SU1134575A1 - Composition for activating surface of products of polymer of formaldehyde with dioxolane - Google Patents
Composition for activating surface of products of polymer of formaldehyde with dioxolane Download PDFInfo
- Publication number
- SU1134575A1 SU1134575A1 SU823572435A SU3572435A SU1134575A1 SU 1134575 A1 SU1134575 A1 SU 1134575A1 SU 823572435 A SU823572435 A SU 823572435A SU 3572435 A SU3572435 A SU 3572435A SU 1134575 A1 SU1134575 A1 SU 1134575A1
- Authority
- SU
- USSR - Soviet Union
- Prior art keywords
- composition
- products
- formaldehyde
- dioxolane
- acid
- Prior art date
Abstract
СОСТАВ ДЛЯ АКТИВАЦИИ ПОВЕРХНОСТИ ИЗДЕЛИЙ ИЗ ПОЛИМЕРА ФОРМАЛЬДЕГИДА С ДИОКСОЛАНОМ, включающий ортофосфорную кислоту, отличающийс тем, что, с целью повышени клеевой способности, состав дополнительно содержит метилвисшет при следующем соотношении компонентов, мае.ч.: Ортофосфорна кислота 99-100 Метилвиолет0,9-1,1COMPOSITION FOR ACTIVATION OF THE SURFACE OF PRODUCTS FROM FORMALDEHYDE POLYMER WITH DIOXOLAN, including orthophosphoric acid, characterized in that, in order to increase the adhesiveness, the composition additionally contains a methyl compound in the following ratio of components, wt. ,one
Description
СОWITH
ел ate
СП I113 Изобретение касаетс разработки состава дл активации поверхности изделий из полимерных материалов на основе формальдегида с диоксоланом перед склеиванием, окрашиванием, металлизацией . Состав может быть использован в различных област х техники дл придани поверхности изделий смачиваемости, высоких адгезионных свойств. Известен состав дл травлени полиолефинов , содержащий перманганат кали с 0,5-1,0 вес.% перекиси марганца или нитрата магни С13. Недостатком известного состава вл етс отсутствие смачиваемости поверхности изделий из полимера формальдегида с диоксоланом, смачиваемость остаетс равной смачиваемости поверхности исходных образцов, отсут ствует взаимодействие кислого раство ра перманганата кали с поверхностью сополимера формальдегида. Высока агрессивность раствора способствует перетравливанию поверхности, по вл ютс трещины. Адгезионна способност поверхности, выражающа с в изменении прочности клеевых соединений (от рыв-отдир) пластмасса-металл, неудовлетворительна , Наиболее близким к изобретению вл етс состав дл активации поверх ocти пластифицированных эластомеров на основе формальдегида с диоксолано содержащий ортофосфорную кислоту 2 Недостатком его вл етс нестабильна смачиваемость поверхности изделий из полиформальдегида и его сополимеров. По истечении определенного времени смачиваемость уменьшаетс , ухудшаетс адгезионна способность поверхности. Цель изобретени - повышение клее вой способности, а именно создание,с става дл активации поверхности изделий из полимера формальдегида с ди оксоланом, обеспечивающего смачиваемость поверхности изделий, повышение адгезионной способности и тем самым обеспечение высокой прочности склеивани изделий из полимера формальдегида с диоксоланом - металл. Поставленна цель достигаетс тем что состав дл активации поверхности изделий из полимера формальдегида с диоксоланом, включакнций ортофосфорну кислоту, дополнительно содержит мети виолет при следующем соотношении компонентов , мае,ч,: Кислота ортофосфорна концентрированна 99-100 Метилвиолет0,9-1,1 Введение в ортофосфорную кислоту метилвиолета способствует повышению смачиваемости, обеспечивает стабильность ее во времени, увеличивает адгезионную способность поверхности издели из ацетальных смол. Приготовление активирующего раствора осуществл ют при комнатной температуре путем введени в концентрированную ортофосфорную кислоту Метил- виолета, перемешивани и нагревани до 50-60 С, В приготовленный таким образом раствор загружают зашкуренные абразивной шкуркой и промытые проточной водой издели из ацетальных смол и выдерживают их в нем 2-3 мин, По истечении указанного времени из раствора вынимают окрашенные в голубой цвет издели , тщательно промывают проточной водой и сушат при 100t в течение 20 мин, Дп активации вз ты образцы пластин из сополимера формальдегида марки СФД-ВН-БС, Оценку состава дл активации поверхности изделий из полимера формальдегида с диоксоланом производ т по краевому углу смачива ни водой поверхности образцов, стабильности угла смачивани водой во времени, по изме eнию прочности клеевых соединений (отрыв - отдир) пластмасса - металл. Активированные образцы полимера формальдегида с диоксоланом склеивают со