TH43009A3 - How to roll a pan for steel plates And pushrod rolling machines - Google Patents

Abstract

DC60 This invention provides a temper rolling method for temper rolling a steel plate to improve the brightness of the steel plate. Without increasing equipment and production requirements, the method used steel plates containing 0.012 wt% or less of carbon (C) and a temper rolling mill, where at least Roller on side stand The top face is a scratch bright roll with a surface roughness (Ra) of 1.2 microns or less, and at least the last stand roller. It is a bright roll with a surface roughness (Ra) of 0.5 microns or less.This invention provides a temper rolling method for temper rolling, steel plates. plate) to improve the brightness of the steel plate. Without increasing equipment and production requirements, the method used steel plates containing 0.012 wt% or less of carbon (C) and a temper rolling mill, where at least Roller on side stand The top page is a scratch bright roll with a surface roughness (Ra) of 1.2 um or less and at least the last location roller. It is a bright roll with a surface roughness (Ra) of 0.5 um or less.

Claims (9)

1. How to roll a pushrod (temper rolling method) for rolling a steel plate. I used a temper rolling mill that was held with the number Much of the roll stands, where at least the rollers on the top front stand, are A scratch bright roll with a surface roughness (Ra) of 1.2 um or less, and at least the last roller on the stand. It is a polished roller with a surface roughness (Ra) of 0.5 um or less, in such a way that the pan roll is dry rolling and in the way that the steel plate contains 0.012 wt% or less of carbon (C). 2. Temper rolling method according to the claim clause 1. Where the rolling machine presses The method of rolling a temper rolling mill is a two stand mill. 3. temper rolling method according to the claim clause 1. or 2. Where the steel plate contains from 0.001 to 0.008 wt% of carbon 4. temper rolling method according to the claim clause 1., 2. or 3. Where the sheet steel is increased from 0.005 to 0.2 wt% of titanium (Ti) and / or from 0.002 to 0.1 Wt% of biobium (Nb). 5. temper rolling method according to one of the above claims Where the steel plate has an increase of not more than 0.15 wt% of aluminum (Al), not more than 0.2 wt% of silicon (Si), 0.1 to 0.5 wt% of manganese (Mn), not more than 0.05 wt%. Of phosphorus (P), and not more than 0.03 wt% of sulfur (S). 6. A temper rolling mill for steel plates with Lots of roller stand Where at least the rollers on the top front stand It is a scratch bright roll with a surface roughness (Ra) of 1.2 um or less, in such a way that at the very least the last stand roller. It is a bright roll with a surface roughness (Ra) between 0.15 and 0.3 um. 7. A rolling mill (temper rolling mill) according to the claim. 6. Two stand mill type rolling machine 8. A rolling mill (temper rolling mill) according to the claim 6. or 7.Where the front stand's scratch bright roll has a minimum surface roughness of 0.20 um. 9. A rolling mill (temper rolling mill) according to the claim. 8.Where the scratch bright roll of the front stand has a surface thickness of 0.5 to 1.0 um 1. 0. What are the rights of a temper rolling mill? One of Clause 5 to 9. Where the last stand's mirror bright roll is a mirror bright roll or a scratch bright roll.