1352015 A. 首先,以電腦軟體繪製出3D模具圖並透過原型機快 速成型出原型模; B. 取出原型模並以矽膠包覆成型出一具模穴(11)之矽 膠模(10); C. 取出矽膠模(10),於矽膠模(10)之模穴(11)内之每 一邊框面注入粉末(21,可設為金屬粉末或陶瓷粉末)至一 適當高度後,再於粉末(21)上方置入若干金屬塊(22,可設 為鋁球或鋁片)至模穴(11)填滿; D. 將填滿粉末(21)及金屬塊(22)之矽膠模(10)置入高 真空鑄型機内,再將液態樹脂(23)注入模穴(11)内,利用 高真空機使液態樹脂(23)完全真空脫泡,並於真空壓力下 使液態樹脂(23)可確實由粉末(21)及金屬塊(22)之縫隙滲 入而將矽膠模(10)之模穴(11)填滿並透過高真空鑄型機成 型出一金屬樹脂模具(20,如第三圖所示); 藉此,使液態樹脂(23)在真空壓力可迅速由金屬塊(22) 之較大縫細渗入產生一道較大之壓製力量以增加粉末(21) 之密度更為均勻,並利用液態樹脂(23)係由金屬塊(22,)之 較大縫隙滲入使其壓製力量足以持續滲透入粉末(21)之較 小綠細而確實填滿金屬塊(22)與粉末(21)間所殘留之縫 隙,以獲得更均勻及更高之密度,使該金屬樹脂模具(20) 之尺寸得以精確控制及防止洩料之問題,進而達無誤差、 無收縮變形之最佳使用狀態。 綜上所述,當知本發明具有產業上利用性與進步性, 且本發明未見於任何刊物,亦具新穎性,當符合專利法第 二十一條及二十二條之規定,爰依法提出發明專利申請, 懇請貴審查委員惠准專利為禱。 7 1352015 唯以上所述者,僅為本發明之其中較佳實施例而已, 當不能以之限定本發明實施之範圍;即大凡依本發明申請 專利範圍所作之均等變化與修飾,皆應仍屬本發明專利涵 蓋之範圍内。 【圖式簡單說明】 第一圖:係為本發明之方塊流程圖。 第二圖:係為本發明之立體流程圖。 第三圖:係為本發明之金屬樹脂模具成型剖面圖。 【主要元件符號說明】 10……矽膠模 11……模穴 20 ......金屬樹脂模具 21 ......粉末 22……金屬塊 23……液態樹脂1352015 A. First, the 3D mold drawing is drawn by computer software and the prototype mold is quickly formed by the prototype machine; B. The prototype mold is taken out and the mold mold (11) is molded with silicone rubber (10); Remove the silicone mold (10), and inject powder (21, which can be set as metal powder or ceramic powder) into each frame surface of the mold cavity (11) of the silicone mold (10) to a suitable height, and then to the powder ( 21) Insert a number of metal blocks (22, which can be set as aluminum balls or aluminum sheets) to fill the cavity (11); D. Fill the powder (21) and the metal block (22) with a plastic mold (10) The liquid resin (23) is injected into the cavity (11), the liquid resin (23) is completely vacuum defoamed by a high vacuum machine, and the liquid resin (23) is made under vacuum pressure. It is indeed filled with the gap between the powder (21) and the metal block (22) to fill the cavity (11) of the silicone mold (10) and form a metal resin mold (20, as shown in the third figure) through a high vacuum mold machine. Thereby, the liquid resin (23) can be quickly infiltrated by the large slit of the metal block (22) under vacuum pressure. The greater the pressing force to increase the density of the powder (21) is more uniform, and the liquid resin (23) is infiltrated by the larger gap of the metal block (22,) so that the pressing force is sufficient to continuously penetrate into the powder (21). The small green is fine and fills the gap between the metal block (22) and the powder (21) to obtain a more uniform and higher density, so that the size of the metal resin mold (20) can be accurately controlled and the discharge prevention is prevented. The problem is to achieve the best use state without error or shrinkage deformation. In summary, when the invention is industrially usable and progressive, and the invention is not found in any publication, it is also novel, and when it complies with the provisions of Articles 21 and 22 of the Patent Law, To file an application for a patent for invention, and ask your reviewer to pay for the patent as a prayer. 7 1352015 The above is only the preferred embodiment of the present invention, and the scope of the present invention is not limited thereto; that is, the equal variation and modification of the scope of the patent application of the present invention should remain The scope of the invention is covered. BRIEF DESCRIPTION OF THE DRAWINGS The first figure is a block flow diagram of the present invention. The second figure is a perspective flow chart of the present invention. Fig. 3 is a sectional view showing the molding of a metal resin mold of the present invention. [Description of main component symbols] 10...矽胶模11......模穴20 ......Metal resin mold 21 ......Powder 22...Metal block 23...Liquid resin