SU753867A1 - Polymeric composition - Google Patents
Polymeric composition Download PDFInfo
- Publication number
- SU753867A1 SU753867A1 SU782649366A SU2649366A SU753867A1 SU 753867 A1 SU753867 A1 SU 753867A1 SU 782649366 A SU782649366 A SU 782649366A SU 2649366 A SU2649366 A SU 2649366A SU 753867 A1 SU753867 A1 SU 753867A1
- Authority
- SU
- USSR - Soviet Union
- Prior art keywords
- fraction
- composition
- styrene
- copolymer
- butadiene
- Prior art date
Description
(54) ПОЛИМЕРНАЯ КОМПОЗИЦИЯ(54) POLYMER COMPOSITION
Изобретение относитс к области переработки пластмасс и касаетс получени композиций на основе поливинилхлорида , примен емых, например, дл получени нетоксичного винилпласта, перерабатываемого методом экструзии, лить под давлением и т. ц. в упаковочные ма териалы и издели . Известна нетоксична композици , содержаща поливинилхлорид, эпоксидированное соевое масло, стеариты кальци и цинка, смазку .1. . Основным недостатком композиции ПВХ на кальций-цинковых стабилизаторах вл етс то, что издели из композиции с применением таких стабилизаторов имеют желтую окраску и низкую прозрачность. Наиболее близкой к предлагаемой L2 вл етс композици , содержаща компоненты при соотношении, вес.%: ПолиБИнилхлорид78 Эпоксидированное соевое масло Диоктилфталат3,9 Смазочные вещества: Смесь неполного эфира жирной кислоты и глицерина 1,2 Стеаринова кислотаО,3 Сополимер метилметакрнлата , бутадиена и стирола9,3 Сложна комплексна система стабилизаторов солей кальци и цинка ( 2:1) СЖК фракции CjQ-CjQ В пластикаторе ( сод.солей 2О%)0,2 Поливиниловый спирт0,2 Бензол ОАО,1 ( целева добавка) Однако ограниченна совместимость ивинилового спирта с поливинилхлори- не позвол ет получить изделий из занной композиции без начальной оки с необходимой прозрачностью. Кротого , применение поливинилового снижает эксплуатационные свойства и;шелий, в частности деформационные х рактеристики и устойчивость к усталос ным нагрузкам. Цель изобретени - устранение жел- тнзны, повышоние прозрачности, улучше ние деформационных характеристик и ус тойчивости к усталостным нагрузкам. Поставленна цель достигаетс тем, ЧТО В пол тинил)слоридную композицию, содержащую сложный комплексный стабилизатор на основе кальций-цинковой соли синтетических жирных кислот фрак ции С. эпоксидироваиное рагтительное масло, диоктилфталат, непол)1Ы эфир жирной кислоты и многоатомного спирта, сополимер метилметакрилата, бутадиена и стирола. Стеариновую кисл ту дополнительно ввод т к кармидол-:и1 ратное соединение карбамида и высших жирных спиртов фракции С| 3:1) при следующем соотношении компонент вес.%: Поливинил хлорид69-90 Комплексный стабилизатор на основе кальций-цинковой соли синтетических жирных кислот фракции С,д ,7-4,7 Эпоксидированное растительное масло 1,8-4,0 Диоктилфталат О,9-6,1 Неполный эфир жирной кислоты и многоатомного спирта (глицерина ) О,4-1,7 Стеаринова кислота 0,01-О,5 Сополимер метил- метакрилата, бутадиена и стирола 3,6-13,5 Кармидал 0,02-0,4 Введение в композицию кармидола позвол ет повысить прозрачносгь мате риала и устранить желтизну. Кроме то го, предотвраща сшивку полимера, ка мидол повышает относительное удлинен при разрыве и увеличивает устойчивос образцов к многократному перегибу. Композици может содержать и цел вь:е добавки в небольших количествах (светостабилизаторы, смазки специаль ного назначени , теноры, антистатики др.). Повышение прозрачности, улучшение деформационных характеристик и устой чивость к усталостным нагрузкам при PAdnOUtlW П TV 0 « т-г п TiiTiTT PI D V .. может быть объ снено, с одной стороны, ингибированием относительных и других возможных радикальных процессов, развиваюлихс при энергетическом распаде ПВ.Ч, или св зыванием в комплексе координ-::цион )1о-ненасыщенных металлов, что характерно дл азотсодержащих стабилизаторов , с другой (в противоположность последним) - высоким эффектом совмещени кармидола с поливинилхлоридом за счет вход щих в состав кармидола химических групп высших жирных спиртов. Сущность изобретени подтверждаетс примерами конкретного выполнени . Пример 1. Композицию состава, вес.