composition with negative dielectric anisotropy, a liquid crystal display element containing the composition, and the like. In particular, it relates to a liquid crystal composition containing a polar compound and a polymerizable compound (or a polymer thereof), and the vertical alignment of liquid crystal molecules can be achieved by the action of these compounds, and a liquid crystal display device.

In liquid crystal display elements, the classification based on the operation mode of liquid crystal molecules is phase change (PC), twisted nematic (TN), super twisted nematic (STN), and electrically controlled birefringence ( Electrically controlled birefringence (ECB), optically compensated bend (OCB), in-plane switching (IPS), vertical alignment (VA), fringe field switching (FFS), Field-induced photo-reactive alignment (FPA) and other modes. The classification based on the driving method of the element is a passive matrix (PM) and an active matrix (AM). PM is classified into static and multiplexed types, and AM is classified into thin film transistors (TFT), metal insulator metal (MIM), etc. TFTs are classified into amorphous silicon and polycrystal silicon. The latter is classified into a high temperature type and a low temperature type according to the manufacturing steps. The classification based on the light source is the reflective type using natural light and the backlight using The transmissive type, and the semi-transmissive type that uses both natural light and backlight.

The liquid crystal display element contains a liquid crystal composition having a nematic phase. The composition has appropriate characteristics. By improving the characteristics of the composition, an AM device with good characteristics can be obtained. The relationship between the two characteristics is summarized in Table 1 below. The characteristics of the composition will be further described based on commercially available AM devices. The temperature range of the nematic phase is related to the temperature range in which the element can be used. The preferred upper limit temperature of the nematic phase is about 70°C or higher, and the preferred lower limit temperature of the nematic phase is about -10°C or lower. The viscosity of the composition is related to the response time of the device. In order to display dynamic images with components, it is preferable that the response time be short. Ideally, the response time is shorter than 1 millisecond. Therefore, it is preferable that the viscosity of the composition is small. It is particularly preferable that the viscosity at low temperature is small.

The optical anisotropy of the composition is related to the contrast ratio of the element. Depending on the mode of the element, large or small optical anisotropy, that is, appropriate optical anisotropy, is required. The product (Δn×d) of the optical anisotropy (Δn) of the composition and the cell gap (d) of the element (Δn×d) is designed to maximize the contrast ratio. Proper product The value of depends on the type of operation mode. In the VA mode device, the value is in the range of about 0.30 μm to about 0.40 μm, and in the IPS mode or FFS mode device, the value is in the range of about 0.20 μm to about 0.30 μm. In these cases, for an element with a small cell gap, a composition having large optical anisotropy is preferable. The large dielectric anisotropy of the composition contributes to the low threshold voltage, small power consumption, and large contrast ratio in the device. Therefore, a large dielectric anisotropy is preferable. The large specific resistance of the composition contributes to the large voltage holding ratio and large contrast ratio of the element. Therefore, it is preferably a composition having a large specific resistance not only at room temperature but also at a temperature close to the upper limit temperature of the nematic phase in the initial stage. It is preferably a composition having a large specific resistance not only at room temperature but also at a temperature close to the upper limit temperature of the nematic phase after long-term use. The stability of the composition to ultraviolet light or heat is related to the life of the element. When the stability is high, the life of the device is long. Such characteristics are better for AM devices used in liquid crystal projectors, liquid crystal televisions, and the like.

In general liquid crystal display devices, the vertical alignment of liquid crystal molecules can be achieved by using a specific polyimide alignment film. In a polymer sustained alignment (PSA) type liquid crystal display element, the effect of the polymer is fully used. First, a composition containing a small amount of polymerizable compound is injected into the device. Then, while applying a voltage between the substrates of the element, the composition was irradiated with ultraviolet rays. The polymerizable compound is polymerized to form a polymer network structure in the composition. In this composition, the polymer can be used to control the alignment of the liquid crystal molecules, so the response time of the element is shortened and the afterimage of the image is improved. Such effects of polymers can be expected in devices with modes such as TN, ECB, OCB, IPS, VA, FFS, and FPA. fruit.

On the other hand, a liquid crystal display element that does not have an alignment film uses a liquid crystal composition containing a polymer and a polar compound. First, a composition containing a small amount of polymerizable compound and a small amount of polar compound is injected into the device. Here, the polar compounds are adsorbed on the surface of the substrate and arranged. The liquid crystal molecules are aligned according to the arrangement. Then, while applying a voltage between the substrates of the element, the composition was irradiated with ultraviolet rays. Here, the polymerizable compound is polymerized and stabilizes the alignment of liquid crystal molecules. In this composition, polymers and polar compounds can be used to control the alignment of liquid crystal molecules, so the response time of the device is shortened, and the afterimage of the image is improved. Furthermore, the step of forming the alignment film is not required in the element without the alignment film. Since there is no alignment film, the interaction between the alignment film and the composition will not reduce the resistance of the device. In devices having modes such as TN, ECB, OCB, IPS, VA, FFS, FPA, etc., such an effect of the combination of a polymer and a polar compound can be expected.

The AM device having the TN mode uses a composition having positive dielectric anisotropy. The AM device having the VA mode uses a composition having negative dielectric anisotropy. The AM device having the IPS mode or the FFS mode uses a composition having positive or negative dielectric anisotropy. A polymer stabilized alignment type AM device uses a composition having positive or negative dielectric anisotropy. Examples of the liquid crystal composition having negative dielectric anisotropy are disclosed in Patent Document 1 to Patent Document 6 below. In the present invention, a polar compound is combined with a polymerizable compound (or a polymer thereof) and a liquid crystal compound, and the composition is used for a liquid crystal display element without an alignment film.

[Prior Art Literature]

[Patent Literature]

[Patent Document 1] International Publication No. 2014/090362 Specification

[Patent Document 2] International Publication No. 2014/094959 Specification

[Patent Document 3] International Publication No. 2013/004372 Specification

[Patent Document 4] International Publication No. 2012/104008 Specification

[Patent Document 5] International Publication No. 2012/038026 Specification

[Patent Document 6] Japanese Patent Laid-Open No. 50-35076

An object of the present invention is a liquid crystal composition containing a polar compound and a polymerizable compound (or a polymer thereof), where the polar compound and the polymerizable compound have high compatibility with the liquid crystal compound. Another object is a liquid crystal composition that can achieve vertical alignment of liquid crystal molecules through the action of the polymer. Another object is a liquid crystal composition, which has a high upper limit temperature of the nematic phase, a low lower limit temperature of the nematic phase, low viscosity, appropriate optical anisotropy, large negative dielectric anisotropy, large specific resistance, and Among the characteristics of high ultraviolet stability and high heat stability, at least one characteristic is satisfied. Another object is a liquid crystal composition having an appropriate balance between at least two characteristics. Another object is a liquid crystal display element containing the composition. Another object is an AM device with short response time, high voltage holding rate, low threshold voltage, high contrast ratio, and long life.

The present invention is a liquid crystal composition containing a polar compound as a first additive and a polymerizable compound having at least three polymerizable groups as a second additive, and having negative dielectric anisotropy, and containing the composition The liquid crystal display element.

One advantage of the present invention is a liquid crystal composition containing a polar compound and a polymerizable compound (or a polymer thereof). Here, the polar compound and the polymerizable compound have high compatibility with the liquid crystal compound. Another advantage is a liquid crystal composition that can achieve vertical alignment of liquid crystal molecules through the action of the polymer. Another advantage is a liquid crystal composition which has a high upper limit temperature of the nematic phase, a low lower limit temperature of the nematic phase, low viscosity, appropriate optical anisotropy, large negative dielectric anisotropy, large specific resistance, and Among the characteristics of high ultraviolet stability and high heat stability, at least one characteristic is satisfied. Another advantage is a liquid crystal composition that has an appropriate balance between at least two characteristics. Another advantage is a liquid crystal display element containing the composition. Another advantage is an AM device with short response time, high voltage retention, low threshold voltage, high contrast ratio, and long life.

The usage of the terms in this manual is as follows. Sometimes the terms "liquid crystal composition" and "liquid crystal display element" are abbreviated as "composition" and "element Pieces". "Liquid crystal display element" is the general term for liquid crystal display panels and liquid crystal display modules. A "liquid crystal compound" is a compound having a liquid crystal phase such as a nematic phase and a smectic phase, and although it does not have a liquid crystal phase, it is used for the purpose of adjusting the temperature range, viscosity, and dielectric anisotropy of the nematic phase. The general term for the compounds mixed in the composition. This compound has, for example, a six-membered ring such as 1,4-cyclohexylene or 1,4-phenylene, and its molecular structure is rod-like. The "polymerizable compound" is a compound added for the purpose of forming a polymer in the composition. The liquid crystal compound having an alkenyl group is not polymerizable in its meaning.

The liquid crystal composition is prepared by mixing a plurality of liquid crystal compounds. To this liquid crystal composition, additives such as optically active compounds, antioxidants, ultraviolet absorbers, pigments, defoamers, polymerizable compounds, polymerization initiators, polymerization inhibitors, and polar compounds are added as necessary. Liquid crystal compounds or additives are mixed in the stated order. Even when an additive is added, the ratio (content) of the liquid crystal compound is represented by a weight percentage (% by weight) based on the weight of the liquid crystal composition that does not contain the additive. The ratio (addition amount) of the additives is represented by the weight percentage (weight %) based on the weight of the liquid crystal composition not containing the additives. Sometimes parts per million by weight (ppm) are used. The ratio of the polymerization initiator and the polymerization inhibitor is exceptionally expressed based on the weight of the polymerizable compound.

The "upper limit temperature of the nematic phase" is sometimes simply referred to as the "upper limit temperature". The "lower limit temperature of the nematic phase" is sometimes referred to simply as the "lower limit temperature". "High specific resistance" means that the composition has a large specific resistance not only at room temperature but also at a temperature close to the upper limit temperature in the initial stage, and not only at room temperature after long-term use, It also has a large specific resistance at a temperature close to the upper limit temperature. "High voltage holding rate" means that the device has a large voltage holding rate not only at room temperature but also at a temperature close to the upper limit temperature in the initial stage, and after long-term use, not only at room temperature, but also at It also has a large voltage holding rate at a temperature close to the upper limit temperature. In a composition or element, characteristics may be studied before and after a time-dependent change test (including an accelerated deterioration test). The expression "increasing dielectric anisotropy" refers to a positive increase in the value of a composition with positive dielectric anisotropy, and a negative value in the case of a composition with negative dielectric anisotropy Increase to the ground.

The compound represented by formula (1) may be abbreviated as "compound (1)". At least one compound selected from the group of compounds represented by formula (1) may be referred to simply as "compound (1)". "Compound (1)" means one compound, a mixture of two compounds, or a mixture of three or more compounds represented by formula (1). The same applies to compounds represented by other formulas. The expression "at least one ‘A’" means that the number of ‘A’ is arbitrary. The expression "at least one'A' can be replaced by'B'" means that when the number of'A' is one, the position of'A' is arbitrary, and when the number of'A' is more than two, their positions Can also choose unlimitedly. This rule also applies to the expression "at least one ‘A’ is replaced by a ‘B’".

Expressions such as "at least one -CH ₂ -may be substituted by -O-" are used in this specification. In this case, -CH ₂ -CH ₂ -CH ₂ -can be converted to -O-CH ₂ -O- by replacing non-adjacent -CH ₂ -with -O-. However, the adjacent -CH ₂ -will not be substituted by -O-. This is because -OO-CH _2- (peroxide) is generated in the substitution. That is, the expression means both "one -CH ₂ -may be substituted by -O-" and "at least two non-adjacent -CH ₂ -may be substituted by -O-". This rule applies not only to the case of substitution with -O-, but also to the case of substitution with a divalent group such as -CH=CH- or -COO-. In the alkyl group, at least one -CH ₂ -is sometimes substituted with a cycloalkylene group having 3 to 8 carbon atoms. The carbon number of the alkyl group is increased by this substitution. At this time, the maximum carbon number is 30. This rule applies not only to monovalent groups such as alkyl groups, but also to divalent groups such as alkylene groups.

In the chemical formula of the component compound, the symbol of the terminal group R ¹ is used for various compounds. In these compounds, two groups represented by any two R ¹ may be the same or different. For example, there is a case where R ¹ of compound (1-1) is ethyl, and R ¹ of compound (1-2) is ethyl. There are also cases where R ¹ of compound (1-1) is ethyl, and R ¹ of compound (1-2) is propyl. This rule applies to other tokens. In formula (1), when a is 2, two rings A exist. In this compound, the two rings represented by the two rings A may be the same or different. This rule also applies to any two rings A when a is greater than 2. This rule applies to other tokens. This rule also applies to situations such as the two -Sp ¹⁰ -P ⁵ of compound (5-7).

Symbols such as A, B, C, and D surrounded by a hexagon respectively correspond to rings such as ring A, ring B, ring C, and ring D, and indicate rings such as six-membered rings and condensed rings. In the formula (5), the diagonal line crossing the hexagon indicates that any hydrogen on the ring can be substituted with a group such as -Sp ¹⁰ -P ⁵ . Subscripts such as'v' indicate the number of substituted groups. When the subscript'v' is 0, there is no such substitution. When the subscript'v' is 2 or more, there are multiple -Sp ¹⁰ -P ⁵ on the ring U. The multiple groups represented by -Sp ¹⁰ -P ⁵ may be the same or different. In the expression "ring A and ring C are independently X, Y or Z", since there are multiple subjects, "independently" is used. When the subject is "ring A", since the subject is singular, "independently" is not used. When "ring A" is used in multiple formulas, the rule of "may be the same or different" applies to "ring A". The same is true for other bases.

2-Fluoro-1,4-phenylene refers to the following two divalent groups. In the chemical formula, fluorine can be leftward (L) or rightward (R). This rule applies to asymmetric divalent groups such as tetrahydropyran-2,5-diyl, which are formed by removing two hydrogens from the ring. This rule also applies to divalent bonding groups such as carbonyloxy (-COO- or -OCO-).

The alkyl group of the liquid crystal compound is linear or branched, and does not include a cyclic alkyl group. Straight-chain alkyl is better than branched alkyl. The same applies to terminal groups such as alkoxy and alkenyl. In order to increase the maximum temperature, the three-dimensional configuration related to 1,4-cyclohexylene is the trans configuration better than the cis configuration.

The present invention includes the following items.

Item 1. A liquid crystal composition containing a polar compound as a first additive and a polymerizable compound having at least three polymerizable groups as a second additive, and having negative dielectric anisotropy.

Item 2. The liquid crystal composition according to Item 1, which contains at least one compound selected from the group of compounds represented by formula (1) as the first component,

In formula (1), R ¹ and R ^{2 are} independently an alkyl group having 1 to 12 carbons, an alkoxy group having 1 to 12 carbons, an alkenyl group having 2 to 12 carbons, and at least one hydrogen is substituted by fluorine or chlorine Alkenyl with 2 to 12 carbons, or alkenyl with 2 to 12 carbons; ring A and ring C are independently 1,4-cyclohexenyl, 1,4-cyclohexenyl, tetrahydropyridine Phenyl-2,5-diyl, 1,4-phenylene, 1,4-phenylene in which at least one hydrogen is replaced by fluorine or chlorine, naphthalene-2,6-diyl, at least one hydrogen is replaced by fluorine or chlorine Substituted naphthalene-2,6-diyl, chroman-2,6-diyl, or chroman-2,6-diyl in which at least one hydrogen is replaced by fluorine or chlorine; ring B is 2,3- Difluoro-1,4-phenylene, 2-chloro-3-fluoro-1,4-phenylene, 2,3-difluoro-5-methyl-1,4-phenylene, 3,4 ,5-Trifluoronaphthalene-2,6-diyl or 7,8-difluorochroman-2,6-diyl; Z ¹ and Z ^{2 are} independently a single bond, -CH ₂ CH ₂ -,- CH ₂ O-, -OCH ₂ -, -COO- or -OCO-; a is 1, 2 or 3, b is 0 or 1, and the sum of a and b is 3 or less.

Item 3. The liquid crystal composition according to item 1 or 2, which contains at least one compound selected from the group of compounds represented by formula (1-1) to formula (1-22) as a first component,

In formulas (1-1) to (1-22), R ¹ and R ^{2 are} independently an alkyl group having 1 to 12 carbons, an alkoxy group having 1 to 12 carbons, and an alkenyl group having 2 to 12 carbons. , Alkenyl groups having 2 to 12 carbons, or alkenyloxy groups having 2 to 12 carbons, in which at least one hydrogen is substituted with fluorine or chlorine.

