TH68705B - High-strength mild steel plates and methods for producing them. - Google Patents

High-strength mild steel plates and methods for producing them.

Info

Publication number
TH68705B
TH68705B TH601003614A TH0601003614A TH68705B TH 68705 B TH68705 B TH 68705B TH 601003614 A TH601003614 A TH 601003614A TH 0601003614 A TH0601003614 A TH 0601003614A TH 68705 B TH68705 B TH 68705B
Authority
TH
Thailand
Prior art keywords
less
molybdenum
vanadium
titanium
carbon
Prior art date
Application number
TH601003614A
Other languages
Thai (th)
Other versions
TH86981A (en
TH86981B (en
Inventor
เซโตะ นายคาซูฮิโร่
โยโกตะ นายทาเกชิ
อาริกะ นายทามาโกะ
โคบายาชิ นายอะกิโอะ
Original Assignee
เจเอ็ฟอี สตีล คอร์ปอเรชั่น
นางสาวอุไรวรรณ ดำรงค์สุนันท์
Filing date
Publication date
Application filed by เจเอ็ฟอี สตีล คอร์ปอเรชั่น, นางสาวอุไรวรรณ ดำรงค์สุนันท์ filed Critical เจเอ็ฟอี สตีล คอร์ปอเรชั่น
Publication of TH86981A publication Critical patent/TH86981A/en
Publication of TH86981B publication Critical patent/TH86981B/en
Publication of TH68705B publication Critical patent/TH68705B/en

Abstract

DC60 (27/10/49) แผ่นเหล็กเหนียวแรงดึงสูงที่มีความแข็งแรงเชิงดึงที่ 980 MPa หรือที่มีความแข็งแรงเชิงดึงที่สูง กว่า พร้อมกับการยืดตัวและความสามารถในการขึ้นรูปปีกโลหะยื่นอย่างดีเยี่ยม, เหมาะสำหรับการอัดขึ้นรูป (press-forming) รูปทรงตัดขวางที่ซับซ้อน เช่น ชิ้นส่วนของรถยนต์, ถูกผลิตขึ้นโดยการปรับเหล็ก หล้าให้ประกอบด้วยสารัตถะสำคัญ ของโครงสร้างเฟสเดี่ยวเฟอร์ไรต์, เพื่อตกตะกอนคาร์ไบด์ที่มี ไททาเนียม, โมลิบดินัม และวานาเดียมที่น้อยกว่า 10 nm ของขนาดอนุภาคเฉลี่ย ในสภาวะกระจาย และ เพื่อให้องค์ประกอบเฉลี่ยของคาร์ไบด์ที่มีไททาเนียม, โมลิบดินัม และวานาเดียมที่เป็นตาม [ V/ (Ti + Mo + V) มากกว่าหรือเท่ากับ 0.3 (อัตราส่วนอะตอม) รูปที่เลือก : รูปที่ 2 แผ่นเหล็กเหนียวแรงดึงสูงที่มีความแข็งแรงเชิงดึงที่ 980 MPa หรือที่มีความแข็งแรงเชิงดึงที่สูง กว่า พร้อมกับการยืดตัวและความสามารถในการขึ้นรูปปีกโลหะยื่นอย่างดีเยี่ยม, เหมาะสำหรับการอัดขึ้นรูป (press-forming) รูปทรงตัดขวางที่ซับซ้อน เช่น ชิ้นส่วนของรถยนต์, ถูกผลิตขึ้นโดยการปรับเหล็ก หล้าให้ประกอบด้วยสารัตถะสำคัญ ของโครงสร้างเฟสเดี่ยวเฟอร์ไรต์, เพื่อตกตะกอนคาร์ไบด์ที่มี ไททาเนียม, โมลิบดินัม และวานาเดียมที่น้อยกว่า 10 nm ของขนาดอนุภาคเฉลี่ย ในสภาวะกระจาย และ เพื่อให้องค์ประกอบเฉลี่ยของคาร์ไบด์ที่มีไททาเนียม, โมลิบดินัม และวานาเดียมที่เป็นตาม [ V/ (Ti + Mo + V) มากกว่าหรือเท่ากับ 0.3 (อัตราส่วนอะตอม) รูปที่เลือก : รูปที่ 2DC60 (27/10/49) High-tensile steel plate with a tensile strength of 980 MPa or higher, along with excellent elongation and formability of metal flanges, suitable