TH12426U - Self-curing dental implant base materials and manufacturing processes. - Google Patents

Self-curing dental implant base materials and manufacturing processes.

Info

Publication number
TH12426U
TH12426U TH1503001256U TH1503001256U TH12426U TH 12426 U TH12426 U TH 12426U TH 1503001256 U TH1503001256 U TH 1503001256U TH 1503001256 U TH1503001256 U TH 1503001256U TH 12426 U TH12426 U TH 12426U
Authority
TH
Thailand
Prior art keywords
powder
self
curing
liquid
base material
Prior art date
Application number
TH1503001256U
Other languages
Thai (th)
Other versions
TH12426A3 (en
TH12426C3 (en
TH12426Y (en
Inventor
เอกวรพจน์ นางปิยะนารถ
เอี่ยมจิรกุล นางสาวณปภา
Original Assignee
มหาวิทยาลัยศรีนครินทรวิโรฒ
Filing date
Publication date
Application filed by มหาวิทยาลัยศรีนครินทรวิโรฒ filed Critical มหาวิทยาลัยศรีนครินทรวิโรฒ
Publication of TH12426A3 publication Critical patent/TH12426A3/en
Publication of TH12426C3 publication Critical patent/TH12426C3/en
Publication of TH12426Y publication Critical patent/TH12426Y/en
Publication of TH12426U publication Critical patent/TH12426U/en

Abstract

แก้ไข 21/9/2559 การประดิษฐ์นี้เกี่ยวข้องกับวัสดุสำหรับทำฐานฟันเทียมชนิดบ่มด้วยตัวเองที่มีคุณสมบัติต่อต้าน เชื้อ ประกอบด้วย ผงอะคริลิกเรซิน ซิลเวอร์นาโนประเภทสารประกอบซิลเวอร์ซีโอไลต์ และส่วนเหลว ของโมโนเมอร์เมทราครัยเลตและ เทอร์เทียรี่ เอมีน มีขั้นตอนการผลิตโดยเติมสารต่อต้านเชื้อจุลินทรีย์ ในส่วนประกอบส่วนผงผสมกับส่วนเหลว ที่อุณหภูมิห้อง ก่อนนำไปซ่อมฐานฟันเทียมที่หลวมให้ผู้ป่วย ใส่ได้ทันที ซึ่งสะดวกรวดเร็ว ทำง่าย ใช้ระยะเวลาสั้น ทำเสร็จภายในชั่วโมงและมีคุณสมบัติต่อต้านเชื้อ อีกด้วย ---------------------------------------------- แก้ไข บทสรุป 07/01/2559 การประดิษฐ์นี้เกี่ยวข้องกับวัสดุสำหรับทำฐานฟันเทียมชนิดบ่มด้วยตัวเองที่มีคุณสมบัติต่อต้าน เชื้อ ประกอบด้วย ผงอะคริลิกเรซิน ซิลเวอร์นาโนประเภทสารประกอบซิลเวอร์ซีโอไลต์ และส่วนเหลว ของโมโนเมอร์เมทราครัยเลตและ เทอร์เทียรี่ เอมีน มีขั้นตอนการผลิตโดยเติมสารต่อต้านเชื้อจุลินทรีย์ ในส่วนประกอบส่วนผงผสมกับส่วนเหลว ที่อุณหภูมิห้อง ก่อนนำไปซ่อมฐานฟันเทียมที่หลวมให้ผู้ป่วย ใส่ได้ทันที ซึ่งสะดวกรวดเร็ว ทำง่าย ใช้ระยะเวลาสั้น ทำเสร็จภายในชั่วโมงและมีคุณสมบัติต่อต้านเชื้อ อีกด้วย --------------------------------------------- คำขอใหม่ปรับปรุง การประดิษฐ์นี้เกี่ยวข้องกับวัสดุสำหรับทำฐานฟันเทียมชนิดบ่มด้วยตัวเองที่มีคุณสมบัติต่อต้าน เชื้อ ประกอบด้วย ผงอะคริลิกเรซิน ซิลเวอร์นาโนประเภทสารประกอบซิลเวอร์ซีโอไลต์ และส่วนเหลว ของโมโนเมอร์เมทราครัยเลดและ เทอร์เทียรี่ เอมีน มีขั้นตอนการผลิตโดยเติมสารต่อต้านเชื้อจุลินทรีย์ ในส่วนประกอบส่วนผงผสมกับส่วนเหลว ที่อุณหภูมิห้อง ก่อนนำไปซ่อมฐานฟันเทียมที่หลวมให้ผู้ป่วย ใส่ได้ทันที ซึ่งสะดวกรวดเร็ว ทำง่าย ใช้ระยะเวลาสั้น ทำเสร็จภายในชั่วโมงและมีคุณสมบัติต่อต้านเชื้อ อีกด้วยRevised 21/09/2016. This invention relates to a self-curing, antimicrobial denture base material. It consists of acrylic resin powder, silver nanoparticles (silver zeolite compound), and a liquid phase of methacrylate and tertiary amine monomers. The manufacturing process involves adding an antimicrobial agent to the powder and liquid components at room temperature. The resulting material can then be used to repair loose denture bases, allowing for immediate insertion. This process is convenient, quick, easy, and takes less than an hour to complete. Furthermore, it possesses antimicrobial properties. ---------------------------------------------- Revised Summary 07/01/2016. This invention relates to a self-curing, antimicrobial denture base material. It consists of acrylic resin powder, silver nanoparticles (silver zeolite compound), and a liquid phase of methacrylate and tertiary amine monomers. The manufacturing process involves adding an antimicrobial agent to the powder and liquid components at room temperature. The resulting material can then be used to repair loose denture bases, allowing for immediate insertion. This process is convenient, quick, easy, and takes less than an hour to complete. Furthermore, it possesses antimicrobial properties. --------------------------------------------- New Request (Revised) This invention relates to a self-curing, antimicrobial denture base material. It comprises acrylic resin powder, silver nanoparticles (silver zeolite compounds), and a liquid phase of methacrylate and tertiary amine monomers. The manufacturing process involves adding antimicrobial agents to the powder and liquid components at room temperature. The resulting material can then be used to repair loose dentures, allowing for immediate and convenient replacement, requiring less than an hour for completion, and possessing antimicrobial properties.