Item 4. The liquid crystal composition according to any one of items 1 to 3, wherein the ratio of the first component is in the range of 10% by weight to 90% by weight based on the weight of the liquid crystal composition.

Item 5. The liquid crystal composition according to any one of items 1 to 4, which contains at least one compound selected from the group of compounds represented by formula (2) as a second component,

In formula (2), R ³ and R ^{4 are} independently an alkyl group having 1 to 12 carbons, an alkoxy group having 1 to 12 carbons, an alkenyl group having 2 to 12 carbons, and at least one hydrogen is substituted by fluorine or chlorine The alkyl group having 1 to 12 carbons, or the alkenyl group having 2 to 12 carbons in which at least one hydrogen is replaced by fluorine or chlorine; ring D and ring E are independently 1,4-cyclohexylene, 1,4-alkylene Phenyl, 2-fluoro-1,4-phenylene or 2,5-difluoro-1,4-phenylene; Z ³ is a single bond, -CH ₂ CH ₂ -, -CH ₂ O-,- OCH ₂ -, -COO- or -OCO-; c is 1, 2 or 3.

Item 6. The liquid crystal composition according to any one of items 1 to 5, which contains at least one compound selected from the group of compounds represented by formula (2-1) to formula (2-13) as The second component,

In formulas (2-1) to (2-13), R ³ and R ^{4 are} independently an alkyl group having 1 to 12 carbons, an alkoxy group having 1 to 12 carbons, and an alkenyl group having 2 to 12 carbons. , Alkyl groups having 1 to 12 carbons in which at least one hydrogen is replaced by fluorine or chlorine, or alkenyl groups having 2 to 12 in carbon numbers in which at least one hydrogen is replaced by fluorine or chlorine.

Item 7. The liquid crystal composition according to Item 5 or Item 6, wherein the ratio of the second component is in the range of 10% by weight to 70% by weight based on the weight of the liquid crystal composition.

Item 8. The liquid crystal composition according to any one of items 1 to 7, which contains a polar compound as the first additive, the polar compound containing a heteroatom selected from nitrogen, oxygen, sulfur, and phosphorus Polar group.

Item 9. The liquid crystal composition according to any one of items 1 to 8, which contains at least one compound selected from the group of polar compounds represented by formula (3) and formula (4) as the first addition Objects, MES-R ⁶ (3)

(R ⁵ ) _x -R ⁶ (4)

In the formula (3), MES is a mesogen group having at least one ring; in the formula (4), R ⁵ is an alkyl group having 4 to 20 carbons. In the alkyl group, at least one -CH ₂ -can pass through -CH =CH-, -CF=CH-, -CH=CF-, -C≡C- or cycloalkylene having 3 to 8 carbon atoms, in these groups, at least one hydrogen may be substituted by fluorine or chlorine; (3) and formula (4), R ⁶ is a polar group of at least one of an oxygen atom with an OH structure, a sulfur atom with an SH structure, and a nitrogen atom with a primary, secondary or tertiary amine structure; x is 1 or 2.

Item 10. The liquid crystal composition according to any one of items 1 to 9, which contains at least one compound selected from the group of polar compounds represented by formula (3-1) as a first additive,

In the formula (3-1), R ⁷ is hydrogen, fluorine, chlorine, or an alkyl group having 1 to 25 carbons. In the alkyl group, at least one -CH ₂ -can pass through -NR ⁰ -, -O-, -S -, -CO-, -CO-O-, -O-CO-, -O-CO-O- or cycloalkylene substituted with carbon number 3 to 8, and at least one tertiary carbon (>CH-) Substituted by nitrogen (>N-), in these groups, at least one hydrogen may be substituted by fluorine or chlorine, where R ⁰ is hydrogen or an alkyl group with 1 to 12 carbons; R ⁸ is a group with 1 to 25 carbons Alkyl, in which at least one -CH ₂ -can be -NR ⁰ -, -O-, -S-, -CO-, -COO-, -OCO-, -OCOO- or carbon number 3 to 8 At least one tertiary carbon (>CH-) may be substituted by nitrogen (>N-), and in these groups, at least one hydrogen may be substituted by fluorine or chlorine, where R ⁰ is hydrogen or An alkyl group with 1 to 12 carbon atoms, wherein R ⁸ has at least one of an oxygen atom of an OH structure, a sulfur atom of an SH structure, or a nitrogen atom of a primary, secondary or tertiary amine structure; ring F and ring G are independent Ground is an aromatic group with 6 to 25 carbons, a heteroaromatic group with 5 to 25 carbons, an alicyclic group with 3 to 25 carbons, or a heteroalicyclic group with 4 to 25 carbons. These groups may It is a condensed ring, in these groups, at least one hydrogen may be substituted by a group T, where the group T is -OH, -(CH ₂ ) _i -OH, fluorine, chlorine, -CN, -NO ₂ , -NCO, -NCS, -OCN, -SCN, -C(=O)N(R ⁰ ) ₂ , -C(=O)R ⁰ , -N(R ⁰ ) ₂ , -(CH ₂ ) _i -N(R ⁰ ) _2. Aryl groups with 6 to 20 carbons, heteroaryl groups with 6 to 20 carbons, alkyl groups with 1 to 25 carbons, alkoxy groups with 1 to 25 carbons, and alkylcarbonyl groups with 2 to 25 carbons , Alkoxycarbonyl having 2 to 25 carbons, alkylcarbonyloxy having 2 to 25 carbons or alkoxycarbonyloxy having 2 to 25 carbons, in which at least one hydrogen may be fluorine or chlorine Substitution, here, R ⁰ is hydrogen or an alkyl group having 1 to 12 carbons, and i is 1, 2, 3, or 4; Z ⁴ is -O-, -S-, -CO-, -CO-O- , -OCO-, -O-CO-O-, -OCH ₂ -, -CH ₂ O-, -SCH ₂ -, -CH ₂ S-, -CF ₂ O-, -OCF ₂ -, -CF ₂ S -, -SCF ₂ -, -(CH ₂ ) _i -, -CF ₂ CH ₂ -, -CH ₂ CF ₂ -, -(CF ₂ ) _i -, -CH=CH-, -CF=CF-,- C≡C-, -CH=CH-COO-, -OCO-CH=CH-, -C(R ⁰ ) ₂ -or a single bond, where R ⁰ is hydrogen or an alkyl group having 1 to 12 carbons, And i is 1, 2, 3, or 4; d is 0, 1, 2, 3, 4, or 5.

Item 11. The liquid crystal composition according to any one of items 1 to 10, which contains at least one compound selected from the group of polar compounds represented by formula (4-1) as a first additive, R ⁹ -R ¹⁰ (4-1)

In formula (4-1), R ⁹ is an alkyl group having 4 to 20 carbons. In the alkyl group, at least one -CH ₂ -can be controlled by -CH=CH-, -CF=CH-, -CH=CF- , -C≡C- or a cycloalkylene having 3 to 8 carbon atoms, in these groups, at least one hydrogen may be substituted by fluorine or chlorine; R ¹⁰ is an alkyl group having 1 to 25 carbon atoms, in which , At least one -CH ₂ -may be substituted with -NR ⁰ -, -O-, -S-, -CO-, -COO-, -OCO-, -OCOO- or a cycloalkylene group having 3 to 8 carbon atoms, At least one tertiary carbon (>CH-) may be substituted by nitrogen (>N-), in these groups, at least one hydrogen may be substituted by fluorine or chlorine, where R ⁰ is hydrogen or an alkane with 1 to 12 carbon atoms. A group, wherein R ¹⁰ has at least one of an oxygen atom of an OH structure, a sulfur atom of an SH structure, and a nitrogen atom of a primary, secondary or tertiary amine structure.

Item 12. The liquid crystal composition according to Item 9, wherein in formula (3) and formula (4) according to Item 9, R ⁶ is a polar group selected from the group consisting of formula (A1) to formula (A4) Base in the group of

此處，R⁰為氫或碳數1至12的烷基；X²為-O-、-CO-、-NH-、-NR^a1-、-S-或單鍵；Z⁹為碳數1至15的伸烷基、碳數5或6的脂環式基或者該些的組合，該些基中，至少一個氫可經-OH、-OR^a1、-COOH、-NH₂、-NHR^a1、-N(R^a1)₂、氟或氯取代；此處，R^a1為碳數1至15的烷基，該烷基中，至少一個-CH₂-可經-C≡C-、-CH=CH-、-COO-、-OCO-、-CO-或-O-取代，該些基中，至少一個氫可經氟或氯取代；環P為碳數6至25的芳香族基或碳數3至25的脂環式基，該些基可為縮合環，該些基中，一個至三個氫可經R^L取代，此處，R^L為-OH、-(CH₂)_r-OH、氟、氯、-CN、-NO₂、-NCO、-NCS、-OCN、-SCN、-C(=O)N(R⁰)₂、-C(=O)R⁰、-N(R⁰)₂、 -(CH₂)_r-N(R⁰)₂、-SH、-SR⁰、碳數6至20的芳基、碳數6至20的雜芳基、碳數1至25的烷基、碳數1至25的烷氧基、碳數2至25的烷基羰基、碳數2至25的烷氧基羰基、碳數2至25的烷基羰氧基或碳數2至25的烷氧基羰氧基，該些基中，至少一個氫可經氟或氯取代，此處，R⁰為氫或碳數1至12的烷基，而且r為1、2、3或4；p為0、1、2或3；q為2、3、4或5。 In formulas (A1) to (A4), Sp ⁴ , Sp ⁶ and Sp ^{7 are} independently single bonds or groups (-Sp"-X"-), where Sp" is an alkylene having 1 to 20 carbon atoms In the alkylene group, at least one -CH ₂ -can pass through -O-, -S-, -NH-, -N(R ⁰ )-, -CO-, -CO-O-, -O-CO -, -O-CO-O-, -S-CO-, -CO-S-, -N(R ⁰ )-CO-O-, -O-CO-N(R ⁰ )-, -N(R ⁰ )-CO-N(R ⁰ )-, -CH=CH- or -C≡C- substitution, in these groups, at least one hydrogen may be substituted by fluorine, chlorine or -CN, and X" is -O- , -S-, -CO-, -CO-O-, -O-CO-, -O-CO-O-, -CO-N(R ⁰ )-, -N(R ⁰ )-CO-,- N(R ⁰ )-CO-N(R ⁰ )-, -OCH ₂ -, -CH ₂ O-, -SCH ₂ -, -CH ₂ S-, -CF ₂ O-, -OCF ₂ -, -CF ₂ S-, -SCF ₂ -, -CF ₂ CH ₂ -, -CH ₂ CF ₂ -, -CF ₂ CF ₂ -, -CH=N-, -N=CH-, -N=N-, -CH =CR ⁰ -, -CY ² =CY ³ -, -C≡C-, -CH=CH-CO-O-, -O-CO-CH=CH- or single bond, where R ⁰ is hydrogen or An alkyl group having 1 to 12 carbons, and Y ² and Y ^{3 are} independently hydrogen, fluorine, chlorine or -CN; Sp ⁵ is >CH-, >CR ^a1 -, >N- or >C<; X ¹ is -OH, -OR ^a1 , -COOH, -NH ₂ , -NHR ^a1 , -N(R ^a1 ) ₂ , -SH, -SR ^a1 ,

Here, R ⁰ is hydrogen or an alkyl group having 1 to 12 carbons; X ² is -O-, -CO-, -NH-, -NR ^a1 -, -S- or a single bond; Z ⁹ is a carbon number of 1 An alkylene group with a carbon number of 5 or 6 or a combination of these groups, in which at least one hydrogen can pass through -OH, -OR ^a1 , -COOH, -NH ₂ , -NHR ^a1 , -N(R ^a1 ) ₂ , fluorine or chlorine substitution; here, R ^a1 is an alkyl group having 1 to 15 carbons, and in the alkyl group, at least one -CH ₂ -can be replaced by -C≡C-, -CH =CH-, -COO-, -OCO-, -CO- or -O- substituted, in these groups, at least one hydrogen may be substituted by fluorine or chlorine; ring P is an aromatic group with 6 to 25 carbons or carbon An alicyclic group having a number of 3 to 25, these groups may be condensed rings, and in these groups, one to three hydrogens may be substituted by R ^L , where R ^L is -OH, -(CH ₂ ) _r- OH, fluorine, chlorine, -CN, -NO ₂ , -NCO, -NCS, -OCN, -SCN, -C(=O)N(R ⁰ ) ₂ , -C(=O)R ⁰ , -N( R ⁰ ) ₂ , -(CH ₂ ) _r -N(R ⁰ ) ₂ , -SH, -SR ⁰ , aryl groups having 6 to 20 carbons, heteroaryl groups having 6 to 20 carbons, 1 to 25 carbons Alkyl group, alkoxy group with 1 to 25 carbons, alkylcarbonyl group with 2 to 25 carbons, alkoxycarbonyl group with 2 to 25 carbons, alkylcarbonyloxy group with 2 to 25 carbons or 2 In these groups, at least one hydrogen may be substituted by fluorine or chlorine. Here, R ⁰ is hydrogen or an alkyl group having 1 to 12 carbons, and r is 1, 2, 3 Or 4; p is 0, 1, 2 or 3; q is 2, 3, 4 or 5.

Item 13. The liquid crystal composition according to Item 9 or Item 10, wherein the first additive is selected from the group of polar compounds represented by formula (3-1-1) to formula (3-1-4) At least one compound of

In formulas (3-1-1) to (3-1-4), R ¹⁵ is an alkyl group having 1 to 8 carbons or fluorine; ring Q and ring R are independently 1,4-cyclohexylene, 1 ,4-phenylene, 2-fluoro-1,4-phenylene, 2-fluoro-1,3-phenylene, 2-ethyl-1,4-phenylene, 2,6-diethyl Phenyl-1,4-phenylene, 2-trifluoromethyl-1,4-phenylene, 2,3-difluoro-1,4-phenylene, 2,5-difluoro-1,4 -Phenylene, 2,6-difluoro-1,4-phenylene or 2,3,5,6-tetrafluoro-1,4-phenylene; ring S is cyclohexyl or phenyl; Z ¹⁰ Is a single bond, -CH ₂ CH ₂ -, -COO- or -OCO-; Z ¹¹ is a single bond, an alkylene group with 1 to 15 carbons, an alicyclic group with 5 or 6 carbons, or a combination of these , In these groups, at least one hydrogen can be substituted by -OH, -OR ^a1 , -COOH, -NH ₂ , -NHR ^a1 , -N(R ^a1 ) ₂ , fluorine or chlorine, where R ^a1 is the number of carbon An alkyl group of 1 to 15, in which at least one -CH ₂ -may be substituted with -C≡C-, -CH=CH-, -COO-, -OCO-, -CO- or -O-, In these groups, at least one hydrogen can be replaced by fluorine or chlorine; Sp ⁴ is a single bond, -CH ₂ CH ₂ -, -CH ₂ CH ₂ CH ₂ -, -CH ₂ O- or -OCH ₂ -; Sp ⁷ is A single bond or an alkylene having 1 to 5 carbon atoms, in which -CH ₂ -may be substituted by -O- or -NH-; s is 0, 1, 2, 3, 4 or 5; X ³ It is -OH, -COOH, -SH, -OCH ₃ or -NH ₂ ; X ⁴ is a single bond or -O-.

Item 14. The liquid crystal composition according to Item 9 or Item 11, wherein the first additive is selected from the group of polar compounds represented by formula (4-1-1) to formula (4-1-29) At least one compound of R ⁹ -OH (4-1-1)

R ⁹ -COOH (4-1-9)

R ⁹ -NH ₂ (4-1-11)

In formulas (4-1-1) to (4-1-29), R ⁹ is an alkyl group having 4 to 20 carbons. In the alkyl group, at least one -CH ₂ -can be controlled by -CH=CH-, -CF=CH-, -CH=CF-, -C≡C- or cycloalkylene having 3 to 8 carbon atoms, in these groups, at least one hydrogen may be substituted by fluorine or chlorine.

Item 15. The liquid crystal composition according to any one of Items 1 to 14, wherein the ratio of the first additive is in the range of 0.05% by weight to 10% by weight based on the weight of the liquid crystal composition.

