TWI265140B - Surface treatment method and mixing apparatus for preparing water-resistant aluminum nitride powder - Google Patents
Surface treatment method and mixing apparatus for preparing water-resistant aluminum nitride powderInfo
- Publication number
- TWI265140B TWI265140B TW92136039A TW92136039A TWI265140B TW I265140 B TWI265140 B TW I265140B TW 92136039 A TW92136039 A TW 92136039A TW 92136039 A TW92136039 A TW 92136039A TW I265140 B TWI265140 B TW I265140B
- Authority
- TW
- Taiwan
- Prior art keywords
- aluminum nitride
- surface treatment
- mixing apparatus
- treatment method
- nitride powder
- Prior art date
Abstract
A surface treatment method and a mixing apparatus for preparing water-resistant aluminum nitride are disclosed. The surface treatment method is to add a surface modifier to aluminum nitride powder to form an admixture, and to mix and heat the admixture in the mixing apparatus of the present invention, and a bridge breaker is installed inside the mixing apparatus for enhancing the surface treatment efficiency for preparing the aluminum nitride powder. The surface modifier suitable for use in the present invention can be lauric acid (C12H24O2; LA), stearic acid (C17H35COOH; SA), oleic acid (C18H34O2; OA), TEOS (Si(OC2H5)4), or silane coupling agent (RSi(OR')3, R'=CH3 or C2H5).
Priority Applications (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
TW92136039A TWI265140B (en) | 2003-12-18 | 2003-12-18 | Surface treatment method and mixing apparatus for preparing water-resistant aluminum nitride powder |
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
TW92136039A TWI265140B (en) | 2003-12-18 | 2003-12-18 | Surface treatment method and mixing apparatus for preparing water-resistant aluminum nitride powder |
Publications (2)
Publication Number | Publication Date |
---|---|
TW200521078A TW200521078A (en) | 2005-07-01 |
TWI265140B true TWI265140B (en) | 2006-11-01 |
Family
ID=38122100
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
TW92136039A TWI265140B (en) | 2003-12-18 | 2003-12-18 | Surface treatment method and mixing apparatus for preparing water-resistant aluminum nitride powder |
Country Status (1)
Country | Link |
---|---|
TW (1) | TWI265140B (en) |
Families Citing this family (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN104448799B (en) * | 2014-11-25 | 2017-02-01 | 浙江俊尔新材料股份有限公司 | Hydrolysis resistance aluminum nitride filled polyamide based heat conduction plastic and preparation method thereof |
CN105132079B (en) * | 2015-07-08 | 2018-10-19 | 清华大学 | A kind of preparation method of the particle modified transformer oil of aluminum nitride nanometer |
CN107954725B (en) * | 2017-11-29 | 2021-03-30 | 上海宇昂水性新材料科技股份有限公司 | Hydrolysis-resistant aluminum nitride powder and preparation method thereof |
-
2003
- 2003-12-18 TW TW92136039A patent/TWI265140B/en not_active IP Right Cessation
Also Published As
Publication number | Publication date |
---|---|
TW200521078A (en) | 2005-07-01 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
RU2011121617A (en) | HYDROPHOBIZING POWDER AND ITS APPLICATION | |
TW347410B (en) | Compositions suitable for polishing silica, silicates, and silicon | |
CN104530967B (en) | Reactive organosilicon waterproofing agent as well as preparation method and application thereof | |
EP1558542A4 (en) | Amine-containing cement processing additives | |
MXPA02008384A (en) | Non-aqueous coating compositions formed from silanes and metal alcoholates. | |
ES2152855A1 (en) | Use of hydroxylamines to enhance the strength of portland cement compositions | |
DE60134970D1 (en) | HIGH GRADE DELAMINATED HEXAGONAL BORONITRIDE POWDER, MANUFACTURING METHOD, AND USES THEREOF | |
WO2004096727A3 (en) | Cementitious material | |
EP1015397A4 (en) | Use of waste glass for concrete | |
MY138857A (en) | High selectivity colloidal silica slurry | |
TWI265140B (en) | Surface treatment method and mixing apparatus for preparing water-resistant aluminum nitride powder | |
CN102939341A (en) | Alkyl- and amino-functionalized siloxanes comprising bis(alkoxysilyl)amine for the mass hydrophobization of inorganic building materials | |
HK1071764A1 (en) | Synthesis and use of alkylalkoxy acyloxysilanes and blends thereof | |
MY136760A (en) | Method for the production of hydroxyalkyl polysiloxanes | |
AU2003238503A1 (en) | Silicon composition | |
BR0114311B1 (en) | manufacture of aluminum-silicon alloys. | |
WO2004031313A3 (en) | Process for the manufacture of alkoxysilanes and alkoxy orthosilicates | |
HK1060556A1 (en) | Method and installation for the dehydroxylation treatment of aluminium silicate. | |
GB0025717D0 (en) | Improvements in or relating to organic compositions | |
EP1004554A3 (en) | The use of polymers in masonry applications | |
CN106479372A (en) | A kind of Clean- composite of lasting light | |
CN1249284A (en) | Multifunctional insulating composite felt (cream) | |
CN106380098A (en) | Aerated concrete gas-forming agent and aerated concrete | |
JP3844458B2 (en) | Cement admixture and cement composition | |
TWI717127B (en) | Core-shell composite material and method for manufacturing the same |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
MM4A | Annulment or lapse of patent due to non-payment of fees |