стальными (ст,40) образцами при помощи кле на основе эпоксидной смолы марки К-153(ТУ 6-05-1584-72) 100 мае,ч,, наполнител двуокиси титана (ТУ 6-09-2166-77) и отвердител марки УП-583 (ТУ 6-09-4227-76), Полимеризацию ведут при 20-25°С в течение 24 ч, В табл, 1 привод тс результаты проверки состава дл активации поверхности изделий из полимера формальдегида с диоксоланом, В табл, 2 приведены данные по изменению краевого угла смачивани поверхности во времени. Как видно из приведенных данных, прочность клеевых соединений изделий, обработанных предложенным способом, на 20-30% выше, чем с применением.SP I113 The invention concerns the development of a composition for the activation of the surface of products from formaldehyde-based polymeric materials with dioxolane before gluing, painting, and metallization. The composition can be used in various fields of technology to give the surface wettability of products, high adhesion properties. A known composition for etching polyolefins containing potassium permanganate with 0.5-1.0 wt.% Manganese peroxide or magnesium nitrate C13. A disadvantage of the known composition is the lack of wettability of the surface of polymer products of formaldehyde with dioxolane, the wettability remains equal to the wettability of the surface of the original samples, the acidic solution of potassium permanganate does not interact with the surface of the formaldehyde copolymer. The high aggressiveness of the solution promotes surface etching, cracks appear. The adhesion ability of the surface, which is expressed in changing the strength of adhesive joints (from the tearing-off) to the plastic-metal, is unsatisfactory. The composition closest to the invention is a composition for activating the surface of plasticized formaldehyde-based elastomers with dioxolane containing phosphoric acid 2 Its disadvantage is unstable wettability of the surface of products from polyformaldehyde and its copolymers. After a certain time, the wettability decreases, the adhesiveness of the surface deteriorates. The purpose of the invention is to increase the adhesive ability, namely to create, with the activation of the surface of polymer products, formaldehyde with dioxolane, ensuring the wettability of the surface of the products, increasing the adhesiveness and thereby ensuring high strength of bonding of polymer products of formaldehyde with dioxolane to metal. The goal is achieved by the fact that the composition for the activation of the surface of polymer products of formaldehyde with dioxolane, including orthophosphoric acid, additionally contains methanol in the following ratio of components, May, h,: Acid orthophosphoric concentrated 99-100 MethylViolet0.9-1.1 Introduction to orthophosphoric methylviolet acid helps to improve wettability, ensures its stability over time, and increases the adhesiveness of the surface of an acetal resin product. Preparation of the activating solution is carried out at room temperature by introducing MethylViolet into concentrated phosphoric acid, mixing and heating to 50-60 ° C. Acetal resin products washed with running water are prepared into the solution prepared in this way and 2 are kept in it. -3 min. After the specified time has elapsed, the blue-colored products are removed from the solution, washed thoroughly with running water and dried at 100 t for 20 min. Astin from a copolymer of formaldehyde, grade SFD-BH-BS, Evaluation of the composition to activate the surface of products from formaldehyde polymer with dioxolane is wetted with the surface of the samples by the edge angle, stability of the wetting angle with water over time, according to the strength of adhesive joints (detachment - tear off ) plastic - metal. Activated samples of formaldehyde polymer with dioxolane are bonded to steel (Art. 40) samples using an adhesive based on K-153 epoxy resin (TU 6-05-1584-72) 100 May, h, titanium dioxide filler (TU 6-09 -2166-77) and the hardener UP-583 (TU 6-09-4227-76), polymerization is carried out at 20-25 ° C for 24 hours. Table 1 shows the results of testing the composition to activate the surface of polymer products. Formaldehyde with dioxolane, Table 2 shows the data on the change in the wetting angle of the surface with time. As can be seen from the above data, the strength of adhesive joints of the products processed by the proposed method is 20-30% higher than with application.
