SU1117282A1 - Method of processing bauxite to alumina - Google Patents
Method of processing bauxite to alumina Download PDFInfo
- Publication number
- SU1117282A1 SU1117282A1 SU833609344A SU3609344A SU1117282A1 SU 1117282 A1 SU1117282 A1 SU 1117282A1 SU 833609344 A SU833609344 A SU 833609344A SU 3609344 A SU3609344 A SU 3609344A SU 1117282 A1 SU1117282 A1 SU 1117282A1
- Authority
- SU
- USSR - Soviet Union
- Prior art keywords
- bauxite
- solution
- mother liquor
- treated
- phosphorus pentoxide
- Prior art date
Abstract
СПОСОБ ПЕРЕРАБОТК1 БОКСИТА НА.ГЛИНОЗЕМ, включающий вышелачиванне боксита упаренным оборотным маточным раствором, отделение-алюминатного раствора от красного шлама, разложение алюминатного раствора с получением гидроокиси алюмини и маточного раствора и выпаривание маточного раствора, отличающийс тем, что, с целью повышени степени извлечени глинозема и сокращени потерь щёлочи за счет удалени из боксита п тиокиси фосфора , перед выщелачиванием боксит обрабатывают маточным раствором, отдел ют твердый осадок от .раствора, последний обрабатывают известью при § соотнощении окиси кальци к п тиокиси фосфора в растворе по массе (Л ( 1-1,Зб):1 с выдержкой в течение 3-4 ч.A BOXIT PROCESSING PROCESS BY NA. GLINOZEM, including the extraction of bauxite by one stripped off working stock solution, separation of the aluminate solution from the red mud, decomposition of the aluminate solution to produce aluminum hydroxide and mother liquor, and evaporation of the mother liquor, characterized in that in order to increase the recovery of alumina and reduction of alkali losses due to removal of phosphorus pentoxide from bauxite; before leaching, bauxite is treated with the mother liquor; solid precipitate is separated from the solution; the latter is treated with lime at § the ratio of calcium oxide to phosphorus pentoxide in solution by weight (L (1-1, 3b): 1 with an exposure time of 3–4 h.
Description
f Изсоретенке отно.ситс к цветной металлургии и может быть использова но дл получени глинозема из бокси тов с повьшенным содержанием п тиокиси фосфора. Известен способ переработки бокс та на глинозем по методу Байера, включающий выщелачивание боксита оборотным щелочно-алюминатным раствором , отделение алюминатного раствора от шлама, разложение алюминат ного раствора декомпозицией с получением гидроокиси алюмини и маточного раствора, кальцинацию гидроокиси алюмини и выпаривание маточного раствора 1 . Недостатком этого способа вл етс то, что он эффективно применим только дл бокситов с низким содержанием п тиокиси фосфора 0,1-0,3%) Наиболее близким к изобретению по технической сув1ности и достигаемому результату вл етс способ переработки ббксита на глинозем, вклю чающий выщелачивание боксита упарен ным оборотным щелочно-алюминатным .маточньм раствором, разбавление пол ченной пульпы, отделение алюминатно го раствора от красного шлама, разложение алюминатного раствора деком позиций с получением гидроокиси алю мини и маточного раствора, выпаривание маточного раствора, где дл удалени п тиокиси фосфора из проце са упаренный маточный раствор охлаж дают до 20-30-С, кристаллизуют фосфат натри и отдел ют его от оборот ного маточного раствора 2 , Недостатками известного способа вл ютс низка степень извлечени глинозема при переработке трудновскрываемых диаспоровых бокситов с высоким содержанием п тиокиси фосфо ра, составл юща 41,5%, и значитель ные потери щелочи, св занные с выве дением фосфора из процесса в виде фосфата натри и составл ющие 2,2 т на I т удал емого . Целью изобретени вл етс повышение степени извлечени глинозема и сокращение потерь щелочи за счет удалени из боксита п тиокиси фосфора . Поставленна цель достигаетс те что согласно способу переработки боксита на глинозем, включающему выщелачивание боксита упаренным обо ротным маточньм раствором, отделение блюнинатного раствора от крас2J ного шлама, разложение алюминатного раствора с получением гидроокиси алюмини