TH183510B - Steel plates, hot dip galvanized steel plates, galvanized steel plates, and manufacturing methods for that. - Google Patents
Steel plates, hot dip galvanized steel plates, galvanized steel plates, and manufacturing methods for that.Info
- Publication number
- TH183510B TH183510B TH1801000189A TH1801000189A TH183510B TH 183510 B TH183510 B TH 183510B TH 1801000189 A TH1801000189 A TH 1801000189A TH 1801000189 A TH1801000189 A TH 1801000189A TH 183510 B TH183510 B TH 183510B
- Authority
- TH
- Thailand
- Prior art keywords
- less
- volume ratio
- thickness
- steel plates
- martensite
- Prior art date
Abstract
------20/03/2561------(OCR) หน้า 1 ของจำนวน 1 หน้า บทสรุปการประติษ^ แผ่นเหล็กกล้า (steel sheet) ตามลักษณะของการประดิษฐ์บัจชุบันมีองค์ประกอบทางเคมี ที่ถูกกำหนดไว้ล่วงหน้า ชํ่งโครงสร้างที่ส่วน 1/4 ของความหนาในแง่ของอัตราส่วนปริมาตร ประกอบด้วยเทมเปอร์มาร์เทนไชต์ 70% หรือมากกว่า และหนํ่งหรือทั้งสองชนิดของเพ่อร์ไรด์ และไบไนต์: โดยรวมน้อยกว่า 20%, ในโครงสร้างที่ส่วน 1/4 ของความหนา, อัตราส่วนปริมาตร ของออสเทไนต์เหลือค้างน้อยกว่า 10%, อัตราส่วนปริมาตรของมาร้เทนไซด์ใหม่เป็น 10% หรือน้อยกว่า, อัตราส่วนปริมาตรของเพิร์ลไลด์เป็น 10% หรือน้อยกว่าและอัตราส่วนปริมาตร ทั้งหมดของออสเทไนด์เหลือค้าง, มาร์เทนไซด์'ใหม่และเพิร้ลไลด์เป็น 15% หรือน้อยกว่า, ความหนาแน่นโดยจำนวนของคาร์ไบด์ชนิดไอร์ออนที่มีแกนหลัก 5 นาโนเมตรหรือมากกว่าใน เทมเปอร์มาร์เทนไซด์ที่ส่วน 1/4 ของความหนาเป็น 5xl07 อนุภาค/ตารางมิลลิเมตรหรือมากกว่า, อัตราส่วนของจำนวนของคาร์ไบด์ชนิค-ธ ในจำนวนของคาร์ไบด์ชนิดไอร้ออนที่มีแกนหลัก 5 นาโนเมตรหรือมากกว่าที่ส่วน 1/4 ของความหนาเป็น 20% หรือมากกว่าและความทนแรงดึงเป็น 780 เมกะพาสคาลหรือสูงกว่า ------------ หน้า 1 ของจำนวน 1 หน้า บทสรุปการประดิษฐ์ แผ่นเหล็กกล้า (steel sheet) ตามลักษณะของการประดิษฐ์ปัจจุบันมีองค์ประกอบทางเคมี ที่ถูกกำหนดไว้ล่วงหน้า ในที่ซึ่งโครงสร้างที่ส่วน 1/4 ของความหนาในแง่ของอัตราส่วนปริมาตร ประกอบด้วยเทมเปอร์มาร์เทนไซต์: 70% หรือมากกว่า และหนึ่งหรือทั้งสองชนิดของเฟอร์ไรต์ และไบไนต์: โดยรวมน้อยกว่า 20%, ในโครงสร้างที่ส่วน 1/4 ของความหนา, อัตราส่วนปริมาตร ของออสเทไนค์เหลือค้างน้อยกว่า 10%, อัตราส่วนปริมาตรของมาร์เทนไซต์ใหม่เป็น 10% หรือ น้อยกว่า, อัตราส่วนปริมาตรของเพิร์ลไลต์เป็น 10% หรือน้อยกว่าและอัตราส่วนปริมาตรทั้งหมด ของออสเทไนต์เหลือค้าง, มาร์เทนไซต์ใหม่และเพิร์ลไลต์เป็น 15% หรือน้อยกว่า, ความหนาแน่น โดยจำนวนของคาร์ไบด์ชนิดไอร์ออนที่มีแกนหลัก 5 นาโนเมตรหรือมากกว่าในเทมเปอร์มาร์เทน ไซต์ที่ส่วน 1/4 ของความหนาเป็น 5X107 อนุภาค/ตารางมิลลิเมตรหรือมากกว่า, อัตราส่วนของ จำนวนของคาร์ไบด์ชนิด-สูตร ในจำนวนของคาร์ไบด์ชนิดไอร์ออนที่มีแกนหลัก 5 นาโนเมตรหรือ มากกว่าที่ส่วน 1/4ของความหนาเป็น20%หรือมากกว่าและความทนแรงดึงเป็น 780 เมกะ พาสคาลหรือสูงกว่า : ------ 20/03/2018 ------ (OCR) page 1 of the number 1 page Summary of sculptures ^ Steel sheet according to the nature of the fabrication. chemical That was predetermined The structure is 1/4 part of the thickness in terms of volume ratio. Contains 70% or more martensite tempers and one or both types of peridot and binaite: less than 20% overall, in a structure at 1/4 part thickness, Volume ratio The residual austenite is less than 10%, the volume ratio of the new martenside is 10% or less, the volume ratio of the pearllide is 10% or less, and the volume ratio is 10% or less. Total residual austenides, new 'martensides' and perlides are 15% or less, density by number of ionic carbides with a core of 5. Nm or more in The martenside at 1/4 part of the thickness is 5xl07 particles / mm2 or more, the ratio of the number of schnick-th carbides. In the number of ionic carbides with a core of 5 nm or more at 1/4 part of the thickness is 20% or more and the tensile strength is 780 Mpa or more - ---------- Page 1 of number 1 page Summary of Invention Steel sheet (steel sheet) according to the nature of the present invention has a chemical composition. That was predetermined Where the structure is 1/4 part of the thickness in terms of volume ratio. Contains tempers, martensite: 70% or more, and one or both types of ferrites and binites: less than 20% overall, in a structure at 1/4 part of the thickness, volume ratio. The residual austenite is less than 10%, the volume ratio of the new martensite is 10% or less, the volume of the pearlite is 10% or less, and the total volume ratio. Of residual austenite, new martensite and pearlite are 15% or less, density by number of ionic carbides with a 5nm core, or Than in the tempera martensite, where 1/4 part of the thickness is 5X107 particles / square millimeter or more, the ratio of the number of formula-type carbides In the number of ionic carbides having a core of 5 nm or more at the 1/4 of the thickness is 20% or more and the tensile strength is 780 Mpa or higher:
Claims (1)