200932961 九、發明說明: 【發明所屬之技術領域】 本發明係有II—種單—藉多重色彩之陽極處理方法,尤指一種一次 即可完成多重色彩之陽極處理之目的,具節省工時、轉使用量少、減少 污染、降低成本、不易造成Μ及不良品少紐點之陽極處理方法。 【先前技術】 按,習知欲產^重顏色之陽極處理方式有下列幾種:200932961 IX. Description of the invention: [Technical field to which the invention pertains] The present invention has an anode treatment method of II-type single-multiple colors, and particularly an anode treatment of multiple colors at one time, which saves man-hours, Anode treatment methods that reduce the amount of use, reduce pollution, reduce costs, and are less prone to defects and defective products. [Prior Art] According to the conventional method, there are several types of anode treatment methods:
第-種:係將加工元件進行脫油、水洗,進行陽極處理而於加工元件上 形成單-顏色,將欲保留之顏色部份塗上抗雜油墨,將加工猶置入盛 有硝酸之處簡内,絲塗上油墨之表面進行表祕色雜後,再將加工 而於前述經硝酸進行 元件置入盛有第二顏色染液之電解槽進行陽極處理, 表面褪色舰之部㈣減二顏色,依_推,依所需顏色之數量以前述 相同之步驟進行處理,於重複步喊成多種顏色時,則以有機溶劑將油墨 清除’最後進行藥水封口於表面形成一 战保遵Μ層,而此種處理方式,其處 理程序繁複,耗費較多工時,益傕旦 用大里之染料’除使成本增加外亦造成 污染。 第二種:先將加工元件進行第一次陽極處理上色程序,而於加工元件表 面形成第-顏色,再以加工切削去除方式欲上第二顏色部份切削去除,並 將該部份之第—顏色去除後,再進行第二顏色之陽極處理上色程序’且’ 除使用加工切除方式外,亦可採用雷射進行對部份表面燒結,以去除 該部位之第-純,依感推,依所f純數量,錢行相同步驟,同樣 於最後再進繼㈣彡,囉具耗時、 5 200932961 耗工及使用較多染料,而使成本增加及造成污染者,且以多次進行染料上 色’使各不同顏色於上色過程產生沾染,進而產生色差,亦使不良品增加。 第三種··其亦先赠極處理之方式進行第—顏色之上色處顯,再使用 越色劍如雙氧水將部份去除,顧行陽極處與行對去除部位之 第-色上色處理,依此類推’最後再進行藥水封口形成—表面保護膜層, 同樣的,具耗時耗工及使用較多染料,而使成本增加及造成污㈣,二以 多次進行染料上色’使各不_色於上色過誠生沾染,進 亦使不良品增加。 色差’ 【發明内容】 〈解決問題之技術手段〉 本發明人有鑑於上述習知多重顏色之陽極處理方式之實用困難及有待 改善之缺失,盼能提供-突破性之設計,明_效果,乃潛心研田、 設計組製,綜《多年從耗·品設計產叙專業技術知轉實務經驗 及研思設計騎之成果,終研㈣本侧—鮮—元料重轉 理方法,以提供使用者。 处 〈對照先前技術之功效〉 本發明之主要目的係一次即 成夕重色衫之陽極處理之特性,且r 省工時、染料使用量少、減 -Ep 降麵本、不料就錢不良品少 茲配合圖式 為使貴審查委員能更了解本發明之結構特徵及其功效 並詳細說明於后。 【實施方式】 Ο Ο 200932961 、請參閱第-圖所示,本發明係有關—種單—元件多重色彩之陽極處理 方法,其主要係將銘質加工元件經由脫油⑴、水洗⑵、化學抛光⑶ (使用酸性或驗性藥水如_、硝酸、驗進行對加工元件之表面腐钱, 去除表面難,呈魏之原色)、進行陽極處雜,其表喊化形成氧化層 ⑷(此氧化層呈多孔細小均勻之活化表面)、於氧化層外進行使用至少 一色以上娜爾U嫩⑸观⑽⑹騎行藥水封口 形成一保護膜層⑺等程序,進而可達—次即可完成多重色彩之陽極處 理之目的,具節省工時、細_少、減少污染、降低成本、不易造成 色差及不良品少等優點,此外,本發明於進行陽極處理,使其表面氧化形 成乳化層⑷,同時使氧化層表面呈多孔細小均勾之活化表面,以易於染 (5 ),其係可_ _、噴塗或手料其中—種方式進行上色。 综上所述,本發明具節省工時、染料㈣量少、減少污染、降低成本、 不易造成色差及不良品少等優點,為—甚具新穎性、進步性及可供產業上 2之發Θ實已符合發明專利之給予要件,爰依法提出專利申請,尚折 貴審查委員能軒魅,並早日賜准本鱗利,實為德便。 【圖式簡單說明】 第-圖係本發财法之流程方塊圖。 【主要元件符號說明】 (1 )脫油 (2) 水洗 (3) 化學搬光 7 200932961 (4) 進行陽極處理使其表面氧化形成氧化層 (5) 於氧化層外進行使用至少一色以上之親水性染料之上色程序 (6) 烘乾程序 (7) 進行藥水封口形成一保護膜層 ❹The first type: the processing element is deoiled, washed, anodized to form a single-color on the processing element, and the color portion to be retained is coated with anti-alias ink, and the processing is placed in the nitric acid. In the case of the ink, the surface of the ink is coated with the surface of the ink, and then processed and placed in the electrolytic cell containing the second color dyeing solution for the anode treatment, the surface of the surface fading ship (four) minus two Color, according to _ push, according to the number of required colors in the same steps as described above, when repeated steps shouted into a variety of colors, the ink is removed with an organic solvent 'final syrup seal on the surface to form a warfare layer However, this kind of treatment method has complicated processing procedures and consumes a lot of man-hours. It is beneficial to use Dali's dyes to reduce pollution and increase pollution. The second method: firstly, the processing component is subjected to the first anodizing process, and the first color is formed on the surface of the processing component, and then the second color portion is cut and removed by the machining cutting removal method, and the portion is After the first color is removed, the second color anodizing process is performed, and in addition to the processing and cutting method, a part of the surface may be sintered by laser to remove the first-purity of the part. Push, according to the pure quantity of the f, the same steps of the money, the same as the last (4) 彡, 啰 time-consuming, 5 200932961 labor and use more dyes, and increase costs and cause polluters, and multiple times The dyeing of