и маточного раствора и выпаривание маточного раствора, перед выщелачиванием боксит обрабатывают маточным раствором, отдел ют твердый . остаток ioT раствора, последний обрабатывают известью при соотношении окиси кальци к п тиокиси фосфора в растворе по массе (1-1,36): с выдержкой в течение 3-4 ч. Способ осуществл ют следующим образом . Измельченный боксит обрабатывают при 80-100 С маточным раствором, содержащим 90-150 г/л Na20 кауст. и 40-140 г/л и выдерживают 0,52 . Полученный раствор отдел ют от твердого остатка боксита и обрабатывают при 80-100 С известью, вз той при соотнощении кальци к п тиокиси фосфора в растворе по массе (1-1,36).. :I, что соответствует мольному отношению (2,55-3,, и выдерживают 3-4 ч. Образовавшийс фосфат кальци от|Дел ют от раствора и направл ют полученный раствор совместно с маточным на предварительную перед вьпцелачиванием обработку боксита, а обесфосфоренный боксит выщелачивают упаренным оборотным маточным раствором, отдел ют алюминатный раствор от красного шлама, выдел ют из алюминатного раствора гидроокись алюмини . При зтом полученный после отделени гидроокиси алюмини маточный раствор дел т на два потока; один из них направл ют на предварительное обесфосфоривание боксита, а второй - на выпарку перед подачей на выщелачивание обесфосфоренного боксита. пример , 00 кг боксита, содержащего, %: 9,2; 2 45,9, SiO П,3, обрабатывают 600 л маточного раствора, содержащего, г/л: кауст, 20 и Р в течение 1 ч. Полученную пульпу отстаивают в сгустителе. В результате сгущени получают 477л осветленного раствора, содержащего , г/л: Na20 кауст 120; AS-Oj 76; Р20с 6,7, В раствор добавл ют 3,4.8 кг извести, исход из отношени СаО к ° массе - 1,, Пульпу после перемешивани при 95 С в течение 4 ч отфильтровывают наf Isoretinka is related to nonferrous metallurgy and can be used to produce alumina from baux with an increased phosphorus pentoxide content. A known method of processing boxing on alumina according to the Bayer method involves leaching bauxite with a recycled alkaline aluminate solution, separating the aluminate solution from the sludge, decomposing the aluminate solution by decomposing to produce aluminum hydroxide and mother liquor, calcining aluminum hydroxide and evaporating the mother liquor 1. The disadvantage of this method is that it is effectively applicable only to bauxites with a low phosphorus pentoxide content of 0.1-0.3%. The closest to the invention in terms of technical sufficiency and the result achieved is a method of processing bbxite to alumina, including leaching bauxite with one stripped off circulating alkaline aluminate solution, a dilution of the pulp, separation of the aluminate solution from the red mud, decomposition of the aluminate solution with a position deck to obtain aluminum hydroxide and masterbatch the evaporation of the mother liquor, where the evaporated mother liquor is cooled to 20-30 ° C to remove phosphorus pentoxide from the process, sodium phosphate is crystallized and separated from the circulating mother liquor 2. The disadvantages of this method are the low recovery of alumina in the processing of difficult-to-digit diaspore bauxites with a high content of phosphorus pentoxide, 41.5%, and a significant loss of alkali, associated with the removal of phosphorus from the process in the form of sodium phosphate and constituting 2.2 tons per It removed. The aim of the invention is to increase the recovery rate of alumina and reduce alkali loss by removing phosphorus pentoxide from bauxite. This goal is achieved in accordance with the method of processing bauxite to alumina, which includes leaching of bauxite with one stripped circulating mother liquor, separating the blueberry solution from the sludge, decomposing the aluminate solution to produce aluminum hydroxide and mother liquor, and evaporating the mother liquor, leaching the bauxite with the mother liquor before leaching are separated