for press-forming complex cross-sections such as automotive parts, is produced by modifying the steel to contain the main components of a single-phase ferrite structure, to precipitate carbides containing titanium, molybdenum, and vanadium with an average particle size of less than 10 nm in the dispersed state, and to ensure the average composition of titanium, molybdenum, and vanadium carbides is [V/(Ti + Mo + V) greater than or equal to 0.3 (atomic ratio)]. Selected image: Figure 2. High-tensile steel plate with a tensile strength of 980 MPa or higher, along with excellent elongation and formability of metal flanges, suitable for press-forming complex cross-sections such as automotive parts, is produced by modifying the steel. The process involves the use of a single-phase ferrite structure to precipitate carbides containing titanium, molybdenum, and vanadium with an average particle size less than 10 nm in a dispersed state, and to achieve an average composition of titanium, molybdenum, and vanadium carbides that conform to [V/(Ti + Mo + V) greater than or equal to 0.3 (atomic ratio)]. (Selected figure: Figure 2)

Claims (8)

9 สิงหาคม 2560 หน้า 2 กว่า ที่ซึ่งคาร์ไบด์มีไททาเนียม, โมลิบดินัม และวานาเดียม, และที่มีน้อยกว่า 10 nm ของขนาดอนุภาค เฉลี่ยตกตะกอนในสภาวะกระจาย, และคาร์ไบด์ที่มีไททาเนียม, โมลิบดินัม และวานาเดียม มีองค์ประกอบ เฉลี่ยที่เป็นตาม [V/ (Ti + Mo + V) (สัญลักษณ์) 0.3], ซึ่งไททาเนียม, โมลิบดีนัม และวานาเดียม ถูกแสดงโดยเปอร์เซ็นต์อะตอม, ประกอบด้วยขั้นของการรีดร้อนแผ่นพื้นเหล็กกล้า (steel slab) ที่ประกอบด้วยมากกว่า 0.06% และไม่มากกว่า 0.24% ของคาร์บอน, 0.3% หรือน้อยกว่าของ ซิลิคอน, 0.5 ถึง 2.0% ของแมงกานีส, 0.06% หรือน้อยกว่าของฟอสฟอรัส, 0.005% หรือ น้อยกว่าของกำมะถัน, 0.06% หรือน้อยกว่าของอัลลูมิเนียม, 0.006% หรือน้อยกว่าของไนโตรเจน, 0.05 ถึง 0.5% ของโมลิบดินัม, 0.03 ถึง 0.2% ของไททาเนียม, มากกว่า 0.15 และไม่มาก กว่า 1.2% ของวานาเดียม, โดยมวล, และส่วนที่เหลือที่เป็นเหล็กและสิ่งเจือปนอาจหลีกเลี่ยงได้ และที่มีองค์ประกอบที่ซึ่งปริมาณของคาร์บอน, ไททาเนียม, โมลิบดินัม และวานาเดียม เป็นตามสูตร (I) ภายใต้เงื่อนไขของอุณหภูมิแต่งผิวที่ 880ํC หรือที่สูงกว่า และที่อุณหภูมิการขดที่ 570ํC หรือที่สูงกว่า 0.8 (สัญลักษณ์) (C/12) / { (Ti/48) + (Mo/96) + (V/51)} (สัญลักษณ์) 1.5 (I) ที่ซึ่ง คาร์บอน, ไททาเนียม, โมลิบดินัม และวานาเดียม ระบุเปอร์เซ็นต์โดยมวลสำหรับแต่ละตัว ของมัน 5.