SU726308A1 - Composition for isolating absorption zones - Google Patents
Composition for isolating absorption zones Download PDFInfo
- Publication number
- SU726308A1 SU726308A1 SU782594057A SU2594057A SU726308A1 SU 726308 A1 SU726308 A1 SU 726308A1 SU 782594057 A SU782594057 A SU 782594057A SU 2594057 A SU2594057 A SU 2594057A SU 726308 A1 SU726308 A1 SU 726308A1
- Authority
- SU
- USSR - Soviet Union
- Prior art keywords
- composition
- water
- drilling
- zones
- absorption
- Prior art date
Description
Изобретение относитс к производству составов дл изол ции зон погло при бурении скважин и может быть использовано дл изол ции зон no Тлощечий в крупнопористых, трещинова тых и закарстованных породах с большим количеством перетоков пластовых вод при вскрытии как одной, так и .не скольких зон поглощений, в нефтега;3овой прсмышленности, геологии и гор ном деле. Известен состав дл изол ции зон поглощений при бурении скважин, содержащий латекс, хлорид кальци и воду 1 . При смешивании всех ингредиентов известного состава происходит мгновенна коагул ци его с образованием твердого продукта, который невозможно прокачать по бурильным трубам в зону поглощени . Поэтому способ й-зол ции зон поглощений этим составом имеет свои особенности: сначала в скважину закачивают райтвор хлорида кальци , а после него - взвесь латек са или же закачивают порци ми раствор хлорида кальци - пресную воду латекс . Однако, если скважина пробурена в пористокавернозных породах и при бурении одновременно вскрыты не сколько зон поглощений, что сопровождаетс по влени ми сильных перетоков вод, то раствор хлорида кальци быстро растекаетс в поры, где он размываетс этими перетоками пластовых вод. Поэтсму веро тность успешного осуществлени jaKoro твида изол ции зон поглощений будет крайне низка . Кроме того, мгновенна коагул ци латекс а контактге,с хлоридом кильци может привести к образованию твердого изол ционного материала не в зоне поглощени , а вблизи трубы, по которой в скважину закачивают латекс и раствор хлорида кальци , т.е. изол ци будет некачественной. Наиболее близким к изобретению по технической сущности и достигаемому результату вл етс состав дл изол ции зон поглощени при бурении скважин, содержащий полиакридамид, глинопорошок и воду, при следующем соотношений ингредиентов, вес.%: Полиак риламид0,2 Глинопорошок31,3 Вода68,3 2J. Однако известный Ьостав с момента. приготовлени в процессе транспортировки по трубам в зону поглощени , а также под действием перетоков пласто ;Й 5Д р&эрь5й-йёгЬ на- отдёЛьйМ: час ,ти и размываетс , что при сильных перетоках пластовых вод делает изо Л ций невозможной. того, извес ный состав обладает низкими закупоривающими свойствами, а именно: низкой пластической прочностью (1,5 2 г/см) и малой густотой, что дажеThe invention relates to the production of compounds for isolating zones absorbed during well drilling and can be used to isolate zones of flattening in large pores, fractured and karsted rocks with a large number of formation water flows at the opening of both one and several absorption zones. in the oil industry; 3rd industry, geology and mining. A known composition for isolating absorption zones in the drilling of wells, containing latex, calcium chloride and water 1. When all the ingredients of a known composition are mixed, it instantly coagulates to form a solid product that cannot be pumped through the drill pipe to the absorption zone. Therefore, the method of solution generation of absorption zones with this composition has its own characteristics: first, the calcareous calcium chloride is pumped into the well, and the latex suspension is pumped into the well, or calcium chloride solution — fresh water latex is pumped in portions. However, if a well is drilled in porous-rock formations and during drilling, several absorption zones are simultaneously opened, which is accompanied by the appearance of strong water flows, the calcium chloride solution quickly spreads into the pores where it is washed away by these flows of formation waters. Therefore, the likelihood of a successful implementation of isolation of absorption zones will be extremely low. In addition, the instantaneous coagulation of latex and kiltiac chloride with chloride can lead to the formation of a solid insulating material not in the absorption zone, but near the pipe through which latex and calcium chloride solution is pumped into the well, i.e. insulation will be poor quality. The closest to the invention to the technical essence and the achieved result is a composition for isolating zones of absorption during drilling, containing polyacridamide, clay powder and water, with the following ratios of ingredients, wt.