TW202009271A - Epoxy-silicone composite composition and use thereof - Google Patents

Abstract

Provided is an epoxy-silicone composite composition, which has a silicone composite and a epoxy composite at an amount ranging from 1:1 to 6:1 by weight. The epoxy composite includes a epoxy resin. The silicone composite has a first silicone gel and a second silicone gel. The expoxy-silicone composition has a low transmission rate to water and vapor, resulting in high resistance to moisture, meanwhile, maintain an enhanced mechanical strength and desired flexibility to meet the need of the industry.

Description

Silicone epoxy resin composite material and its application

The invention relates to a silicon water epoxy resin composite material with high water and gas barrier properties, which is a material formula applicable to the manufacturing process of bottle cap gaskets.

The sealed container is covered with a metal claw cover made of aluminum plate or tinned thin plate at the mouth of the can, and a gasket is provided on the inside of the claw cover, so that the claw cover and the can body are tightly combined, so that the contents of the can body are completely blocked from the environment To maintain the freshness of the contents. Gasket materials must have appropriate flexibility and mechanical strength. Polyvinyl chloride (PVC) formulations as gasket materials require high levels of plasticizers to achieve the desired processability. However, in addition to the potential problems of environmental pollution, high levels If the plasticizer is in contact with the contents, there will be doubts about food safety.

In order to avoid food safety concerns, silicone rubber is processed as a gasket material without adding additional plasticizers to replace the PVC compound formulation. However, although the silicone material itself has a high degree of fluidity and softness, it is suitable for the process of bottle cap gaskets, but it has the problem of insufficient mechanical strength and insufficient water blocking properties, which cannot meet the sealing needs, but affects the preservation of the content. Expiration date.

It can be seen that the gasket of the prior art may have potential toxicity problems if it adopts PVC formula. Although the alternative silicone formula meets the requirements of food safety, it can not meet the demand of high water and gas barrier, and it can not maintain a good sealing effect. Disadvantages, it is necessary to invent an alternative material to improve the existing problems.

In order to solve the problem of lack of effective water and gas barrier characteristics caused by the existing silicone gaskets, the present invention proposes a silicone epoxy resin compound formula, which can be applied to the manufacturing process of the metal claw cover gasket. The composite material of the present invention makes the gasket The finished film achieves the desired water blocking effect without food safety concerns, and there is no risk of environmental pollution when it is directly burned after recycling, and it can fully comply with the production and processing process of the existing metal claw cover factory gasket, and solve the PVC formula Toxicity, lack of mechanical strength in silicone formulations, and other types of elastomer materials cannot be directly introduced into trial production on existing production lines.

The invention provides a silicone epoxy resin composite material, which comprises a silicone formula and an epoxy resin formula, the weight ratio of the silicone formula and the epoxy resin formula is between 1:1 and 6:1, wherein the epoxy resin The formula contains an epoxy resin, the silicone formula contains a first high-flow silica gel or a second high-flow silica gel, wherein the first high-flow silica gel has a vinyl Silicone collagen glue with siloxane structure, which contains a platinum catalyst; the second high fluidity silicone collagen glue is a silicone collagen glue with a vinyl siloxane structure and a siloxane bonded structure, It contains an inhibitor.

On the other hand, the present invention also provides a method for manufacturing a silicone claw cover material for manufacturing a metal claw cover, wherein the metal claw cover is provided with a ring-shaped silicone epoxy material using a rotary coating device, and its steps contain:

Obtaining a silicone epoxy resin composite material: mix a silicone formula S containing a first high fluidity silica collagen A and a second high fluidity silica collagen B with an epoxy resin to a 1:1 ratio Mix with a weight ratio of 6:1 and put into a glue mixing module for glue mixing to obtain a silicone rubber epoxy composite material;

Coating step: The silicone epoxy resin composite material is introduced into a one-point glue device, and dripped or injected into one of the inner surfaces of a metal claw cover, and then the silicon claw cover is coated on the metal claw cover by spin coating A resin composite material, rotating the composite material on the edge of the inner surface of the metal claw cover to form a ring-shaped silicone epoxy gasket; and

Cross-linking step: The silicone epoxy resin gasket coated on the metal claw cover is cross-linked by means of heat-assisted drying.