วิธีการสำหรับผลิตแผ่นเหล็กเหนียวแรงดึงสูงตามข้อถือสิทธิข้อ 4. ประกอบด้วย ขั้นของการอาบสังกะสีแบบจุ่มร้อนลงบนผิวหน้าของแผ่นเหล็กเหนียวหลังจากการรีดร้อน ------------------------------------------------------------------------------------------------------------------------------------------------------ แก้ไข 16/02/2560 1. แผ่นเหล็กเหนียวแรงดึงสูงที่ประกอบด้วย เฟสเฟอร์ไรต์ของอัตราส่วนเนื้อที่ที่ 95% หรือมากกว่า, ที่มี 980 MPa หรือที่มีความแข็งแรงเชิงดึงที่สูงกว่า ที่ซึ่งคาร์ไบต์มีไททาเนียม, โมลิบดินัม และวานาเดียม และที่มีน้อยกว่า 10 nm ของขนาดอนุภาคเฉลี่ย ตกตะกอนในสภาวะ กระจาย, และคาร์ไบด์ที่มีไททาเนียม, โมลิบดินัมและวานาเดียม มีองค์ประกอบเฉลี่ยที่เป็นตาม [V/ (Ti + Mo + V) (สูตร) 0.3], ซึ่งไททาเนียม, โมลิบดินัม และวานาเดียมถูกแสดงโดย เปอร์เซ็นต์อะตอม, ประกอบด้วยมากกว่า 0.06% และไม่มากกว่า 0.24% ของคาร์บอน, 0.3% หรือน้อยกว่าของซิลิคอน, 0.5 ถึง 2.0% ของแมงกานีส, 0.06% หรือน้อยกว่าของฟอสฟอรัส, 0.005% หรือน้อยกว่าของกำมะถัน, 0.06% หรือน้อยกว่าของอัลลูมิเนียม, 0.006% หรือน้อยกว่า ของไนโตรเจน, 0.05 ถึง 0.5% ของโมลิบดินัม, 0.03 ถึง 0.2% ของไททาเนียม, มากกว่า 0.15 และไม่มากกว่า 1.2% ของวานาเดียม, โดยมวล, และส่วนที่เหลือที่เป็นเหล็กและสิ่งเจือปนที่ ไม่อาจหลีกเลี่ยงได้และที่มีองค์ประกอบที่ซึ่งปริมาณของคาร์บอน, ไททาเนียม, โมลิบดินัม และ วานาเดียม เป็นตามสูตร (I) 0.8 (สูตร) (C/12)/{ (Ti/48) + (Mo/96) + (V/51)} (สูตร) 1.5 (I) ที่ซึ่ง คาร์บอน, ไททาเนียม, โมลิบดินัม และวานาเดียม ระบุเปอร์เซ็นต์โดยมวลสำหรับแต่ละตัวของมัน 2. แผ่นเหล็กเหนียวแรงดึงสูงตามข้อถือสิทธิข้อ 1, ที่ซึ่งแผ่นเหล็กเหนียวเป็นแผ่นเหล็ก เหนียวรีดร้อนขนาดความหนาบาง (thin gauge hot-rolled steel sheet) ที่มี ความหนาของแผ่นที่ 2.5 มม. หรือที่มีความหนาของแผ่นที่น้อยกว่า 3. แผ่นเหล็กเหนียวแรงดึงสูงตามข้อหนึ่งข้อใดของข้อถือสิทธิข้อ 1. หรือ 2. ที่ซึ่งแผ่น เหล็กเหนียวมีฟิล์มอาบสังกะสีแบบจุ่มร้อนอยู่บนนั้น 4. วิธีการสำหรับผลิตแผ่นเหล็กเหนียวแรงดึงสูงของโครงสร้างโลหะ ที่ประกอบด้วย เฟส เฟอร์ไรต์ของอัตราส่วนเนื้อที่ที่ 95% หรือมากกว่า, ที่มี 980 MPa หรือที่มีความแข็งแรงเชิงดึงที่สูง กว่า ที่ซึ่งคาร์ไบด์มีไททาเนียม, โมลิบดินัม และวานาเดียม, และที่มีน้อยกว่า 10 มม. ของขนาดอนุภาค เฉลี่ยตกตะกอนในสภาวะกระจาย, และคาร์ไบด์ที่มีไททาเนียม, โมลิบดินัม และวานาเดียม มีองค์ประกอบ เฉลี่ยที่เป็นตาม [V/ (Ti + Mo + V) (สูตร) 0.3], ซึ่งไททาเนียม, โมลิบดีนัม และวานาเดียม ถูกแสดงโดยเปอร์เซ็นต์อะตอม, ประกอบด้วยขั้นของการรีดร้อนแผ่นพื้นเหล็กกล้า (steel slab) ที่ประกอบด้วยมากกว่า 0.06% และไม่มากกว่า 0.24% ของคาร์บอน, 0.3% หรือน้อยกว่าของ ซิลิคอน, 0.5 ถึง 2.0% ของแมงกานีส, 0.06% หรือน้อยกว่าของฟอสฟอรัส, 0.005% หรือ น้อยกว่าของกำมะถัน, 0.06% หรือน้อยกว่าของอัลลูมิเนียม, 0.006% หรือน้อยกว่าของไนโตรเจน, 0.05 ถึง 0.5% ของโมลิบดินัม, 0.03 ถึง 0.2% ของไททาเนียม, มากกว่า 0.15 และไม่มาก กว่า 1.2% ของวานาเดียม, โดยมวล, และส่วนที่เหลือที่เป็นเหล็กและสิ่งเจือปนอาจหลีกเลี่ยงได้ และที่มีองค์ประกอบที่ซึ่งปริมาณของคาร์บอน, ไททาเนียม, โมลิบดินัม และวานาเดียม เป็นตามสูตร (I) ภายใต้เงื่อนไขของอุณหภูมิแต่งผิวที่ 880 ํC หรือที่สูงกว่า และที่อุณหภูมิการขดที่ 570 ํC หรือที่สูงกว่า 0.8 (สูตร) (C/12) / { (Ti/48) + (Mo/96) + (V/51)} (สูตร) 1.5 (I) ที่ซึ่ง คาร์บอน, ไททาเนียม, โมลิบดินัม และวานาเดียม ระบุเปอร์เซ็นต์โดยมวลสำหรับแต่ละตัว ของมัน 5. วิธีการสำหรับผลิตแผ่นเหล็กเหนียวแรงดึงสูงตามข้อถือสิทธิข้อ 4. ประกอบด้วย ขั้นของการอาบสังกะสีแบบจุ่มร้อนลงบนผิวหน้าของแผ่นเหล็กเหนียวหลังจากการรีดร้อน -----------------------------August 9, 2017, page 2. More than where carbides contain titanium, molybdenum, and vanadium, and have particle sizes less than 10 nm. The average precipitated dispersed state, and carbides containing titanium, molybdenum, and vanadium, have an average composition according to [V/(Ti + Mo + V) (symbol) 0.3], where titanium, molybdenum, and vanadium are represented by atomic percentages, comprise hot-rolled steel slabs containing more than 0.06% and not more than 0.24% carbon, 0.3% or less of silicon, 0.5 to 2.0% of manganese, 0.06% or less of phosphorus, 0.005% or less of sulfur, 0.06% or less of aluminum, 0.006% or less of nitrogen, 0.05 to 0.5% of molybdenum, 0.03 to 0.2% of titanium, and more than 0.15 and not more than 1.2%. of vanadium, by mass, and the remainder of iron and impurities may be avoided and having a composition in which the amounts of carbon, titanium, molybdenum and vanadium are according to the formula (I) under the conditions of surface finishing temperature of 880°C or higher and coiling temperature of 570°C or higher 0.8 (symbol) (C/12) / { (Ti/48) + (Mo/96) + (V/51)} (symbol) 1.5 (I) in which carbon, titanium, molybdenum and vanadium are specified as percentages by mass for each of them. 5. The method for producing high tensile steel plates according to claim 4. consists of a step of hot-dip galvanizing on the surface of the ductile steel plate after hot rolling. ------------------------------------------------------------------------------------------------------------------------------------------------------ Revised 16/02/2017 1. High tensile steel plates composed of Ferrite phases of a volume ratio of 95% or greater, with a tensile strength of 980 MPa or higher, in which carbides containing titanium, molybdenum, and vanadium and with an average particle size less than 10 nm are precipitated in a dispersed state, and carbides containing titanium, molybdenum, and vanadium have an average composition according