Item 16. The liquid crystal composition according to any one of items 1 to 15, which contains at least one compound selected from the group of polymerizable compounds represented by formula (5) as a second additive,

In formula (5), ring T and ring V are independently cyclohexyl, cyclohexenyl, phenyl, 1-naphthyl, 2-naphthyl, tetrahydropyran-2-yl, 1,3-dioxyl Alk-2-yl, pyrimidin-2-yl or pyridin-2-yl, in these rings, at least one hydrogen may be fluorine, chlorine, alkyl having 1 to 12 carbons, alkoxy having 1 to 12 carbons , Or at least one hydrogen is substituted by a fluorine or chlorine substituted alkyl group having 1 to 12 carbons; ring U is 1,4-cyclohexylene, 1,4-cyclohexenylene, 1,4-phenylene, Naphthalene-1,2-diyl, naphthalene-1,3-diyl, naphthalene-1,4-diyl, naphthalene-1,5-diyl, naphthalene-1,6-diyl, naphthalene-1,7 -Diyl, naphthalene-1,8-diyl, naphthalene-2,3-diyl, naphthalene-2,6-diyl, naphthalene-2,7-diyl, tetrahydropyran-2,5-di Group, 1,3-dioxane-2,5-diyl, pyrimidine-2,5-diyl or pyridine-2,5-diyl, in these rings, at least one hydrogen can be fluorine, chlorine, carbon An alkyl group having 1 to 12, an alkoxy group having 1 to 12 carbons, or at least one hydrogen is substituted with an alkyl group having 1 to 12 carbons substituted by fluorine or chlorine; Z ¹² and Z ^{13 are} independently a single bond or carbon An alkylene having a number of 1 to 10, in which at least one -CH ₂ -may be substituted by -O-, -CO-, -COO- or -OCO-, and at least one -CH ₂ CH ₂ -may be Substituted by -CH=CH-, -C(CH ₃ )=CH-, -CH=C(CH ₃ )- or -C(CH ₃ )=C(CH ₃ )-, in these groups, at least one hydrogen May be substituted by fluorine or chlorine; P ⁴ , P ⁵ and P ⁶ are polymerizable groups; Sp ⁹ , Sp ¹⁰ and Sp ^{11 are} independently a single bond or an alkylene group having 1 to 10 carbon atoms. In the alkylene group, At least one -CH ₂ -can be substituted by -O-, -COO-, -OCO- or -OCOO-, and at least one -CH ₂ CH ₂ -can be substituted by -CH=CH- or -C≡C-, the In these groups, at least one hydrogen may be substituted by fluorine or chlorine; t is 0, 1 or 2; u, v and w are independently 0, 1, 2, 3 or 4, and the sum of u, v and w is 3. the above.

Item 17. The liquid crystal composition according to Item 16, wherein in formula (5) according to Item 16, P ⁴ , P ⁵ and P ^{6 are} independently selected from formula (P-1) to formula (P- 5) Groups in the group of aggregate groups,

In formulas (P-1) to (P-5), M ¹ , M ² and M ^{3 are} independently hydrogen, fluorine, an alkyl group with a carbon number of 1 to 5, or carbon in which at least one hydrogen is substituted by fluorine or chlorine The number is an alkyl group of 1 to 5.

Item 18. The liquid crystal composition according to any one of items 1 to 17, which contains at least one selected from the group of polymerizable compounds represented by formulas (5-1) to (5-7) Compound as the second additive,

In formula (5-1) to formula (5-7), P ⁴ , P ⁵ and P ^{6 are} independently selected from the group of polymerizable groups represented by formula (P-1) to formula (P-3) In the base,

Here, M ¹ , M ² and M ^{3 are} independently hydrogen, fluorine, an alkyl group having 1 to 5 carbons, or an alkyl group having 1 to 5 carbons in which at least one hydrogen is replaced by fluorine or chlorine; Sp ⁹ , Sp ¹⁰ and Sp ^{11 are} independently a single bond or an alkylene having 1 to 10 carbon atoms, in which at least one -CH ₂ -may be substituted by -O-, -COO-, -OCO- or -OCOO- , And at least one -CH ₂ CH ₂ -may be substituted by -CH=CH- or -C≡C-, and in these groups, at least one hydrogen may be substituted by fluorine or chlorine.

Item 19. The liquid crystal composition according to any one of Items 16 to 18, wherein the ratio of the second additive is in the range of 0.03% by weight to 10% by weight based on the weight of the liquid crystal composition.

Item 20. A liquid crystal display element comprising the liquid crystal composition according to any one of Items 1 to 19.

Item 21. The liquid crystal display element according to Item 20, wherein the operation mode of the liquid crystal display element is IPS mode, VA mode, FFS mode or FPA mode, and the driving mode of the liquid crystal display element is an active matrix mode.

Item 22. A polymer stable alignment type liquid crystal display element, comprising the liquid crystal composition according to any one of Items 1 to 19, and the polymerizable compound in the liquid crystal composition is polymerized.

Item 23. A liquid crystal display element without an alignment film, which contains the following items The liquid crystal composition according to any one of items 1 to 19, wherein the polymerizable compound in the liquid crystal composition is polymerized.

Item 24. Use of the liquid crystal composition according to any one of Items 1 to 19 in a liquid crystal display element.

Item 25. Use of the liquid crystal composition according to any one of Items 1 to 19 in a polymer stabilized alignment type liquid crystal display element.

Item 26. Use of the liquid crystal composition according to any one of Items 1 to 19 in a liquid crystal display element that does not have an alignment film.

The present invention also includes the following items. (a) A method of manufacturing a liquid crystal display element, which comprises disposing the above-mentioned liquid crystal composition between two substrates, and irradiating light with a voltage applied to the composition, so that the polymerizable compound contained in the composition Polymerization is performed to manufacture the above-mentioned liquid crystal display element. (b) The above liquid crystal composition, wherein the upper limit temperature of the nematic phase is 70°C or higher, the optical anisotropy (measured at 25°C) at a wavelength of 589nm is 0.08 or higher, and the dielectric anisotropy at a frequency of 1kHz ( Measured at 25°C) is -2 or less.

The present invention also includes the following items. (c) The above composition, although the compounds (5) to (7) described in JP 2006-199941 A are liquid crystal compounds with positive dielectric anisotropy, the above composition contains At least one compound in the group of these compounds. (d) The above composition containing at least two of the above polar compounds. (e) The aforementioned composition further containing a polar compound different from the aforementioned polar compound. (f) The above composition contains one, two or at least three optically active compounds, antioxidants, ultraviolet absorbers, pigments, and defoamers Additives such as agents, polymerizable compounds, polymerization initiators, polymerization inhibitors, and polar compounds. (g) AM device containing the above composition. (h) A device containing the above-mentioned composition and having TN mode, ECB mode, OCB mode, IPS mode, FFS mode, VA mode, or FPA mode. (i) A transmission element containing the above composition. (j) Use the above composition as a composition having a nematic phase. (k) Use as an optically active composition by adding an optically active compound to the above composition.

The composition of the present invention will be described in the following order. First, the composition of the composition will be explained. Second, the main characteristics of the component compounds and the main effects of the compounds on the composition will be explained. Thirdly, the combination of the components in the composition, the preferable ratio of the components, and the basis will be described. Fourth, the preferred form of the component compounds will be described. Fifth, the preferred component compounds are shown. Sixth, additives that can be added to the composition will be described. Seventh, the synthesis method of the component compounds will be described. Finally, the use of the composition will be explained.

First, the composition of the composition will be explained. The composition of the present invention is classified into composition A and composition B. In addition to the liquid crystal compound selected from the compound (1) and the compound (2), the composition A may further contain other liquid crystal compounds, additives, and the like. The "other liquid crystal compound" is a liquid crystal compound different from the compound (1) and the compound (2). Such compounds are mixed in the composition for the purpose of further adjusting the characteristics. The additives are optically active compounds, antioxidants, ultraviolet absorbers, pigments, defoamers, polymerizable compounds, polymerization initiators, polymerization inhibitors, polar compounds, and the like.

Composition B essentially only includes compounds selected from compound (1) and compound (2) The liquid crystal compound. "Substantially" means that although the composition may contain additives, it does not contain other liquid crystal compounds. Compared with composition A, the number of components of composition B is small. From the viewpoint of cost reduction, composition B is superior to composition A. The composition A is superior to the composition B from the viewpoint that the characteristics can be further adjusted by mixing other liquid crystal compounds.

Second, the main characteristics of the component compounds and the main effects of the compounds on the characteristics of the composition will be explained. Based on the effects of the present invention, the main characteristics of the component compounds are summarized in Table 2. In the notation in Table 2, L means large or high, M means medium, and S means small or low. The symbols L, M, and S are classifications based on the qualitative comparison between component compounds, and the symbol 0 means that the value is zero or close to zero.

When the component compounds are mixed in the composition, the main effects of the component compounds on the characteristics of the composition are as follows. The compound (1) increases the dielectric anisotropy. Compound (2) increases the upper limit temperature or decreases the viscosity. The compound (3) or the compound (4) is adsorbed on the surface of the substrate by the action of the polar group and controls the alignment of the liquid crystal molecules. In order to obtain the desired effect, these compounds must High compatibility of crystalline compounds. Compound (5) forms a polymer by polymerization. Since the polymer stabilizes the alignment of liquid crystal molecules, the response time of the device is shortened and the afterimage of the image is improved.

Thirdly, the combination of the components in the composition, the preferable ratio of the components, and the basis will be described. A preferable combination of the components in the composition is compound (1) + compound (2). The vertical alignment of liquid crystal molecules can be achieved by combining polar compounds and polymerizable compounds (or polymers thereof) in the composition. If the "other liquid crystal compound" is small, the same effect can be achieved even if it is added to the composition.

In order to increase the dielectric anisotropy, the preferred proportion of the compound (1) is about 10% by weight or more, and in order to reduce the viscosity, the preferred proportion of the compound (1) is about 90% by weight or less. A particularly desirable ratio is in the range of about 15% by weight to about 80% by weight. A particularly preferred ratio is in the range of about 20% by weight to about 70% by weight.

In order to increase the maximum temperature or reduce the viscosity, the preferred ratio of the compound (2) is about 10% by weight or more, and in order to increase the dielectric anisotropy, the preferred ratio of the compound (2) is about 70% by weight or less. A particularly desirable ratio is in the range of about 10% by weight to about 65% by weight. A particularly preferred ratio is in the range of about 15% by weight to about 60% by weight.

The compound (3) and the compound (4) are added to the composition for the purpose of controlling the alignment of liquid crystal molecules. In order to align the liquid crystal molecules, the preferred ratio of compound (3) or compound (4) is about 0.05% by weight or more. In order to prevent poor display of the device, the preferred ratio of compound (3) or compound (4) is about 10%. Weight% or less. A particularly preferred ratio is in the range of about 0.1% by weight to about 7% by weight. A particularly preferred ratio is in the range of about 0.5% by weight to about 5% by weight.

The compound (5) is added to the composition for the purpose of being suitable for a polymer stable alignment type element. In order to improve the long-term reliability of the device, the preferred ratio of the compound (5) is about 0.03% by weight or more, and in order to prevent poor display of the device, the preferred ratio of the compound (5) is about 10% by weight or less. A particularly preferred ratio is in the range of about 0.1% by weight to about 2% by weight. A particularly preferred ratio is in the range of about 0.2% by weight to about 1.0% by weight.

Fourth, the preferred form of the component compounds will be described. In formula (1) and formula (2), R ¹ and R ^{2 are} independently an alkyl group having 1 to 12 carbons, an alkoxy group having 1 to 12 carbons, an alkenyl group having 2 to 12 carbons, at least one hydrogen Alkenyl groups having 2 to 12 carbons or alkenyloxy groups having 2 to 12 carbons substituted with fluorine or chlorine. In order to improve the stability to ultraviolet rays or heat, preferably R ¹ or R ² is an alkyl group having 1 to 12 carbons. In order to increase the dielectric anisotropy, preferably R ¹ or R ² is 1 to 12 carbons.的alkoxy。

R ³ and R ^{4 are} independently an alkyl group having 1 to 12 carbons, an alkoxy group having 1 to 12 carbons, an alkenyl group having 2 to 12 carbons, or a carbon number of 1 to 12 in which at least one hydrogen is substituted by fluorine or chlorine Or an alkenyl group having 2 to 12 carbons in which at least one hydrogen is replaced by fluorine or chlorine. In order to improve the stability to ultraviolet rays or heat, preferably R ³ or R ⁴ is an alkyl group having 1 to 12 carbons. In order to lower the minimum temperature or reduce the viscosity, preferably R ³ or R ⁴ is a carbon number of 2 to 12's alkenyl.

Preferred alkyl groups are methyl, ethyl, propyl, butyl, pentyl, hexyl, heptyl or octyl. In order to reduce the viscosity, particularly preferred alkyl groups are ethyl, propyl, butyl, pentyl or heptyl.

The preferred alkoxy groups are methoxy, ethoxy, propoxy, butoxy, pentoxy Oxy, hexyloxy or heptoxy. In order to reduce the viscosity, particularly preferred alkoxy groups are methoxy or ethoxy.

The preferred alkenyl groups are vinyl, 1-propenyl, 2-propenyl, 1-butenyl, 2-butenyl, 3-butenyl, 1-pentenyl, 2-pentenyl, 3 -Pentenyl, 4-pentenyl, 1-hexenyl, 2-hexenyl, 3-hexenyl, 4-hexenyl or 5-hexenyl. In order to reduce the viscosity, particularly preferred alkenyl groups are vinyl, 1-propenyl, 3-butenyl or 3-pentenyl. The preferred configuration of -CH=CH- in these alkenyl groups depends on the position of the double bond. In order to reduce viscosity and other reasons, preferred among alkenyl groups such as 1-propenyl, 1-butenyl, 1-pentenyl, 1-hexenyl, 3-pentenyl, and 3-hexenyl Trans configuration. Among alkenyl groups such as 2-butenyl, 2-pentenyl, and 2-hexenyl, the cis configuration is preferred.

Preferred alkenyloxy groups are vinyloxy, allyloxy, 3-butenyloxy, 3-pentenyloxy or 4-pentenyloxy. In order to reduce the viscosity, particularly preferred alkenyloxy groups are allyloxy or 3-butenyloxy.

Preferred examples of alkyl groups in which at least one hydrogen is replaced by fluorine or chlorine are fluoromethyl, 2-fluoroethyl, 3-fluoropropyl, 4-fluorobutyl, 5-fluoropentyl, 6-fluorohexyl, 7 -Fluoroheptyl or 8-fluorooctyl. In order to increase the dielectric anisotropy, particularly preferred examples are 2-fluoroethyl, 3-fluoropropyl, 4-fluorobutyl or 5-fluoropentyl.

Preferred examples of alkenyl groups in which at least one hydrogen is replaced by fluorine or chlorine are 2,2-difluorovinyl, 3,3-difluoro-2-propenyl, 4,4-difluoro-3-butenyl, 5,5-difluoro-4-pentenyl or 6,6-difluoro-5-hexenyl. In order to reduce the viscosity, a particularly preferred example is 2,2-difluorovinyl or 4,4-difluoro-3-butenyl.

