SU393224A1 - ENAMEL - Google Patents
ENAMELInfo
- Publication number
- SU393224A1 SU393224A1 SU1498691A SU1498691A SU393224A1 SU 393224 A1 SU393224 A1 SU 393224A1 SU 1498691 A SU1498691 A SU 1498691A SU 1498691 A SU1498691 A SU 1498691A SU 393224 A1 SU393224 A1 SU 393224A1
- Authority
- SU
- USSR - Soviet Union
- Prior art keywords
- enamel
- sro
- cao
- na2sif6
- moos
- Prior art date
Description
1one
Изобретение относитс к составу эмали дл антикоррозионной защиты химической аппаратуры .This invention relates to an enamel composition for anti-corrosion protection of chemical apparatus.
Известна эмаль, включающа SiOs, ВгОз, ZrOz, NaaO, LigO, NaaSiFg, CaO, SrO, МоОзС целью расширени интервала обжига эмаль содержит указанные компоненты в следующих количествах (вес. %):The enamel is known, including SiOs, BrOz, ZrOz, NaaO, LigO, NaaSiFg, CaO, SrO, MoOsC with the aim of extending the burning interval the enamel contains these components in the following amounts (wt.%)
53-58 0,1-4 12-17 7-19 2-5 3-6 53-58 0.1-4 12-17 7-19 2-5 3-6
s . 1-6 0,1 - 10 0,1-2s. 1-6 0.1 - 10 0.1-2
е того,e addition
0,1-3 До 0,50.1-3 To 0.5
В таблице приведены основные свойства предлагаемой эмали.The table shows the main properties of the proposed enamel.
В качестве примера может быть приведен следующий состав: SiO2 - 54,9; В2Оз - 2,0; ZrOa-12,7; Na2O-9,2; Li2O-4,0; Na2SiF6- 4,6; CaO-1,9; SrO -6, МоОз-1,0; SO3 - 2,5; АЬОз -0,5.As an example, the following composition can be given: SiO2 - 54.9; B2O3 - 2.0; ZrOa-12,7; Na2O-9.2; Li2O-4.0; Na2SiF6- 4.6; CaO-1,9; SrO-6, MoOS-1.0; SO3 - 2.5; HOS = -0.5.
Дл изготовлени эмалевого шликера используют гранул т, содержащий 100 вес. ч.For the manufacture of the enamel slip, granulate containing 100 wt. h
эмали, 2,0 вес. ч. окиси хрома, 3,0 вес. ч. глины глуховской, 0,1 вес. ч. молибденовокислого аммони и 40 вес. ч. воды.enamel, 2.0 wt. including chromium oxide, 3.0 weight. including clay Glukhovsky, 0.1 weight. including ammonium molybdate and 40 wt. h of water.
ТаблицаTable
10ten
1515
Предмет изобретени Subject invention
Эмаль, включающа Si02, ВаОз, ZrO2, Na2O, Li2O, Na2SiF6, CaO, SrO, МоОз, отличающа с тем, что, с целью расширени интервала обжига, она содержит указанные компоненты в следующих количествах (вес. %):Enamel, including SiO2, BaO3, ZrO2, Na2O, Li2O, Na2SiF6, CaO, SrO, MOOZ, characterized in that, in order to extend the burning interval, it contains these components in the following amounts (wt.%):
SiO253-58SiO253-58
В2Оз0,1-4B2Oz0,1-4
ZrO212-17ZrO212-17
Na2O7-19 3 Li20 2-5 NasSiFe 3-6 СаО 1-6 SrO 0,1-10 393224 4 МоОз 0,1-2 и, кроме того, 5Оз 0,1-3 АЬОз До 0,5Na2O7-19 3 Li20 2-5 NasSiFe 3-6 CaO 1-6 SrO 0.1-10 393224 4 MoOs 0.1-2 and, moreover, 5Oz 0.1-3 AlO3 To 0.5