TR201405701A2 - Synthetic method of obtaining an electric arc furnace base forging mortar. - Google Patents

Synthetic method of obtaining an electric arc furnace base forging mortar.

Info

Publication number
TR201405701A2
TR201405701A2 TR2014/05701A TR201405701A TR201405701A2 TR 201405701 A2 TR201405701 A2 TR 201405701A2 TR 2014/05701 A TR2014/05701 A TR 2014/05701A TR 201405701 A TR201405701 A TR 201405701A TR 201405701 A2 TR201405701 A2 TR 201405701A2
Authority
TR
Turkey
Prior art keywords
mortar
obtaining
electric arc
synthetic method
arc furnace
Prior art date
Application number
TR2014/05701A
Other languages
Turkish (tr)
Inventor
Gürcan Hüseyi̇n
Korkmaz Hakan
Özdemi̇r Beyhan
Uçak Merve
Original Assignee
Kuemas Manyezit Sanayi A S
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Kuemas Manyezit Sanayi A S filed Critical Kuemas Manyezit Sanayi A S
Priority to TR2014/05701A priority Critical patent/TR201405701A2/en
Publication of TR201405701A2 publication Critical patent/TR201405701A2/en
Priority to PCT/TR2015/000207 priority patent/WO2015178866A1/en

Abstract

Buluş; demir-çelik sektöründeki elektrik ark ocaklarının astar kaplaması olarak kullanılan taban dövme harcına ilişkin a) Manyezitin kalsine edilmesi, b) Kalsine manyezit, dolomit ve demir oksitin istenilen ölçülerde tartılıp mikserde karıştırılması, c) (b) adımında elde edilen karışımın 1800-2200 ºC dereceler arasında döner fırında sinterlenmesi adımlarını içeren bir taban dövme harcı üretim yöntemidir.Invention; a) Calcining of magnesite, b) Weighing calcined magnesite, dolomite and iron oxide to desired dimensions and mixing in the mixer, c) 1800-2200 ºC degrees is a method of manufacturing a base forging mortar comprising the steps of sintering in a rotary kiln.

TR2014/05701A 2014-05-22 2014-05-22 Synthetic method of obtaining an electric arc furnace base forging mortar. TR201405701A2 (en)

Priority Applications (2)

Application Number Priority Date Filing Date Title
TR2014/05701A TR201405701A2 (en) 2014-05-22 2014-05-22 Synthetic method of obtaining an electric arc furnace base forging mortar.
PCT/TR2015/000207 WO2015178866A1 (en) 2014-05-22 2015-05-21 Method for synthetic production of base forging mortar for electric arc furnace

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
TR2014/05701A TR201405701A2 (en) 2014-05-22 2014-05-22 Synthetic method of obtaining an electric arc furnace base forging mortar.

Publications (1)

Publication Number Publication Date
TR201405701A2 true TR201405701A2 (en) 2014-12-22

Family

ID=53761472

Family Applications (1)

Application Number Title Priority Date Filing Date
TR2014/05701A TR201405701A2 (en) 2014-05-22 2014-05-22 Synthetic method of obtaining an electric arc furnace base forging mortar.

Country Status (2)

Country Link
TR (1) TR201405701A2 (en)
WO (1) WO2015178866A1 (en)

Family Cites Families (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CA713616A (en) * 1965-07-13 M. Atlas Leon Dolomitic refractory
GB992271A (en) * 1962-06-04 1965-05-19 Basic Inc Dolomitic refractory
US3901721A (en) * 1974-05-13 1975-08-26 Corning Glass Works Dolomite-magnesite refractory and batch therefor
US3940279A (en) * 1974-06-17 1976-02-24 Corning Glass Works Size-graded ternary batch for bonded basic refractory shapes
DE3118481C2 (en) * 1981-05-09 1985-09-05 Dolomitwerke GmbH, 5603 Wülfrath Process for the production of sintered dolomite with low porosity and good resistance to hydration
DE3209836A1 (en) * 1982-03-18 1983-09-29 Dolomitwerke GmbH, 5603 Wülfrath METHOD FOR PRODUCING SINTERDOLOMITE IN A SHAFT OVEN AND SHAFT OVEN FOR IMPLEMENTING THE METHOD
DE3828997C1 (en) * 1988-08-26 1989-12-21 Dolomitwerke Gmbh, 5603 Wuelfrath, De
US5908801A (en) * 1997-05-23 1999-06-01 Servicios Industriales Penoles, S.A. De C.V. Process for the production of synthetic dolomite
CN1266827A (en) * 2000-03-28 2000-09-20 营口青花集团有限公司 Immersed-in-wax burnt conite brick and its making process

Also Published As

Publication number Publication date
WO2015178866A1 (en) 2015-11-26

Similar Documents

Publication Publication Date Title
PL3098512T3 (en) Rotary furnace and method of operating a rotary furnace
IL263442A (en) Production of carbon-based oxide and reduced carbon-based oxide on a large scale
PL3027310T3 (en) Mixed metal iron oxides and uses thereof
EP2947060A4 (en) Magnesia-carbon brick
GB201909044D0 (en) Low portland silica-lime cements
HK1208856A1 (en) Magnesia cement and manufacturing method thereof
IL289443A (en) Cementitious reagents, methods of manufacturing and uses thereof
EP3499163A4 (en) Sintering furnace
GB2588536B (en) Metal oxide cement
ZA201807143B (en) Cerium- and zirconium-based mixed oxide
DK3368492T3 (en) Process for the preparation of a cement clinker substitute consisting primarily of calcined clay
DK3125949T3 (en) Dendronized metal oxide nanoparticles, method of preparation and applications thereof
ZA201706520B (en) An adjuvant for a cement or a refractory concrete composition, the uses thereof, and cement and refractory concrete compositions
PT3374129T (en) Sintered, polycrystalline, flat, geometrically structured ceramic grinding element, method for the production thereof, and use thereof
PL3466900T3 (en) Building elements made from binders hardening by combined hydration and carbonation
GB202002268D0 (en) Sintered ceramic bodies and applications thereof
SG11202109028RA (en) Production method for cement clinker and cement clinker powder
PL3219688T3 (en) Cement clinker line and a method for operating a cement clinker line
EA201300478A1 (en) MANUFACTURING OF BONDED LIME FROM NATURAL CHALK IN A ROTATING KILN
TR201405701A2 (en) Synthetic method of obtaining an electric arc furnace base forging mortar.
GB2547547B (en) Cement compositions having fast setting times and high compressive strengths
EP3633296A4 (en) Dual-purpose sintering furnace
MX340425B (en) Arch brick, cylindrical internal lining of a rotary kiln and rotary kiln.
PL3219689T3 (en) Cement clinker line and a method for operating a cement clinker line
PL3732143T3 (en) Aluminous cement