It can be known from the above description that the present invention has the following advantages:

1. The present invention uses silicone as the main material, which has the advantage of non-toxicity compared with the existing paw cover material PVC, and further improves the water and gas barrier properties of the silicone material by adding epoxy resin, and greatly improves the quality of the paw cover material.

2. The present invention is developed specifically for spin coating of spin coating equipment, which can be matched with the existing coating production and equipment, can be beneficial to industrial utilization, and greatly reduce the cost of the possible increase in the change of the manufacturing process, which is beneficial to the producer It is easier to accept and adopt the technology proposed by the present invention.

Please refer to FIG. 1, which is a method for manufacturing a metal claw cover gasket of the silicone epoxy composite material of the present invention. The steps include:

Steps for obtaining silicone epoxy resin composite material: take a silicone formula S and an epoxy resin formula containing a first high-flow silica collagen A and a second high-flow silica collagen B at a 1:1 weight ratio E is mixed in a weight ratio of 1:1 to 6:1 and placed in a glue mixing module 12 for glue mixing; a selective filler C and a dilution aid D can be added to the silicone formulation S or epoxy formulation E respectively , And pre-mixed and modified in the pre-mix tank 10 in advance, and then placed in the mixing module 12 for mixing, to obtain a silicone epoxy resin composite material; and the filler C and the dilution aid D can also be Adding the silicone formula S and the epoxy resin formula E and mixing is not limited herein.

Coating step: The silicone epoxy resin composite material after mixing/modification is introduced into the one-point glue device 13, and dripped or injected into an inner surface of a metal claw cover 14, and then the metal claw is applied by spin coating The silicone epoxy composite material is coated on the cover 14 so that the composite material is distributed on the edge of the inner surface of the metal claw cover 14 to form a ring of silicone epoxy gasket material, as shown in FIG. 2;

Cross-linking step: The silicone epoxy resin material applied to the metal claw cover is cross-linked by means of heat-assisted drying.

Wherein, the aforementioned epoxy resin formulation E includes an epoxy resin with a weight ratio of 1:1 to 4:1 and a curing agent, and a selective reaction accelerator less than 10wt% and the optional filler C . The epoxy equivalent weight (EEW) of the epoxy resin is about 190 to 210 g/Eq. Preferably, the epoxy equivalent of the epoxy resin is about 204-205 g/Eq. Among them, the epoxy resin preferably includes an aliphatic epoxy compound (aliphatic epoxy). Among them, the curing agent preferably includes an acid anhydride curing agent, such as, but not limited to, 4-methylhexahydrophthalic anhydride (MeHHPA), which can prevent the rubber compound from yellowing and discoloration. The reaction accelerator may be preferably 2,4,6-tris(dimethylaminomethyl)phenol (abbreviated as DMP-30). Among them, the filler C includes talc (Talc), silicon dioxide (SiO ₂ ), titanium dioxide (titanium dioxide, TiO ₂ ) or clay (clay), in addition to being a filler, it can further improve the thermal stability of epoxy resin And/or reduce the water vapor transmission rate.

The first high-flow silica gel A is a silica gel with a vinyl siloxane structure, which includes a vinyl substituent, and the first high-flow silica gel A may contain an organic Peroxide catalyst (Organic Peroxide), an organometallic chelate catalyst, an organic amine catalyst or a platinum catalyst, the amount of the aforementioned catalyst is preferably 10wt% or less to facilitate the reaction, the organic peroxide The catalyst may be benzyl peroxide (Benzoyl peroxide), 2,4-dichlororobenzoyl peroxide (2,4-dichorobenzoyl peroxide), t-butyl peroxybezoate (t-butyl peroxybezoate), di-tert Di-tert-butyl peroxide; the organometallic chelate catalyst may be organic tin carboxylate (Et ₂ Sn(OAc) ₂ , Bu ₂ Sn(OAc) ₂ ), organic tin chelate (Bu ₂ Sn(OCOC ₇ H ₁₅ ) ₂ , Bu ₂ Sn(OCOC ₁₁ H ₂₃ ) ₂ ), organic titanium compounds (Ti(OBu) ₄ Ti(OSiMe ₃ ) ₄ ) and other compounds.