to [V/(Ti + Mo + V) (formula) 0.3], in which titanium, molybdenum, and vanadium are represented by... The atomic percentage consists of more than 0.06% and no more than 0.24% carbon, 0.3% or less silicon, 0.5 to 2.0% manganese, 0.06% or less phosphorus, 0.005% or less sulfur, 0.06% or less aluminum, 0.006% or less nitrogen, 0.05 to 0.5% molybdenum, 0.03 to 0.2% titanium, more than 0.15 and no more than 1.2% vanadium, by mass, and the remainder being iron and impurities. It is unavoidable and contains a composition in which the amounts of carbon, titanium, molybdenum and vanadium are according to the formula (I) 0.8 (formula) (C/12)/{ (Ti/48) + (Mo/96) + (V/51)} (formula) 1.5 (I) in which carbon, titanium, molybdenum and vanadium are specified as percentages by mass for each of them. 2. High tensile steel plate according to claim 1, in which the steel plate is a thin gauge hot-rolled steel sheet with a thickness of 2.5 mm or less. 3. High tensile steel plate according to any one of claim 1 or 2, in which the steel plate has a hot-dip galvanized film on it. 4. Method for the production of high tensile steel plates of metal structures. Containing a ferrite phase with a volume ratio of 95% or more, possessing a tensile strength of 980 MPa or higher, where the carbides contain titanium, molybdenum, and vanadium, and have particle sizes less than 10 mm. The average precipitated dispersed state, and carbides containing titanium, molybdenum, and vanadium, have an average composition according to [V/(Ti + Mo + V) (formula) 0.3], where titanium, molybdenum, and vanadium are represented by atomic percentages, comprise the hot-rolled steel slabs containing more than 0.06% and not more than 0.24% carbon, 0.3% or less of silicon, 0.5 to 2.0% of manganese, 0.06% or less of phosphorus, 0.005% or less of sulfur, 0.06% or less of aluminum, 0.006% or less of nitrogen, 0.05 to 0.5% of molybdenum, 0.03 to 0.2% of titanium, and more than 0.15 and not more than 1.2%. of vanadium, by mass, and the remainder of iron and impurities may be avoided and with a composition in which the amounts of carbon, titanium, molybdenum and vanadium are according to formula (I) under the conditions of surface finishing temperature of 880 °C or higher and coiling temperature of 570 °C or higher 0.8 (formula) (C/12) / { (Ti/48) + (Mo/96) + (V/51)} (formula) 1.5 (I) in which carbon, titanium, molybdenum and vanadium are specified as percentages by mass for each of them. 5. The method for producing high tensile steel