the dyes causes the different colors to become contaminated during the coloring process, which in turn causes chromatic aberration and also increases the number of defective products. The third type is also the first to give the first color to the color, and then use the more color sword such as hydrogen peroxide to remove the part, taking care of the anode and the line to remove the first color Treatment, and so on, and finally the formation of the syrup seal - the surface protective film layer, the same, time-consuming and labor-intensive and use more dyes, and increase the cost and pollution (four), two times dye dyeing ' Let each color not be colored and stained with sincerity, and the increase will also increase the number of defective products. Color difference' [Technical means] The present inventors have in view of the practical difficulties of the conventional multi-color anode treatment method and the lack of improvement, and hope to provide a breakthrough design, Dedicated to research and design, system design, comprehensive "for many years from the consumption of product design and production of professional technology to know the practical experience and research and design of the ride, the final research (four) this side - fresh - yuan material re-transfer method to provide use By. The main purpose of the present invention is the characteristics of the anode treatment of the one-time color grading shirt, and the labor time, the amount of dye used is small, the -Ep is reduced, and the defective product is unexpectedly The lesser fits the schema to give your review board a better understanding of the structural features and efficacy of the present invention and is described in detail below. [Embodiment] Ο Ο 200932961, please refer to the figure - Figure, the present invention relates to a single-element multi-color anode treatment method, which mainly uses the de-oiling (1), water washing (2), chemical polishing (3) (Using acid or mineral water such as _, nitric acid, testing the surface of the processing components, to remove the surface, it is difficult to remove the surface, the original color of Wei), the anode is miscellaneous, and its surface is shattered to form an oxide layer (4) (this oxide layer A porous fine uniform activation surface), using at least one color above the oxide layer, using Naer U Nen (5) Guan (10) (6) riding a chemical seal to form a protective film layer (7) and the like, and then can achieve multiple colors of the anode treatment The purpose of the invention is to save labor, reduce the pollution, reduce the cost, and not easily cause chromatic aberration and less defective products. In addition, the present invention performs anodizing treatment to oxidize the surface to form an emulsified layer (4) while making the oxide layer. The surface is made of a porous, small, and evenly activated surface for easy dyeing (5), which can be colored by means of __, spraying or hand-dyed. In summary, the invention has the advantages of saving man-hours, less dye (four), reducing pollution, reducing cost, not easily causing chromatic aberration and less defective products, and is very novel, progressive and available for the industry. The tamping has already met the requirements for the invention patents, and the patent application was filed according to law, and the review committee of the company was able to revive it, and it was a good place to be granted as soon as possible. [Simple description of the diagram] The first-graph is a block diagram of the process of this financial method. [Explanation of main component symbols] (1) Deoiling (2) Washing (3) Chemical transfer 7 200932961 (4) Anodic treatment to oxidize the surface to form an oxide layer (5) Use at least one color of hydrophilicity outside the oxide layer Coloring process of dyes (6) Drying procedure (7) Sealing the syrup to form a protective film ❹