Ring A and ring C are independently 1,4-cyclohexylene, 1,4-cyclohexenylene, tetrahydropyran-2,5-diyl, 1,4-phenylene, at least one hydrogen Fluorine or chlorine substituted 1,4-phenylene, naphthalene-2,6-diyl, naphthalene-2,6-diyl with at least one hydrogen substituted by fluorine or chlorine, chroman-2,6-diyl Or Chroman-2,6-diyl in which at least one hydrogen is replaced by fluorine or chlorine. Preferred ring A or ring C is 1,4-cyclohexylene, 1,4-cyclohexenylene, tetrahydropyran-2,5-diyl, 1,4-phenylene, 2-fluoro -1,4-phenylene, 2,3-difluoro-1,4-phenylene, 3,4,5-trifluoronaphthalene-2,6-diyl or 7,8-difluorochromane -2,6-diyl. Particularly preferred ring A or ring C is 1,4-cyclohexylene or 1,4-phenylene. Among these rings, in order to reduce the viscosity, the preferred ring A or ring C is 1,4-cyclohexylene. In order to increase the dielectric anisotropy, the preferred ring A or ring C is tetrahydropyran-2, For the 5-diyl group, in order to increase the optical anisotropy, the preferred ring A or ring C is 1,4-phenylene. Tetrahydropyran-2,5-diyl is

，較佳為

or

, Preferably

Ring B is 2,3-difluoro-1,4-phenylene, 2-chloro-3-fluoro-1,4-phenylene, 2,3- Difluoro-5-methyl-1,4-phenylene, 3,4,5-trifluoronaphthalene-2,6-diyl or 7,8-difluorochroman-2,6-diyl. The preferred ring B is 2,3-difluoro-1,4-phenylene, 2-chloro-3-fluoro-1,4-phenylene, or 7,8-difluorochroman-2,6 -Two bases. Particularly preferred ring B is 2,3-difluoro-1,4-phenylene or 2-chloro-3-fluoro-1,4-phenylene. A particularly preferred ring B is 2,3-difluoro-1,4-phenylene. Among these rings, in order to reduce the viscosity, the preferred ring B is 2,3-difluoro-1,4-phenylene, and in order to reduce the optical anisotropy, the preferred ring B is 2-chloro-3-fluoro -1,4-phenylene, in order to increase the dielectric anisotropy, the preferred ring B is 7,8-difluorochroman-2,6-diyl.

Ring D and ring E are independently 1,4-cyclohexylene, 1,4-phenylene, 2-fluoro-1,4-phenylene or 2,5-difluoro-1,4-phenylene . In order to reduce the viscosity or to increase the upper limit temperature, the ring D or ring E is preferably 1,4-cyclohexylene. In order to reduce the lower limit temperature, the ring D or ring E is preferably 1,4-phenylene.

Z ¹ and Z ^{2 are} independently a single bond, -CH ₂ CH ₂ -, -CH ₂ O-, -OCH ₂ -, -COO- or -OCO-. In order to reduce the viscosity, preferably Z ¹ or Z ² is a single bond, in order to reduce the lower limit temperature, preferably Z ¹ or Z ² is -CH ₂ CH ₂ -, in order to increase the dielectric anisotropy, the preferred Z ¹ Or Z ² is -CH ₂ O- or -OCH ₂ -. Z ³ is a single bond, -CH ₂ CH ₂ -, -CH ₂ O-, -OCH ₂ -, -COO- or -OCO-. In order to reduce the viscosity, the preferred Z ³ is a single bond, in order to reduce the lower limit temperature, the preferred Z ³ is -CH ₂ CH ₂ -, and in order to increase the upper limit temperature, the preferred Z ³ is -COO- or -OCO-.

a is 1, 2 or 3, b is 0 or 1, and the sum of a and b is 3 or less. In order to reduce the viscosity, the preferred a is 1, and in order to increase the upper limit temperature, the preferred a is 2 or 3. In order to reduce the viscosity, the preferable b is 0, and in order to reduce the lower limit temperature, the preferable b is 1. c is 1, 2 or 3. In order to reduce the viscosity, the preferred c is 1, in order to increase The upper limit temperature, preferably c is 2 or 3.

In formula (3), MES is a mesogenic group having at least one ring. Mesogenic groups are well known to those skilled in the art. A mesogenic group refers to a moiety that contributes to the formation of a liquid crystal phase when the compound has a liquid crystal phase (mesophase). A preferred example of compound (3) is compound (3-1).

In formula (4), R ⁵ is an alkyl group having 4 to 20 carbons. In the alkyl group, at least one -CH ₂ -can be controlled by -CH=CH-, -CF=CH-, -CH=CF-,- C≡C- or cycloalkylene having 3 to 8 carbon atoms, in these groups, at least one hydrogen may be substituted by fluorine or chlorine. x is 1 or 2, preferably 1.

Preferable R ⁵ is an alkyl group having 4 to 20 carbons. Particularly preferred R ⁵ is an alkyl group having 6 to 18 carbon atoms. At least one -CH ₂ -may be substituted with -CH=CH-, -CF=CH-, -CH=CF-, -C≡C- or -O-, and at least one hydrogen may be substituted with fluorine or chlorine.

In formulas (3) and (4), R ⁶ is a polar group. Since the compound (3) and the compound (4) are added to the composition, they are preferably stable to ultraviolet rays or heat. When the compound (3) and the compound (4) are added to the composition, it is preferable that the compound does not reduce the voltage holding ratio of the device. The compound (3) and the compound (4) preferably have low volatility. The preferred molar mass is 130 g/mol or more. A particularly preferred molar mass is in the range of 150 g/mol to 500 g/mol.

The polar group has a non-covalent bonding interaction with the surface of the glass substrate or the metal oxide film. Preferred polar groups have heteroatoms selected from the group of nitrogen, oxygen, sulfur and phosphorus. Preferred polar groups have at least one or at least two of these heteroatoms. Particularly preferred polar groups are selected from alcohols, primary, secondary and tertiary amines, ketones, A monovalent group derived by removing hydrogen from a compound in the group of carboxylic acid, thiol, ester, ether, thioether, and a combination of these. The structure of these groups may also be linear, branched, cyclic, or a combination of these. Particularly preferred polar groups have at least one of oxygen atoms of OH structure or nitrogen atoms of primary, secondary or tertiary amine structure. The best polar group is hydroxyl (carbon-OH).

Examples of the polar group R ⁶ are groups represented by formula (A1) to formula (A4).

In formulas (A1) to (A4), Sp ⁴ , Sp ⁶ and Sp ^{7 are} independently single bonds or groups (-Sp"-X"-), and X" is bonded to ring P. Sp" is the number of carbons The alkylene group having 1 to 20 is preferably an alkylene group having 1 to 12 carbon atoms. In the alkylene group, at least one -CH ₂ -can pass through -O-, -S-, -NH-, -N( R ⁰ )-, -CO-, -CO-O-, -O-CO-, -O-CO-O-, -S-CO-, -CO-S-, -N(R ⁰ )-CO- O-, -O-CO-N(R ⁰ )-, -N(R ⁰ )-CO-N(R ⁰ )-, -CH=CH- or -C≡C- substitution, among these groups, at least A hydrogen can be replaced by fluorine, chlorine or -CN, X" is -O-, -S-, -CO-, -CO-O-, -O-CO-, -O-CO-O-, -CO- N(R ⁰ )-, -N(R ⁰ )-CO-, -N(R ⁰ )-CO-N(R ⁰ )-, -OCH ₂ -, -CH ₂ O-, -SCH ₂ -,- CH ₂ S-, -CF ₂ O-, -OCF ₂ -, -CF ₂ S-, -SCF ₂ -, -CF ₂ CH ₂ -, -CH ₂ CF ₂ -, -CF ₂ CF ₂ -, -CH =N-, -N=CH-, -N=N-, -CH=CR ⁰ -, -CY ² =CY ³ -, -C≡C-, -CH=CH-CO-O-, -O- CO-CH=CH- or a single bond, where R ⁰ is hydrogen or an alkyl group having 1 to 12 carbons, and Y ² and Y ^{3 are} independently hydrogen, fluorine, chlorine or -CN. Preferred X" is -O-, -S-, -CO-, -COO-, -OCO-, -O-COO-, -CO-NR ⁰ -, -NR ⁰ -CO-, -NR ⁰ -CO-NR ⁰ -or single bond. Sp ⁵ is >CH-, >CR ^a1 -, >N- or >C<. That is, Sp ⁵ in formula (A2) is >CH-, >CR ^a1 -or >N-, and Sp ⁵ in formula (A3) means >C<.

The preferred Sp" is -(CH ₂ ) _p1 -, -(CH ₂ CH ₂ O) _q1 -CH ₂ CH ₂ -, -CH ₂ CH ₂ -S-CH ₂ CH ₂ -or -CH ₂ CH _2- NHCH ₂ CH ₂ -, where p1 is an integer from 1 to 12, and q1 is an integer from 1 to 3. A preferred group (-Sp"-X"-) is -(CH ₂ ) _p1 -, -(CH ₂ ) _p1 -O-, -(CH ₂ ) _p1 -O-CO-, -(CH ₂ ) _p1 -O-CO-O-, where p1 and q1 have the meanings shown above. Especially preferred groups Sp" is ethylene, propylene, butylene, pentylene, hexyl, heptyl, octyl, nonyl, decyl, undecyl, dodecyl, Stearyl, ethyleneoxyethylene, methyleneoxybutylene, ethylenethioethylene, ethylene-N-methyliminoethylene, 1-methylethylene, vinylene , Propylene and butylene.

此處，R^a1為碳數1至15的烷基，該烷基中，至少一個-CH₂-可經-C≡C-、-CH=CH-、-COO-、-OCO-、-CO-或-O-取代，該些基中，至少一個氫可經氟或氯取代，R⁰為氫或碳數1至12的烷基。 X ¹ is -NH ₂ , -NHR ^a1 , -N(R ^a1 ) ₂ , -OR ^a1 , -OH, -COOH, -SH, -SR ^a1 ,

Here, R ^a1 is an alkyl group having 1 to 15 carbon atoms. In the alkyl group, at least one -CH ₂ -can be controlled by -C≡C-, -CH=CH-, -COO-, -OCO-, -CO -Or -O- substitution, in these groups, at least one hydrogen may be substituted by fluorine or chlorine, and R ⁰ is hydrogen or an alkyl group having 1 to 12 carbons.

X ² is -O-, -CO-, -NH-, -NR ^a1 -, -S- or a single bond, Z ⁹ represents an alkylene group having 1 to 15 carbons, an alicyclic group having 5 to 6 carbons Or a combination of at least one ring and an alkylene group, in these groups, at least one hydrogen can be passed through -OH, -OR ^a1 , -COOH, -NH ₂ , -NHR ^a1 , -N(R ^a1 ) ₂ , fluorine or chlorine Instead, here, R ^a1 has the meaning shown above. p is 0, 1, 2, or 3. q is 2, 3, 4, or 5.

The ring P is an aromatic group having 6 to 25 carbons or an alicyclic group having 3 to 25 carbons, and these groups may be condensed rings. In these groups, one to three hydrogens may be substituted by ^RL . R ^L is -OH, -(CH ₂ ) _r -OH, fluorine, chlorine, -CN, -NO ₂ , -NCO, -NCS, -OCN, -SCN, -C(=O)N(R ⁰ ) ₂ , -C(=O)R ⁰ , -N(R ⁰ ) ₂ , -(CH ₂ ) _r -N(R ⁰ ) ₂ , -SH, -SR ⁰ , aryl groups with 6 to 20 carbons, carbon number Heteroaryl groups having 6 to 20, alkyl groups having 1 to 25 carbons, alkoxy groups having 1 to 25 carbons, alkylcarbonyl groups having 2 to 25 carbons, alkoxycarbonyl groups having 2 to 25 carbons, carbon numbers An alkylcarbonyloxy group having 2 to 25 or an alkoxycarbonyloxy group having 2 to 25 carbons. In these groups, at least one hydrogen may be substituted by fluorine or chlorine. Here, R ⁰ is hydrogen or a carbon number of 1 to 12's alkyl group.

Particularly preferred nitrogen-containing groups R ⁶ are -NH ₂ , -NH-(CH ₂ ) _n3 H, -(CH ₂ ) _n -NH ₂ , -(CH ₂ ) _n -NH-(CH ₂ ) _n3 H,- NH-(CH ₂ ) _n -NH ₂ , -NH-(CH ₂ ) _n -NH-(CH ₂ ) _n3 H, -(CH ₂ ) _n1 -NH-(CH ₂ ) _n2 -NH ₂ , -(CH ₂ ) _n1 -NH-(CH ₂ ) _n2 -NH-(CH ₂ ) _n3 H, -O-(CH ₂ ) _n -NH ₂ , -(CH ₂ ) _n1 -O-(CH ₂ ) _n -NH ₂ , -(CH ₂ ) _n1 -NH-(CH ₂ ) _n2 -OH, -O-(CH ₂ ) _n1 -NH-(CH ₂ ) _n2 -NH ₂ , -O-(CH ₂ ) _n1 -NH-( CH ₂ ) _n2 -OH or -(CH ₂ ) _n1 -NH-(CH ₂ ) _n2 -NH-(CH ₂ ) _n3 H, where n, n1, n2 and n3 are independently integers from 1 to 12, Preferably, it is 1, 2, 3 or 4.

Particularly preferred non-nitrogen-containing groups R ⁶ are -OH, -(CH ₂ ) _n -OH, -O-(CH ₂ ) _n -OH, -[O-(CH ₂ ) _n1 -] _n2 -OH, -COOH , -(CH ₂ ) _n -COOH, -O-(CH ₂ ) _n -COOH or -[O-(CH ₂ ) _n1 -] _n2 -COOH, where n, n1 and n2 are independently 1 to 12 The integer of is preferably 1, 2, 3 or 4.

From the viewpoint of high solubility in the liquid crystal composition, R ^{6 is} particularly preferably -OH or -NH ₂ . -OH is superior to -O-, -CO- or -COO- because of its high anchoring force. Particularly preferred is a group having multiple heteroatoms (nitrogen, oxygen). The compound having such a polar group is effective even at a low concentration.

In the formula (3-1), R ⁷ is hydrogen, fluorine, chlorine, and an alkyl group having 1 to 25 carbons. In the alkyl group, at least one -CH ₂ -can be controlled by -NR ⁰ -, -O-, -S -, -CO-, -CO-O-, -O-CO-, -O-CO-O- or cycloalkylene substituted with carbon number 3 to 8, and at least one tertiary carbon (>CH-) Substitution by nitrogen (>N-), in these groups, at least one hydrogen may be substituted by fluorine or chlorine, where R ⁰ is hydrogen or an alkyl group having 1 to 12 carbons.

R ⁸ is an alkyl group having 1 to 25 carbon atoms. In the alkyl group, at least one -CH ₂ -may be -NR ⁰ -, -O-, -S-, -CO-, -COO-, -OCO-, -OCOO- or a cycloalkylene having 3 to 8 carbon atoms, where R ⁰ is hydrogen or an alkyl group having 1 to 12 carbon atoms, and at least one tertiary carbon (>CH-) can be substituted by nitrogen (>N- ) Substitution, and at least one hydrogen may be substituted with fluorine or chlorine, wherein R ⁸ has at least one of an oxygen atom of an OH structure, a sulfur atom of an SH structure, or a nitrogen atom of a primary, secondary or tertiary amine structure.

Ring F and ring G are independently an aromatic group with 6 to 25 carbons, a heteroaromatic group with 5 to 25 carbons, an alicyclic group with 3 to 25 carbons, or a heteroalicyclic group with 4 to 25 carbons In these groups, at least one hydrogen may be substituted by a group T, where the group T is -OH, -(CH ₂ ) _i -OH, fluorine, chlorine, -CN,- NO ₂ , -NCO, -NCS, -OCN, -SCN, -C(=O)N(R ⁰ ) ₂ , -C(=O)R ⁰ , -N(R ⁰ ) ₂ , -(CH ₂ ) _i -N(R ⁰ ) ₂ , aryl groups having 6 to 20 carbons, heteroaryl groups having 6 to 20 carbons, alkyl groups having 1 to 25 carbons, alkoxy groups having 1 to 25 carbons, and 2 carbons At least one of the alkylcarbonyl groups having to 25 alkylcarbonyl groups, the alkoxycarbonyl groups having 2 to 25 carbons, the alkylcarbonyloxy groups having 2 to 25 carbons, or the alkoxycarbonyloxy groups having 2 to 25 carbons, Hydrogen may be substituted by fluorine or chlorine. Here, R ⁰ is hydrogen or an alkyl group having 1 to 12 carbons, and i is 1, 2, 3, or 4.

Z ⁴ is -O-, -S-, -CO-, -CO-O-, -OCO-, -O-CO-O-, -OCH ₂ -, -CH ₂ O-, -SCH ₂ -,- CH ₂ S-, -CF ₂ O-, -OCF ₂ -, -CF ₂ S-, -SCF ₂ -, -(CH ₂ ) _i -, -CF ₂ CH ₂ -, -CH ₂ CF ₂ -,- (CF ₂ ) _i -, -CH=CH-, -CF=CF-, -C≡C-, -CH=CH-COO-, -OCO-CH=CH-, -C(R ⁰ ) ₂ -or A single bond. Here, R ⁰ is hydrogen or an alkyl group having 1 to 12 carbons, and i is 1, 2, 3, or 4.

d is 0, 1, 2, 3, 4, or 5.

