TW200835385A - Method for extending lifetime of organic light-emitting diode - Google Patents
Method for extending lifetime of organic light-emitting diode Download PDFInfo
- Publication number
- TW200835385A TW200835385A TW96104945A TW96104945A TW200835385A TW 200835385 A TW200835385 A TW 200835385A TW 96104945 A TW96104945 A TW 96104945A TW 96104945 A TW96104945 A TW 96104945A TW 200835385 A TW200835385 A TW 200835385A
- Authority
- TW
- Taiwan
- Prior art keywords
- organic light
- emitting diode
- water
- light
- polymer
- Prior art date
Description
200835385 九、發明說明: 【發明所屬之技術領域】 本發明係有關於有機發光二極體,尤其有關於一種延 長有機發光二極體壽命之方法。 、 【先前技術】 有機發光二極體,由於具有省電、高亮度之優勢,已 成為照明崎興獅’然—般的有機發光二極體(况肋) 70件本身在製造過程中即常會有水氣的侵入,例如: 銦錫⑽;indium-tin-Gxide)基板表面的錢,有二材 料中所含的水氣’真空驗腔體中_的微量水氣,金屬 電極形成後自界面及有機層中擴散進來的水氣等等,這此 都會造成元件的有機材料氧化或電極的劣化,使得元^ 壞。 貝 即便這些不良因素都能以嚴謹的製程控管予以減到最 低’-倾紐的有機發光二極體成品減要㈣從空氣 • 巾再度擴散進入的水氣的嚴峻考驗。亦即,水氣的進二通 常演變成有機發光二極體使用壽命的大幅下降。一般廣為 人所採取的職是研翻疏水性高(hydiOphQbie,即,水 滴在其上因表面張力大而致接觸角(_加如咖)大) 的封裝材料以及其特殊的後續表面處理。然而,這類的措 般僅能制極財_轉,是鮮水滴不易附 著在封裝材料上’水蒸汽(或水氣)仍然可藉由擴散穿透 此封裝層進而侵襲有機發光二極體内部。事實上,空氣中 的氧也以同樣的方式進入而氧化元件中的有機材料,而進 5 200835385 一步加快劣化的時程。 【發明内容】 羡此,本發明之主要目的在 絕水氣與氧氣的技術手段 光二極體壽命之方m 、。種可延長有機發 、, 町,心不忐,其透過阻絕水_ 來曰加有機發光二極體的可使用期限。 二達述目的,本發明係在封裝時,讓—古八 包覆該有機發光二極體,該高 :子液體
的能 隔氧且疏水之紐,因此透射=有翻、絕緣、 f極體之周圍,即可藉該高分子液體具有排=機發 =阻絕有機發光二極體與水氣與氧氣的接觸,亦即可 避免有機發光二極财製造完叙後,於使用過程中再受 氣的侵害’進而提升有機發光二極體的壽命: 為使貴委員對本發明之特徵、目的及功效,有更加 深入之瞭解與綱,_舉触實施顺配合圖式說明如 后: 清參閱「第i圖」所示。本發明係提供一種延長有機 务光-極體*命之方法,其可用於增加—有機發光二極體 ίο的使用壽命,首先係先提供一高分子液體20,該高分子 液體20為一透明、絕緣且不溶於水之液狀物,一般稱之為 「假水」。 目前常見的「假水」,為是3M公司的消防用產品,屬 於其 Novec 1230 Fire Protection Fluid 系列,分為 3M Fluorinert Electronic Liquid 和 3M Novec Engineered 6 200835385
Fluids二類。這一系列的假水產品具備高超的吸熱能力, 但在外觀上卻與水難以分別,且無色無味。儘管傾倒出時 及流動的樣子都如水—般,但卻不會把物件絲,例如, 可以將正在工作中的筆記型電腦整個浸泡在假水裡面,卻 只會洗出汙物而不會造成短路,因_為符合現代消防所 需’尤其是胁置放重要文件、精密儀H、高價值貨品等 之處所。 、口口、
本發明實驗所選用的是3Μ公司上述產品系列中的