%: 78 поливинилхлорида; 3,9 комплексного стабилизатора на основе кальцийцинковой соли синтетических жирных, кислот фракции C|(j -C2(j; 3,1 эпоксидированного растительного масла; 3,9 диоктил- фталата; 1,2 неполного эфира жирной кислоты и глицерина; 0,3 стеариновой кислоты; 9,3 сополимера метилметакри- лата бутадиена и стирола; 0,2 кармидола и 0,1 бензача ОА (целева добавка), приготавливают перемешиванием в скоростном лабораторном смесителе при 90 С 30 мин. Полученную композицию экструдируют на микроэкструдере при температуре по зонам С-1-170, 11-180, головка-185 и скорости оборотов черв ка 20 об/мин с получением образцов в виде непрерывной ленты шириной 25 NfM, ТОЛЩТ1НОЙ 0,5 мм, затем полученные образцы подпрессовывают на прессе при 175 С при добавлении 5 кгс/см . в течение 5 мин. Пример 2. Состав и режим при готовлени композиции, как в примере 1, только содержание кармидача 0,4, ПВХ 77,8. Пример 3. Состав и режим приготовлен 1 композиции, как в npnKieре 1, тачько содержание кармиаола 0,02, ПВХ 78,18. Пример 4. Образцы из KONinoзнции состава, вес./о: 69 ПОЛИБИНИЛКЛО- рида; 4,7 пасты; 4,0 эпоксидированного растительного масла; 6,1 дноктилфталата; 1,7 неполного эфира жирной кислоты и глицерина; 0,47 стеариновой кислоты; 13,5 сополимера метилметакрилата бутадиена и стирола; 0,15 кармндола и 0,38 бензола ОА (целева добавка), приготавливают, KSK в примере 1. Пример 5. Образцы из композиции состава, вес.% : ОО па ивинилхлгThe invention relates to the field of plastics processing and relates to the preparation of compositions based on polyvinyl chloride, used, for example, to obtain a non-toxic vinyl plastic, processed by extrusion, injection molding, and so on. in packing materials and products. A known non-toxic composition containing polyvinyl chloride, epoxidized soybean oil, calcium and zinc stearites, a lubricant .1. . The main disadvantage of the PVC composition on calcium-zinc stabilizers is that the products of the composition using such stabilizers have a yellow color and low transparency. Closest to the proposed L2 is a composition containing components at a ratio, wt.%: PolyBinyl chloride78 Epoxidized soybean oil Dioctyl phthalate 3,9 Lubricants: Mixture of partial fatty acid ester and glycerin 1,2 Stearic acid O, 3 Methyl methaccrylate copolymer, butadiene and styrene 9,3 Complex complex system of stabilizers of calcium and zinc salts (2: 1) FFA fraction CjQ-CjQ In a plasticizer (salt 2O%) 0.2 Polyvinyl alcohol0.2 Benzene OAO, 1 (target additive) However, limited compatibility of vinyl alcohol with poly inilhlori- does not allow to obtain articles from the composition without an initial bound Oka with the necessary transparency. Mild, the use of polyvinyl reduces the performance properties and; shelium, in particular, deformation characteristics and resistance to fatigue loads. The purpose of the invention is the elimination of yellowness, increased transparency, improvement of deformation characteristics and resistance to fatigue loads. The goal is achieved by the fact that polyethylene (II) is a fluoride composition containing a complex complex stabilizer based on the calcium-zinc salt of synthetic fatty acids of fraction C. and styrene. Stearic acid is additionally injected to the karmidol-: and1 the combination of carbamide and higher fatty alcohols fraction C | 3: 1) in the following ratio of component wt.%: Polyvinyl chloride 69-90 Complex stabilizer based on calcium-zinc salt of synthetic fatty acids fraction C, d, 7-4.7 Epoxidized vegetable oil 1.8-4.0 Dioctyl phthalate O, 9-6.1 Partial ester of fatty acid and polyhydric alcohol (glycerin) O, 4-1.7 Stearic acid 0.01-O, 5 Copolymer of methyl methacrylate, butadiene and styrene 3.6-13.5 Karmidal 0.02 -0.4 Introduction of karmidol into the composition allows to increase the transparency of the material and eliminate yellowness. In addition, by preventing polymer cross-linking, Kamidol increases the relative elongation at break and increases the resistance of the samples to multiple bending. The composition may also contain a purpose: e additives in small quantities (light stabilizers, special purpose lubricants, tenors, antistatic agents, etc.). Increased transparency, improved deformation characteristics and resistance to fatigue loads with PAdnOUtlW P TV 0 «t-r TiiTiTT PI DV .. can be explained, on the one hand, by inhibiting relative and other possible radical processes that develop during the energy decay of the PV. H, or by bonding in a complex the coordinate - :: ционцион) 1o-unsaturated metals, which is typical of nitrogen-containing stabilizers, on the other (as opposed to the latter) - by the high effect of combining carmidol with polyvinyl chloride due to the rmidola chemical groups of higher fatty alcohols. The invention is confirmed by examples of specific performance. Example 1. The composition of the composition, wt.