plates according to claim 4. consists of a step of hot-dip galvanizing on the surface of the steel plate after hot rolling. ----------------------------- 1. แผ่นเหล็กเหนียวแรงดึงสูงที่ประกอบโดยจำเป็นด้วย โครงสร้างเฟสเดี่ยวเฟอร์ไรต์ ที่มี 980 MPa หรือที่มีความแข็งแรงเชิงดึงสูงกว่า ที่ซึ่งคาร์ไบด์มีไททาเนียม, โมลิบดินัม และวานาเดียม และ มีน้อยกว่า 10 nm ของขนาดอนุภาคเฉลี่ย ตกตะกอนในสภาวะกระจาย, และคาร์ไบด์ที่มีไททาเนียม, โมลิบดินัมและวานาเดียม มีองค์ประกอบเฉลี่ยที่เป็นตาม [V/ (Ti + Mo + V) มากกว่าหรือเท่ากับ 0.3] ซึ่ง ไททาเนียม, โมลิบดินัม และวานาเดียมถูกแสดงโดยเปอร์เซ็นต์อะตอม1. High-tensile strength steel plates are required to be composed of a single-phase ferrite structure with a tensile strength of 980 MPa or higher, in which titanium, molybdenum, and vanadium carbides with an average particle size of less than 10 nm are precipitated in a dispersed state, and titanium, molybdenum, and vanadium carbides have an average composition according to [V/(Ti + Mo + V) ≥ 0.3], where titanium, molybdenum, and vanadium are represented by atomic percentages. 2. แผ่นเหล็กเหนียวแรงดึงสูงตามข้อถือสิทธิข้อ 1. ที่ซึ่งองค์ประกอบเฉลี่ยของ คาร์ไบด์ เป็นตาม a = 0.6, ถึง 1.4, b = 0.6 ถึง 1.4, และ c = 1.4 ถึง 2.8, ใน ขณะที่ a + b + c = 4, ที่ซึ่ง a : b : c : เป็นอัตราส่วนอะตอมของไททาเนียม : โมลิบดินัม : วานาเดียม2. High-tensile strength steel plate according to claim 1, where the average composition of carbides is a = 0.6 to 1.4, b = 0.6 to 1.4, and c = 1.4 to 2.8, while a + b + c = 4, where a : b : c : is the atomic ratio of titanium : molybdenum : vanadium. 3. แผ่นเหล็กเหนียวแรงดึงสูงตามข้อถือสิทธิข้อ 1, ที่ประกอบด้วยมากกว่า 0.06% และไม่มากกว่า 0.24 % ของคาร์บอน, 0.3% หรือน้อยกว่าของซิลิคอน, 0.5 ถึง 2.0 % ของ แมงกานีส, 0.06% หรือน้อยกว่าของฟอสฟอรัส, 0.005% หรือน้อยกว่าของกำมะถัน, 0.06 % หรือ น้อยกว่าของอัลลูมิเนียม, 0.006 % หรือน้อยกว่าของไนโตรเจน, 0.05 ถึง 0.5 % ของโมลิบดินัม, 0.03 ถึง 0.2 % ของไททาเนียม, มากกว่า 0.15 และไม่มากกว่า 1.2 % ของวานาเดียม โดยมวล และส่วนที่เหลือที่เป็นเหล็กและสิ่งเจือปนที่ไม่อาจหลีกเลี่ยงได้ และมีองค์ประกอบที่ซึ่งปริมาณของ คาร์บอน, ไททาเนียม, โมลิบดินัม และวานาเดียม เป็นตามสูตร (I) 0.8 น้อยกว่าหรือเท่ากับ (C/12) / { (Ti/48) + (Mo/096) + (V/51) } มากกว่าหรือเท่ากับ 1.5 (I) ที่ซึ่ง คาร์บอน, ไททาเนียม, โมลิบดินัม และวานาเดียม ระบุเปอร์เซ็นต์โดยมวลสำหรับแต่ละตัวของ มัน3. High-tensile steel plates according to claim 1, containing more than 0.06% and not more than 0.24% carbon, 0.3% or less silicon, 0.5 to 2.0% manganese, 0.06% or less phosphorus, 0.005% or less sulfur, 