Heat-indicating paper Download PDF

Info

Publication number
SU717201A1
SU717201A1 SU772558123A SU2558123A SU717201A1 SU 717201 A1 SU717201 A1 SU 717201A1 SU 772558123 A SU772558123 A SU 772558123A SU 2558123 A SU2558123 A SU 2558123A SU 717201 A1 SU717201 A1 SU 717201A1
Authority
SU
USSR - Soviet Union
Prior art keywords
coating
paper
heat
weight
sensitive
Prior art date
Application number
SU772558123A
Other languages
Russian (ru)
Inventor
Светлана Александровна Ильина
Светлана Ивановна Панасюк
Виктор Васильевич Матвеев
Любовь Ивановна Лисенкина
Наталья Алексеевна Вакулина
Нина Никитична Хлестова
Original Assignee
Предприятие П/Я А-3917
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Предприятие П/Я А-3917 filed Critical Предприятие П/Я А-3917
Priority to SU772558123A priority Critical patent/SU717201A1/en
Application granted granted Critical
Publication of SU717201A1 publication Critical patent/SU717201A1/en

Description

(54) ТЕРМОИНДЖАТОРНАЯ БУМАГА(54) THERMAL INFORMATION PAPER

Claims (3)

Изобретение относитс  к облаете измерительной техники, э именно, к Чермойнпикаторам , позвол ющим регистрировать температуру за счет видимого измененн  состо в:и  вещества, вход5гш:его в состав индшсатора, и мгжет примен тьс  в авиационной , машиностроительной ., хим1тчес- кой, радиотехнической и других отрасл х промышленности. Известна термоиндтйсаторна  бумага, содержаща  бумагу-основу и покрытие, состо щее из веществ, чувствительных к определенным температурам в интервале 62-156°С l. Покрытие изрестной бумаги состоит из дл  62°С - пальметиновой кислоты; 70°С - стеариновой кислоты и с геарата железа в соотношении. 90 С - стеариновой кислоты и стеа рата мапга  в соотношешга 1:1. ..,..,.....-400 С -стеариновой кислоты стеарат железа в сооттгошенив 5:1, 110°С-стеарата магни , -стеарата цинка и стеариновой кислоты в соотношении 1:1, 130 С - стеарата цинка, 145°С стеарата кобальта, 15 бЯз - етеарата натри . . Указанна  термоиндикаторна  бумага имеет низкую чувствительность, недостаточную точность измерени  температуры, а также низкую водо-, масло- и бензостойкость . Цель изобретени  - обеспечение возможности измерени  температур в интервале 25-70 0, повышение чувствительное-ти и .точности измерени . Поставленна  цель достигаетс  тем, что термоиндикаторное покрытие в качестве термочувствительного вещества содержит эф ры стеариновой кислоты при следуюжем соотношении компонентов ( вес%): Термочувствительное вещество7-10 Св зующее10-15 пигмент.0,01-0,15 Органи еский растворитель Остальное Толщина дтокрыти  составл ет 10 20 мкм. rioKpSffBe дбпШнительио содержит прозрачную ппенку, например из фторолона. В качестве св зующего используют фенолфЬрмаахьцегидную смолу, совмещенную с йоливинилбутирале л в этиловом спирте. В качестве бумаги-основы нсполь зуют графитированную бумагу черного цве или другую термостойкую бумагу. Термоиндикаторную бумагу готов т следующим образом 1 на бумагу-основу одним из известных способов (окунаниемв . кистью, краскораспылителем, с помощью устройс гва прижимных валков и т.п.) нанос т слой термочувствительной суспензии толщиной 10-20 мкм. После полного высыхани  термочувствительный спой пбкры вают прозрачной пленкой, например, из фгоролона.. Изобретение иллюстрируетс  следующими примерами. Пример 1. Термоиниикаторную .бумагу на 25С готов т следующим образом: бумагу-основу покрывают термочувствительной суспензией, состо щей из 8 вес.% бутилового эфира стеариновой ки лоты, 10 вес.% фенол форма ль дегидной см лы, совмещенной с попивиьшлбутиралем ,vi S2 вес.% этилового спирта. После .высыж ни  толщина покрыти  составл ет 10 мкм На покрытие нанос т слой фторолона. Пример 2. Термоиндикаторную бумагу на готов т следуютдим образом: бумагу-основу покрывают термочувствительной суспензией, состо щей из 9,94 вес.% этилового эфира стеариновой кислоты, 0,06 вес.%мётипенового голубог 13 ъес,% фенолформальдегйдной смолы, совмещенной с поливийилбутиралем, .и 77 вес.% этилового спирта. После высыхани топигана покрыти  составл ет 11 м На покрытие нанос т слой фторолона. Пример 3, Термоинднкаторную бумагу на 35 С готов  следующим обра зом; бумагу-основу. йокрываю1Т термочувствительной суспензией, состо щей из 8,40-вес.% метилового э ра стеариново кислоты, ОД вес.% бромэт лоеого синего 12,50 вес.% фенолформальдегидной смолы совмещенной с полшвинилбутиралем, и 79 вес.% этилового спирт .После высыхан тбпщина покрыти  составл ет 12 мкм,Н покрытие тшнос т слой фторолона. Пример 4. Термоиндйкаториую бумагу на 40°С готов т следующим образом: бумагу-основу покрывают термочувствительной суспензией, состогпцей из 7,8 вес.% бензилрвого эфира стеариновой кислоты, 0,15 вес.% уарамина, 14 вес.% фенолформальдегидной смолы, совмещенной с поливинилбутиралем, и 78 вес.