Claims (3)

แก้ไข 21/9/2559 1. วัสดุฐานฟันเทียมชนิดบ่มด้วยตัวเอง ประกอบด้วย ส่วนผง 100 กรัม ส่วนเหลว 50 มิลลิลิตร โดยส่วนผง ประกอบด้วย ผงอะคริลิก 99.01% โดยน้ำหนัก ซิลเวอร์นาโน 0.99% โดยน้ำหนัก ส่วนเหลว ประกอบด้วย โมโนเมอร์เมทิลเมทราครัยเลต เทอร์เทียรี่ เอมีน 2. กรรมวิธีในการผลิตวัสดุฐานฟันเทียมชนิดบ่มด้วยตัวเอง ตามข้อถือสิทธิ 1 มีขั้นตอนดังนี้ ก. นำส่วนผงของอะคริลิกชนิดบ่มด้วยตัวเอง ผสมกับส่วนของอนุภาคซิลเวอร์นาโนได้ เป็นส่วนผง ข. นำส่วนผงที่ได้ จากข้อ ก ผสมกับส่วนเหลว ได้แก่ โมโนเมอร์เมทิลเมทราครัยเลตให้ เข้ากันที่อุณหภูมิห้อง โดยใช้เวลา 3 นาที 30 วินาที 3. การใช้วัสดุฐานฟันเทียมชนิดบ่มด้วยตัวเอง ตามข้อถือสิทธิ 1 หรือ 2 ที่ซึ่งใช้ซ่อมฐานฟัน เทียมชนิดบ่มด้วยตัวเองได้ทันที เมื่อฐานฟันเทียมแตกหัก บิ่น หรือซี่ฟันเทียมหลุด --------------------------------------- แก้ไข 07/01/2559 1. วัสดุฐานฟันเทียมชนิดบ่มด้วยตัวเอง ประกอบด้วย ส่วนผง 100 กรัม ส่วนเหลว 50 มิลลิลิตร โดยส่วนผงประกอบด้วย ผงอะคริลิก 99.01% โดยน้ำหนัก ซิลเวอร์นาโน 0.99% โดยน้ำหนัก ส่วนเหลว ประกอบด้วย โมโนเมอร์เมทิลเมทราครัยเลต เทอร์เทียรี่ เอมีน 2. กรรมวิธีการผลิตวัสดุฐานฟันเทียมชนิดบ่มด้วยตัวเอง ตามข้อถือสิทธิ 1 มีขั้นตอนดังนี้ ก.นำส่วนผงของอะคริลิกชนิดบ่มด้วยตัวเอง ผสมกับส่วนของอนุภาคซิลเวอร์นาโนได้ เป็นส่วนผง ข. นำส่วนผงที่ได้ จากข้อ ก. ผสมส่วนเหลว ได้แก่ โมโนเมอร์เมทิลเมทราครัยเลต ให้เข้ากันที่อุณหภูมิห้อง โดยใช้เวลา 3 นาที 30 วินาที สามารถนำไปใช้งานในการซ่อมฐานฟัน เทียมชนิดบ่มด้วยตัวเองได้ทันที ในกรณีฐานฟันเทียมเกิดการแตกหัก บิ่น หรือซี่ฟันเทียมหลุด --------------------------------------------------------------------------------------------------------------------- คำขอใหม่ปรับปรุงRevised 21/9/2016 1. The self-curing denture base material consists of 100 g of powder and 50 ml of liquid. The powder consists of 99.01% by weight of acrylic powder and 0.99% by weight of silver nanoparticles. The liquid consists of methyl methacrylate monomer tertiary amine. 2. The manufacturing process of the self-curing denture base material according to claim 1 involves the following steps: a. The self-curing acrylic powder is mixed with the silver nanoparticles to obtain the powder portion. b. The powder portion from step a is then mixed with the liquid portion, methyl methacrylate monomer, at room temperature for 3 minutes and 30 seconds. 3. The self-curing denture base material according to claim 1 or 2 can be used to immediately repair self-curing denture bases when they break, chip, or the denture tooth becomes loose. --------------------------------------- Revised 07/01/2016 1. Self-curing denture base material consists of 100 g of powder and 50 ml of liquid. The powder consists of 99.01% by weight of acrylic powder and 0.99% by weight of silver nanoparticles. The liquid consists of methyl methacrylate monomer and tertiary amine. 