TH164738A - Formulation used to produce 100% Geopolymer from waste material. - Google Patents
Formulation used to produce 100% Geopolymer from waste material.Info
- Publication number
- TH164738A TH164738A TH1601005370A TH1601005370A TH164738A TH 164738 A TH164738 A TH 164738A TH 1601005370 A TH1601005370 A TH 1601005370A TH 1601005370 A TH1601005370 A TH 1601005370A TH 164738 A TH164738 A TH 164738A
- Authority
- TH
- Thailand
- Prior art keywords
- waste
- geopolymer
- weight
- materials
- total mixture
- Prior art date
Abstract
วัสดุจีโอโพลิเมอร์จากวัสดุเหลือทิ้ง 100% ตามการประดิษฐ์นี้ ประกอบด้วย เถ้าหนักจาก โรงไฟฟ้าแม่เมาะที่ 65 - 75 เปอร์เซ็นต์โดยน้ำหนักของส่วนผสมทั้งหมด สารละลายด่างที่เป็นของเสีย จากกระบวนการกัดผิวโลหะอลูมิเนียม 15 - 35 เปอร์เซ็นต์โดยน้ำหนักของส่วนผสมทั้งหมด และ/ หรือสารละลายด่างที่ได้จากการต้มเถ้าแกลบในสารละลายด่างที่เป็นของเสียจากกระบวนการกัดผิว อลูมิเนียม 0 - 15 เปอร์เซ็นต์โดยน้ำหนักของส่วนผสมทั้งหมด ชิ้นงานจีโอโพลิเมอร์ที่สังเคราะห์ได้มี คุณสมบัติหลังบ่มชิ้นงานไว้เป็นเวลา 28 วันดังนี้ ค่าความแข็งแรงต่อแรงกด (Compressive sterngth) อยู่ระหว่าง 15.83-28.91 เมกะปาสคาล ค่าความหนาแน่น (Bulk density) อยู่ระหว่าง 1.50 - 1.77 กรัมต่อลูกบาศก์เซนติเมตร และค่าการดูดซึมน้ำ (Water absorption) อยู่ระหว่างร้อยละ 17.23 - 24.66 วัสดุจีโอโพลิเมอร์จากวัสดุเหลือทิ้ง 100% นี้มีความแข็งแรงมากเพียงพอ ที่จะนำไปประยุกต์ใช้เป็น วัสดุก่อสร้างจำพวกอิฐหรือกระเบื้องตกแต่ง ทดแทนวัสดุจำพวกซีเมนต์ คอนกรีต หรือเซรามิก นับเป็นการลดการใช้ทรัพยากรธรรมชาติและพลังงานในกระบวนการผลิต และเป็นการเพิ่มมูลค่าของ วัสดุเหลือทิ้งต่างๆ จากภาคอุตสาหกรรมให้นำกลับมาใช้ประโยชน์ได้สูงสุดอีกด้วย The 100% waste geopolymer under the invention contains the heavy ash from the Mae Moh power plant at 65–75% by weight of the total mixture. Waste alkaline solution From the surface milling of 15 - 35% aluminum by weight of the total mixture and / or the alkali solution obtained by boiling rice husk ash in the alkaline solution of 0 - 15% aluminum surface waste. Weight of all ingredients Synthetic geopolymer specimens have Properties after aging for 28 days are as follows: Compressive sterngth is between 15.83-28.91 MPa, bulk density is between 1.50 - 1.77 g / cm3. And the water absorption value is between 17.23% - 24.66%. This 100% geopolymer from this waste material is strong enough. To be applied as Building materials such as bricks or decorative tiles Substituting materials such as cement, concrete or ceramic, reducing the use of natural resources and energy in the production process. And increasing the value of Various waste materials From the industry to bring it back to its maximum benefit as well
Claims (2)