% этилового спирта. После высыхани  толщина покрыти  составл ет 12 мкм. На покрытиенанос т слой фторолона. Пример 5. Термоиндикаторную бумагу на 5О С готов т следующим образок : бумагу-основу покрывают термочувствительной суспензией, сост о щей из S,98 вес,% фенилового эфира стеариновой кислоты, 0,01 вес. бриллиантового зеленого и 0,01 вес.% аурамина, 15 вес,% (| нолформальдегидной смолы, совмещенной споливинилбутиралем и 76 вес,% этилового спирта. После высыхани  толщина покрыTHia составл ет 15 мкм. На покрытие нанос т слой фторолона. Пример 6. Термоиндикаторную бумагу на 65°С готов т,следующим образом: бумагу-основу покрывают термочувствительной , суспензией, состо щей из 10 вес.% тристеарина, ОД вес.%метиленового голубого, 10,9 вес.% .фенолформальдеидной смолы, совмещенной с поливинил- бутиралем и 79 вес.% этилового спирта. После высыхани  толщина покрыти  составл ет 20 мкм. На покрытие нанос т.слой фгоролона,. Пример 7. Термоиндикаторную бумагу на 70°С готов т следующим образом: бумагу-основу покрывают термочувствительной суспензией, состо щей из 7.,0 вес,% этиленгликопьдистеарата, 0,03 вес.% хризоидина, 13,97 вес.% фенопформа ьдегидной смолы, совмещенной с поливинилбутиралем, и 79 вес,% этилового спирта. После высыхани  толщина покрыти  составл ет 10 мкм. На покрытие нанос т слой фгоролона. Использование термочувствительного вещества в суспензии. менее 7 вес.% не обеспечивает удовлетворительной укрывистости бумаги-основы, выше 10 вес,% увеличивает толщину сло  покрыти , чти приводит к уменьшению чувствительности термоиндикаторной бумаги. Содержащиес  в покрытии термочувствительньге ветпества способны при оп-, ределенных температурах плавитьс , обтажа  контрастную бумагу-основу. При QtdM чувствительность бумаги и точность измерени  повышаетс  за счет тонкого сло  покрыти , 571 На есеггне на покрытие прозрачной . пленки, например, из фторолоиа позвол ет повысить влаго, масло- и бензостойкость термоиндикаторной бумаги. Формула изобретени  1, Термоиндикаторна  бумага, содержаща  бумагу-основу и термоинцикаторное покрытие, состо щее из термочувствительного вещества, св зующего, пигмента и растворител , отличающа с   тем, что, с целью обеспечери  измерени  температуры в интервале 25-70, повышени  чувствительности и точности измерени , термо ндикаторное покрытрйё в качестве термочувствительного .вещества содержит эфиры стеариновой кислоты при следующем соотношении компонентов ( вес. %): 1 Те рмочувствительное вещество Св зующее 10-15 Пигмент 0,О1-ОД5 Растворитель Остальное The invention relates to the field of measuring equipment, namely, to the Chermyoinpikator that allow recording the temperature due to the visible change in: and the substance entering5: it is part of the detector, and can be used in the aeronautical, engineering, chemical, radio engineering and other industries. Thermal injection paper is known, which contains a base paper and a coating consisting of substances sensitive to specific temperatures in the range of 62-156 ° C l. The imitation paper coating consists of, for 62 ° C, palmetic acid; 70 ° C - stearic acid and iron gearate ratio. 90 C - stearic acid and stearate mapa in the ratio of 1: 1. .., .., .....- 400 C-stearic acid iron stearate in accordance with the ratio of 5: 1, 110 ° C magnesium stearate, zinc stearate and stearic acid in a ratio of 1: 1, 130 C - zinc stearate, 145 ° C cobalt stearate, 15 BZA - sodium tetarate. . This thermal indicator paper has low sensitivity, insufficient temperature measurement accuracy, as well as low water, oil and petrol resistance. The purpose of the invention is to make it possible to measure temperatures in the range of 25-70 0, to increase the sensitivity and measurement accuracy. The goal is achieved by the fact that the heat-indicating coating as a heat-sensitive substance contains the effect of stearic acid with the following ratio of components (wt%): Heat-sensitive substance 7-10 Binder 10-15 pigment 0,01-0,15 Organic solvent Remaining Thickness of cover em 10 20 microns. rioKpSffBe dbpshnitelio contains a transparent foam, for example, from fluorolone. As a binder, phenolbenyl resin is used, combined with ylivinyl butyral l in ethanol. As a base paper, black graphite paper or other heat-resistant paper is used. Heat-tracing paper is prepared as follows: 1 a layer of heat-sensitive suspension with a thickness of 10-20 microns is applied by one of the known methods (dipping, brush, spray gun, using a device of roll presses, etc.). After complete drying, the heat-sensitive coat is opened with a transparent film, for example, from folorone. The invention is illustrated by the following examples. Example 1. A 25 ° C thermal paper is prepared as follows: the base paper is coated with a heat-sensitive suspension consisting of 8 wt.