известного состава, при хорошей стабильной смачиваемости.:known composition, with good stable wettability .:
Применение предлагаемого состава не вызывает деструкцию полимера формальдегида с диоксоланом, упрощаетс технологи подготовки поверхности к склеиванию, улучшаютс услови труда ..The application of the proposed composition does not cause the destruction of the formaldehyde polymer with dioxolane, simplifies the technology of surface preparation for bonding, improves working conditions.
Таблица 1Table 1
Кислотаортофосфорна конц. 98 ,Метилвиолет 0,9Acid orthophosphorus conc. 98, MethylViolet 0.9
Кислота ортофосфорна конц. 98 Метилвиолет 1,0Acid orthophosphorus conc. 98 MethylViolet 1.0
Кислота ортофосфорна конц. 98 Метилвиолет 1,1Acid orthophosphorus conc. 98 MethylViolet 1.1
Кислота ортофосфорна конц. 99Acid orthophosphorus conc. 99
Кислота ортофосфорна конц. 99 Метилвиолет 1,0Acid orthophosphorus conc. 99 Methyl violet 1.0
Кислота ортофосфорн конц. 99 Метилвиолет 1,1 Кислота ортофосфорна (Сонц. 100 Метилвиолет 0,9Acid orthophosphorus conc. 99 Methyl Violet 1.1 Orthophosphoric acid (Sonts. 100 Methyl Violet 0.9
Кислота ортофосфорна конц. 100 Метилвиолет 1,0Acid orthophosphorus conc. 100 Methyl violet 1.0
Кислота ортофосфорна конц. 100 Метилвиолет 1,1Acid orthophosphorus conc. 100 MethylViolet 1.1
Кислота ортофосфорна конц. 101 Метилвиолет 0,9Acid orthophosphorus conc. 101 Methyl violet 0.9
Кислота ортофосфорна конц. 101 Метилвиолет 1,0Acid orthophosphorus conc. 101 Methyl violet 1.0
300300
Поверхность п тниста The surface is mottled
320320
320320
370370
379379
375375
390390
380380
396396
окрашиваниеstaining
Неравномерное окрашиваниеUneven staining
Кислота ортофосфорна конц. 101Acid orthophosphorus conc. 101
Метилвиолет 1,1MethylViolet 1.1
Известный Famous
Кислота серна 30 вес.% Перманганат кали 5 вес. Нитрат магни 0,5 вес.% Вода 64,5 вес.%Sulfuric acid 30 wt.% Potassium permanganate 5 wt. Magnesium nitrate 0.5 wt.% Water 64.5 wt.%
ПрототипPrototype
Кислота ортофосфорна Orthophosphoric acid
конц.conc.
Кислота ортофосфорна конц. 100 Метилвиолет 0,9Acid orthophosphorus conc. 100 MethylViolet 0.9
Кислота ортофосфорна конц. 100 Метилвиолет 1,1Acid orthophosphorus conc. 100 MethylViolet 1.1
Прототип Кислота ортофосфорна конц.Prototype Acid orthophosphorus conc.
Продолжение табл. 1Continued table. one
Неравномерное Uneven
320 окрашивание320 staining
Не склеиваетс Does not stick together
300300
Таблица 2table 2
2828
2525
30thirty
2525
2 82 8
2525
7878
8383
8181
Claims (1)