SU424826A1 - CHEMICALLY RESISTANT GLASS - Google Patents
CHEMICALLY RESISTANT GLASSInfo
- Publication number
- SU424826A1 SU424826A1 SU1757128A SU1757128A SU424826A1 SU 424826 A1 SU424826 A1 SU 424826A1 SU 1757128 A SU1757128 A SU 1757128A SU 1757128 A SU1757128 A SU 1757128A SU 424826 A1 SU424826 A1 SU 424826A1
- Authority
- SU
- USSR - Soviet Union
- Prior art keywords
- chemically resistant
- resistant glass
- glass
- bao
- liao
- Prior art date
Description
1one
Изобретение относитс к составам стекол, используемым в электровакуумной промышленности .This invention relates to glass formulations used in the electrovacuum industry.
Известно химически стойкое стекло, включающее SiO2, АЬОз, ВаОз, ВаО, Na2O, KzO, LiaO.A chemically resistant glass is known, including SiO2, ABO3, BaO3, BaO, Na2O, KzO, LiaO.
Цель изобретени - повысить радиационную устойчивость стекла.The purpose of the invention is to increase the radiation resistance of glass.
Достигаетс это тем, что оно дополнительно содержит C&zOs при следующем соотношении компонентов, вес. %:This is achieved by the fact that it additionally contains C & zOs in the following ratio of components, weight. %:
SiOa 65-70; AlgOs 7-10; ВаОз 15-18; ВаО 2-3; NazO 1,5-3,0; КаО 1,5-3,0; LiaO 0,5- 1,5; Се20зО,5-1,5.SiOa 65-70; AlgOs 7-10; BaOz 15-18; WAO 2-3; NazO 1.5-3.0; Kao 1.5-3.0; LiaO 0.5-1.5; Se20zO, 5-1,5.
Пример. Предлагаемое стекло содержит следующие компоненты, вес. % SiOa - основа; АШз 8,0; БаОз 18,0; ВаО 3,0; ЫагО 3,0; КгО 3,0; LiaO 0,7; C&zOs 0,7.Example. The proposed glass contains the following components, weight. % SiOa - basis; ASH 8.0; BaOz 18.0; BAO 3.0; Yo 3.0; CgO 3,0; LiaO 0.7; C & zOs 0.7.
Стекло обладает следующими свойствами: Температура варки, °С 1500-1550 Температура разм гчени , °С575Glass has the following properties: Cooking temperature, ° C 1500-1550 Softening temperature, ° С575
Температура отжига, °СAnnealing temperature, ° С
верх.510top.510
нижн.410bottom.410
Коэффициент термического расширени Thermal expansion coefficient
а 20-300°С 1/град52-10Термостойкость , °Сне менее 200a 20-300 ° С 1 / grad52-10Thermost resistance, ° Sne less than 200
Химическа устойчивость соответствует 1 гидравлическому классу.Chemical stability corresponds to 1 hydraulic class.
На чертеже изображены кривые спектрального пропускани описываемого стекла до и после облучени .The figure shows the spectral transmission curves of the described glass before and after irradiation.
Предмет изобретени Subject invention
Химически стойкое стекло, включающее SiOa, АЬОз. ВзОз, ВаО, NaoO, , Li-O, отличающеес тем, что, с целью повышени радиационной устойчивости, оно дополнительно содержит СеоОз при следующем соотношении jvOMiioHCHTOB, вес. %; SiO2 - 65-70; А1,О, - 7-10; В,0з - 15,0-18,0; ВаО - 2,0-3.0; ЫаЮ - 1,5-3,0; - 1,5-3,0; LhO - 0,5-1.5; СеоОз - 0,5-1,5.Chemically resistant glass, including SiOa, ABOZ. VaOz, BaO, NaoO,, Li-O, characterized in that, in order to increase the radiation stability, it additionally contains SeOOz in the following ratio jvOMiioHCHTOB, weight. %; SiO2 - 65-70; A1, O, 7-10; B, 0h - 15.0-18.0; BaO - 2.0-3.0; NaYu - 1.5-3.0; - 1.5-3.0; LhO - 0.5-1.5; SeoOz - 0.5-1.5.
34D3605SIJ Ш Ш VW Ш 48П 5Bli34D3605SIJ W W VW W 48P 5Bli