TH171447B - Production of polyethylene products with improved stability, toughness and formability - Google Patents
Production of polyethylene products with improved stability, toughness and formabilityInfo
- Publication number
- TH171447B TH171447B TH1601004580A TH1601004580A TH171447B TH 171447 B TH171447 B TH 171447B TH 1601004580 A TH1601004580 A TH 1601004580A TH 1601004580 A TH1601004580 A TH 1601004580A TH 171447 B TH171447 B TH 171447B
- Authority
- TH
- Thailand
- Prior art keywords
- polymer
- tref
- curve
- average
- ratio
- Prior art date
Abstract
แก้ไข 7/10/2559 พอลิเมอร์และระบบและวิธีการผลิตและใช้สิ่งเดียวกันนี้ได้รับการอธิบายเอาไว้ในคำขอนี้ พอ ลิเมอร์รวมถึงเอทิลีน และอัลฟ่า โอเลฟินหนึ่งตัวเป็นอย่างน้อยที่มีคาร์บอนอะตอมตังแต่ 4 ถึง 20 อะตอมพอลิเมอร์มีอัตราส่วนของดัชนีการหลอม (MIR) มากกว่าประมาณ 40 พอลิเมอร์ยังคงมีค่า สำหรับ Mw1/Mw2 ประมาณ 2.0 เป็นอย่างน้อยที่ซึ่ง Mw1/Mw2 คืออัตราส่วนของนํ้าหนักโมเลกุล เฉลี่ยโดยนํ้าหนัก(Mw) สำหรับครึ่งแรกของกราฟการชะที่อุณหภูมิสูงขึ้น (TREF)จากการวิเคราะห์ การแยกลำดับส่วนแบบขวาง (CFC) ต่อ Mw สำหรับครึ่งที่สองของกราฟ TREF พอลิเมอร์ยังคงมีค่า สำหรับ Tw1 - Tw2 น้อยกว่าประมาณ -15 องศาเซลเซียส ที่ซึ่ง Tw1 - Tw2 คือความแตกต่างของ อุณหภูมิในการชะเฉลี่ยโดยนํ้าหนัก (Tw) สำหรับครึ่งแรกของกราฟ TREF กับ Tw สำหรับครึ่งที่สอง ของกราฟ TREF --------------------- พอลิเมอร์และระบบและวิธีการผลิตและใช้สิ่งเดียวกันนี้ได้รับการอธิบายเอาไว้ในคำขอนี้ พอ ลิเมอร์รวมถึงเอทิลีน และอัลฟ่า โอเลฟินหนึ่งตัวเป็นอย่างน้อยที่มีคาร์บอนอะตอมตั้งแต่ 4 ถึง 20 อะตอมพอลิเมอร์มีอัตราส่วนของดัชนีการหลอม (MIR) มากกว่าประมาณ 40 พอลิเมอร์ยังคงมีค่า สำหรับ Mw1/Mw2 ประมาณ 2.0 เป็นอย่างนร้อยที่ซึ่ง Mw1/Mw2 คืออัตราส่วนของน้ำหนักโมเลกุล เฉลี่ยโดยน้ำหนัก(Mw) สำหรับครึ่งแรกของกราฟการชะอุณหภูมิสูงขึ้น (TREF)จากการวิเคราะห์ การแยกลำดับส่วนแบบขวาง (CFC) ต่อ Mw สำหรับครึ่งที่สองของกราฟ TREF พอลิเมอร์ยังคงมีค่า สำหรับ Tw1 - Tw2 น้อยกว่าประมาณ -15 องศาเซลเซียส ที่ซึ่ง Tw1 -Tw2 คือความแตกต่างของ อุณหภูมิในการชะเฉลี่ยโดย (Tw) สำหรับครึ่งแรกของกราฟ TREF กับ Tw สำหรับครึ่งที่สอง ของกราฟ TREF Edit 7/10/2016 The same polymers and systems and methods for their manufacture and use have been described in this request. The polymer includes ethylene and alpha olefins. One is at least 4 to 20 carbon atoms, the polymer has a ratio of about 40 more melting index (MIR) than the polymer, still at least about 2.0 for Mw1 / Mw2. Where Mw1 / Mw2 is the ratio of molecular weight. Average by weight (Mw) for the first half of the elution curve at higher temperatures. (TREF) from analysis The cross-sequence separation (CFC) per Mw for the second half of the polymer TREF curve remains approximately -15 ° C less for Tw1 - Tw2, where Tw1 - Tw2 is the difference of Average wt (Tw) elution temperature for the first half of the TREF versus Tw curve for the second half of the TREF curves --------------------- polymer. The same systems and methods for producing and using are described in this request.Polymers, including ethylene and one alpha olefin, have at least one carbon atom. From 4 to 20 atoms, the polymer had a melting index ratio (MIR) approximately 40 more than the polymer, still hundreds of thousands of values for Mw1 / Mw2, where Mw1 / Mw2 is the weight ratio. Molecules Average by weight (Mw) for the first half of the elevated temperature elution curve. (TREF) from analysis The cross-sectional sequence (CFC) per Mw for the second half of the polymer TREF curve remained about -15 ° C less for Tw1 - Tw2, where Tw1 -Tw2 was the difference of Average elution temperature by (Tw) for the first half of the TREF and Tw for the second half of the TREF curve.
