SU1350147A1 - Method of preparing composition for coating sports grounds - Google Patents
Method of preparing composition for coating sports grounds Download PDFInfo
- Publication number
- SU1350147A1 SU1350147A1 SU864003625A SU4003625A SU1350147A1 SU 1350147 A1 SU1350147 A1 SU 1350147A1 SU 864003625 A SU864003625 A SU 864003625A SU 4003625 A SU4003625 A SU 4003625A SU 1350147 A1 SU1350147 A1 SU 1350147A1
- Authority
- SU
- USSR - Soviet Union
- Prior art keywords
- mixture
- temperature
- composition
- rubber
- crumb
- Prior art date
Abstract
Изобретение относитс к области строительных материалов и может быть использовано при изготовлении покрытий спортивных площадок, теннисных кортов, а также покрытий дорог. Цель изобретени - повьшение трещиностой- кости при резких колебани х температуры и температуростойкости покрыти .- Композицию дл покрыти спортивных площадок готов т путем смешени стекловолокна , обработанного олигоэфир- акрилатом с нагретым битумом и со смесью минерального порошка с 46,5- 53,0% резиновой крошки от общего ее количества. Затем смесь выдерживают при в течение 4,5-5,5 ч, охлаждают и ввод т в нее смесь песка с оставшейс резиновой крошкой. После этого осуществл ют окончательное перемешивание . Композици содержит 1,9- 3,1 мас.% битума, 9,4-10,8 мас.% стекловолокна , 7,0-10,0 мас.% олигоэфир- акрилата, 36,1-39,7 мас.% резиновой крошки, 8,6-14,0 мас.% минерального порошка и 28,0-30,6 мас.% песка. Отношение 6 изг изменении температуры от -40 до (20 циклов) к (Л при 86-90-10- туростойкость 0,83-0,88. 2 табл. %, темпера- -j СО СП 4 The invention relates to the field of building materials and can be used in the manufacture of sports fields, tennis courts, and road surfaces. The purpose of the invention is to increase the fracture toughness with sharp fluctuations in temperature and temperature resistance of the coating. Composition for covering sports grounds is prepared by mixing fiberglass treated with oligoester acrylate with heated bitumen and a mixture of mineral powder from 46.5-53.0% rubber crumbs from its total. The mixture is then kept for 4.5-5.5 hours, cooled, and a mixture of sand with the remaining crumb rubber is introduced into it. Thereafter, final mixing is carried out. The composition contains 1.9–3.1 wt.% Bitumen, 9.4–10.8 wt.% Glass fiber, 7.0–10.0 wt.% Oligoester-acrylate, 36.1–39.7 wt.% rubber crumb, 8.6-14.0 wt.% mineral powder and 28.0-30.6 wt.% sand. The ratio of 6 of the change in temperature from -40 to (20 cycles) to (L at 86-90-10-torsional resistance 0.83-0.88. 2 tab.%, Temperature- -j CO SP 4
Description
1one
Изобретение относитс к строительным материалам и может быть использовано при изготовлении локрытий спор- .тийных площадок, теннисных кортов, а .также покрытий дорог.The invention relates to construction materials and can be used in the manufacture of lokryti sportiynyh sites, tennis courts, as well as road pavement.
Целью изобретени вл етс повьгие- ние трещиностойкости при резких колебани х температуры и температуростой- коети покрыти .The aim of the invention is to increase the crack resistance with sharp fluctuations in temperature and temperature resistance of the coating.
Способ осуществл етс следующим образом.The method is carried out as follows.
Стекловолокно обрабатывают олиго- эфиракрилатом и ввод т в нагретый битум. В эту смесь ввод т минеральны порошок, перемешанный с частью резиновой крошки. Смесь выдерживают при lAO-lGO C в течение 4,5-5,5 ч. Это приводит к протеканию химических превращений, св занных с процессами полимеризации и сополимеризации оли- гоэфиракрилата, с частичной иммоби1350147 . 2The fiberglass is treated with oligo ether acrylate and introduced into the heated bitumen. Mineral powder mixed with a part of rubber crumb is introduced into this mixture. The mixture was incubated at lAO-lGO C for 4.5-5.5 h. This leads to chemical transformations associated with the processes of polymerization and copolymerization of the oligomerically acrylate, with partial immobilization 1350147. 2
лизацией битумных радикалов. Затем смесь охлаждают до 95--105 С и ввод т. в нее смесь песка с оставшейс частью резиновой крошки.lithization of bituminous radicals. The mixture is then cooled to 95-105 ° C and a mixture of sand and the remaining part of the rubber crumb is introduced into it.
Поэтапное введение резиновой крошки позвол ет повысить ее содержание в композиции при меньшем содержании битума. The phased introduction of crumb rubber makes it possible to increase its content in the composition with a lower bitumen content.
Q Дл изготовлени покрыти используют следующие материсшы: битум БНД 90/30, стекловолокно, олигозфиракри- лат марки (продукт олигоконден- . сации три-этиленгликол , фталевого ан15 гщт,рида и метакриловой кислоты), минеральный порошок - перлит с удельной поверхностью 2000 , резинова крошка, песок кварцевыйQ For the manufacture of the coating, the following materials are used: BND 90/30 bitumen, fiberglass, oligosphyracrylate brand (an oligocondensate product of tri-ethylene glycol, phthalic antioxidant, read and methacrylic acid), mineral powder - perlite with a specific surface 2000, rubber crumb, quartz sand
2020
Примеры конкретного выполнени способа и. свойства получаемого порошка приведены в табл. 1 и 2. ( .. . Examples of a specific implementation of the method and. the properties of the obtained powder are given in table. 1 and 2. (...
( 1,99,4.7,0К.,О21,0 (53)18,728,01604,595(1,99,4.7,0К., О21,0 (53) 18,728,01604,595
г 2,,710,28,511,119,2- (44./) 15,029,31305,0100 g 2, 710,28,511,119,2- (44./) 15,029,31305,0100
3 3,110,810,88,616,8(46,5)19,330,61405,5ld53 3,110,810,88,616,8 (46,5) 19,330,61405,5ld5
, ,
86 87 90 0,83 0,85 0,8886 87 90 0.83 0.85 0.88
6 .106-10
138138
850850
6,2-10 6,7-106.2-10 6.7-10
140 146140 146
860 870860 870
0,0041 0,0041 0-,00420.0041 0.0041 0-, 0042
4,44.4
4,4 4,54.4 4.5
Примеры конкретного выполнени способа и. свойства получаемого порошка приведены в табл. 1 и 2. ( .. . Examples of a specific implementation of the method and. the properties of the obtained powder are given in table. 1 and 2. (...
Т блнца IT blint I
47 0,3647 0.36
6,2-10 6,7-105 3,9-106.2-10 6.7-105 3.9-10
140 146140 146
860 870860 870
4,4 4,54.4 4.5
Как видно из приведенных данных, покрытие, полученное по предлагаемому способу, обладает высокой трещино- стойкостью при резких колебани х температуры , а также высокой температу- ростойкостью.As can be seen from the above data, the coating obtained by the proposed method has a high crack resistance with sharp temperature fluctuations, as well as high temperature resistance.
Claims (1)