%: 78 polyvinyl chloride; 3.9 complex stabilizer based on calcium zinc salt of synthetic fatty acids of fraction C | (j –C2 (j; 3.1 epoxidized vegetable oil; 3.9 dioctyl phthalate; 1.2 partial ester of fatty acid and glycerol; 0.3 stearic acid; 9.3 copolymer of methyl methacrylate butadiene and styrene; 0.2 carmidol and 0.1 benzach OA (target additive), prepared by mixing in a high-speed laboratory mixer at 90 C for 30 minutes. The resulting composition is extruded on a micro-extruder at a temperature in zones C-1-170, 11-180, head-185 and rotational speed h rv ka 20 rpm to obtain samples in the form of a continuous tape width of 25 NfM, with a thickness of 0.5 mm, then the samples obtained are pressed in a press at 175 C with the addition of 5 kgf / cm for 5 minutes. Example 2. Composition and mode when preparing the composition as in example 1, only the content of karmidach 0.4, PVC 77.8. Example 3. Composition and mode prepared 1 composition, as in npnKiere 1, the amount of karmiaol 0.02, PVC 78.18. Example 4. Samples from a KONino composition, w / v: 69 POLYBINYLCLORIDE; 4.7 paste; 4.0 epoxidized vegetable oil; 6.1 Doctilphthalate; 1.7 fatty acid partial ester and glycerol; 0.47 stearic acid; 13.5 copolymer of methyl methacrylate butadiene and styrene; 0.15 carmindol and 0.38 benzene OA (target additive), prepared, KSK in example 1. Example 5. Samples from the composition, wt.%: OO pa ivinylhlg
сидированного растительного масла; 0,9 диокгилфталата; 0,45 неполного эфира жирной кислоты и глицерина; 0,1 стеариновой кислоты; 3,6 сополимера метилметакрилата бутадиена и стирола; 0,1 кармидола и 0,35 бензола ОА (целева аобйвка), приготавливают, как в примере 1.seed oil; 0.9 dioxgilphthalate; 0.45 fatty acid partial ester and glycerol; 0.1 stearic acid; 3,6 copolymer of methyl methacrylate butadiene and styrene; 0.1 carmidol and 0.35 benzene OA (target release) are prepared as in Example 1.
Пример 6. Состав и режимы при готовлени композиции и образцов из нее такие же, как в примере 1, только кармидол отсутствует.Example 6. The composition and modes of preparation of the composition and samples from it are the same as in example 1, only karmidol is absent.
Пример 7. Состав и режимы приготовлени композиции и образцов изExample 7. The composition and modes of preparation of the composition and samples from
78 82 74 7978 82 74 79
71 5371 53
желтыйyellow
светло-желтый ( в известной компози66 ции) Как видно из данных таблицы, образец № 1 (оптимальный вариант) характеризуетс отсутствием желтизны, прозрачностью выше известной композиции на 12%, повышенными деформационными показател ми, относительное удлинение при разрыве увеличилось в 6 раз и устой чивость к усталостным нагрузкам по сравнению с известной композицией увеличилась в 2 раза. Использование предлагаемой композиции позволит получать издели с необходимой прозрачностью, с улучшенными деформационными свойствами и повышенной устойчивостью к ударным нагрузкам.. Применение этой композиции, вместо вы8676light yellow (in a known composition66) As can be seen from the table, sample No. 1 (the best option) is characterized by the absence of yellowness, transparency above the known composition by 12%, increased deformation indicators, the relative elongation at break has increased 6 times and stability to fatigue loads compared to the known composition increased by 2 times. The use of the proposed composition will make it possible to obtain products with the necessary transparency, with improved deformation properties and enhanced resistance to shock loads. The use of this composition, instead of 886
нее такие же, как в примере 1, только вместо кармидола вЬедено 0,2 поливинилового спирта.it is the same as in example 1, but instead of karmidol 0.2 polyvinyl alcohol is applied.
Образцы оценивают по показател м: 5Светопропускание {%) при Л 420нмSamples evaluated by indicators: 5 Light transmission {%) at L 420nm
по ГОСТ 15875-70, визуальна оценка цвета , физико-механические свойства: предел текучести при раст жении и относительное удлинение при разрыве по ГОСТ 11262-68, устойчивость к многократному перегибу на угол 180 при посто нной нагрузке на образец ЗО кгс/см.according to GOST 15875-70, a visual assessment of color, physical and mechanical properties: yield strength during stretching and elongation at break according to GOST 11262-68, resistance to multiple bending at an angle of 180 with a constant load on the sample of 30 kgf / cm.
Результаты испытаний приведены в таблице.The test results are shown in the table.
82 89 82 89
486486
464 57 471 429 91464 57 471 429 91
51 51
512 48 468512 48 468
462462
10ten
Claims (2)