% Butyl ester of stearic acid, 10 wt.% Phenol form dehydrated resin combined with water, vi S2 wt.% ethyl alcohol. After the coating, no coating thickness is 10 µm. A layer of fluorolone is applied to the coating. Example 2. Thermal indicator paper is prepared as follows: base paper is coated with a heat-sensitive suspension consisting of 9.94% by weight of ethyl ester of stearic acid, 0.06% by weight of a methyl bovine 13 kg,% of phenol-formaldehyde resin, combined with polyvinyl butyrate , and 77 wt.% ethyl alcohol. After the topigan has dried, the coating is 11 m. A layer of fluorolone is applied to the coating. Example 3, 35 ° C thermal paper is ready as follows; base paper. A 1T heat sensitive suspension consisting of 8.40% by weight methyl ester stearic acid, OD% by weight bromoethanol blue 12.50% by weight phenol-formaldehyde resin combined with half-vinyl butyral, and 79% by weight ethyl alcohol. the coating is 12 µm, H coating the thickness of the fluorolone layer. Example 4. A 40 ° C thermal paper is prepared as follows: the base paper is coated with a heat-sensitive suspension of 7.8% by weight of stearic acid benzyl ester, 0.15% by weight of uaramine, 14% by weight of phenol-formaldehyde resin, combined with polyvinyl butyral, and 78 wt.% ethyl alcohol. After drying, the coating thickness is 12 µm. On the surface a layer of fluorolon is applied. Example 5. Thermo indicator paper at 5 ° C is prepared as follows: the base paper is coated with a temperature-sensitive suspension consisting of S, 98% by weight, of stearic acid phenyl ester, 0.01% by weight. brilliant green and 0.01 wt.% auramine, 15 wt.% (| nolol formaldehyde resin combined with spolivinyl butyral and 76 wt.% ethanol. After drying, the coating thickness is 15 microns. A layer of fluorotone is applied to the coating. Example 6. Thermo Indicator The paper at 65 ° C is prepared as follows: the base paper is coated with a heat sensitive, suspension consisting of 10 wt.% tristearin, OD wt.% methylene blue, 10.9 wt.% phenol formaldehyde resin combined with polyvinyl butylurel. and 79 wt.% ethyl alcohol. After drying, the thickness of the pok The digging is 20 microns. On the coating of the deposited carbon fiber layer, Example 7. A heat treatment paper at 70 ° C is prepared as follows: the base paper is coated with a temperature-sensitive suspension consisting of 7., 0 wt.% ethylene glycol distearate, 0, 03% by weight of chrysoidin, 13.97% by weight of phenopformed dehydrogenous resin combined with polyvinyl butyral, and 79% by weight of ethanol. After drying, the coating thickness is 10 µm. A layer of fluorol is applied to the coating. The use of heat-sensitive substances in suspension. less than 7 wt.% does not provide a satisfactory hiding power of the base paper, above 10 wt.% increases the thickness of the coating layer, almost leads to a decrease in the sensitivity of thermal indicator paper. The vegetation contained in the heat-sensitive coating is capable of melting at certain temperatures, by cutting the contrasting base paper. With QtdM, paper sensitivity and measurement accuracy is enhanced by a thin coating layer, 571, which is transparent to the coating. film, for example, from fluorololium allows to increase the moisture, oil and petrol resistance of thermal indicator paper. Claim 1, Thermal indicator paper comprising a base paper and a thermal inactivator coating consisting of a temperature sensitive substance, a binder, a pigment and a solvent, in order to measure the temperature in the range of 25-70, to increase the sensitivity and accuracy of measurement thermosensitive coating as a thermosensitive substance contains esters of stearic acid in the following ratio of components (wt.%): 1 Test substance Binding 10-15 Pigment 0, O1-OD5 Solution Tel rest 2.Термоиндикаторна  бумага по п.1, отличают а  с  тем, что толщина покрыти  составл ет 10-20 мкм. 2. Thermal indicator paper according to claim 1, is distinguished by the fact that the coating thickness is 10-20 microns. 3.Термоиндикаторна  бумага по п., 1, отличаюша с   тем, что покрытие дополнительно содержит прозрачную пленку, например из фторолона. Источники информаци , прин тые во внимание при экспертизе 1, Двччэрское свидетельство СССР № 455182, кл. D 21 Н 1/40, 1968 (прототип).3. Thermal indicator paper according to claim 1, is different in that the coating additionally contains a transparent film, for example of fluorolone. Sources of information taken into account in the examination of 1, Dvchersky certificate of the USSR No. 455182, cl. D 21 H 1/40, 1968 (prototype).
SU772558123A 1977-12-23 1977-12-23 Heat-indicating paper SU717201A1 (en)