2. The manufacturing process for the self-curing denture base material as per claim 1 involves the following steps: a. Mix the self-curing acrylic powder with the silver nanoparticles to obtain the powder. b. Mix the powder from step a with the liquid, methyl methacrylate monomer, at room temperature for 3 minutes and 30 seconds. The material can then be immediately used to repair self-curing denture bases in case of breakage, chipping, or dislodging of the denture. --------------------------------------------------------------------------------------------------------------------- New and revised application 1. วัสดุฐานฟันเทียมชนิดบ่มด้วยตัวเอง ประกอบด้วย ส่วนผง 100 กรัม ส่วนเหลว 50 มิลลิลิตร โดยส่วนผงประกอบด้วย ผงอะคริลิก 99.01% โดยน้ำหนัก ซิลเวอร์นาโน 0.99% โดยน้ำหนัก ส่วนเหลว ประกอบด้วย โมโนเมอร์เมทิลเมทราครัยเลต เทอร์เทียรี่ เอมีน1. Self-curing denture base material consists of 100 g of powder and 50 ml of liquid. The powder consists of 99.01% by weight acrylic powder and 0.99% by weight silver nanoparticles. The liquid consists of methyl methacrylate tertiary amine monomer. 2. กรรมวิธีการผลิตวัสดุฐานฟันเทียมชนิดบ่มด้วยตัวเอง ตามข้อถือสิทธิ 1 มีขั้นตอนดังนี้ ก.นำส่วนผงของอะคริลิกชนิดบ่มด้วยตัวเอง ผสมกับส่วนของอนุภาคซิลเวอร์นาโนได้ เป็นส่วนผง ข. นำส่วนผงที่ได้ จากข้อ ก. ผสมส่วนเหลว ได้แก่ โมโนเมอร์เมทิลเมทราครัยเลตให้ เข้ากันที่อุณหภูมิห้อง โดยใช้เวลา 3 นาที 30 วินาที2. The manufacturing process for the self-curing dental base material as per claim 1 involves the following steps: a. The self-curing acrylic powder is mixed with the silver nanoparticles to obtain a powder. b. The powder from step a is then mixed with the liquid component, methyl methacrylate monomer, at room temperature for 3 minutes and 30 seconds. 3. การใช้วัสดุฐานฟันเทียมชนิดบ่มด้วยตัวเอง ตามข้อถือสิทธิ 1 หรือ 2 ที่ซึ่งใช้ซ่อมฐานฟัน เทียมชนิดบ่มด้วยตัวเองได้ทันที เมื่อฐานฟันเทียมแตกหัก บิ่น หรือซี่ฟันเทียมหลุด -------------------------------------------------------------------------------------------------3. The use of self-curing denture base materials, as per claim 1 or 2, which allow for immediate repair of self-curing denture bases when the base breaks, chips, or the denture tooth becomes dislodged.
TH1503001256U 2015-08-20 Self-curing dental implant base materials and manufacturing processes. TH12426U (en)