The second high fluidity silica gel B is a silica gel with a vinyl siloxane structure and a silicon-hydrogen (Si-H) bonded siloxane structure, which contains an inhibitor 10wt % Or less, the inhibitor may preferably be acetylene alcohol (Acetylene alcohol), which can be used as a stable inhibitor during storage and production to prevent the second high fluidity silica gel B and the first high fluidity Silica gel A cross-linking reaction occurs too quickly during the mixing step, resulting in the problem that it cannot be applied.

The filler C can be added in an amount of up to 50 wt%, which may include talc (Talc), titanium dioxide (TiO ₂ ), silicon dioxide (SiO ₂ ), clay or nano clay, wherein, Adding the filler C can provide a color to the silicone formulation S and/or the epoxy resin formulation E, and shearing and dispersing so that the filler C can be uniformly dispersed in the silica gel A containing the first high fluidity In the silicone formula S with the second highest fluidity silicone collagen B. Among them, the layered silicates can be provided to the epoxy resin, and sheared and dispersed so that the filler C can be evenly dispersed in the silicone formulation S.

The addition amount of the dilution aid D is added according to the fluidity requirement of the silicone epoxy resin composite material, which includes a silicone oil, a tetracyclic silicone oil and/or a food grade white wax oil, and the dilution aid D is For improving the processability of the first high fluidity silica gel A or the second high fluidity silica gel B, wherein the silicone oil can increase the first high fluidity silica gel A or the The processability of the second highest fluidity silica gel B can also increase its lubricity. The tetracyclic silicone oil has a volatile property and will gradually evaporate during the cross-linking process, so it will not affect the first high fluidity silica gel A, the second high fluidity silica gel B and the ring The physical properties of the oxygen resin formulation E, thereby simultaneously satisfying the processing conditions of the kneading and upgrading process and increasing its processability. The addition of the food-grade white wax oil is used for lubrication, and it is preferable to select the food-grade white wax oil with low volatility, which is partially precipitated or coated on the surface of the cross-linked silicone epoxy resin composite material, which can be improved The silicone epoxy resin composite material originally has dry characteristics and increases its self-lubricating effect, thereby greatly improving the material physical properties and processing characteristics. During use, the lubricity of the metal claw cover and the corresponding can body can be increased when screwed, so that It is easier to spin the two together.

The step of obtaining the silicone epoxy resin composite material preferably includes: taking the silicone formula S containing the weight ratio of the first high-flow silica collagen A and the second high-flow silica collagen B to the weight ratio of 1:1; The epoxy resin formulation E is mixed from 1:1 to 6:1 to form a silicone epoxy resin mixture, and the filler C is added to the silicone epoxy resin mixture to knead. Preferably, the filler C can be mixed with the filler first Dilution aid D is mixed and dispersed evenly before being mixed with the silicone epoxy resin mixture.

In the step of obtaining the silicone epoxy resin composite material, the type of the glue mixing module 12 is not limited, and may be a mixing device of a double liquid glue mixing machine or a glue mixing gun, which is mainly capable of containing the first high The fluid silicone collagen A is mixed with the silicone formulation S and epoxy resin formulation E of the second highest fluid silicone collagen B.

In the cross-linking step, the heat-assisted drying method is oven heating, direct heating drying or infrared heating.

The coating step includes: introducing the silicone epoxy resin composite material completed by the mixing into a one-point glue equipment 13 and using injection to perform the silicone epoxy resin composite material of a metal claw cover 14 with a rotary coating machine Coating, and in the process of rotating and centrifuging, the silicone epoxy resin composite material is formed into a silicone epoxy resin material annularly distributed at the edge of an inner surface of the metal claw cover 14, wherein the aforementioned rotation The coating process speed is adjusted in accordance with the viscosity and flow characteristics of the silicone epoxy resin composite material. The illustrated speed is about 1800 rpm. By appropriately controlling the rotation speed, the silicone epoxy resin composite material can achieve the effect of preliminary defoaming and dispersion at the same time during the spin coating process, and the silicone epoxy resin composite material of the present invention is specifically spin coating for spin coating equipment The cloth is developed and can be matched with the existing coating and equipment to facilitate the use of the industry.