%: Polyacrylamide 0.2 Clay powder 31.3 Water 68.3 2J. However, the known “cost” from the moment. preparation in the process of transportation through pipes to the absorption zone, as well as under the influence of the flow of the reservoir; 5D p & In addition, the known composition has low sealing properties, namely: low plastic strength (1.5 2 g / cm) and low density, which even
7 в Учае малых перетсэков пластовых ,вод не обеспечивает надежиую из6л 1 ЙЙН 5 55 91® й буровых растворов ЕЕелзь изобретени - получение состава , который обладал бы свойством -неразмь1ваеМостй. с мойента его приго Товменй и поййШётнними закупоривающими свойствами с сЬхра нёнйем прокачиваемости ,7 in the Ucha of small re-seams of formations, water does not provide reliable out of 6 l 1 YIN 5 55 91® th drilling fluids of the invention EE - obtaining a composition that would have the property-ineptism. from the moyenta of his prefecture Tovmeny and poyyotnym sealing properties with shhra nenya pumpability,
Поетжтеенна Ц0Ль достигаетс со СтавЬм, содержашйм полимер, глинопо iiiuuiOK и воду, в котором.в качестве полимера используют латекс, а в с ё йнгрёдйейтывз ты в следующем соотношении , Bec,%s. Латёкст .28,5-61,4 Poetzhteenna Ts0L'i is reached with Stavm, contains polymer, clay-based iiiuuiOK and water, in which latex is used as polymer, and in the following ratio, Bec,% s. Latekost .28,5-61,4
Глинопорошок1 5,4-28. ,6 ,Dry mud 1 5.4-28. , 6,
Вода Остальное, Дл получёниЯ прёдлагйёмого с;ос ава в лабораторных уславй хйспользойались: ;;;--- - ----«--.. . ла.текс СКС-50 КГП, ТУ 38-103 -156, эмульси белого цвета;Water Else, To receive the proposed with; wasp in laboratory labs using: ;;; --- - ---- "- ... la.tex SKS-50 KGP, TU 38-103 -156, white emulsion;
глинопорошок АлЬметьевскиЙ ТУ 39-043-74, сорт III; , .. . Ёостав и свойств а йзвёстНоГр ... clay powder Al'metyevsk TU 39-043-74, grade III; .. The composition and properties of starfish ...
вода водопроводна , обща жесткость 5-6 млг-экв/л.the water is tap, the total hardness is 5-6 mlg-eq / l.
Получение предлагаемого состава в лабораторных услови х проводилось следующим образом.The preparation of the proposed composition under laboratory conditions was carried out as follows.
Вначале готовили 40%-ный глинистый раствор из глинопорошка и воды в лабораторной мешалке, перемешива их в течение 20 мин со скоростью 1000 ofe/мин. Затем в полученную смес при непрерывном перемешивании медленно вливали латекс и продолжали перемешивание еще в течение 0,5-1 мин с той же скоростью, в результате чего был получен предлагаемый состав дл изол ции-зон поглощений.Initially, a 40% clay solution was prepared from clay powder and water in a laboratory mixer, mixing them for 20 minutes at a rate of 1000 of e / min. Then, the latex was slowly poured into the resulting mixture with continuous stirring and the stirring continued for another 0.5-1 min at the same rate, with the result that the proposed composition was obtained for isolating absorption zones.
Лабораторными испытани ми были установлены предельные и оптимальные значени ингредиентов предлагаемого состава по наличию свойства неразмывйёйЬети и прокачиваемости, а также по закупориваюгшм свойствам этого состава (по пластической прочности и густоте) . .The laboratory tests established the limiting and optimal values of the ingredients of the proposed composition according to the presence of non-washable properties and pumpability, as well as clogging properties of this composition (according to plastic strength and density). .
Дл получени сравнительных данных в лабораторных услови х был приготовлен также и известный состав, содержащими полиакриламид, глинопорошок и воду.To obtain comparative data in the laboratory, a well-known composition was also prepared, containing polyacrylamide, clay powder and water.
