TH23873Y - Film sheets containing basil seed mucilage extract and the manufacturing process of such films. - Google Patents

Abstract

------10/01/2022------(OCR) A film containing basil seed mucilage extract and its manufacturing process involves the following ingredients: Hydroxypropyl methyl cellulose, Carbomer, basil seed mucilage extract, Propylene glycol or Glycerin, and Simethicone. The manufacturing process of the film containing basil seed mucilage extract begins by adding Hydroxypropyl methyl cellulose, Carbomer, and basil seed mucilage extract to water. All ingredients are then mixed thoroughly. At room temperature, add propylene glycol or glycerin and simethicone, then place the mixture at 20-30°C. Afterward, bake at 40-70°C. The study found that the basil seed mucilage extract has the ability to be used as a mucilage binder in films. The maximum force required to detach the film containing basil seed mucilage extract from the mucous membrane was 0.78 Newtons, and it remained adhering to the mucous membrane for more than 7 hours. The film containing basil seed mucilage extract and its manufacturing process consists of hydroxypropyl methyl cellulose, carbomer, basil seed mucilage extract, propylene glycol, and simethicone. The manufacturing process involves adding hydroxypropyl methyl cellulose, carbomer, and basil seed mucilage extract to water, then mixing all ingredients thoroughly at room temperature. Propylene glycol and simethicone were then added to the mixture, and the mixture was left to stand at 20-30°C. It was then baked at 40-70°C. The study results showed that the basil seed mucilage extract has the ability to be used as an adhesive for mucilage films. The maximum force required to detach the film containing the basil seed mucilage extract from the mucilage was 0.78 Newtons, and it remained adhering to the mucilage for more than 7 hours.

Claims (3)

------10/01/2022------(OCR) 1. Film containing basil seed mucilage extract, composed of: Hydroxypropyl methyl cellulose 20.00 - 40.00% by mass; Carbomer 10.00 - 20.00% by mass; Basil seed mucilage extract 5.00 - 20.00% by mass; Propylene glycol or Glycerin 20.00 - 40.00% by mass; Simethicone 1.00 - 1.50% by mass. 2. Manufacturing process of film containing basil seed mucilage extract. According to Claim 1, the following procedure is followed: a. Add hydroxypropyl methyl cellulose, carbomer, and chia seed mucilage extract to water. b. Mix all ingredients from step a together at room temperature for 5-15 minutes. c. Add propylene glycol or glycerin and simethicone to the mixture from step b and leave the mixture at 20-30°C for 8-24 hours. d. Then pour the mixture from step c into molds and bake the molds at 40-70°C for 36-48 hours. ------------ Claim 1. Films containing basil seed mucilage extract consisted of: Hydroxypropyl methyl cellulose 20.00 - 40.00% by mass, Carbomer 10.00 - 20.00% by mass, Basil seed mucilage extract 5.00 - 20.00% by mass, Propylene glycol 20.00 - 40.00% by mass, and Simethicone 1.00 - 1.50% by mass. 2. A film containing mucilage extract from basil seeds, as per claim 1, where propylene glycol can be replaced by glycerin. 3. The process for producing films containing mucilage extract from basil seeds, as per claim 1 or 2, involves the following steps: a. Add hydroxypropyl methyl cellulose, carbomer, and mucilage extract to water. b. Mix all ingredients from step a together at room temperature for 5-15 minutes. c. Add propylene glycol and simethicone to the mixture from step b and leave the mixture at 20-30°C for 8-24 hours. d. Pour the mixture from step c into a mold and bake the mold at 40-70°C for 36-48 hours.