The cross-linking step: the silicone epoxy resin composite material coated on the metal claw cover 14 is cross-linked, so that the silicone epoxy resin composite material is tightly fixed to the inner surface of the metal claw cover 14. The cross-linking can be accompanied by a heat-assisted drying method to improve production efficiency. The heat-assisted drying method is to reduce the curing time of the silicone epoxy resin composite material on the metal claw cover 14 after spin coating to achieve a fast cross-linking effect, and its manufacturing parameters can be, for example, a temperature of 170°C for about 3hr minutes, The silicone epoxy resin composite material is cured. The type of the heat-assisted drying means is not limited, and it may be an oven, direct contact heating, infrared heating or the like. In order to enable the first high-flow silica gel A and the second high-flow silica gel B to quickly complete the cross-linking reaction at high temperature, the first high-flow silica gel A is preferred The platinum catalyst, which is a platinum compound or complex catalyst, may be a platinum divinyltetramethyldisilaxane solution (Karstedt catalyst), which can be used to promote the first high fluidity silica gel A A catalyst that reacts quickly with the second highest fluidity silica gel B.

Please refer to FIG. 2, which is a cross-sectional view of a metal claw cover with a silicone gasket according to a preferred embodiment of the present invention, wherein the silicone epoxy resin composite material is annularly distributed inside one of the metal claw covers 14 after spin coating At the edge of the surface, a heat-assisted drying method is used to perform a cross-linking process to cure the metal claw cover with a silicone gasket.

Listed below are various embodiments of the present invention:

[Example 1]

Mix epoxy resin with 4-methylhexahydrophthalic anhydride (MeHHPA) and 2,4,6-tris(dimethylaminomethyl)phenol (DMP-30 for short) as epoxy resin formulation E for future use. The first high-fluidity silicone collagen A and the second-highest fluidity silicone collagen B with a weight ratio of 1:1 are weighed as silicone formula S, preferably the silicone formula S contains 40 phr of silicone oil thinner, Then add epoxy resin formula E, the ratio of the silicone formula S to the epoxy resin formula E is preferably 3:1, and put into the pre-mixing tank 10, and then mix with 120phr of silicone oil diluent containing 40phr, proceed Stir and knead for 20 minutes, the filler is preferably talcum powder, and the talc powder can be added up to 50wt%, has the best water and gas barrier properties, and then the silicone epoxy resin composite material after mixing is placed in a vacuum In the oven, vacuum is taken to remove the bubbles generated by the mixing and mixing. The defoamed silicone epoxy resin composite material is introduced into the mold and baked at 170°C for 3 hours to form.

Among them, for the other formulations of the silicone formula S and the epoxy resin formula E containing the first high fluidity silica gel A and the second high fluidity silica collagen B, please refer to the description of the mixing and modification method in the embodiment content.

Test the water resistance of the silicone epoxy resin composite material after crosslinking.

The water resistance test results of the silicone epoxy resin composite material are shown in Table 1. The test method is to test the water vapor transmission rate (WVTR) in the solid state of the finished product to evaluate the water resistance and oxygen resistance . Results Compared with the existing pure silicone material with a thickness of 0.609 mm, the water vapor transmission rate is 131 gm/[m ² -day], and the water vapor transmission rate (WVTR) of the silicone epoxy resin composite with a thickness of 0.861 mm can be reduced to 36.97 gm/[m ² -day], showing that the properties of water and gas barriers are indeed greatly improved.

Table 1.

Based on the foregoing description, the present invention has the following features:

1. The use of silicone epoxy resin composite material has high water resistance, to solve the technical problems that the metal claw cover using polyvinyl chloride gasket may pose a threat to the human body and the environment, and the lack of proper water resistance and mechanical stress using silicone gasket.

2. The composite material of the present invention has both the desired high water and gas barrier properties and other required characteristics, and achieves the desired viscosity. It can be used with existing equipment, which can greatly reduce the cost of replacing materials and help Use of industry.