Данные об ингредиентном составе и свойствах известного и предлагаемого составов приведены в табл. 1. . . . Т а б л и ц а 1 и предлагаемого составов дл изол ции зон поглощени Data on the ingredient composition and properties of the known and proposed formulations are given in table. one. . . . TABLE 1 and proposed formulations for isolating absorption zones
П 21,0 31,6 1. 1:3 Оста ль ное 2. lT2 28,5 28,6 То же ... . -з---1 5 .1 -54,5 S;Jt:L: :i..;k,.;..a;...-.,: Д.,.. 4. 2:1 мый состав НетО Час- Прока тично чивараз- етс . мнваетс Не То же размываетс То же Небольшой избыток латексаP 21.0 31.6 1. 1: 3 Remaining 2. lT2 28.5 28.6 The same .... -3 --- 1 5 .1 -54,5 S; Jt: L:: i ..; k,.; .. a; ...-.,: D., .. 4. 2: 1 The composition of the NLR is ChasParable. Not the same is blurred The same A slight excess of latex
5. 2,5:1 66,6 13,4 31,5 68,3 0,2 Нет5. 2.5: 1 66.6 13.4 31.5 68.3 0.2 No
1 :313
6.6
Предельные и оптимальные значени ингредиентов предлагаемого состава, вы вленные на основании испытаний, приведены в табл. 2.The limiting and optimal values of the ingredients of the proposed composition, determined on the basis of the tests, are given in Table. 2
Т а б л и ц а 2 йредлагаемый составT a b l and c a 2 proposed composition
54,554.5
28,5-61,428.5-61.4
15,4-28,6 18,2 Остальное Остальное15.4-28.6 18.2 Else Else
По материалам лабораторных испытаний установлено, что предлагаемый состав по сравнению с известным составом обладает с момента его приготов-г. лени свойством неразмываемости, кроме того, пластическа прочность его выше в 7-35 раз, а густота - выше в. 7-33 раза.According to the materials of laboratory tests, it has been established that the proposed composition, as compared with the known composition, has from the moment of its preparation. This property of indecomposability, moreover, its plastic strength is 7-35 times higher, and its density is higher than. 7-33 times.
Кроме того, что предлагаемый состав обладает свойством неразмываемости и повышенными закупоривающими свойствами, он также сохран ет св.ойство прокачиваемости и может быть легко доставлен в зоны поглощени существующим цементировочным оборудованием .In addition to the fact that the proposed composition has the property of indecipability and enhanced clogging properties, it also preserves the pumpability property and can be easily delivered to the absorption zones with existing cementing equipment.
Благодар указанным свойствам предлагаемый состав обеспечивает каDue to these properties, the proposed composition provides
Продолжение табл.1Continuation of table 1
Час- . Hour
.Образуютзбыток тично с отатекса.It is an excess of tichi with otateks
50% размыдельные ваетс сгустки состава с большим избытком латекса50% scouring clumps of compound with a large excess of latex.
Известный состав Known composition
1,5-2 Размы- ваетс 1.5-2 Blurred
чественную изол цию как.одной, так и нескольких зон поглощений при большом количестве перетоков пластовых вод за одну обработку в то врем , как при использовании известных составов требуетс производить эту обработку несколько раз.effective isolation of both single and multiple absorption zones with a large number of overflows of formation water during a single treatment, while using known compounds it is required to perform this treatment several times.
Ожидаемый экономический эффект за одну обработку при ликвидации поглощени составл ет пор дка 8 тыс, руб.The expected economic effect for one treatment at liquidation of absorption is about 8 thousand rubles.
Технологи получени предлагаемого составаВ производственных услови х весьмаПроста, используетс известное традиционное оборудование, вход щие в состав ингредиенты недорогие и недефицитныеi Предлагаемый состав может быть немедленно приготовлен на любых буровых предпри ти х непосредственно перед его применением. The production technology of the proposed composition In a very simple production environment, the well-known conventional equipment is used, the ingredients are inexpensive and non-deficient. The proposed composition can be immediately prepared in any drilling enterprise immediately before its use.
Claims (2)