In formula (4-1), R ⁹ is an alkyl group having 4 to 20 carbons. In the alkyl group, at least one -CH ₂ -can be controlled by -CH=CH-, -CF=CH-, -CH=CF- , -C≡C- or a cycloalkylene group having 3 to 8 carbon atoms, in these groups, at least one hydrogen may be substituted by fluorine or chlorine.

R ¹⁰ is an alkyl group having 1 to 25 carbons. In the alkyl group, at least one -CH ₂ -may be -NR ⁰ -, -O-, -S-, -CO-, -COO-, -OCO-, -OCOO- or a cycloalkylene having 3 to 8 carbon atoms, where R ⁰ is hydrogen or an alkyl group having 1 to 12 carbon atoms, and at least one tertiary carbon (>CH-) can be substituted by nitrogen (>N- ) Substitution, and at least one hydrogen may be substituted by fluorine or chlorine, wherein R ¹⁰ has at least one of an oxygen atom of an OH structure, a sulfur atom of an SH structure, and a nitrogen atom of a primary, secondary or tertiary amine structure.

In formulas (3-1-1) to (3-1-4), R ¹⁵ is an alkyl group having 1 to 8 carbon atoms or fluorine. Ring Q and ring R are independently 1,4-cyclohexylene, 1,4-phenylene, 2-fluoro-1,4-phenylene, 2-fluoro-1,3-phenylene, 2- Ethyl-1,4-phenylene, 2,6-diethyl-1,4-phenylene, 2-trifluoromethyl-1,4-phenylene, 2,3-difluoro-1 ,4-phenylene, 2,5-difluoro-1,4-phenylene, 2,6-difluoro-1,4-phenylene or 2,3,5,6-tetrafluoro-1, 4-phenylene. Ring S is cyclohexyl or phenyl.

Z ¹⁰ is a single bond, -CH ₂ CH ₂ -, -COO- or -OCO-. Z ¹¹ is a single bond, an alkylene group having 1 to 15 carbon atoms, an alicyclic group having 5 or 6 carbon atoms, or a combination of these groups. In these groups, at least one hydrogen may pass through -OH, -OR ^a1 , -COOH, -NH ₂ , -NHR ^a1 , -N(R ^a1 ) ₂ , fluorine or chlorine substituted, where R ^a1 is an alkyl group having 1 to 15 carbons, and in the alkyl group, at least one -CH _2- It may be substituted by -C≡C-, -CH=CH-, -COO-, -OCO-, -CO- or -O-. In these groups, at least one hydrogen may be substituted by fluorine or chlorine.

Sp ⁴ is a single bond, -CH ₂ CH ₂ -, -CH ₂ CH ₂ CH ₂ -, -CH ₂ O- or -OCH ₂ -. Sp ⁷ is a single bond or an alkylene group having 1 to 5 carbon atoms. In the alkylene group, -CH ₂ -may be substituted with -O- or -NH-. X ³ is -OH, -COOH, -SH, -OCH ₃ or -NH ₂ . X ⁴ is a single bond or -O-. s is 0, 1, 2, 3, 4, or 5.

The aromatic group refers to an aryl group or a substituted aryl group. The heteroaryl group refers to an aromatic group having at least one heteroatom. The aryl group and the heteroaryl group may be monocyclic or polycyclic. That is, these groups have at least one ring, the ring may be condensed (for example, naphthyl), the two rings may be connected by a covalent bond (for example, biphenyl), or may have a combination of a condensed ring and a linking ring . Preferred heteroaryl groups have at least one heteroatom selected from the group of nitrogen, oxygen, sulfur, and phosphorus.

Preferred aryl or heteroaryl groups have carbon numbers of 6 to 25, and can also be five-membered, six-membered or seven-membered rings. The preferred aryl or heteroaryl group may be a monocyclic ring, and may also be a bicyclic or tricyclic ring. These groups may be condensed rings or substituted.

、苝、稠四苯、稠五苯、苯并芘、茀、茚、茚并茀、螺二茀中去除一個氫而衍生的一價基。 The preferred aryl groups are derived from benzene, biphenyl, terphenyl, [1,1':3',1"] terphenyl, naphthalene, anthracene, binaphthyl, phenanthrene, pyrene, dihydropyrene,

, Perylene, thick tetracene, thick pentacene, benzopyrene, stilbene, indene, indeno pyrene, spirodipine, a monovalent group derived by removing one hydrogen.

Preferred heteroaryl groups are selected from pyrrole, pyrazole, imidazole, 1,2,3-triazole, 1,2,4-triazole, tetrazole, furan, thiophene, selenophene, oxazole, isooxazole Azole, 1,2-thiazole, 1,3-thiazole, 1,2,3-oxadiazole, 1,2,4-oxadiazole, 1,2,5-oxadiazole, 1,3,4- Five-membered ring compounds such as oxadiazole, 1,2,3-thiadiazole, 1,2,4-thiadiazole, 1,2,5-thiadiazole, 1,3,4-thiadiazole or pyridine , Pyridazine, pyrimidine, pyrazine, 1,3,5-triazine, 1,2,4-triazine, 1,2,3-triazine, 1,2,4,5-tetrazine, 1,2 ,3,4-tetrazine, 1,2,3,5-tetrazine and other six-membered ring compounds are monovalent groups derived by removing one hydrogen.

The preferred heteroaryl groups are also selected from indole, isoindole, indoleazine, indazole, benzimidazole, benzotriazole, purine, naphthimidazole, phenanthrimidazole, pyridoimidazole (pyridimidazole), pyrazinoimidazole, quinoxaline imidazole, benzoxazole, naphthoxazole, anthraoxazole, phenanthroxazole, isoxazole, benzothiazole, benzofuran, isobenzo Furan, dibenzofuran, quinoline, isoquinoline, pteridine, benzo-5,6-quinoline, benzo-6,7-quinoline, benzo-7,8-quinoline, benziso Quinoline, acridine, phenothiazine, phenoxazine, benzopyridazine, benzopyrimidine, quinoxaline, phenazine, naphthyridine, azacarbazole, benzocarboline, phenanthridine, phenanthrazine, thiophene One derived from the removal of one hydrogen from condensed ring compounds such as and [2,3b]thiophene, thieno[3,2b]thiophene, dithienothiophene, isobenzothiophene, dibenzothiophene, benzothiadiazolethiophene, etc. Price base. A preferred heteroaryl group is also a monovalent group derived by removing one hydrogen from a ring formed by combining two groups selected from the five-membered ring, six-membered ring, and condensed ring. These heteroaryl groups may be substituted with alkyl, alkoxy, thioalkyl, fluoro, fluoroalkyl, aryl or heteroaryl groups.

The alicyclic group may be saturated or may also be unsaturated. That is, these groups may have only single bonds, or may have a combination of single bonds and multiple bonds. Saturated rings are better than unsaturated rings.

The alicyclic group may be one ring, or may be multiple rings. Preferred examples of these groups are monocyclic, bicyclic or tricyclic rings having 3 to 25 carbon atoms, and these groups may be condensed rings or substituted. Preferred examples of these groups are five-membered ring, six-membered ring, seven-membered ring or eight-membered ring. In these groups, at least one carbon may be substituted by silicon, at least one >CH- may be substituted by >N-, and At least one -CH ₂ -may be substituted with -O- or -S-.

Preferred alicyclic groups are selected from five-membered rings such as cyclopentane, tetrahydrofuran, tetrahydrothiofuran, pyrrolidine, cyclohexane, cyclohexene, tetrahydropyran, tetrahydrothiopyran, Six-membered rings such as 1,3-dioxane, 1,3-dithiane, and piperidine, seven-membered rings such as cycloheptane, Tetrahydronaphthalene, decahydronaphthalene, indane, bicyclo[1.1.1]pentane, bicyclo[2.2.2]octane, spiro[3.3]heptane, octahydro-4,7-methyleneindan, etc. A divalent group derived from the removal of two hydrogens in a condensed ring.

In formula (5), P ⁴ , P ⁵ and P ^{6 are} independently polymerizable groups. Preferably P ⁴ , P ⁵ or P ⁶ is a group selected from the group of polymerizable groups represented by formula (P-1) to formula (P-5). Particularly preferred P ⁴ , P ⁵ or P ⁶ is a group represented by formula (P-1), formula (P-2) or formula (P-3). Particularly preferred P ⁴ , P ⁵ or P ⁶ is a group represented by formula (P-1) or formula (P-2). The most preferable P ⁴ , P ⁵ or P ⁶ is a group represented by formula (P-1). The preferred group represented by the formula (P-1) is -OCO-CH=CH ₂ or -OCO-C(CH ₃ )=CH ₂ . The wavy lines of formula (P-1) to formula (P-5) indicate the bonding position.

In formulas (P-1) to (P-5), M ¹ , M ² and M ^{3 are} independently hydrogen, fluorine, an alkyl group with a carbon number of 1 to 5, or carbon in which at least one hydrogen is substituted by fluorine or chlorine The number is an alkyl group of 1 to 5. In order to improve the reactivity, preferred M ¹ , M ² or M ³ are hydrogen or methyl. More preferably, M ¹ is hydrogen or methyl, and more preferably M ² or M ³ is hydrogen.

Sp ⁹ , Sp ¹⁰ and Sp ^{11 are} independently a single bond or an alkylene group having 1 to 10 carbon atoms. In the alkylene group, at least one -CH ₂ -may be -O-, -COO-, -OCO- or -OCOO- substituted, and at least one -CH ₂ CH ₂ -may be substituted with -CH=CH- or -C≡C-. In these groups, at least one hydrogen may be substituted with fluorine or chlorine. Preferably Sp ⁹ , Sp ¹⁰ or Sp ¹¹ is a single bond, -CH ₂ CH ₂ -, -CH ₂ O-, -OCH ₂ -, -COO-, -OCO-, -CO-CH=CH- or- CH=CH-CO-. Particularly, Sp ⁹ , Sp ¹⁰ or Sp ¹¹ is a single bond.

Ring T and ring V are independently cyclohexyl, cyclohexenyl, phenyl, 1-naphthyl, 2-naphthyl, tetrahydropyran-2-yl, 1,3-dioxan-2-yl, Pyrimidine-2-yl or pyridin-2-yl, in these rings, at least one hydrogen can be passed through fluorine, chlorine, alkyl with 1 to 12 carbons, alkoxy with 1 to 12 carbons, or at least one hydrogen A fluorine or chlorine substituted alkyl group having 1 to 12 carbon atoms. Preferably ring T or ring V is phenyl. Ring U is 1,4-cyclohexenylene, 1,4-cyclohexenylene, 1,4-phenylene, naphthalene-1,2-diyl, naphthalene-1,3-diyl, naphthalene-1 ,4-diyl, naphthalene-1,5-diyl, naphthalene-1,6-diyl, naphthalene-1,7-diyl, naphthalene-1,8-diyl, naphthalene-2,3-diyl , Naphthalene-2,6-diyl, naphthalene-2,7-diyl, tetrahydropyran-2,5-diyl, 1,3-dioxane-2,5-diyl, pyrimidine-2, 5-diyl or pyridine-2,5-diyl, in these rings, at least one hydrogen may be fluorine, chlorine, alkyl with 1 to 12 carbons, alkoxy with 1 to 12 carbons, or at least one The hydrogen is substituted with an alkyl group having 1 to 12 carbons substituted with fluorine or chlorine. Preferred ring U is 1,4-phenylene or 2-fluoro-1,4-phenylene.

Z ¹² and Z ^{13 are} independently a single bond or an alkylene group having 1 to 10 carbon atoms. In the alkylene group, at least one -CH ₂ -may be -O-, -CO-, -COO- or -OCO- Substitution, and at least one -CH ₂ CH ₂ -can be replaced by -CH=CH-, -C(CH ₃ )=CH-, -CH=C(CH ₃ )- or -C(CH ₃ )=C(CH ₃ )-Substitution, in these groups, at least one hydrogen may be substituted with fluorine or chlorine. Preferably Z ¹² or Z ¹³ is a single bond, -CH ₂ CH ₂ -, -CH ₂ O-, -OCH ₂ -, -COO- or -OCO-. Z ¹² or Z ¹³ is particularly preferably a single bond.

t is 0, 1, or 2. Preferably t is 0 or 1. u, v and w are independently 0, 1, 2, 3, or 4, and the sum of u, v, and w is 3 or more. Preferably u, v or w is 1 or 2.

Fifth, the preferred component compounds are shown. Preferred compound (1) is the compound (1-1) to the compound (1-22) described in Item 3. Among these compounds, it is preferable that at least one of the first components is compound (1-1), compound (1-3), compound (1-4), compound (1-6), compound (1-8) or Compound (1-10). Preferably at least two of the first components are compound (1-1) and compound (1-6), compound (1-1) and compound (1-10), compound (1-3) and compound (1- 6) Compound (1-3) and compound (1-10), compound (1-4) and compound (1-6) or a combination of compound (1-4) and compound (1-8).

Preferred compound (2) includes compound (2-1) to compound (2-13) described in Item 6. Among these compounds, at least one of the second components is preferably compound (2-1), compound (2-3), compound (2-5), compound (2-6), compound (2-8) or Compound (2-9). Preferably at least two of the second components are compound (2-1) and compound (2-3), compound (2-1) and compound (2-5) or compound (2-1) and compound (2- 6) The combination.

Preferred compound (3) includes compound (3-1-1) to compound (3-1-4) described in Item 13. Among these compounds, it is preferable that at least one of the first additives is compound (3-1-1). Preferably, at least two of the first additives are a combination of compound (3-1-1) and compound (3-1-2).

Preferred compound (4) includes compound (4-1-1) to compound (4-1-29) described in Item 14. Generally speaking, compound (3) is superior to compound (4).

Particularly preferred compound (3-1) is selected from the following compounds.

In formulas (3-1-1-1) to (3-1-4-4), R ¹⁵ is an alkyl group having 1 to 8 carbon atoms or fluorine.

Particularly preferred compound (4-1) is selected from the following compounds (4-1-1-1) to (4-1-29-1).

Preferred compound (5) includes compound (5-1) to compound (5-7) described in Item 18. Among these compounds, it is preferable that at least one of the second additives is compound (5-2), compound (5-5) or compound (5-7). Preferably at least two of the second additives are compound (5-1) and compound (5-2), compound (5-2) and compound (5-5) or compound (5-2) and compound (5-2) -7) combination.

Sixth, additives that can be added to the composition will be described. Such additives include optically active compounds, antioxidants, ultraviolet absorbers, pigments, defoamers, polymerizable compounds, polymerization initiators, polymerization inhibitors, polar compounds, and the like. For the purpose of causing a helical structure of liquid crystal molecules to impart a torsion angle, an optically active compound is added to the composition. Examples of such compounds are compound (6-1) to compound (6-5). A preferable ratio of the optically active compound is about 5 wt% or less. A particularly preferable ratio is in the range of about 0.01% by weight to about 2% by weight.

In order to prevent the decrease in specific resistance caused by heating in the atmosphere, or to maintain a large voltage holding ratio not only at room temperature but also at a temperature close to the upper limit temperature after the element is used for a long time, the Antioxidant is added to the composition. Preferred examples of antioxidants are compound (7) in which n is an integer from 1 to 9, and the like.

In compound (7), preferred n is 1, 3, 5, 7, or 9. A particularly good n is 7. The compound (7) with n being 7 has low volatility and is therefore effective for maintaining a large voltage retention rate not only at room temperature but also at a temperature close to the upper limit temperature after the device is used for a long time. In order to obtain the above effect, the preferred ratio of the antioxidant is about 50 ppm or more. In order not to lower the upper limit temperature or to increase the lower limit temperature, the preferred ratio of the antioxidant is about 600 ppm or less. A particularly preferred ratio is in the range of about 100 ppm to about 300 ppm.

Preferred examples of ultraviolet absorbers are benzophenone derivatives, benzoate derivatives, triazole derivatives and the like. In addition, light stabilizers such as amines with steric hindrance are also preferable. In order to obtain the above effects, the preferred ratio of these absorbents or stabilizers is about 50 ppm or more. In order not to lower the upper limit temperature or increase the lower limit temperature, the preferred ratio of these absorbents or stabilizers is about 10000 ppm or less. A particularly preferred ratio is in the range of about 100 ppm to about 10000 ppm.