S‧‧‧ Silicone formula E‧‧‧Epoxy resin formula A‧‧‧The first high fluidity silica collagen glue B‧‧‧The second highest fluidity silica collagen glue C‧‧‧filler D‧‧‧ Dilution aid 10‧‧‧Premix tank 11‧‧‧Storage tank 12‧‧‧Glue mixing module 13‧‧‧Dispensing equipment 14‧‧‧Metal claw cover

FIG. 1 is a schematic diagram of a preferred process of the present invention. 2 is a cross-sectional view of a preferred metal claw cover of the present invention.

S‧‧‧ Silicone formula

E‧‧‧Epoxy resin formula

A‧‧‧The first high fluidity silica gel

B‧‧‧The second highest fluidity silica gel

C‧‧‧filler

D‧‧‧Dilution aid

10‧‧‧Premix tank

11‧‧‧Storage tank

12‧‧‧Mixed plastic module

13‧‧‧Dispensing equipment

14‧‧‧Metal claw cover

Claims (10)

A silicone epoxy resin composite material, comprising a silicone formula and an epoxy resin formula, the weight ratio of the silicone formula and the epoxy resin formula is in the range of 1:1 to 6:1, wherein the epoxy resin The formula contains an aliphatic epoxy compound. The silicone formula contains a first high-flow silica gel or a second high-flow silica collagen with a weight ratio of 1:1. The silica gel is a silica gel with a vinyl siloxane structure, which contains a platinum catalyst; the second high fluidity silica gel is a silica with a vinyl siloxane structure and a silicon-hydrogen bond Siloxane glue with oxane structure contains an inhibitor. For example, the silicone epoxy resin composite material of the first patent application, wherein the epoxy equivalent (EEW) of the epoxy resin formulation is about 190 to about 210 g/Eq. For example, the silicone epoxy resin composite material according to item 1 or 2 of the patent application, wherein the epoxy resin formulation includes an epoxy resin and a curing agent in a weight ratio of 1:1 to 4:1. For example, the silicone epoxy resin composite material of the third item in the patent application scope, wherein the curing agent is 4-methylhexahydrophthalic anhydride (MeHHPA). For example, the silicone epoxy resin composite material according to item 1 or 2 of the patent application, wherein the first high fluidity silica collagen glue contains an organic peroxide catalyst, an organic metal chelate catalyst or an organic amine A catalyst, wherein the organic peroxide catalyst is dibenzoyl peroxide, 2,4-dichlorobenzoyl peroxide, tert-butyl peroxybenzoate or di-tert-butyl peroxide; the organometallic chelate The substance is an organic tin carboxylate, an organic tin chelate or an organic titanium compound; the inhibitor is acetylene alcohol; and the platinum catalyst is platinum in a solution of divinyltetramethyldisilazane. For example, the silicone epoxy resin composite material of patent application item 1 or 2, which contains filler up to 50wt%. For example, the silicone epoxy resin composite material of the sixth patent application, wherein the filler contains talc, titanium dioxide, silicon dioxide or clay. For example, the silicone epoxy resin composite material according to item 1 or 2 of the patent application includes a dilution aid, and the dilution aid contains a silicone oil. A manufacturing method of silicone epoxy resin material for manufacturing a metal claw cover, wherein the metal claw cover is provided with a ring-shaped silicone epoxy material using a rotary coating device, and the steps include: providing a patent application scope The silicone epoxy resin composite material according to any one of items 1 to 8; coating step: the silicone epoxy resin composite material is introduced into a one-point glue equipment, and dripped or injected into one of the inner surfaces of a metal claw cover, and then Spin coating the metal claw cover with the silicone epoxy resin composite material, so that the composite material is rotated and distributed on the edge of the inner surface of the metal claw cover to form a ring-shaped silicone epoxy gasket; and Linking step: The silicone epoxy resin gasket coated on the metal claw cover is cross-linked by means of heat-assisted drying. For example, in the patent application, the 9th silicone epoxy resin material is used in the manufacturing method of the metal claw cover. In the coating process, when the rotation speed of the centrifugal process is greater than 1800rpm, the effect of defoaming and dispersion is achieved; In the process, heat-assisted drying is used for cross-linking; and another part of the dilution aid is added for dilution so that the viscosity is less than 7000 Cps.