SU833617A1 - Glass - Google Patents
Glass Download PDFInfo
- Publication number
- SU833617A1 SU833617A1 SU792830057A SU2830057A SU833617A1 SU 833617 A1 SU833617 A1 SU 833617A1 SU 792830057 A SU792830057 A SU 792830057A SU 2830057 A SU2830057 A SU 2830057A SU 833617 A1 SU833617 A1 SU 833617A1
- Authority
- SU
- USSR - Soviet Union
- Prior art keywords
- cao
- glass
- oxide
- mgo
- certificate
- Prior art date
Description
1one
Изобретение относитс к составам химически стойких стекол дл внутреннего остекловывани металлических труб.This invention relates to chemically resistant glass compositions for the internal vitrification of metal tubes.
Известно химически стойкое стекло fl включающее, вес.%: SiOj 6075; Г -2.0 до 5; МдО 2-5; СаО 3-1р; SrO 0,2-1,8; BjO 2-5; TiOi 0,2-1,8. Это стекло по химической устойчивости относитс к 1-му гидролитическому классу и обладает температурой оплавлени выше .Known chemically resistant glass fl including, wt.%: SiOj 6075; G -2.0 to 5; MDO 2-5; CaO 3-1p; SrO 0.2-1.8; BjO 2-5; TiOi 0.2-1.8. This glass is chemically resistant to the 1st hydrolytic class and has a higher melting point.
Наиболее близким к предлагаемому вл етс химически стойкое стекло 2, состава, вес.%: SiO. 53-71, AIzO , 4,5-10; BiOa 5-10; СаО 3,2-6; MgO 0,1-2,1, N32.0 5-8; KjO 0,1-2; BaO 0,5-10; SrO 0,5-10. Стекло характеризуетс хорошими химическими и . термическими свойствами.Chemically resistant glass 2, composition, wt.%: SiO, is closest to the proposed one. 53-71, AIzO, 4.5-10; BiOa 5-10; CaO 3.2-6; MgO 0.1-2.1, N32.0 5-8; KjO 0.1-2; BaO 0.5-10; SrO 0.5-10. Glass is characterized by good chemical and. thermal properties.
К недостаткам известных стекол относ тс мала смачивающа и адгезионна способность к стали, низкие значени КЛТР и высокие температуры оплавлени (вьпле 800 С) .The disadvantages of the known glasses are low wetting and adhesive ability to steel, low CTE values and high melting temperatures (800 C).
Цель изобретени - увеличение смачивающей и адгезионной способности к стали.The purpose of the invention is to increase the wetting and adhesive ability of steel.
Указанна цель достигаетс тем, что известное стекло, включающееThis goal is achieved by the fact that the known glass, including
, СаО, МдО, ,, CaO, MDO,,
S102, AI-J.03.S102, AI-J.03.
v - V у 111 i З ,...jTv - V y 111 i З, ... jT
дополнительно содержит , ZnO и, по крайней мере , один оксид из группы . СеО , La О , Nd О , Рг О , СоО при следующем соотношении ингредиентов масс.%additionally contains ZnO and at least one oxide from the group. CEO, La O, Nd O, Pg O, CoO in the following ratio of ingredients by weight.%
SiOcL .53-71SiOcL .53-71
AI2.0-J 1,3-4AI2.0-J 1,3-4
62.054-1262.054-12
СаО 3,5-8CaO 3,5-8
00
МдО1,3-4,2MDO1,3-4,2
Na O9-16Na O9-16
LiiO4-8LiiO4-8
ZnO 0,5-10 И, по крайней мере, один оксид из ZnO 0.5-10 And at least one oxide of
5 группы5 groups
СеОа, ,Ceoa,
,,,,
Pr.j.O а, 1-1, 5Pr.j.O a, 1-1, 5
СоО 0,5-2,5Soo 0,5-2,5
00
В табл. 1 приведены конкретные составы стекла.In tab. 1 shows the specific glass compositions.
Эти стекла обладают высокой сцепл ющей способностью к металлу трубы и имеют температуру оплавлени These glasses have a high adhesion to the metal of the pipe and have a flashing temperature.
5 700-710 С.5 700-710 C.
Свойства стекол представлены вProperties of glasses are presented in
табл. 2.tab. 2
Стекло предлагаемого состава может широко использоватьс дл покрыти к нефт ным водам.The glass of the inventive composition can be widely used for coating to oil waters.
Таблица 1Table 1
Температура оплавлени , С . 709 705 711 Коэффициент термического расширени , (1/°С) X 10 110 120 .129 Химическа устойчивость к 2н. NaOH, потери 50 50 49,9 мг/дм (XV-1) (XV-I) (XV-I) Melting point, C. 709 705 711 Thermal expansion coefficient, (1 / ° C) X 10 110 120 .129 Chemical resistance to 2n. NaOH, losses 50 50 49.9 mg / dm (XV-1) (XV-I) (XV-I)
Claims (2)