In order to be suitable for a guest host (GH) mode device, dichroic dyes such as azo dyes and anthraquinone dyes are added to the composition. The preferred ratio of the pigment is in the range of about 0.01% by weight to about 10% by weight. To prevent foaming, antifoaming agents such as dimethyl silicone oil and methyl phenyl silicone oil are added to the composition. In order to obtain the above effect, the preferred ratio of the defoamer is about 1 ppm or more, and in order to prevent display failure, the preferred ratio of the defoamer is about 1000 ppm or less. A particularly preferred ratio is in the range of about 1 ppm to about 500 ppm.

In order to be suitable for polymer stable alignment (PSA) type components, use Polymeric compound. Compound (5) is suitable for this purpose. The compound (5) and a polymerizable compound different from the compound (5) may be added to the composition together. Preferred examples of such polymerizable compounds are acrylates, methacrylates, vinyl compounds, vinyloxy compounds, propenyl ethers, epoxy compounds (oxetane, oxetane), vinyl ketones And other compounds. A particularly preferred example is acrylate or methacrylate. Based on the total weight of the polymerizable compound, the preferred ratio of the compound (5) is about 10% by weight or more. A particularly preferable ratio is about 50% by weight or more. A particularly preferred ratio is about 80% by weight or more. A particularly preferred ratio is also 100% by weight. By changing the type of compound (5), or by combining another polymerizable compound with compound (5) at an appropriate ratio, the reactivity of the polymerizable compound or the pretilt angle of liquid crystal molecules can be adjusted. By optimizing the pretilt angle, a short response time of the device can be achieved. The alignment of the liquid crystal molecules is stabilized, so a large contrast ratio or a long life can be achieved.

The polymerizable compound is polymerized by ultraviolet irradiation. It is also possible to perform polymerization in the presence of an appropriate initiator such as a photopolymerization initiator. Appropriate conditions for carrying out the polymerization, appropriate types of initiators, and appropriate amounts are known to those skilled in the art and are described in the literature. For example, as a photopolymerization initiator, Irgacure 651 (registered trademark; BASF), Irgacure 184 (registered trademark; BASF) or Darocur 1173 (registered trademark; BASF) is suitable for free radical polymerization. Based on the total weight of the polymerizable compound, the preferred ratio of the photopolymerization initiator is in the range of about 0.1% by weight to about 5% by weight. A particularly desirable ratio is in the range of about 1% by weight to about 3% by weight.

When storing polymerizable compounds, in order to prevent polymerization, polymerization can also be added Inhibitor. The polymerizable compound is usually added to the composition without removing the polymerization inhibitor. Examples of polymerization inhibitors are hydroquinone, hydroquinone derivatives such as methylhydroquinone, 4-tert-butylcatechol, 4-methoxyphenol, phenothiazine, and the like.

Polar compounds are organic compounds with polarity. Here, no compound having an ionic bond is included. Atoms such as oxygen, sulfur, and nitrogen are negatively charged and tend to have partial negative charges. Carbon and hydrogen are neutral or have a tendency to have a partial positive charge. Polarity is caused by the uneven distribution of partial charges among atoms of different species in the compound. For example, the polar compound has at least one partial structure such as -OH, -COOH, -SH, -NH ₂ , >NH, and >N-.

Seventh, the synthesis method of the component compounds will be described. These compounds can be synthesized by known methods. Illustrate the synthesis method. Compound (1-1) was synthesized by the method described in Japanese Patent Application Publication No. Hei 2-503441. Compound (2-1) was synthesized by the method described in Japanese Patent Application Laid-Open No. 59-176221. Compound (3-1) was synthesized by the method described in International Publication No. 2012-038026. Part of compound (4) is commercially available. Compound (5-1) was synthesized by the method described in International Publication No. 2013-161576. A part of compound (7) is commercially available. The compound of formula (7) where n is 1 can be obtained from Sigma-Aldrich Corporation. Compound (7) in which n is 7 is synthesized by the method described in the specification of U.S. Patent No. 3660505.

Compounds without a description of the synthesis method can be synthesized by the method described in the following book: "Organic Syntheses" (John Wiley & Sons, Inc.), "Organic Reactions" (Organic Reactions) , John Wiley & Sons Publishing Company), "Comprehensive Organic Synthesis" (Pergamon Press), New Experimental Chemistry Lecture (Maruzen), etc. The composition is prepared from the compound obtained in the above manner by a known method. For example, the component compounds are mixed and then heated to dissolve each other.

Finally, the use of the composition will be explained. Most of the compositions have a lower limit temperature of about -10°C or lower, an upper limit temperature of about 70°C or higher, and an optical anisotropy in the range of about 0.07 to about 0.20. A composition having an optical anisotropy in the range of about 0.08 to about 0.25 can be prepared by controlling the ratio of the component compounds or by mixing other liquid crystal compounds. Furthermore, it is also possible to prepare a composition having an optical anisotropy in the range of about 0.10 to about 0.30 through trial and error. The device containing this composition has a large voltage holding ratio. This composition is suitable for AM devices. The composition is particularly suitable for transmission type AM devices. The composition can be used as a composition having a nematic phase, and can be used as an optically active composition by adding an optically active compound.

This composition can be used for AM devices. It can also be used for PM devices. The composition can be used for AM devices and PM devices with PC, TN, STN, ECB, OCB, IPS, FFS, VA, FPA and other modes. It is particularly preferred for AM devices with TN, OCB, IPS, FFS and other modes. In an AM device with an IPS mode or an FFS mode, when no voltage is applied, the alignment of the liquid crystal molecules may be parallel to the glass substrate, or may be vertical. These elements can be reflective, transmissive or semi-transmissive. It is preferably used for transmissive elements. Can also be used for amorphous silicon-TFT elements or polysilicon-TFT elements Pieces. The composition can also be used for microencapsulation (microencapsulation) to produce nematic curvilinear aligned phase (NCAP) type elements or a polymer formed by forming a three-dimensional network polymer in the composition A polymer dispersed (PD) type device.

An example of a method of manufacturing an existing polymer stable alignment type element is described below. Assemble an element including two substrates, which are called an array substrate and a color filter substrate. The substrate has an alignment film. At least one of the substrates has an electrode layer. The liquid crystal compounds are mixed to prepare a liquid crystal composition. A polymerizable compound is added to this composition. If necessary, additives can be further added. The composition is injected into the device. Light irradiation is performed in a state where a voltage is applied to the element. Preferably it is ultraviolet light. The polymerizable compound is polymerized by light irradiation. This polymerization produces a polymer-containing composition. The polymer stabilized alignment type element is manufactured in the sequence described above.

In this sequence, when a voltage is applied, the liquid crystal molecules are aligned by the action of the alignment film and the electric field. According to this alignment, the molecules of the polymerizable compound are also aligned. Since the polymerizable compound is polymerized by ultraviolet rays in this state, a polymer that maintains the alignment is produced. With the effect of the polymer, the response time of the device is shortened. Since the afterimage of the image is the poor operation of the liquid crystal molecules, the afterimage is also improved by the effect of the polymer. In addition, the polymerizable compound in the composition may be polymerized in advance, and the composition may be arranged between the substrates of the liquid crystal display element.

An example of a method of manufacturing an element without an alignment film is described below. Inject the mixture of liquid crystal compound, polymerizable compound and polar compound Alignment film components. Light irradiation is performed in a state where a voltage is applied to the element. The polymerizable compound is polymerized by light irradiation. By this polymerization, a layer of a composition containing a polymer and a polar compound is formed on the substrate.

In this sequence, the polar compounds are arranged on the substrate due to the interaction between the polar groups and the surface of the substrate. The polar compound aligns liquid crystal molecules. When a voltage is applied, the alignment of the liquid crystal molecules is further promoted, and the polymerizable compound is also aligned according to the alignment. Since the polymerizable compound is polymerized by ultraviolet rays in this state, a polymer that maintains the alignment is produced. Due to the effect of the polymer, the alignment of the liquid crystal molecules is additionally stabilized, and the response time of the device is shortened. Since the afterimage of the image is the poor operation of the liquid crystal molecules, the afterimage is also improved by the effect of the polymer.

[Example]

The present invention will be further described in detail through examples. The present invention is not limited by these embodiments. The present invention includes a mixture of composition (M1) and composition (M2). The present invention also includes a mixture obtained by mixing at least two of the compositions of the examples. The synthesized compound is identified by nuclear magnetic resonance (NMR) analysis and other methods. The characteristics of the compound, composition, and device were measured by the following methods.

NMR analysis: DRX-500 manufactured by Bruker BioSpin was used for measurement. ^{In the 1} H-NMR measurement, the sample is dissolved in a deuterated solvent such as CDCl ₃ and the measurement is performed at room temperature under conditions of 500 MHz and a cumulative number of 16 times. Use tetramethylsilane as the internal standard. ^{In the 19} F-NMR measurement, CFCl _{3 was} used as an internal standard, and the measurement was carried out at 24 times of accumulation. In the description of NMR spectroscopy, s means singlet, d means doublet, t means triplet, q means quartet, and quin means quintet. (quintet), sex refers to sextet, m refers to multiplet, and br refers to broad.

Gas chromatographic analysis: GC-14B gas chromatograph manufactured by Shimadzu Corporation was used for measurement. The carrier gas is helium (2mL/min). The sample vaporization chamber was set to 280°C, and the detector (flame ionization detector (FID)) was set to 300°C. For the separation of component compounds, a capillary column DB-1 manufactured by Agilent Technologies Inc. (length 30m, inner diameter 0.32mm, film thickness 0.25μm; fixed liquid phase is dimethyl polysiloxane; No polarity). After the column was kept at 200°C for 2 minutes, the temperature was increased to 280°C at a rate of 5°C/min. After preparing the sample into an acetone solution (0.1% by weight), 1 μL of it was injected into the sample vaporization chamber. The recorder is a C-R5A Chromatopac manufactured by Shimadzu Corporation or its equivalent. The obtained gas chromatogram shows the retention time of the peak corresponding to the component compound and the peak area.

The solvent used to dilute the sample can be chloroform, hexane, etc. In order to separate the component compounds, the following capillary column can be used. HP-1 (length 30m, inner diameter 0.32mm, film thickness 0.25μm) manufactured by Agilent Technologies, Rtx-1 (length 30m, inner diameter 0.32mm, film thickness 0.25μm) manufactured by Restek Corporation ), SGE International Pty. Ltd) BP-1 (length 30m, inner diameter 0.32mm, film thickness 0.25μm). For the purpose of preventing overlapping of compound peaks, a capillary column CBP1-M50-025 (length 50 m, inner diameter 0.25 mm, film thickness 0.25 μm) manufactured by Shimadzu Corporation can be used.

The ratio of the liquid crystal compound contained in the composition can be calculated by the method described below. A gas chromatograph (FID) was used to analyze the mixture of liquid crystal compounds. The peak area ratio in the gas chromatogram corresponds to the ratio of liquid crystal compounds. When using the capillary column described above, the correction factor of various liquid crystal compounds can be regarded as 1. Therefore, the ratio (weight %) of the liquid crystal compound can be calculated from the area ratio of the peak.

Measurement sample: When measuring the characteristics of the composition and the device, the composition is directly used as the sample. When measuring the characteristics of the compound, a sample for measurement was prepared by mixing the compound (15% by weight) in the mother liquid crystal (85% by weight). Based on the value obtained by the measurement, the property value of the compound is calculated by an extrapolation method. (Extrapolated value)={(Measured value of sample)-0.85×(Measured value of mother liquid crystal)}/0.15. When the smectic phase (or crystal) precipitates at 25°C under this ratio, the ratio of the compound to the mother liquid crystal is 10% by weight: 90% by weight, 5% by weight: 95% by weight, and 1% by weight: 99% by weight. The order of% changes. This extrapolation method is used to obtain the maximum temperature, optical anisotropy, viscosity, and dielectric anisotropy values related to the compound.

The following mother liquid crystals are used. The ratio of component compounds is expressed in% by weight.

Measurement method: Use the following method to measure the characteristics. Most of these methods are methods described in the JEITA standard (JEITA. ED-2521B) reviewed and designated by the Japan Electronics and Information Technology Industries Association (JEITA) or modified methods. No thin film transistor (TFT) was installed on the TN element used for the measurement.

(1) The upper limit temperature of the nematic phase (NI; °C): Place the sample on a hot plate of a melting point measuring device equipped with a polarizing microscope, and heat it at a rate of 1 °C/min. The temperature at which a part of the sample changes from a nematic phase to an isotropic liquid is measured. The upper limit temperature of the nematic phase is sometimes referred to simply as the "upper limit temperature".

(2) Lower limit temperature of nematic phase (TC; ℃): put the sample with nematic phase into a glass bottle and freeze at 0℃, -10℃, -20℃, -30℃ and -40℃ After 10 days of storage in the container, the liquid crystal phase was observed. For example, when the sample maintains a nematic phase at -20°C and changes to a crystalline or smectic phase at -30°C, the T _{C is} described as <-20°C. The lower limit temperature of the nematic phase is sometimes referred to simply as the "lower limit temperature".

(3) Viscosity (bulk viscosity; η; measured at 20°C; mPa·s): The E-type rotary viscometer manufactured by Tokyo Keiki Co., Ltd. was used for the measurement.

(4) Viscosity (rotational viscosity; γ1; measured at 25°C; mPa·s): According to M. Imai et al., "Molecular Crystals and Liquid Crystals", Vol. 259, The measurement was performed by the method described on page 37 (1995). A sample was injected into a VA device with a distance (cell gap) of 20 μm between two glass substrates. A voltage was applied stepwise in units of 1 volt in the range of 39 volts to 50 volts to the device. After the voltage was not applied for 0.2 seconds, the voltage was repeatedly applied under the conditions of applying only one rectangular wave (rectangular pulse; 0.2 seconds) and no application (2 seconds). The peak current and peak time of the transient current generated by the application are measured. The value of rotational viscosity is obtained from these measured values and the calculation formula (8) on page 40 of the paper by M. Imai et al. The dielectric anisotropy required for this calculation is measured by the method described in Measurement (6).

(5) Optical anisotropy (refractive index anisotropy; Δn; measured at 25°C): Using light with a wavelength of 589 nm, it was measured with an Abbe refractometer with a polarizing plate attached to an eyepiece. After rubbing the surface of the main shaft in one direction, drop the sample onto the main shaft. The refractive index n∥ is measured when the direction of polarized light is parallel to the direction of rubbing. The refractive index n⊥ is measured when the direction of polarized light is perpendicular to the direction of rubbing. The value of optical anisotropy is calculated according to the formula of △n=n∥-n⊥.

(6) Dielectric anisotropy (△ε; measured at 25℃): According to △ε=ε ∥-ε⊥ formula to calculate the value of dielectric anisotropy. The dielectric constant (ε∥ and ε⊥) is measured as follows.

1) Measurement of dielectric constant (ε∥): Coat a fully cleaned glass substrate with octadecyl triethoxysilane (0.16 mL) in ethanol (20 mL). After rotating the glass substrate with a spinner, it was heated at 150°C for 1 hour. A sample was placed in a VA element with a distance (cell gap) of 4 μm between two glass substrates, and the element was sealed with an adhesive cured with ultraviolet rays. A sine wave (0.5 V, 1 kHz) was applied to the device, and after 2 seconds, the dielectric constant ε (∥) in the long axis direction of the liquid crystal molecules was measured.

2) Measurement of dielectric constant (ε⊥): Coat a polyimide solution on a sufficiently cleaned glass substrate. After firing the glass substrate, rubbing treatment is performed on the resulting alignment film. The sample was injected into a TN device with a gap (cell gap) of 9 μm between two glass substrates and a twist angle of 80 degrees. A sine wave (0.5V, 1kHz) was applied to the device, and after 2 seconds, the dielectric constant (ε⊥) in the minor axis direction of the liquid crystal molecules was measured.

(7) Threshold voltage (Vth; measured at 25°C; V): LCD5100 luminance meter manufactured by Otsuka Electronics Co., Ltd. was used for measurement. The light source is a halogen lamp. Place the sample in a normally black mode (normally black mode) VA device with a distance (cell gap) of 4μm between two glass substrates and an anti-parallel rubbing direction, and use a UV-cured adhesive to make the device seal. The voltage (60 Hz, rectangular wave) applied to the device was gradually increased from 0V to 20V in units of 0.02V. At this time, the element was irradiated with light from the vertical direction, and the amount of light passing through the element was measured. Made when the amount of light reaches the maximum, the transmittance is 100%, and when the amount of light is the smallest Voltage-transmittance curve with 0% transmittance at time. The threshold voltage is expressed as the voltage when the transmittance reaches 10%.

