SU381702A1 - METAL-CERAMIC MATERIAL BASED ON BORID - Google Patents
METAL-CERAMIC MATERIAL BASED ON BORIDInfo
- Publication number
- SU381702A1 SU381702A1 SU1711344A SU1711344A SU381702A1 SU 381702 A1 SU381702 A1 SU 381702A1 SU 1711344 A SU1711344 A SU 1711344A SU 1711344 A SU1711344 A SU 1711344A SU 381702 A1 SU381702 A1 SU 381702A1
- Authority
- SU
- USSR - Soviet Union
- Prior art keywords
- metal
- ceramic material
- borid
- material based
- aluminum
- Prior art date
Description
1one
Изобретение относитс к металлокерамическим огнеупорным материалам, которые могут быть использованы в технике высоких температур в качестве материала дл испарительных элементов.This invention relates to cermet refractory materials that can be used in high temperature engineering as a material for evaporation elements.
Известен металлокерамически материал на основе борида титана, содержащий 10-85% нитрида бора.Metal-ceramic material based on titanium boride containing 10-85% boron nitride is known.
С целью повышени стойкости к тепловым ударам, удельного сопротивлени и устойчивости по отношению к расплавленному алюминию и его парам в предлагаемый металлокерамический материал введены карбид бора и алюминий при следуюшем соотношении компонентов (в вес. %):In order to increase resistance to thermal shock, resistivity and resistance to molten aluminum and its vapors, boron carbide and aluminum are introduced into the metal-ceramic material, with the following ratio of components (in wt.%):
Нитрид бора15-40Boron nitride15-40
Карбид бора15-20Carbide boron15-20
Алюминий10-20Aluminum10-20
Борид титанаостальноеBoride titan
Дл получени описываемого материала подвергают гор чему прессованию смесь порошков борида титана, нитрида бора, карбида бора и алюминиевой пудры в графитовых пресс-формах при температуре 1900°С, давле2To obtain the described material, a mixture of titanium boride powders, boron nitride, boron carbide and aluminum powder in graphite molds at a temperature of 1900 ° C, pressure is subjected to hot pressing.
Н1ИИ 200 кг/см н времени NIIII 200 kg / cm N time
выдерлчки 15- 20 мин.Release time 15–20 min.
Указанный металлокерамический материал имеет следующие свойства: термостойкость (1500-20°С) 30 тенлосмен (без разрушени ), удельное электросопротивление 2500 мком-см, стойкость по oтнooJeнию к алюминию и его парам - 1500°С, 10 час, не взаимодействует.The specified cermet material has the following properties: heat resistance (1500–20 ° C) 30 tenlomans (without destruction), electrical resistivity 2500 µm-cm, resistance to aluminum and its pairs - 1500 ° C, 10 hours, does not interact.
10ten
Предмет пзобретени Subject matter
Металлокерамический материал на основе борида титана, содержащий нитрид бора, отличающийс тем, что, с целью повышени стойкости к тепловым здарам, удельного сопротивлени и устойчивости по отношению к расилавленному алюминию и его парам, в Hiero введены карбид бора и алюминий приA titanium boride metal-ceramic material containing boron nitride, characterized in that, in order to increase resistance to heat, resistivity and resistance to fermented aluminum and its vapors, boron carbide and aluminum are introduced into Hiero
следующем next
соотношенииratio
компонентов ( в вес. %):components (in wt.%):
Нитрид бора Boron nitride
15-40 Карбид бора 15-40 Boron carbide
15-20 Алюминий15-20 Aluminum
10-2010-20
Борид титанаBorid titanium
остальноеrest