SU1497192A1 - Polymeric composition - Google Patents
Polymeric composition Download PDFInfo
- Publication number
- SU1497192A1 SU1497192A1 SU874290699A SU4290699A SU1497192A1 SU 1497192 A1 SU1497192 A1 SU 1497192A1 SU 874290699 A SU874290699 A SU 874290699A SU 4290699 A SU4290699 A SU 4290699A SU 1497192 A1 SU1497192 A1 SU 1497192A1
- Authority
- SU
- USSR - Soviet Union
- Prior art keywords
- polyolefin
- stabilizer
- coal
- liquid product
- thermal stability
- Prior art date
Abstract
Изобретение относитс к области стабилизации полиолефинов. Изобретение позвол ет повысить термостабильность полиолефинов (температура начала разложени стабилизированного полиэтилена и полипропилена, определенна методом ТГА, повышаетс на 59-61°С по сравнению с нестабилизированными полимерами), что достигаетс использованием композиции, содержащей полиолефин и стабилизатор - жидкий продукт суперкритического растворени угл при следующем соотношении компонентов, мас.%: полиолефин 90-95, жидкий продукт суперкритического растворени угл 5-10. 1 табл.This invention relates to the field of stabilizing polyolefins. The invention improves the thermal stability of polyolefins (the temperature of the onset of decomposition of stabilized polyethylene and polypropylene, determined by TGA, increases by 59-61 ° C compared to unstabilized polymers), which is achieved using a composition containing polyolefin and stabilizer - a liquid product of supercritical carbon dissolution with the following component ratio, wt.%: polyolefin 90-95, liquid product of supercritical dissolution of coal 5-10. 1 tab.
Description
(Л(L
сwith
Изобретение относитс к переработке и эксплуатации пластмасс, и касаетс стабилизированных композиций на основе полиолефинов.The invention relates to the processing and operation of plastics, and relates to stabilized polyolefin-based compositions.
Цель изобретени - повьшение термостабильности .The purpose of the invention is to increase the thermal stability.
В качестве стабилизатора используют жидкий продукт, полученный в ре- з ьтате суперкритического растворени угл (СКР).A liquid product obtained as a result of supercritical carbon dissolution (SCR) is used as a stabilizer.
Полученный продукт представл ет собой жидкую в зкую смолу (кинематическа в зкость при равна 1,1 Ю ) со средней мол.м. 250- 350, раствор ющуюс в хлороформе, спиртах, тетрагидрофуране, пиридине, и нераствор ющуюс в воде, содержащую парамагнитные частицы ( л 10 сп/г 1The resulting product is a liquid viscous resin (kinematic viscosity at 1.1 U) with an average mol.m. 250-350, dissolved in chloroform, alcohols, tetrahydrofuran, pyridine, and water-insoluble, containing paramagnetic particles (l 10 jp / g 1
Групповой состав, %:Group composition,%:
Мальтены 80-85Maltena 80-85
Ас.фапьтены 6-10AS.Faptyena 6-10
Предасфальтены ОстальноеPredasphaltes Rest
Мальтены - пентано-растворима часть смолы, остаток представл ет собой смесь асфальтенов и предасфаль- тенов, из которой в аппарате Соксле- та толуолом можно экстрагировать ас- фальтены.Maltenes - pentano-soluble part of the resin, the residue is a mixture of asphaltenes and pre-asphaltenes, from which asphalthenes can be extracted with toluene in the Soxlet apparatus.
Элементный состав, %: С 78-79; Н 8,5-9,5; S + N 1; О - остальное.The elemental composition,%: C 78-79; H 8.5-9.5; S + N 1; Oh - the rest.
Фракционный состав.Fractional composition.
н.к. 20Ь°С - бензинова фракци (10-15%);nk 20 ° C - gasoline fraction (10-15%);
200-250 с - керосинолигроинова фракци (40-45%);200-250 s - kerosene oligroin fraction (40-45%);
Больше - мазутна фракци (остальное). More - fuel oil fraction (the rest).
