TH62766B - High strength parts And a method for producing the same thing - Google Patents
High strength parts And a method for producing the same thingInfo
- Publication number
- TH62766B TH62766B TH501004317A TH0501004317A TH62766B TH 62766 B TH62766 B TH 62766B TH 501004317 A TH501004317 A TH 501004317A TH 0501004317 A TH0501004317 A TH 0501004317A TH 62766 B TH62766 B TH 62766B
- Authority
- TH
- Thailand
- Prior art keywords
- hydrogen
- drilling
- cutting
- machining
- reduced
- Prior art date
Abstract
DC60 (26/07/54) ชิ้นส่วนที่มีความแข็งแรงสูง และวิธีการสำหรับการผลิตสิ่งนี้สามารถถูกจัดเตรียมซึ่งชิ้นส่วน นั้นแสดงความต้านทานและความแข็งแรงต่อความเปราะจากไฮโดรเจนหลังจากการขึ้นรูปที่อุณหภูมิ สูง ตัวอย่างเช่น บรรยากาศในเตาเผาที่ให้ความร้อนสามารถมีไฮโดรเจนน้อยกว่าประมาณ 10% และ/ หรือ มีจุดน้ำค้างประมาณ 30องศาเซลเซียส หรือ น้อยกว่า ปริมาณของไฮโดรเจนที่แทรกซึมแผ่นเหล็กกล้าใน ระหว่างการให้ความร้อนสามารถถูกลดลงด้วยวิธีนั้น หลังจากการขึ้นรูป การทำให้แข็งที่ทำให้เย็นลง อย่างรวดเร็วในชุดประกอบแม่แบบ และการทำให้เป็นรูปร่างภายหลังสามารถถูกดำเนินการ การทำ ให้เป็นรูปร่างภายหลังสามารถรวมถึงการตัดเฉือนที่ตามมาด้วยการขึ้นรูปด้วยการตัดเฉือนซ้ำ หรือ การอัด; การเจาะด้วยใบมีดตัดที่มีความกว้างฐานที่ลดลงอย่างต่อเนื่อง; การเจาะด้วยเครื่องมือที่มีใบมีด โค้ง และส่วนที่ยื่นออกมาที่ปลายของใบมีดตัด, ซึ่งใบมีดโค้งอาจรวมถึงส่วนบ่าที่มีรัศมี และ/หรือ มุม ที่กำหนดไว้; การตัดหลอมรวม เป็นต้น ความเค้นที่เหลืออยู่ของแรงดึงหลังจากการเจาะสามารถถูก ลดลง และความต้านทานต่อความเปราะจากไฮโดรเจนสามารถถูกปรับปรุง ชิ้นส่วนที่มีความแข็งแรงสูงและวิธีการสำหรับการผลิตสิ่งเหล่านี้สามารถถูกจัดเตรียมซึ่งชิ้นส่วนนั้นแสดงความต้านทานและความแข็งแรงต่อความเปราะจากไฮโดรเจนหลังจากการขึ้นรูปที่อุณหภูมิสูงตัวอย่างเช่นบรรยายกาศในเตาเผาที่ให้ความร้อนสามารถมีไฮโดรเจนน้อยกว่าประมาณ10%และ/หรือมีจุดน้ำค้างประมาณ30ํ ซ หรือน้อยกว่าปริมาณของไฮโดรเจนที่แทรกซึมแผ่นเหล้กกล้าในระหว่างการให้ความร้อนสามารถถูกลดลงด้วยวิธีนั้นหลังจากการขึ้นรูปการทำให้แข็งที่ทำให้เย็นลงอย่างรวดเร็วในชุดประกอบแม่แบบและการทำให้เป็นรูปร่างภายหลังสามารถถูกดำเนินการการทำให้เป็นรูปร่างภายหลังสามารถรวมถึงการตัดเฉือนที่ตามมาด้วยการขึ้นรูปด้วยการตัดเฉลือนซ้ำหรือการอัด;การเจาะด้วยใบมีดตัดที่มีความกว้างฐานที่ลดลงอย่างต่อเนื่อง;การเจาะด้วยเครื่องมือที่มีใบมีดโค้งและส่วนที่ยื่นออกมาที่ปลายของใบมีดตัด,ซึ่งใบมีดโค้งอาจรวมถึงส่วนบ่าที่มีรัศมีและ/หรือมุมที่กำหนดไว้;การตัดหลอมรวมเป็นต้นความเค้นที่เหลืออยู่ของแรงดึงหลังจากการเจาะสามารถถูกลดลงและความต้านทานต่อความเปราะจากไฮโดรเจนสามารถถูกปรับปรุง DC60 (26/07/54), high strength parts. And a method for manufacturing this can be provided in which parts For example, an atmosphere in a heated furnace can contain approximately 10% less hydrogen and / or a dew point of approx. 30 ° C or less, the amount of hydrogen penetrating the steel plate in During heating can be reduced that way. After forming Hardening that cools A quick glance at the template assembly. And subsequent shaping can be performed.Subsequent shaping can include machining that is followed by re-machining or compression molding; Drilling with cutting blades with a continuously reduced base width; Drilling with tools with curved blades and protrusions at the end of the cutting blade, where the curved blade may include a shoulder with a defined radius and / or angle; Cutting fused, etc. The residual tensile stresses after drilling can be reduced and the resistance to hydrogen brittleness can be improved. High-strength parts and methods for their manufacture can be provided in which parts show resistance and strength to hydrogen-induced brittleness after high temperature molding. In a heated furnace, there can be approximately 10% less hydrogen and / or about 30 ํ or less dew point, the amount of hydrogen that penetrates the plates during heating can be reduced that way. After machining, the rapid cooling hardening in the template assembly and subsequent shaping can be performed.Subsequent shaping can include machining that is followed by shearing. Repetitive cutting or compression; drilling with cutting blades with a continuously reduced base width; tool drilling with curved blades and protrusions at the tip of the cutting blade. , In which a curved blade may include a shoulder with a predetermined radius and / or angle; fused cut, etc.The residual tensile stresses after drilling can be reduced and the resistance to brittleness from hydrogen can Updated
Claims (1)