solid. the remainder of the ioT solution, the latter is treated with lime at a ratio of calcium oxide to phosphorus pentoxide in the solution by weight (1-1.36): with a holding time of 3–4 hours. The method is carried out as follows. Crushed bauxite is treated at 80-100 ° C with a stock solution containing 90-150 g / l of Na20 caustic. and 40-140 g / l and withstand 0.52. The resulting solution is separated from the solid residue of bauxite and treated at 80-100 ° C with lime taken at a ratio of calcium to phosphorus pentoxide in solution by weight (1-1.36) ..: I, which corresponds to the molar ratio (2.55 -3 ,, and incubated for 3-4 hours. Calcium phosphate formed from the | Divided from the solution and the resulting solution was sent together with the mother liquor to preliminary treatment of bauxite before extruding, and the dephosphorized bauxite was leached with one stripped circulating mother liquor, the aluminate solution was separated from the red sludge is isolated and aluminate solution aluminum hydroxide. In this case, the mother liquor obtained after separation of aluminum hydroxide is divided into two streams, one of which is directed to preliminary dephosphorization of bauxite, and the second is sent to the evaporation before leaching of the freeze-dried bauxite, for example, 00 kg of bauxite containing, %: 9.2; 2 45.9, SiO P, 3, are treated with 600 l of mother liquor containing, g / l: caust, 20 and P for 1 h. The resulting slurry is settled in a thickener. As a result of condensation, 477 l of a clarified solution is obtained, containing, g / l: Na20 caust 120; AS-Oj 76; P20c 6.7, 3.4.8 kg of lime is added to the solution, proceeding from the ratio of CaO to ° mass - 1 ,, The pulp after stirring at 95 ° C for 4 hours is filtered on
33
нуТчфильтре, как промывают гор чей водой. При этом получают 7,2 кг продукта, содержащего, %: PjOy 34,44 СаО 48,3; NajO 1,53; . 0,97, Si02 0,3 , 0,21 .Well filter as washed with hot water. This gives 7.2 kg of a product containing,%: PjOy 34.44 CaO 48.3; NajO 1.53; . 0.97, Si02 0.3, 0.21.
Указанный продукт вл етс фосфоритной мукой первого сорта. Потери с фосфоритной мукой составл ют 44 кг на 1 т удал емого Said product is a first grade phosphate flour. Losses with phosphate rock are 44 kg per tonne removed
После удалени п тиокиси фосфора раствор объемом 477 л содержит,t/л: Иа,(Э кауст. 120; 75,8, 1,50. К раствору добавл ют 123 л маточного раствора и направл ют на обработку новой порции боксита. Обработанный боксит направл ют на выщелачивание по способу Байера. Из824After removal of phosphorus pentoxide, the 477 L solution contains, t / L: Ia, (O caust. 120; 75.8; 1.50. To the solution, 123 L of mother liquor is added and sent to the processing of a new bauxite batch. Processed bauxite is leached by the Bayer method.
влечение глинозема при этом составл ет 72,8%.the attraction of alumina in this case is 72.8%.
Пример 2. 100 кг боксита аналогичного состава обрабатывают маточным щелочно-алюминатным раство ром в услови х по примеру 1. Полученный раствор (477 л) отдел ют от боксита, дел т его на 100 равных частей (по 47,7 л)и каждую частьExample 2. 100 kg of bauxite of a similar composition are treated with an alkaline aluminate uterine solution under the conditions of example 1. The resulting solution (477 l) is separated from bauxite, divided into 100 equal parts (47.7 l) and each part
обрабатывают известью при различных соотношени х по массе СаО к в растворе и времени выдержки при 95 С , Растворы отдел ют от осадков, добавл ют к ним по 12 ,3 л свежего маточного раствора и направл ют на об ,работку 10 навесок того же боксита массой по 10 кг.are treated with lime at different ratios of CaO to mass in solution and aging time at 95 ° C. The solutions are separated from the precipitates, 12, 3 l of fresh mother liquor are added to them and sent for treatment, 10 batches of the same bauxite mass on 10 kg.
Claims (1)