SU833624A1 - Frit for enamel coating - Google Patents
Frit for enamel coating Download PDFInfo
- Publication number
- SU833624A1 SU833624A1 SU792833803A SU2833803A SU833624A1 SU 833624 A1 SU833624 A1 SU 833624A1 SU 792833803 A SU792833803 A SU 792833803A SU 2833803 A SU2833803 A SU 2833803A SU 833624 A1 SU833624 A1 SU 833624A1
- Authority
- SU
- USSR - Soviet Union
- Prior art keywords
- frit
- enamel coating
- cao
- bao
- coating
- Prior art date
Description
1one
Изобретение относитс к составам кислотостойких легкоплавких стекловидных эмалей дл стали и предназначено дл защиты стального оборудовани от воздействи агрессивных сред и может найти применение в химческой , нефтехимической и других отрасл х промышленности.The invention relates to compositions of acid-resistant low-melting vitreous enamels for steel, and is intended to protect steel equipment from exposure to aggressive media and can be used in the chemical, petrochemical, and other industries.
Известен состав фритты дл эмалевого покрыти содержащий, масс SiOo. 50-70; СаО 1-10; Ка.0 1-6; NajO 4-12; LiiO 0,5-6; SrO 2-5; TiOa 1-8; CaFa 0,5-8; Na SiFfc 2-6; ZrO,l-12; MoOii 0,1-4; 0,5-8; CrjT)- 0,5-7.The composition of the Frit for an enamel coating containing, SiOo masses is known. 50-70; CaO 1-10; Ka.0 1-6; NajO 4-12; LiiO 0.5-6; SrO 2-5; TiOa 1-8; CaFa 0.5-8; Na SiFfc 2-6; ZrO, l-12; MoOii 0.1-4; 0.5-8; CrjT) - 0.5-7.
Стеклоэмалевое покрытие, полученное на основе указанной фритты, характеризуетс следующими физико-химическими показател ми: Температура обжига , СGlass coating, obtained on the basis of the specified Frit, is characterized by the following physico-chemical indicators: Roasting temperature, C
740-760740-760
Химическа устойчивость (по методу кип чени в 20% HCI в течение 4 ч), мг/см Chemical stability (according to the method of boiling in 20% HCl for 4 h), mg / cm
0,03-0,15 Термостойкость, (по методу теплосмен ),°С - 220-260 Интервал обжига,с 60-ЙО0,03-0,15 Heat resistance, (according to the heat exchange method), ° C - 220-260 Firing interval, s 60-YO
Наибблее близким к предлагаемому вл етс состав фритты 2, содержащий , масс.% SiOT. 35-45; 2-8; 6,0,, 8-22; Na-iO 16-24; 0,1- . 2;СоаОз 0,1-0,5;СаО 2-12;ZrO 1-12;ВаО l-8;Ti02 0,5-5; CaF, 2,510; MgO 0,1-0,8.The closest to the proposed one is the composition of Frit 2, containing, wt.% SiOT. 35-45; 2-8; 6.0 ,, 8-22; Na-iO 16-24; 0.1-. 2; CoaOz 0.1-0.5; CaO 2-12; ZrO 1-12; BaO 1 -8; Ti02 0.5-5; CaF, 2.510; MgO 0.1-0.8.
Недостатком известных составов вл етс неширокий интервал обжига )60-80 С, что при эмалировании крупногабаритной аппаратуры не обеспечивает надежного равномерного оплавлени покрыти на всей поверхности аппарата из-за наличи перепадов температур в печи по ее высоте в пределах 50-60 С.A disadvantage of the known compositions is the narrow firing interval of 60-80 ° C, which, when enameling large-sized equipment, does not ensure reliable even fusing of the coating on the entire surface of the device due to the presence of temperature drops in the furnace along its height within 50-60 ° C
Цель изобретени - асширение интервала обжига.The purpose of the invention is to extend the firing interval.
Указанна цель достигаетс тем, что фритта дл эмалевого покрыти , включающа .S i 0., ZrO., СаО, ЛО, Caf, ВаО, , дополнительно содержит Lijtu, И при следующем соотношении компонентов, масс.%: 5102 56-64; ZrOa 2-4; 15-19; СаО 1,5-4; TiOi 1,8-5; CaFa. АЬО 1-2,5; 2-5;This goal is achieved by the fact that the frit for the enamel coating, including .Si 0., ZrO., CaO, LO, Caf, BaO,, additionally contains Lijtu, And in the following ratio of components, wt.%: 5102 56-64; ZrOa 2-4; 15-19; Cao 1.5-4; TiOi 1.8-5; CaFa. ABO 1-2.5; 2-5;
2-7; ВаО 1-4; feyju-,, 1,2-3.2-7; BaO 1-4; feyju- ,, 1,2-3.
Изобретение по сн етс конкретны;ми составс1ми, содержащими, масс.%:The invention is illustrated by specific compositions containing, in wt.%:
59,5 64,056,059.5 64.056.0
S-i02S-i02
2,0 3,04,02.0 3.0.04.0
ZrOo.ZrOo.
19,0 15,017,019.0 15,017.0
Nag ОNag o
5,0 3,02,05.0 3.02.0
Li-zOLi-zO
2,0 4,01,52.0 4.01.5
CaOCao
1,8 2,55,01.8 2.55.0
TiOa.Tioa.
4 ,,5 2,07,04 ,, 5 2,07,0
CaFaCafa
3,0 1,04,0 3.0 1.04.0
BaOBaO
2,0 2,5. 1,02.0 2.5. 1.0
1,2 3,02,51.2 3.02.2
Покрыти , полученныена основе писываемьох составов фритт, обладат следующими свойствами:The coatings obtained on the basis of the composition of frits will have the following properties:
720720
740740
720720
0,09 0,120.09 0.12
0,110.11
220220
260260
240240
720740720900 900 о 880720740720900 900 about 880
(160) (160) (180) ги приготовлени фритты едующие операции: расчет(160) (160) (180) the preparation of frit-eating operations: calculation
и составление шихты, смешение компонентов , плавка, гранул ци , помол.and blending, blending, melting, granulation, grinding.
Плав т шихту при 1300-1350с в газовых печах в течение 180-210 мин, гранул цию провод т мокрым способом, а помол и приготовление клинкера в соответствии с общеприн той технологией эмалировани .Float the mixture at 1300-1350s in gas furnaces for 180-210 minutes, the granulation is carried out wet, and the grinding and preparation of clinker in accordance with the standard enameling technology.
Предлагаемые составы имеют широки интервал обжига и низкую температуру обжига, что способствует значительному улучшению качества эмалевого покрыти химической аппаратуры за счет устранени короблени и-других дефектов эмалировани и увеличению срока ее службы.The proposed formulations have a wide firing range and a low firing temperature, which contributes to a significant improvement in the quality of the enamel coating of chemical equipment by eliminating warping and other enameling defects and increasing its service life.
Claims (2)