Fluorinert Electronic Liquid FC-40,其在室溫時為無 色、無味且絕緣之液態,工作溫度範圍在-57度到155度之 間,其主要是一種穩定的單個長鍵化合物,主要 CF3CF2C(〇)CF(CF3)2。 接著,本發明係利用該高分子液體20,亦即上述之「假 水」來封裝該有機發光二極體1〇,使該高分子液體2〇包^ 在該有機發光二極體1Q之删,因此即可隔絕該有機發光 一極體10與外界之水氣及氧氣的接觸。 本發明之實驗係分成實驗組與對照組兩組同時進行, 其中實驗、组,係使用該高分子液體2〇(FC-4〇)包覆整個有機 發光二極體10 ;而触組,則是未經任何處理之有機發光 2體10。本發明同時在室溫與高溫等二種實驗環境下進 了實驗’其巾室溫為25度,紐55%__;而高溫則使用 ^溫箱控制環境’前期為50度,後期增溫至7G度,溼度 刀別為17%、3%,以加快有機發光二極體1〇壽命衰減速度。 7 200835385 、,實驗中所使用的有機發光二極體l〇,發光源皆為白 光’並採用相同之製程條件’以不斷電持續點亮有機發光 極體10的方式’作固定間隔時間作量測。並使用光譜儀 在定點量測有機發光二極體10光強度,其可連接到電腦上 利用HMT Optics光譜檢測系統分析,其使用軟體為 多功能光學特性檢測系統,其適肢長為25Gnra到85〇譲, 實驗設定接光譜波長範圍為300nm到75〇nm。 • 請再參閱「第2圖」與「第3圖」所示,其分別為本 發明在室溫與冑溫下’實驗組麟·之實驗數據比較, 其為有機發光二極體1〇之光強度隨著時間的變化關係圖, X軸為有機發光二極體10連續使用壽命天數,¥轴為有機 發光二極體10光強度,根據線性擬合可得到一個直線方程 式’來推算有機發光二極體10壽命。 如第2圖」所示,L1為室溫中有機發光二極體1〇 之光強度變化,由線性擬合得直線方程式為¥= 齡 -53· 5_4騎+獅.519542 ’ L2為室溫中使用高分子 液體20(F040)覆蓋有機發光二極體1〇之光強度變化,由 線性擬合得直線方程式為γ = —43·44354469*χ + 8035.517344。 而如「第3圖」所,L3為高溫中有機發光二極體1〇 光強度變化’由線性擬合得直線方程式為γ= 176· 787111*Χ+6956· 292735,L4為高溫中覆蓋有機發光二 極體10光強度變化,由線性擬合得直線方程式為 8 200835385 -168. 7277436*X+7644. 337179 〇 由實驗結果可以發現,在室溫下,有覆蓋高分子液體 〇(FC 40)之有機發光一極體1〇(實驗組)的連續使用的天 數可達到185天(線性擬合結果),而未經過處理的有機 發光二極體1G(對照組)連續使用的的天數為146天(線性 擬a、、、σ果)連,使用奇命延長約27%。而在怪溫箱裡(高溫) 的貝驗發現彼此的差距並不大,有無覆蓋高分子液體 20(FC-40)之有機發光二極體1〇皆以很快的速度衰減,但 亦可看出有覆蓋高分子液體200^40)之有機發光二極體 10的壽命仍然較長。 如上所述,本發明透過高分子液體20來阻絕水氣與氧 氣進入有機發光二極體10,因此可延長連續使用壽命約 27/,本發明係藉由該高分子液體2〇具有排拒水的能力, 來阻絕有機發光二極體10與水氣與氧氣的接觸,而延緩有 機發光二極體10的惡化時程,據而提升有機發光二極體1〇 的使用壽命。 綜上所述僅為本發明的較佳實施例而已,並非用來限 定本發明之實施範圍,即凡依本發明申請專利範圍之内容 所為的等效變化與修飾,皆應為本發明之技術範疇。 【圖式簡單說明】 第1圖’係本發明高分子液體包覆有機發光二極體之示 意圖。 第2圖,係本發明在室溫下,實驗組與對照組之比較圖。 9 200835385 第3圖,係本發明在高溫下,實驗組與對照組之比較圖。 【主要元件符號說明】 10 :有機發光二極體 20 :南分子液體
Claims (1)
- 200835385 十、申請專利範園: 1、一種延長有機發光二極體壽命 , 可p〈万去,用於增加一 有機赉光二極體的使用壽命,其步驟包含: 提供-高分子紐,該高分该料—翻、絕緣且 具疏水性之液狀物; 利用該高分子㈣雜該錢發光二贿,使該高分 ^液體包覆在該有機發光二極體之,以隔絕該有機ς 光二極體與外界之水氣及氧氣的接觸。 一 2如申呀專利範圍第丨項所述之背光模組結構,並中 該高分子㈣為歡的糊長鍵化合物。 八 古3、如申請專利範圍帛2項所述之背光模組結構,其中 該呵分子㈣的主要構造為⑶謂⑽⑽咖。11