0.06% or less aluminum, 0.006% or less nitrogen, 0.05 to 0.5% molybdenum, 0.03 to 0.2% titanium, more than 0.15 and not more than 1.2% vanadium by mass, and the remainder being iron and unavoidable impurities. And there is an element in which the amounts of carbon, titanium, molybdenum and vanadium are according to the formula (I) 0.8 less than or equal to (C/12) / { (Ti/48) + (Mo/096) + (V/51) } greater than or equal to 1.5 (I) where carbon, titanium, molybdenum and vanadium are specified as percentage by mass for each of them. 4. แผ่นเหล็กเหนียวแรงดึงสูงตามข้อถือสิทธิข้อ 2. ที่ประกอบด้วยมากกว่า 0.06% และไม่ มากกว่า 0.24% ของคาร์บอน, 0.3% หรือน้อยกว่าของซิลิคอน, 0.5 ถึง 2.0% ของแมงกานีส, 0.6% หรือน้อยกว่าของฟอสฟอรัส, 0.005% หรือน้อยกว่าของกำมะถัน, 0.06% หรือน้อยกว่าของ อัลลูมิเนียม, 0.06% หรือน้อยกว่าของไนโตรเจน, 0.05 ถึง 0.5% ของโมลิบดินัม, 0.03 ถึง 0.2% ของไททาเนียม, มากกว่า 0.15 และไม่มากกว่า 1.2% ของวานาเดียม โดยมวล และส่วนที่ เหลือที่เป็นเหล็กและสิ่งเจือปนที่ไม่อาจหลีกเลี่ยงได้ และมีองค์ประกอบที่ซึ่งปริมาณของคาร์บอน, ไททาเนียม, โมลิบดินัม และวานาเดียม เป็นตามสูตร (I) 0.8 น้อยกว่าหรือเท่ากับ (C/12) / { (Ti/48) + (Mo/096) + (V/51) } มากกว่าหรือเท่ากับ 1.5 (I) ที่ซึ่ง คาร์บอน, ไททาเนียม, โมลิบดินัม และวานาเดียม ระบุเปอร์เซ็นต์โดยมวลสำหรับแต่ละตัวของ มัน4. High-tensile steel plates according to claim 2. Containing more than 0.06% and not more than 0.24% of carbon, 0.3% or less of silicon, 0.5 to 2.0% of manganese, 0.6% or less of phosphorus, 0.005% or less of sulfur, 0.06% or less of aluminum, 0.06% or less of nitrogen, 0.05 to 0.5% of molybdenum, 0.03 to 0.2% of titanium, more than 0.15 and not more than 1.2% of vanadium by mass, with the remainder being iron and unavoidable impurities. And there is an element in which the amounts of carbon, titanium, molybdenum and vanadium are according to the formula (I) 0.8 less than or equal to (C/12) / { (Ti/48) + (Mo/096) + (V/51) } greater than or equal to 1.5 (I) where carbon, titanium, molybdenum and vanadium are specified as percentages by mass for each of them. 5. แผ่นเหล็กเหนียวแรงดึงสูงตามข้อหนึ่งข้อใดของข้อถือสิทธิข้อ 1. ถึง 4. ที่ซึ่งแผ่นเหล็ก เหนียวเป็นแผ่นเหล็กเหนียวรีดร้อนขนาดความหนาบาง (thin gauge hot-rolled steel sheet) ที่มีความหนาของแผ่นที่ 2.5 มม. หรือที่ที่น้อยกว่า5. High-tensile steel sheet according to any one of the claims 1 through 4, where the steel sheet is a thin gauge hot-rolled steel sheet with a thickness of 2.5 mm or less. 6. แผ่นเหล็กเหนียวแรงดึงสูงตามข้อหนึ่งข้อใดของข้อถือสิทธิข้อ 1. ถึง 