Publications (2)
| Publication Number | Publication Date |
|---|---|
| TH171447B true TH171447B (en) | 2017-12-14 |
| TH171447A TH171447A (en) | 2017-12-14 |
Family
ID=
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| PH12016501561A1 (en) | Producing polyethylene products with improved stiffness, toughness, and processability | |
| CL2019002997A1 (en) | Means to increase the molecular weight and decrease the density of ethylene interpolymers using homogeneous catalyst formulations. | |
| AR111477A1 (en) | MEANS TO INCREASE THE MOLECULAR WEIGHT AND REDUCE THE DENSITY OF THE ETHYLENE INTERPOLYMERS THROUGH THE USE OF FORMULATIONS OF HOMOGENEOUS AND HETEROGENIC CATALYSTS | |
| MY181088A (en) | Polyethylene for pipes | |
| BR112016029364A2 (en) | ethylene-based polymer composition for improved strength films | |
| EA033278B1 (en) | METHOD FOR PRODUCING SOLID MgClSUPPORTED CATALYST COMPONENT | |
| BR112016029439A2 (en) | olefin polymerization process | |
| MA41339B1 (en) | Expandable aromatic vinyl polymer pellets and expanded vinyl aromatic polymer foam comprising geopolymer composites and their use | |
| MX2016008041A (en) | Catalyst system for polymerisation of an olefin. | |
| EA201691283A1 (en) | CATALYTIC SYSTEM FOR POLYMERIZATION OF OLEFIN | |
| WO2015105738A3 (en) | Chromium (iii) catalyst systems with activator-supports | |
| SA519402232B1 (en) | Process for Preparing Polypropylene Composition | |
| EA201691268A1 (en) | CATALYTIC SYSTEM FOR OLEFIN POLYMERIZATION | |
| BR112017008723A2 (en) | propylene homopolymer or copolymer, polypropylene composition, article, processes for producing a propylene homopolymer or copolymer and for producing a polypropylene composition, melt transformation process for producing an article, and, use of the homopolymer and / or copolymer of propylene. | |
| WO2016053594A8 (en) | Process for preparing a brominated elastomer with improved mooney viscosity stability | |
| BR112015024284A2 (en) | PROCESS FOR THE POLYMERIZATION OF PROPYLENE IN THE PRESENCE OF A POLYMERIZATION CATALYST AND PROCESS FOR THE PRODUCTION OF TUBES | |
| MX2017006396A (en) | Polyethylene composition having high stress cracking resistance. | |
| BR112016002597A2 (en) | method for producing an ethylene-based polymer in a polymerization process using a self-limiting agent | |
| JP2016504446A5 (en) | ||
| TH171447B (en) | Production of polyethylene products with improved stability, toughness and formability | |
| BR112016013022A2 (en) | PROCESS FOR PREPARING A SECOND PROPYLENE-BASED POLYMER FROM A FIRST PROPYLENE-BASED POLYMER | |
| TH171447A (en) | ||
| Kemalov | Developments of additives the depressor dispersing structures to oil fuels | |
| TH171224B (en) | Polyethylene composition with flexibility and high temperature resistance. Suitable for application to pipes | |
| EA035521B9 (en) | Barrier layers |