(8) Voltage retention rate (VHR-1; measured at 25°C; %): The TN device used for the measurement has a polyimide alignment film, and the interval (cell gap) between two glass substrates is 5 μm. After the device is injected with the sample, it is sealed with a UV-curing adhesive. A pulse voltage (5V, 60 microseconds) was applied to the TN device for charging. The attenuated voltage was measured in a period of 16.7 milliseconds with a high-speed voltmeter, and the area A between the voltage curve per unit period and the horizontal axis was obtained. Area B is the area when the voltage is not attenuated. The voltage retention rate is expressed by the percentage of area A to area B.

(9) Voltage retention rate (VHR-2; measured at 80°C; %): The voltage retention rate was measured in the same procedure as above except that it was measured at 80°C instead of 25°C. The obtained value is represented by VHR-2.

(10) Voltage retention rate (VHR-3; measured at 25°C; %): After irradiating ultraviolet rays, the voltage retention rate is measured to evaluate the stability to ultraviolet rays. The TN device used for the measurement has a polyimide alignment film, and the cell gap is 5 μm. The sample was injected into the element, and light was irradiated for 20 minutes. The light source is an ultra-high pressure mercury lamp USH-500D (manufactured by Ushio Motor), and the distance between the element and the light source is 20 cm. In the measurement of VHR-3, the attenuated voltage was measured during 16.7 milliseconds. The composition with large VHR-3 has large stability to ultraviolet rays. VHR-3 is preferably 90% or more, and more preferably 95% or more.

(11) Voltage holding rate (VHR-4; measured at 25°C; %): After the TN element with the sample injected was heated in a thermostat at 80°C for 500 hours, the voltage retention was measured to evaluate the stability to heat. In the measurement of VHR-4, the attenuated voltage was measured during 16.7 milliseconds. A composition with a large VHR-4 has a large stability to heat.

(12) Response time (τ; measured at 25°C; ms): The LCD5100 luminance meter manufactured by Otsuka Electronics Co., Ltd. was used for the measurement. The light source is a halogen lamp. The low-pass filter is set to 5kHz. The sample was placed in a VA device having a distance (cell gap) between two glass substrates of 3.5 μm and no alignment film. The device is sealed with an adhesive that is cured by ultraviolet light. While applying a voltage of 30 V to the device, ultraviolet rays of 78 mW/cm ² (405 nm) were irradiated for 449 seconds (35 J). For the irradiation of ultraviolet rays, a multi-metal lamp M04-L41 for ultraviolet curing made by EYE GRAPHICS Co., Ltd. was used. A rectangular wave (120 Hz) was applied to this element. At this time, the element was irradiated with light from the vertical direction, and the amount of light passing through the element was measured. When the amount of light reaches the maximum, the transmittance is regarded as 100%, and when the amount of light is minimum, the transmittance is regarded as 0%. The maximum voltage of the rectangular wave is set so that the transmittance becomes 90%. The minimum voltage of the rectangular wave is set to 2.5V at which the transmittance becomes 0%. The response time is expressed by the time (rise time; rise time; milliseconds) required for the transmittance to change from 10% to 90%.

(13) Elastic constant (K11: splay elastic constant, K33: bend elastic constant; measured at 25°C; pN): EC- manufactured by TOYO Corporation was used for measurement. Type 1 spring constant tester. The distance between the two glass substrates (cell gap) is 20μm vertically Inject the sample into the component. A charge of 20 volts to 0 volts was applied to the device, and the capacitance and applied voltage were measured. Use the formula (2.98) and formula (2.101) on page 75 of "Liquid Crystal Device Handbook" (Nikkan Kogyo Kogyo) to fit the measured capacitance (C) and applied voltage (V). Equation (2.100) obtains the value of the elastic constant.

(14) Specific resistance (ρ; measured at 25°C; Ωcm): Put 1.0 mL of the sample in a container equipped with electrodes. A DC voltage (10V) was applied to the container, and the DC current after 10 seconds was measured. The specific resistance is calculated by the following formula. (Specific resistance)={(voltage)×(capacitance of container)}/{(DC current)×(dielectric constant of vacuum)}.

(15) Pretilt angle (degrees): A spectroscopic ellipsometer M-2000U (manufactured by J.A. Woollam Co., Inc.) was used for the measurement of the pretilt angle.

(16) Alignment stability (liquid crystal alignment axis stability): The change of the liquid crystal alignment axis on the electrode side of the liquid crystal display element was evaluated. Measure the liquid crystal alignment angle Φ (before) on the electrode side before the stress is applied, then apply a rectangular wave of 4.5V, 60Hz to the device for 20 minutes, buffer for 1 second, and measure the liquid crystal alignment on the electrode side again after 1 second and 5 minutes later Angle Φ(after). From these values, the following formula was used to calculate the change ΔΦ (deg.) of the liquid crystal alignment angle after 1 second and 5 minutes later.

△Φ(deg.)=Φ(after)-Φ(before) (Equation 2)

Based on J. Hilfick, B. Jensen, C. Hessinger, J.F. Elman, E. Montebach, D. Bryant and PJ Boss (J. Hilfiker, B. Johs, C. Herzinger, JFElman, E. Montbach, D. Bryant, and PJBos), "Thin Solid Films", 455 -456, (2004)596-600 is used as a reference to carry out these measurements. It can be said that the smaller the ΔΦ, the smaller the rate of change of the liquid crystal alignment axis, and the better the stability of the liquid crystal alignment axis.

The examples of the composition are shown below. The component compounds are represented by symbols based on the definition in Table 3 below. In Table 3, the three-dimensional configuration related to 1,4-cyclohexylene is the trans configuration. The number in parentheses after the symbolized compound indicates the chemical formula to which the compound belongs. The symbol (-) refers to other liquid crystal compounds. The ratio (percentage) of the liquid crystal compound is the weight percentage (% by weight) based on the weight of the liquid crystal composition containing no additives. Finally, the characteristic values of the composition are summarized.

Examples of components

1. Raw materials

The polar compound-added composition is injected into the element without the alignment film. After irradiating ultraviolet rays, the vertical alignment of the liquid crystal molecules in the device was studied. First, the raw materials will be described. The raw materials are suitable from composition (M1) to composition (M18), polar compound (PC-1) to polar compound (PC-33), polymerizable compound (RM-1) to polymerizable compound (RM-7) select. The composition is as follows.

[Composition (M1)]

NI=73.2℃; Tc<-20℃; △n=0.113; △ε=-4.0; Vth=2.18V; η=22.6 mPa. s.

[Composition (M2)]

NI=82.8℃; Tc<-30℃; △n=0.118; △ε=-4.4; Vth=2.13V; η=22.5mPa. s.

[Composition (M3)]

3-HB(2F,3F)-O2 (1-1) 7%

NI=78.1℃; Tc<-30℃; △n=0.107; △ε=-3.2; Vth=2.02V; η=15.9mPa. s.

[Composition (M4)]

NI=88.5℃; Tc<-30℃; △n=0.108; △ε=-3.8; Vth=2.25V; η=24.6mPa. s; VHR-1=99.1%; VHR-2=98.2%; VHR-3=97.8%.

[Composition (M5)]

NI=81.1℃; Tc<-30℃; △n=0.119; △ε=-4.5; Vth=1.69V; η=31.4mPa. s.

[Composition (M6)]

NI=98.8℃; Tc<-30℃; △n=0.111; △ε=-3.2; Vth=2.47V; η=23.9mPa. s.

[Composition (M7)]

NI=77.5℃; Tc<-30℃; △n=0.084; △ε=-2.6; Vth=2.43V; η=22.8mPa. s.

[Composition (M8)]

NI=70.6℃; Tc<-20℃; △n=0.129; △ε=-4.3; Vth=1.69V; η=27.0mPa. s.

[Composition (M9)]

NI=93.0℃; Tc<-30℃; △n=0.123; △ε=-4.0; Vth=2.27V; η=29.6mPa. s.

[Composition (M10)]

NI=87.6℃; Tc<-30℃; △n=0.126; △ε=-4.5; Vth=2.21V; η=25.3mPa. s.

[Composition (M11)]

3-B(F)BB-2 (2-7) 3%

3-B(F)BB-2 (2-7) 3%

NI=93.0℃; Tc<-20℃; △n=0.124; △ε=-4.5; Vth=2.22V; η=25.0mPa. s.

[Composition (M12)]

NI=76.4℃; Tc<-30℃; △n=0.104; △ε=-3.2; Vth=2.06V; η=15.6mPa. s.

[Composition (M13)]

NI=78.3℃; Tc<-20℃; △n=0.103; △ε=-3.2; Vth=2.17V; η=17.7mPa. s.

[Composition (M14)]

NI=81.2℃; Tc<-20℃; △n=0.107; △ε=-3.2; Vth=2.11V; η=15.5mPa. s.

[Composition (M15)]

NI=88.7℃; Tc<-30℃; △n=0.115; △ε=-1.9; Vth=2.82V; η=17.3mPa. s.

[Composition (M16)]

NI=89.9℃; Tc<-20℃; △n=0.122; △ε=-4.2; Vth=2.16V; η=23.4 mPa. s.

[Composition (M17)]

NI=77.1℃; Tc<-20℃; △n=0.101; △ε=-3.0; Vth=2.04V; η=13.9mPa. s.

[Composition (M18)]

NI=75.9℃; Tc<-20℃; △n=0.114; △ε=-3.9; Vth=2.20V; η=24.7mPa. s.

The first additive is a polar compound (PC-1) to a polar compound (PC-33).

The second additive is a polymerizable compound (RM-1) to a polymerizable compound (RM-7).

2. Vertical alignment of liquid crystal molecules

Example 1

The polar compound (PC-1) was added to the composition (M1) at a ratio of 5% by weight and the polymerizable compound (RM-1) at a ratio of 0.5% by weight. The mixture was injected on a hot stage at 100° C. into a device with a gap (cell gap) of 4.0 μm between two glass substrates and no alignment film. The device was irradiated with ultraviolet rays (28J) using an ultra-high pressure mercury lamp USH-250-BY (manufactured by Ushio Motor) to polymerize the polymerizable compound. This element was placed in a polarization microscope in which the polarization element and the analyzer were arranged orthogonally, and the element was irradiated with light from below to observe whether there was light leakage. When the liquid crystal molecules are fully aligned and light does not pass through the device, the vertical alignment is judged to be "good". When the light passing through the element is observed, it is indicated as "bad".

Example 2 to Example 33 and Comparative Example 1

Use a mixture of composition, polar compound, and polymerizable compound Elements with alignment films. In the same manner as in Example 1, the presence or absence of light leakage was observed. The results are summarized in Table 4. In Comparative Example 1, for comparison, no polymerizable compound was added.

As can be seen from Table 4, in Examples 1 to 33, although the composition, polar compound, or polymerizable compound was changed, no light leakage was observed. This result shows that even if there is no alignment film in the device, the vertical alignment is good, and the liquid crystal The particles are aligned stably. On the other hand, in Comparative Example 1, light leakage was observed. This result indicates that the vertical alignment is not good. Therefore, it is understood that the polymer produced from the polymerizable compound plays an important role in the vertical alignment of liquid crystal molecules.

[Industrial availability]

The liquid crystal composition of the present invention can be used in liquid crystal projectors, liquid crystal televisions, and the like.

Claims (19)

A liquid crystal composition containing a polar compound other than the compound represented by formula (7) as a first additive and a polymerizable compound having at least three polymerizable groups as a second additive, and having a negative dielectric Anisotropy,

In formula (7), n is an integer from 1 to 9, and the liquid crystal composition contains at least one compound selected from the group of polymerizable compounds represented by formula (5) as a second additive,

In formula (5), ring T and ring V are independently cyclohexyl, cyclohexenyl, phenyl, 1-naphthyl, 2-naphthyl, tetrahydropyran-2-yl, 1,3-dioxyl Alk-2-yl, pyrimidin-2-yl or pyridin-2-yl, in these rings, at least one hydrogen may be fluorine, chlorine, alkyl having 1 to 12 carbons, alkoxy having 1 to 12 carbons , Or at least one hydrogen is substituted by a fluorine or chlorine substituted alkyl group having 1 to 12 carbons; ring U is 1,4-cyclohexylene, 1,4-cyclohexenylene, 1,4-phenylene, Naphthalene-1,2-diyl, naphthalene-1,3-diyl, naphthalene-1,4-diyl, naphthalene-1,5-diyl, naphthalene-1,6-diyl, naphthalene-1,7 -Diyl, naphthalene-1,8-diyl, naphthalene-2,3-diyl, naphthalene-2,6-diyl, naphthalene-2,7-diyl, tetrahydropyran-2,5-di Group, 1,3-dioxane-2,5-diyl, pyrimidine-2,5-diyl or pyridine-2,5-diyl, in these rings, at least one hydrogen can be fluorine, chlorine, carbon An alkyl group having 1 to 12, an alkoxy group having 1 to 12 carbons, or at least one hydrogen is substituted with an alkyl group having 1 to 12 carbons substituted by fluorine or chlorine; Z ¹² and Z ^{13 are} independently a single bond or carbon An alkylene having a number of 1 to 10, in which at least one -CH ₂ -may be substituted by -O-, -CO-, -COO- or -OCO-, and at least one -CH ₂ CH _2- Can be substituted by -CH=CH-, -C(CH ₃ )=CH-, -CH=C(CH ₃ )- or -C(CH ₃ )=C(CH ₃ )-, among these groups, at least one Hydrogen may be substituted by fluorine or chlorine; P ⁴ , P ⁵ and P ⁶ are polymerizable groups; Sp ⁹ , Sp ¹⁰ and Sp ^{11 are} independently single bonds or alkylene groups having 1 to 10 carbon atoms. Among them, at least one -CH ₂ -can be substituted by -O-, -COO-, -OCO- or -OCOO-, and at least one -CH ₂ CH ₂ -can be substituted by -CH=CH- or -C≡C- , In these groups, at least one hydrogen may be replaced by fluorine or chlorine; t is 0, 1 or 2; u, v and w are independently 0, 1, 2, 3 or 4, and the sum of u, v and w For 3 or more. The liquid crystal composition described in item 1 of the scope of patent application, which contains at least one compound selected from the group of compounds represented by formula (1) as the first component,

In formula (1), R ¹ and R ^{2 are} independently an alkyl group having 1 to 12 carbons, an alkoxy group having 1 to 12 carbons, an alkenyl group having 2 to 12 carbons, and at least one hydrogen is substituted by fluorine or chlorine Alkenyl with 2 to 12 carbons, or alkenyl with 2 to 12 carbons; ring A and ring C are independently 1,4-cyclohexenyl, 1,4-cyclohexenyl, tetrahydropyridine Phenyl-2,5-diyl, 1,4-phenylene, 1,4-phenylene in which at least one hydrogen is replaced by fluorine or chlorine, naphthalene-2,6-diyl, at least one hydrogen is replaced by fluorine or chlorine Substituted naphthalene-2,6-diyl, chroman-2,6-diyl, or chroman-2,6-diyl in which at least one hydrogen is replaced by fluorine or chlorine; ring B is 2,3- Difluoro-1,4-phenylene, 2-chloro-3-fluoro-1,4-phenylene, 2,3-difluoro-5-methyl-1,4-phenylene, 3,4 ,5-Trifluoronaphthalene-2,6-diyl or 7,8-difluorochroman-2,6-diyl; Z ¹ and Z ^{2 are} independently a single bond, -CH ₂ CH ₂ -,- CH ₂ O-, -OCH ₂ -, -COO- or -OCO-; a is 1, 2 or 3, b is 0 or 1, and the sum of a and b is 3 or less. The liquid crystal composition according to the second item of the patent application, which contains at least one compound selected from the group of compounds represented by formula (1-1) to formula (1-22) as a first component,

In formulas (1-1) to (1-22), R ¹ and R ^{2 are} independently an alkyl group having 1 to 12 carbons, an alkoxy group having 1 to 12 carbons, and an alkenyl group having 2 to 12 carbons. , Alkenyl groups having 2 to 12 carbons, or alkenyloxy groups having 2 to 12 carbons, in which at least one hydrogen is substituted with fluorine or chlorine. The liquid crystal composition according to the second item of the scope of patent application, wherein the ratio of the first component is in the range of 10% by weight to 90% by weight based on the weight of the liquid crystal composition. The liquid crystal composition according to the first item of the scope of patent application, which contains at least one compound selected from the group of compounds represented by formula (2) as a second component,