4. ที่ซึ่งแผ่นเหล็ก เหนียวมีฟิล์มอาบสังกะสีแบบจุ่มร้อนอยู่บนนั้น6. A high-tensile steel plate as per any of Claims 1 through 4, on which the steel plate is coated with a hot-dip galvanized film. 7. วิธีการสำหรับผลิตแผ่นเหล็กเหนียวแรงดึงสูงที่มี 980 MPa หรือที่มีความแข็งแรงเชิงดึงที่ สูงกว่า ประกอบด้วยขั้นของการรีดร้อนและแผ่นพื้นเหล็กกล้า (steel slab) ที่ประกอบด้วยมากกว่า 0.06% และไม่มากกว่า 0.24% ของคาร์บอน, 0.3% หรือน้อยกว่าของซิลิคอน, 0.5 ถึง 2.0% ของแมงกานีส, 0.06% หรือน้อยกว่าของฟอสฟอรัส, 0.005% หรือน้อยกว่าของกำมะถัน, 0.06% หรือน้อยกว่าของอัลลูมิเนียม, 0.006% หรือน้อยกว่าของไนโตรเจน, 0.05 ถึง 0.5% ของโมลิบดินัม, 0.03 ถึง 0.2% ของไททาเนียม, มากกว่า 0.15 และไม่กว่ากว่า 1.2% ของวานาเดียม โดยมวล และส่วนที่เหลือที่เป็นเหล็กและสิ่งเจือปนที่ไม่อาจหลีกเลี่ยงได้ และมีองค์ประกอบที่ซึ่งปริมาณของ คาร์บอน, ไททาเนียม, โมลิบดินัม และวานาเดียม เป็นตามสูตร (I) ภายใต้เงื่อนไขของอุณหภูมิแต่งผิวที่ 880 ํC หรือที่สูงกว่า และที่อุณหภูมิการขดที่ 570 ํC หรือที่สูงกว่า 0.8 น้อยกว่าหรือเท่ากับ (C/12) / { (Ti/48) + (Mo/096) + (V/51) } มากกว่าหรือเท่ากับ 1.5 (I) ที่ซึ่ง คาร์บอน, ไททาเนียม, โมลิบดินัม และวานาเดียม ระบุเปอร์เซ็นต์โดยมวลสำหรับแต่ละตัวของ มัน7. The method for producing high-tensile steel plates with a tensile strength of 980 MPa or higher consists of hot rolling and steel slab steps containing more than 0.06% and not more than 0.24% carbon, 0.3% or less silicon, 0.5 to 2.0% manganese, 0.06% or less phosphorus, 0.005% or less sulfur, 0.06% or less aluminum, 0.006% or less nitrogen, 0.05 to 0.5% molybdenum, 0.03 to 0.2% titanium, more than 0.15 and not more than 1.2% vanadium by mass, with the remainder being unavoidable iron and impurities. and having a composition in which the amounts of carbon, titanium, molybdenum and vanadium are according to the formula (I) under the conditions of a surface treatment temperature of 880 °C or higher and a coiling temperature of 570 °C or higher 0.8 less than or equal to (C/12) / { (Ti/48) + (Mo/096) + (V/51) } greater than or equal to 1.5 (I) where carbon, titanium, molybdenum and vanadium are specified as percentage by mass for each of them. 8. วิธีการสำหรับผลิตแผ่นเหล็กเหนียวแรงดึงสูงตามข้อถือสิทธิข้อ 7. ยังประกอบด้วยขั้นของ การอาบสังกะสีแบบจุ่มร้อนลงบนผิวหน้าของแผ่นเหล็กเหนียวหลังจากการรีดร้อน8. The method for producing high-tensile steel sheets under claim 7 also includes the step of hot-dip galvanizing the surface of the steel sheet after hot rolling.
TH601003614A 2006-07-31 High-strength mild steel plates and methods for producing them. TH68705B (en)