Ароматичность по данным ПНР (отношение числа ароматических протонов, к общему числу протонов) равна 40и CD Aromaticity according to the NDP data (the ratio of the number of aromatic protons to the total number of protons) is 40 and CD
ts9ts9
314314
50%. Данные свидетельствуют о содержании в основном производных бензола , т.е. одно дерной ароматики. Степень замещени в кольце равна 60-70%. Жидкий продукт (ж.п.) СКР угл ввод т в полимер в количестве 5-10 мас.% путем смешени его с полимером в совместном растворителе, после отгонки которого и высушива- ни смеси до посто нной массы провод т съемку дериватограмм и определение физико-механических показателей.50%. The data indicate the content mainly of benzene derivatives, i.e. one scent aroma. The degree of substitution in the ring is 60-70%. The liquid product (g.) Of the CRS coal is introduced into the polymer in an amount of 5-10 wt.% By mixing it with the polymer in a co-solvent, after which is distilled off and the mixture is dried to constant weight, the derivatograms are taken and the physical -mechanical indicators.
Изобретение иллюстрируетс следующими примерами.The invention is illustrated by the following examples.
Пример 1, Полипропилен (ПП). Навеску ж.п. СКР угл раствор ют в хлороформе, нанос т на порошок ПП при непрерывном перемешивании, испар ют избыток збтороформй, после чего образец высушивают в вакуумном су- шиJзьнoм шкафу при 50 С до постоййЯой массы.Example 1, Polypropylene (PP). Hitch w. The CRS of the coal is dissolved in chloroform, applied to the PP powder with continuous stirring, the excess of bthoroform is evaporated, after which the sample is dried in a vacuum dried cabinet at 50 ° C to a constant mass.
П р и м е р 2. Полиэтилен высокого давлени (ПЭВД). 5 г ПЭВД и соот- бетствукш ую навеску ж.п. СКР угл раствор ют до полного растворени в 200 мл кип щего октана, раствор выливают на стекло и после испарени на воздухе растворител образец досуши- вают до посто нной массы в вакуумном сушильном шкафу при .PRI mme R 2. High pressure polyethylene (LDPE). 5 g LDPE and corresponding sockets The carbon CRS is dissolved until completely dissolved in 200 ml of boiling octane, the solution is poured onto glass, and after the solvent is evaporated in air, the sample is dried to constant weight in a vacuum oven at.
Композиции полимеров с промышленными стабилизаторами готов т анапо-Polymer compositions with industrial stabilizers are prepared by anapo-
н.а. - нефт ные асфальтеныon. - oil asphaltenes
2424
гично, т.е. путем смешивани полимера и стабилизатора в совместном растворителе .gich, i.e. by mixing the polymer and stabilizer in a co-solvent.
Повьш1ение термостабипьности показано в р де примеров методом термографии . Навеску образца (50 кг) помещают в прибор Дериватограф, нагревание провод т на воздухе со скоростью подъема температуры 5 С/мин.Thermal stability is shown in a number of examples by thermography. A sample of the sample (50 kg) is placed in the device derivatograph, heating is carried out in air at a rate of temperature rise of 5 C / min.
Образцы дл измерени прочности при раст жении ( р) готов т на установке дл определени показател текучести расплава термопластов ИИРТ-М путем продавливани массы полимера или композиции его со стабилизатором через отверсти диаметром 2 мм, при 230°С дл ПП (груз ,16 кгс) и при 190 С дл ПЭВД (груз 2,16 кгс). Полученные образцы в виде прутков ° предварительно взвешивают и определ ют показатель текучести расплава (ПТР), затем разрывают на разрывной машине ЕМУ-005-1. при скорости раздви- жени захватов 10 мм/мин. Температуру разм гчени по ВИКа (Tg) определ ют по стандартной методике (ГОСТ 11088-83) по скорости подъема температуры и нагрузке 10 н.Samples for measuring tensile strength (p) are prepared at the facility for determining the melt flow index of thermoplastic IIRT-M thermoplastic materials by pushing the polymer mass or its composition with a stabilizer through 2 mm diameter holes at 230 ° C for PP (load, 16 kgf) and at 190 ° C for LDPE (load 2.16 kgf). The obtained samples in the form of rods, ° C, are pre-weighed and the melt flow rate (MFR) is determined, then ruptured on an EMU-005-1 tensile testing machine. with a gripping speed of 10 mm / min. The softening temperature of the PIC (Tg) is determined by the standard method (GOST 11088-83) according to the rate of temperature rise and the load of 10 n.
Термостабильность и некоторые физико-механические свойства исследуемых образцов приведены в таблице.Thermal stability and some physicomechanical properties of the studied samples are shown in the table.
5 14971926 ,5 14971926,
Claims (1)