In formula (2), R ³ and R ^{4 are} independently an alkyl group having 1 to 12 carbons, an alkoxy group having 1 to 12 carbons, an alkenyl group having 2 to 12 carbons, and at least one hydrogen is substituted by fluorine or chlorine The alkyl group having 1 to 12 carbons, or the alkenyl group having 2 to 12 carbons in which at least one hydrogen is replaced by fluorine or chlorine; ring D and ring E are independently 1,4-cyclohexylene, 1,4-alkylene Phenyl, 2-fluoro-1,4-phenylene or 2,5-difluoro-1,4-phenylene; Z ³ is a single bond, -CH ₂ CH ₂ -, -CH ₂ O-,- OCH ₂ -, -COO- or -OCO-; c is 1, 2 or 3. The liquid crystal composition as described in item 5 of the scope of patent application, which contains at least one compound selected from the group of compounds represented by formula (2-1) to formula (2-13) as a second component,

In formulas (2-1) to (2-13), R ³ and R ^{4 are} independently an alkyl group having 1 to 12 carbons, an alkoxy group having 1 to 12 carbons, and an alkenyl group having 2 to 12 carbons. , Alkyl groups having 1 to 12 carbons in which at least one hydrogen is replaced by fluorine or chlorine, or alkenyl groups having 2 to 12 in carbon numbers in which at least one hydrogen is replaced by fluorine or chlorine. The liquid crystal composition according to item 5 of the scope of patent application, wherein the ratio of the second component is in the range of 10% by weight to 70% by weight based on the weight of the liquid crystal composition. The liquid crystal composition according to the first item of the patent application, which contains a polar compound as the first additive, and the polar compound contains a polar group having a heteroatom selected from nitrogen, oxygen, sulfur, and phosphorus. The liquid crystal composition according to the first item of the patent application, which contains at least one compound selected from the group of polar compounds represented by formula (3) and formula (4) as a first additive, MES-R ⁶ (3) (R ⁵ ) _x -R ⁶ (4) In formula (3), MES is a mesogen group having at least one ring; in formula (4), R ⁵ is an alkyl group having 4 to 20 carbons, so In the alkyl group, at least one -CH ₂ -can be substituted by -CH=CH-, -CF=CH-, -CH=CF-, -C≡C- or a cycloalkylene having 3 to 8 carbon atoms, which In these groups, at least one hydrogen can be replaced by fluorine or chlorine; in formula (3) and formula (4), R ⁶ is an oxygen atom with an OH structure, a sulfur atom with an SH structure, and a primary, secondary or tertiary amine structure At least one polar group in the nitrogen atom; x is 1 or 2. The liquid crystal composition as described in item 9 of the scope of patent application, which contains at least one compound selected from the group of polar compounds represented by formula (3-1) as a first additive,

In the formula (3-1), R ⁷ is hydrogen, fluorine, chlorine, or an alkyl group having 1 to 25 carbons. In the alkyl group, at least one -CH ₂ -can pass through -NR ⁰ -, -O-,- S-, -CO-, -CO-O-, -O-CO-, -O-CO-O- or cycloalkylene substituted with carbon number 3 to 8, and at least one tertiary carbon (>CH-) It may be substituted by nitrogen (>N-). In these groups, at least one hydrogen may be substituted by fluorine or chlorine. Here, R ⁰ is hydrogen or an alkyl group having 1 to 12 carbons; R ⁸ is 1 to 25 carbons. In the alkyl group, at least one -CH ₂ -can be -NR ⁰ -, -O-, -S-, -CO-, -COO-, -OCO-, -OCOO- or carbon number 3 Cycloalkylene substitution to 8, at least one tertiary carbon (>CH-) may be substituted with nitrogen (>N-), in these groups, at least one hydrogen may be substituted with fluorine or chlorine, where R ⁰ is Hydrogen or an alkyl group having 1 to 12 carbon atoms, wherein R ⁸ has at least one of an oxygen atom of an OH structure, a sulfur atom of an SH structure, or a nitrogen atom of a primary, secondary or tertiary amine structure; ring F and ring G is independently an aromatic group having 6 to 25 carbons, a heteroaromatic group having 5 to 25 carbons, an alicyclic group having 3 to 25 carbons, or a heteroalicyclic group having 4 to 25 carbons, which The group may be a condensed ring, and in these groups, at least one hydrogen may be substituted by a group T, where the group T is -OH, -(CH ₂ ) _i -OH, fluorine, chlorine, -CN, -NO ₂ ,- NCO, -NCS, -OCN, -SCN, -C(=O)N(R ⁰ ) ₂ , -C(=O)R ⁰ , -N(R ⁰ ) ₂ , -(CH ₂ ) _i -N( R ⁰ ) ₂ , an aryl group having 6 to 20 carbons, a heteroaryl group having 6 to 20 carbons, an alkyl group having 1 to 25 carbons, an alkoxy group having 1 to 25 carbons, an alkane having 2 to 25 carbons A carbonyl group, an alkoxycarbonyl group having 2 to 25 carbons, an alkylcarbonyloxy group having 2 to 25 carbons, or an alkoxycarbonyloxy group having 2 to 25 carbons, in which at least one hydrogen may be fluorinated Or substituted with chlorine, where R ⁰ is hydrogen or an alkyl group having 1 to 12 carbons, and i is 1, 2, 3, or 4; Z ⁴ is -O-, -S-, -CO-, -CO- O-, -OCO-, -O-CO-O-, -OCH ₂ -, -CH ₂ O-, -SCH ₂ -, -CH ₂ S-, -CF ₂ O-, -OCF ₂ -, -CF ₂ S-, -SCF ₂ -, -(CH ₂ ) _i -, -CF ₂ CH ₂ -, -CH ₂ CF ₂ -, -(CF ₂ ) _i -, -CH=CH-, -CF=CF- , -C≡C-, -CH=CH-COO-, -OCO-CH=CH-, -C(R ⁰ ) ₂ -or a single bond, where R ⁰ is hydrogen or an alkane with 1 to 12 carbon atoms Base, and i is 1, 2, 3, or 4; d is 0, 1, 2, 3, 4, or 5. The liquid crystal composition according to the ninth item of the patent application, which contains at least one compound selected from the group of polar compounds represented by formula (4-1) as a first additive, R ⁹ -R ¹⁰ (4 -1) In formula (4-1), R ⁹ is an alkyl group having 4 to 20 carbons. In the alkyl group, at least one -CH ₂ -can be controlled by -CH=CH-, -CF=CH-,- CH=CF-, -C≡C- or a cycloalkylene group having 3 to 8 carbon atoms, in these groups, at least one hydrogen may be replaced by fluorine or chlorine; R ¹⁰ is an alkyl group having 1 to 25 carbon atoms, In the alkyl group, at least one -CH ₂ -can be extended by -NR ⁰ -, -O-, -S-, -CO-, -COO-, -OCO-, -OCOO- or carbon number 3 to 8. Cycloalkyl substitution, at least one tertiary carbon (>CH-) can be substituted with nitrogen (>N-), in these groups, at least one hydrogen can be substituted with fluorine or chlorine, where R ⁰ is hydrogen or carbon number An alkyl group of 1 to 12, wherein R ¹⁰ has at least one of an oxygen atom of an OH structure, a sulfur atom of an SH structure, and a nitrogen atom of a primary, secondary or tertiary amine structure. The liquid crystal composition according to the ninth item of the scope of patent application, wherein in formula (3) and formula (4) as described in the ninth item of the scope of patent application, R ⁶ is selected from formula (A1) to formula (A4) The groups in the group of polar groups,

In formulas (A1) to (A4), Sp ⁴ , Sp ⁶ and Sp ^{7 are} independently single bonds or groups (-Sp"-X"-), where Sp" is an alkylene having 1 to 20 carbon atoms In the alkylene group, at least one -CH ₂ -can be controlled by -O-, -S-, -NH-, -N(R ⁰ )-, -CO-, -CO-O-, -O- CO-, -O-CO-O-, -S-CO-, -CO-S-, -N(R ⁰ )-CO-O-, -O-CO-N(R ⁰ )-, -N( R ⁰ )-CO-N(R ⁰ )-, -CH=CH- or -C≡C- substituted, in these groups, at least one hydrogen may be substituted with fluorine, chlorine or -CN, and X" is -O -, -S-, -CO-, -CO-O-, -O-CO-, -O-CO-O-, -CO-N(R ⁰ )-, -N(R ⁰ )-CO-, -N(R ⁰ )-CO-N(R ⁰ )-, -OCH ₂ -, -CH ₂ O-, -SCH ₂ -, -CH ₂ S-, -CF ₂ O-, -OCF ₂ -,- CF ₂ S-, -SCF ₂ -, -CF ₂ CH ₂ -, -CH ₂ CF ₂ -, -CF ₂ CF ₂ -, -CH=N-, -N=CH-, -N=N-,- CH=CR ⁰ -, -CY ² =CY ³ -, -C≡C-, -CH=CH-CO-O-, -O-CO-CH=CH- or single bond, where R ⁰ is hydrogen Or an alkyl group having 1 to 12 carbons, and Y ² and Y ^{3 are} independently hydrogen, fluorine, chlorine or -CN; Sp ⁵ is >CH-, >CR ^a1 -, >N- or >C<; X ¹ For -OH, -OR ^a1 , -COOH, -NH ₂ , -NHR ^a1 , -N(R ^a1 ) ₂ , -SH, -SR ^a1 ,

Here, R ⁰ is hydrogen or an alkyl group having 1 to 12 carbons; X ² is -O-, -CO-, -NH-, -NR ^a1 -, -S- or a single bond; Z ⁹ is a carbon number of 1 An alkylene group with a carbon number of 5 or 6 or a combination of these groups, in which at least one hydrogen can pass through -OH, -OR ^a1 , -COOH, -NH ₂ , -NHR ^a1 , -N(R ^a1 ) ₂ , fluorine or chlorine substitution; here, R ^a1 is an alkyl group with 1 to 15 carbons, and in the alkyl group, at least one -CH ₂ -can be replaced by -C≡C-,- CH=CH-, -COO-, -OCO-, -CO- or -O- substituted, in these groups, at least one hydrogen may be substituted by fluorine or chlorine; ring P is an aromatic group with 6 to 25 carbons or An alicyclic group having 3 to 25 carbon atoms, these groups may be condensed rings, in these groups, one to three hydrogens may be substituted by R ^L , where R ^L is -OH, -(CH ₂ ) _r -OH, fluorine, chlorine, -CN, -NO ₂ , -NCO, -NCS, -OCN, -SCN, -C(=O)N(R ⁰ ) ₂ , -C(=O)R ⁰ , -N (R ⁰ ) ₂ , -(CH ₂ ) _r -N(R ⁰ ) ₂ , -SH, -SR ⁰ , aryl groups with 6 to 20 carbons, heteroaryl groups with 6 to 20 carbons, 1 to carbons 25 alkyl group, carbon number 1 to 25 alkoxy group, carbon number 2 to 25 alkylcarbonyl group, carbon number 2 to 25 alkoxycarbonyl group, carbon number 2 to 25 alkylcarbonyloxy group or carbon number 2-25 alkoxycarbonyloxy, in these groups, at least one hydrogen may be substituted by fluorine or chlorine, where R ⁰ is hydrogen or an alkyl group having 1 to 12 carbons, and r is 1, 2, 3 or 4; p is 0, 1, 2 or 3; q is 2, 3, 4 or 5. The liquid crystal composition according to claim 9, wherein the first additive is at least one selected from the group of polar compounds represented by formula (3-1-1) to formula (3-1-4) A compound,

In formulas (3-1-1) to (3-1-4), R ¹⁵ is an alkyl group having 1 to 8 carbons or fluorine; ring Q and ring R are independently 1,4-cyclohexylene, 1 ,4-phenylene, 2-fluoro-1,4-phenylene, 2-fluoro-1,3-phenylene, 2-ethyl-1,4-phenylene, 2,6-diethyl Phenyl-1,4-phenylene, 2-trifluoromethyl-1,4-phenylene, 2,3-difluoro-1,4-phenylene, 2,5-difluoro-1,4 -Phenylene, 2,6-difluoro-1,4-phenylene or 2,3,5,6-tetrafluoro-1,4-phenylene; ring S is cyclohexyl or phenyl; Z ¹⁰ Is a single bond, -CH ₂ CH ₂ -, -COO- or -OCO-; Z ¹¹ is a single bond, an alkylene group with 1 to 15 carbons, an alicyclic group with 5 or 6 carbons, or a combination of these , In these groups, at least one hydrogen can be replaced by -OH, -OR ^a1 , -COOH, -NH ₂ , -NHR ^a1 , -N(R ^a1 ) ₂ , fluorine or chlorine, where R ^a1 is the number of carbons An alkyl group of 1 to 15, in which at least one -CH ₂ -may be substituted with -C≡C-, -CH=CH-, -COO-, -OCO-, -CO- or -O-, In these groups, at least one hydrogen may be replaced by fluorine or chlorine; Sp ⁴ is a single bond, -CH ₂ CH ₂ -, -CH ₂ CH ₂ CH ₂ -, -CH ₂ O- or -OCH ₂ -; Sp ⁷ It is a single bond or an alkylene having 1 to 5 carbon atoms, in which -CH ₂ -can be substituted by -O- or -NH-; s is 0, 1, 2, 3, 4 or 5; X ³ is -OH, -COOH, -SH, -OCH ₃ or -NH ₂ ; X ⁴ is a single bond or -O-. The liquid crystal composition according to claim 9, wherein the first additive is at least one selected from the group of polar compounds represented by formula (4-1-1) to formula (4-1-29) A compound, R ⁹ -OH (4-1-1)

R ⁹ -COOH (4-1-9)

R ⁹ -NH ₂ (4-1-11)

In formulas (4-1-1) to (4-1-29), R ⁹ is an alkyl group having 4 to 20 carbons. In the alkyl group, at least one -CH ₂ -may be controlled by -CH=CH- , -CF=CH-, -CH=CF-, -C≡C- or cycloalkylene having 3 to 8 carbon atoms, in these groups, at least one hydrogen may be substituted by fluorine or chlorine. The liquid crystal composition according to the first item of the scope of patent application, wherein the ratio of the first additive is in the range of 0.05% by weight to 10% by weight based on the weight of the liquid crystal composition. The liquid crystal composition according to item 1 of the patent application, wherein in the formula (5), P ⁴ , P ⁵ and P ^{6 are} independently selected from formula (P-1) to formula (P-5) The groups in the group of aggregate groups,

In formulas (P-1) to (P-5), M ¹ , M ² and M ^{3 are} independently hydrogen, fluorine, an alkyl group with a carbon number of 1 to 5, or carbon in which at least one hydrogen is substituted by fluorine or chlorine The number is an alkyl group of 1 to 5. The liquid crystal composition according to the first item of the patent application, which contains at least one compound selected from the group of polymerizable compounds represented by formulas (5-1) to (5-7) as a second additive ,

In formula (5-1) to formula (5-7), P ⁴ , P ⁵ and P ^{6 are} independently selected from the group of polymerizable groups represented by formula (P-1) to formula (P-3) In the base,

Here, M ¹ , M ² and M ^{3 are} independently hydrogen, fluorine, an alkyl group having 1 to 5 carbons, or an alkyl group having 1 to 5 carbons in which at least one hydrogen is replaced by fluorine or chlorine; Sp ⁹ , Sp ¹⁰ and Sp ^{11 are} independently a single bond or an alkylene group having 1 to 10 carbon atoms. In the alkylene group, at least one -CH ₂ -may be -O-, -COO-, -OCO- or -OCOO- And at least one -CH ₂ CH ₂ -can be substituted by -CH=CH- or -C≡C-, in these groups, at least one hydrogen can be substituted by fluorine or chlorine. The liquid crystal composition according to the first item of the scope of patent application, wherein the ratio of the second additive is in the range of 0.03% by weight to 10% by weight based on the weight of the liquid crystal composition. A liquid crystal display element containing the liquid crystal composition according to any one of the first to the 18th patent applications.