Inventors: Нелли Ивановна Соболева; Лариса Леонтьевна Ванина; Олег Петрович Галанов; Татьяна Викторовна Логинова; Татьяна Михайловна Суглобова; Рихард Эдуардович Иоонас; Михаил Михайлович Танасков; Николай Анатольевич Куташов; Вячеслав Станиславович Шлык; Василий Иванович Лаврентьев; Виктор Николаевич Алеканкин
Original assignee: Предприятие П/Я А-3832; Научно-Исследовательский Институт Сланцев
Priority date: 1981-02-16
Filing date: 1981-02-16
Publication date: 1982-08-23

Description

(54) РЕЗИНОВАЯ СМЕСЬ НА ОСНОВЕ НЕНАСЫЩЕННОГО КАУЧУКА (54) RUBBER MIXTURE BASED ON UNSATURATED RUBBER

Изобретение относитс к переработке полимеров и может быть использовано в резиновой промыипенности, в частности дл производства резинотехнических изделий. , Одним из способов переработки полимеров вл етс наполнение их различного рода веществами-наполнител ми , позвол ющими получить вулканизаты с необходимь1м комплексом свойств. Известна резинова смесь на основе ненасыщенного каучука, включающа серуускорительную вулканизующую группу и наполнитель (мел, каолин) l . Однако несмотр на их низкую стоимость , эти наполнители вл ютс природным сырьем, запасы которого небесконечны . В то же врем возникла пот-, ребность использовани побочных продуктов и отходов, образующихс в процессе различных производств. Известна также резинова смесь на основе хлоропренового каучука, в кото рой используетс отход производства - зола сланцев, образующа с при сжигании прибалтийского сланца. Золу ввод т в смесь в количестве 50 Mac.4i на 100 мае.ч. хлоропреново- го каучука и имеет следующий состав,% Эта резинова смесь характеризуетс высокой скоростью вулканизации , стойкостью к преждевременной вулканизации , кроме того, она близка к предлагаемой по содержанию сланцев золы 2 . Однако известна смесь вл етс неприемлимой дл практического использовани . Наиболее близкой к предлагаемой вл етс резинова смесь 3 на основе ненасыщенного каучука, включающа серуускорительную вулканизующую группу и неусиливающий наполнитель мел , и имеюща следующий состав, мае.ч.: Каучук СКИ-3 (изопреновый) 30,0 Каучук СКМС-ЗОАРКМ-15 (метилстирольный ) 70,0 Регенерат РКТ 30,0 Окись цинка5,0 Параоксинеозон 1,5 Мел75,0 fyQpaKC .10,0 Сера3,0 Альтакс1,0 ТиурамО,2 Техуглерол ПМ-ЗОВ70,0 Масло ПН-б12,0 Однако известные смеси имеют длительный период вулканизации и резины характеризуютс хорошими физико-механическими свойствами и низкой стойкостью к действию неорганических $ кислот. Цель изобретени - увеличение ско рости вулканизации смеси и повышение стойкости резин из нее к действию неорганических кислот при сохране- 20 НИИ физико-механических показателей резин. Поставленна цель достигаетс тем, что резинова смесь на основеThe invention relates to the processing of polymers and can be used in the rubber industry, in particular for the manufacture of rubber products. One of the methods for processing polymers is to fill them with various kinds of filler materials, which make it possible to obtain vulcanizates with the necessary complex properties. A known rubber mixture based on unsaturated rubber, comprising a sulfur-accelerating vulcanizing group and a filler (chalk, kaolin) l. However, despite their low cost, these fillers are natural raw materials whose reserves are finite. At the same time, there was a need for the use of by-products and waste generated during various production processes. Also known is a rubber mixture based on chloroprene rubber, which uses production waste — shale ash, which is produced when the Baltic shale is burned. The ash is injected into the mixture in an amount of 50 Mac.4i per 100 mash. chloroprene rubber and has the following composition,% This rubber mixture is characterized by a high rate of vulcanization, resistance to premature vulcanization, in addition, it is close to the proposed content of ash shale 2. However, the known mixture is not acceptable for practical use. Closest to the present invention is a rubber mixture 3 based on unsaturated rubber, which includes a sulfur-accelerating vulcanizing group and a non-reinforcing filler, chalk, and has the following composition, mac.: SKI-3 (isoprene) 30.0 Rubber methylstyrene) 70.0 Regenerate PKT 30.0 Zinc Oxide5.0 Paraoxine ozone 1.5 Mel75.0 fyQpaKC .10.0 Sulfur3.0 Altax1.0 TiuramO, 2 Technical carbon PM-ZOV70.0 Oil Mon-B12.0 However, known mixture have a long period of vulcanization and the rubber is characterized by good physical and mechanical properties and low resistance to the action of inorganic acids. The purpose of the invention is to increase the rate of vulcanization of the mixture and increase the resistance of rubbers from it to the action of inorganic acids while maintaining the 20 physico-mechanical indicators of rubber. The goal is achieved by the fact that the rubber mixture based on

100100

5,0 7,0 нен сер пу кач вую при тов рез из 5.0 7.0 hen serr

100100

30 7030 70

100 100 100 100

3,03,03,03,0

0,27 2,0 2;0 1,25 1,250.27 2.0 2; 0 1.25 1.25

1,01,01.01.0

0,20,20.20,2

О .25About .25

5,05.0

1,0 1.0

30303030

42 242 2

70707070

оabout

1,51,51,51,5

1,0 1,0 1,0 1,01.0 1.0 1.0 1.0

2,02.0

20 2020 20

30 асыщенного каучука, включающа уускорительную вулканизующую труп и неусйлйвакиций наполнитель, в естве последнего содержит сланцезолу состава вес.%: следующем соотношении компоненсмеси , мае.ч.: Каучук Серуускорительна вулканизую3 ,25-11,52 ща группа 40-80 Сланцева зола Готов т резиновые смеси. Состав иновой смеси и свойства резин нее приведены в таблице.30 of the saturated rubber, including the accelerator vulcanizing corpse and unsupplemented filler, the latter contains slate-containing composition in wt.%: The following component ratio of mixture, m.ch.: mixes. The composition of the new mixture and the properties of rubber are given in the table.

DpOAomnm aenmwDpOAomnm aenmw

Claims

Claim

A rubber mixture based on unsaturated rubber, including a sulfur accelerating vulcanizing group and a non-reinforcing filler, characterized in that, in order to increase the rate of vulcanization of the mixture and increase the resistance of rubber to inorganic acids while maintaining the physical and mechanical properties of rubbers, VNIIPI order 6205/40 contains as a filler shale ash composition, wt.%:

SiOi 30-40 A1 2 0 ₃ 5-10 5 Feo 0-j 5-10 CaO 30-50 MgO 2 -5 so ₃ 5-10

Yu in the following ratio of components of the mixture, parts by weight:

'' Rubber 100

Serum Accelerator Vulcanizing - ’

15th group 3.25-11.52

Shale Ash 40-80