SU763410A1 - Method of producing lead-molybdate pigment - Google Patents
Method of producing lead-molybdate pigment Download PDFInfo
- Publication number
- SU763410A1 SU763410A1 SU772546643A SU2546643A SU763410A1 SU 763410 A1 SU763410 A1 SU 763410A1 SU 772546643 A SU772546643 A SU 772546643A SU 2546643 A SU2546643 A SU 2546643A SU 763410 A1 SU763410 A1 SU 763410A1
- Authority
- SU
- USSR - Soviet Union
- Prior art keywords
- lead
- crown
- solution
- molybdate
- mixture
- Prior art date
Description
1one
Изобретение относитс к области получени свинцово-молибдатных кронов, примен емых в качестве пигментов при изготовлении авто- и сельскохоз йственных эмалей, красок дл кожи и по- 5 лиграфии.The invention relates to the field of producing lead-molybdate crowns, used as pigments in the manufacture of auto and agricultural enamels, paints for leather and polygraphy.
Известные способы получени свинцово-молибдатного крона включают процесс осаждени пигмента из раствора нитрата свинца и раствора, содержа- 10 щего хромат, сульфат- и молибдатионы , с последующей модификацией поверхности пигмента различными соединени ми дл улучшени его эксплуатационных свойств.15Known methods for producing lead-molybdate krone include the process of precipitating pigment from a solution of lead nitrate and a solution containing chromate, sulphate and molybdation, followed by modifying the surface of the pigment with various compounds to improve its performance properties.
При этом известные процессы осаждени обычно провод т при постепенном сливе раствора, содержащего указанные ионы, в раствор нитрата свинца при посто нно мен ющейс величине из-20 бытка ионов свинца в реакционной смеси 1 и 2 .In this case, the known precipitation processes are usually carried out with a gradual discharge of the solution containing the indicated ions into the lead nitrate solution at a constant value of from -20 bytes of lead ions in the reaction mixture 1 and 2.
Однако известные способы не позвол ют получить крона светло- и желтооранжевого цвета с высокой кроющей 25 способностью.However, the known methods do not allow to obtain a crown of light and yellow orange color with high opacity 25.
Известен способ получени свинцово-молибдатного крона путем его осаждени из раствора нитрата свинца и раствора смеси осадителей, содержаще-30A known method for producing a lead-molybdate crown by precipitating it from a solution of lead nitrate and a solution of a mixture of precipitants containing 30
22
го хромат-, сульфат- и молибдат- ионы , при одновременном сливе исходнъйх растворов -при избытках ионов свинца и рН реакционной смеси более 2,1 f chromate, sulfate, and molybdate ions, while simultaneously draining the initial solutions — with an excess of lead ions and the pH of the reaction mixture is more than 2.1 f
Известны.м способом получают преимущественно ораилсево-красные крона с кроющей способностью пор дка 2024 г/м2.In the known manner, a predominantly orailseed-red crown with a covering power of about 2024 g / m2 is obtained.
Однако получить пигменты светлои желто-оранжевого оттенка цвета с высокой кроющей способностью по данному способу не представл етс возможным .However, it is not possible to obtain pigments of a light yellow-orange hue with a high hiding power by this method.
Целью изобретени вл етс получение крона светло- и желто-оранжевого цвета с повышенной кроющей способностью ,Поставленна цель достигаетс описываег-лым способом получени свинцовомолибдатного крона осаждением его из раствора нитрата свинца и раствора смеси осадителей, содержащего хроматсульфат и молибдат-ионы, путем приливани раствора нитрата свинца к раствору смеси осадителей до рН 1,9-2,0. При этом дл получени крона светлооранжевого цвета осаждение ведут Б течение 1-5 мин, а дл получени крона желто-оранжевого цвета осаждение зедут в течение 20-25 мин. ПредлагаемыйThe aim of the invention is to obtain a light and yellow-orange crown with increased opacity, the goal is achieved by the described method of producing the lead molybdate crown by precipitating it from lead nitrate solution and precipitating mixture solution containing chromate sulfate and molybdate ions by adding nitrate solution lead to a solution of a mixture of precipitants to a pH of 1.9-2.0. At the same time, in order to obtain a crown of light orange color, the deposition of B takes 1–5 minutes, and to obtain a crown of yellow-orange color, precipitation will occur for 20–25 minutes. Proposed
способ обеспечивает получение светлс и желто-оранжевого крона с кроющей способностью, соответственно равной 18-20 и 23-24 г/м.the method provides light and yellow-orange krone with a covering power of 18-20 and 23-24 g / m, respectively.
Пример 1. Раствор нитрата свинца с концентрацией 200,6 г/л, имеющий рН 4,0, постепенно в течение 1 мин приливают при к раствору смеси осадителей, содержащей в г/л: Сг20з 46,2, MoOj 10,02, SO 5,74 и NaOH 12 и имеющей рН 7,2 при посто нном перемешивании и поддержании рН суспензии 1,9 до полного исчезновени избытка хромат-, сульфати молибдат- ионов/ затем суспензию оставл ют на вызревание в течение 10 мин, после чего модифицируют соединени ми кремни , алюмини и сурьмы После нейтрализации крон отмывают от водорастворимых солей и сушат при . Получают светло-оранжевый крон с кроющей способностью 18 г/м, имеющей крас щую способность 100%.Example 1. A solution of lead nitrate with a concentration of 200.6 g / l, having a pH of 4.0, is gradually poured over a period of 1 min while the solution of a mixture of precipitants containing g / l: Cr20z 46.2, MoOj 10.02, SO 5.74 and NaOH 12 and having a pH of 7.2 with constant stirring and maintaining the pH of the suspension to 1.9 until the disappearance of the excess chromate, molybdate sulfate ions completely disappears / then the suspension is left to aging for 10 minutes, after which the compounds are modified mi silicon, aluminum and antimony. After neutralizing the crowns, they are washed from water-soluble salts and dried at. A light orange crown with a covering power of 18 g / m, having a coloring power of 100%, is obtained.
Пример 2. Осаждение пигмента осуществл ют аналогично примеру 1 но при приливании раствора нитрата свинца в раствор смеси осадителей в течение 5 мин с последующим вызреванием также в течение 5 мин получают светло-оранжевый крон с кроющей способностью - 20 г/м и крас щей спосоностью 100%.Example 2. The pigment is deposited analogously to example 1, but by adding a solution of lead nitrate to a solution of a mixture of precipitants for 5 minutes, followed by aging, a light orange crown with a covering power of 20 g / m and a color of 100 is obtained for 5 minutes %
Пример 3. Получение крона провод т аналогично примеру 1 при условии приливани исходного раствора нитрата свинца в смесь осадителей в течение 20 мин. В результате получают желто-оранжевый крон с кроющей и крас щей способностью соответственно 2,3 г/м и 100%.Example 3. The preparation of the crown is carried out analogously to example 1, provided that the initial solution of lead nitrate is poured into the mixture of precipitating agents for 20 minutes. As a result, yellow-orange crowns with a covering and dyeing power of 2.3 g / m and 100%, respectively, are obtained.
Расширенна цветова гамма свинцово-молибдатного крона по данному изобретению и улучшенные пигментные его характеристики значительно расшир ют возможности применени этого пигмента в лакокрасочной промышленности .The extended color gamut of the lead-molybdate crown according to this invention and its improved pigment characteristics greatly expand the possibilities of using this pigment in the paint industry.
Claims (3)