SU117808A1 - Heat resistant acid resistant solder - Google Patents
Heat resistant acid resistant solderInfo
- Publication number
- SU117808A1 SU117808A1 SU592123A SU592123A SU117808A1 SU 117808 A1 SU117808 A1 SU 117808A1 SU 592123 A SU592123 A SU 592123A SU 592123 A SU592123 A SU 592123A SU 117808 A1 SU117808 A1 SU 117808A1
- Authority
- SU
- USSR - Soviet Union
- Prior art keywords
- resistant
- solder
- acid
- heat
- heat resistant
- Prior art date
Description
Кислотостойких и жаропрочных припоев дл пайки деталей реактивных двигателей из нержавеющей, жаропрочной и кислотоупорной сталей , удовлетворительно работающих, в насто щее врем нет.Acid-resistant and heat-resistant solders for soldering jet engine parts made of stainless, heat-resistant and acid-resistant steels, which work satisfactorily, are not currently available.
Предлагаемый жаропрочный и кислотостойкий припой содержит марганца 20-30%, хрома 6-12%, кремни 0,5-1,5%, молибдена 0,5- 0,7%, остальное количество составит никель. Т. пл. припо 1140-1160°.The proposed heat-resistant and acid-resistant solder contains manganese 20-30%, chromium 6-12%, silicon 0.5-1.5%, molybdenum 0.5-0.7%, the remaining amount will be nickel. T. pl. Solder 1140-1160 °.
Длительна 100-часова прочность соединений из нержавеющей стали марки XI18H9T, па нных этим припоем при 800 и 850°, соответственно равна 6 и 4 кг/мм.The durability of the 100-hour strength of stainless steel XI18H9T joints brazed with this solder at 800 and 850 °, respectively, is 6 and 4 kg / mm.
Описываемый припой пригоден дл пайки нержавеющих, кислотоупорных и жаропрочных сплавов, длительно работающих при температурах до 850° в среде азотной кислоты и других.The described solder is suitable for soldering stainless, acid-resistant and heat-resistant alloys, which work for a long time at temperatures up to 850 ° in the medium of nitric acid and others.
Предмет изобретени Subject invention
Жаропрочный кислотостойкий припой на никелевой основе, состо щий из марганца, хрома, кремни и молибдена, отличающийс 1ем,что дл получени припо , пригодного к длительной работе в агрессивной среде при температуре в пределах вОО-850°, устанавливают нижеследующий состав припо в процентах: марганца 20-30; хрома 6- 12; кремни 0,5-1,5; молибдена 0,5-0,7 и остальное количество составл ет никель.A heat-resistant, nickel-based, acid-resistant solder consisting of manganese, chromium, silicon and molybdenum, characterized by 1 that, in order to obtain a solder suitable for long-term operation in an aggressive environment at a temperature of BOO-850, the following composition of solder is established in percent: 20-30; chromium 6-12; silicon 0.5-1.5; molybdenum is 0.5-0.7 and the remainder is nickel.