SU1594196A1 - Liquid footwear polish - Google Patents

Abstract

The invention relates to household chemicals, in particular to polishing compositions intended for the care of leather products. The invention allows to improve the water barrier properties of the film by using a composition containing, in wt%: montan wax 2.0-6.0, ceresin or paraffin 2.0-6.0, oxidized polyethylene wax 1.0-3.0 , diethylethanolamine 1.6-3.6, stearic acid 1.0-5.0, ethylene glycol or polyethylene glycol 1.0-5.0, tetrabutoxytitanium 1.0-3.0, turpentine or white spirit 10.0-30, 0 polyethylsiloxane liquid 0.5-1.5, dye 0.003-0.04, perfume 0.1-0.3, water - the rest. 2 tab.

Description

The invention relates to household chemicals, in particular to polishing compositions intended for the care of leather products.

The purpose of the invention is to improve the waterproof properties of the film.

The cream is prepared as follows.

Weights of wax, stearic acid, dye are melted in a heated tank equipped with a stirrer at 105t5 C. After melting, the mixture is stirred for another 10-15 minutes, after which the solvent is added. The temperature of the mass is maintained within 90 ± 5 ° C. After mixing for 5-10 minutes, TBT, PES-4, amine, ethylene glycol are added, the mass is stirred for 5-10 minutes, after which water heated to 95t5 is added. - heat mass. One third of the water is poured slowly, in small portions.

and the rest is uninterrupted. After the water has been injected, the emulsion is immediately cooled and a perfume is added at 50 ± 5 ° C.

The compositions of the liquid cream are given in table. one.

To determine the water-repellent properties (hydrophobicity of the film), the chromic leather substrate with an emulsion coating is treated with the test cream and after 20-24 hours the wetting angle is measured on the device for determining the wetting angle. The stability of the agent is determined by an accelerated method: by centrifuging for 10 minutes at 6000 rpm (method AS-nffi 1290-57). Emulsions that are not delaminating when they are being tested on a centrifuge are considered resistant.

ate

Epesk film units scales

Film accumulation, mg / cm. Film water resistance, G score, film idiophobicity, hail. Stability means consistency means

The elasticity of the film, the number of bends

17

a, 6

100 87 on

56

1712

0.90,8

10080

8982

Unstable Liquid

54. 50

Claims (1)

Claim .15 Liquid shoe polish containing montan wax, ceresin or paraffin, oxidized polyethylene wax, turpentine or white spirit, diethylethanolamine, stearic acid, ethylene glycol-20 or propylene glycol and water, in order to improve the water protective properties films, tetrabutoxytitanium, polyethylsiloxane liquid, dye and perfume in the following ratio of components, wt.%. Montana wax 2.0-6.0 Ceresin or Paraffin 2.0-6.0 Oxidized Polyethylene Wax 1.0-3.0 Diethylethanolamine 1.6-3.6 Stearic acid 1.0-5.0 Ethylene glycol or propylene glycol 1,0-5,0 Tetrabutoxytitanium 1.0-3.0 Turpentine or Whitespirit 10.0-30.0 Polyethylsiloxane liquid 0.5-1.5 Dye 0,003-0,4 Odorant 0.1-0.3 Water · Rest Table 1 Component Massive composition, ratio % for and.... 3 Montana wax "Varadur E" or modified montan wax "E" 2.0 4.0 6.0 Oxidized polyethylene wax B-262, B-233 1.0 2.0 3.0 ~ 75.80 Ceresin marks or marks in paraffin oil _of B _2, ^B 3 ^"B +" ^T 2.0 4.0 6.0 Stearic acid technical 1.0 3.0 5.0 · Diethylethanolamine 1.6 2.6 3.6 Polyethylsiloxane liquid 0.5 1.0 1.5 ^; Tetrabutoxytitanium 1.0 2.0 3.0 Ethylene glycol or propylene. glycol 1.0 3.0 5.0 Turpentine or white spirit (nefras C4-155 / 200) 10.0 20.0 30.0 Dye 0,003 0.5 0.1 Odorant 0.1 0.2 0.3 Water Rest 1594196 < table 2 Indicators for composition Specifications one 2 3 Base an object Glitter film unit scales sixteen 17 17 12 Dust accumulation film mg / cm ² 0.6 0.6. 0.9 0.8 Water resistance of the film, score 100 100 100 80 Film hydrophobicity, hail. 89 87 89 82 Means stability Stable Unstable Consistency means Liquid Liquid The elasticity of the film, bend 56 56 54. 50