SU1112035A1 - Composition for coating natural leather - Google Patents
Composition for coating natural leather Download PDFInfo
- Publication number
- SU1112035A1 SU1112035A1 SU823532008A SU3532008A SU1112035A1 SU 1112035 A1 SU1112035 A1 SU 1112035A1 SU 823532008 A SU823532008 A SU 823532008A SU 3532008 A SU3532008 A SU 3532008A SU 1112035 A1 SU1112035 A1 SU 1112035A1
- Authority
- SU
- USSR - Soviet Union
- Prior art keywords
- skin
- composition
- organic
- rosin
- polyterpenes
- Prior art date
Abstract
СОСТАВ ДЛЯ ПОКРЫТИЯ НАТУРАЛЫ ОЙ РСОЖИ, включающий политерпены или оксиполитерпены, парафин и органическое соединение, о т л и ч а ютем , что, с целью повышещ и и ни гидрофобных свойств кожи и формоустойчиБости г зделий из нее, состав содержит в качестве органического соединени канифоль и дополнительнопол1П5зобутилен и органический растворитель при след; по1цем соотношении коьаюнентов, мае. %: Политерпены или оксиполитерпены , 14-18 Парафин2-3 . Канифоль0,2-0,5 Полиизобзтилен 0,5-2,0 Органический растворительОсталь юеCOMPOSITION FOR THE COATING OF NATURALS OF THE OWN RJPI, including polyterpenes or oxypolyperpenes, paraffin and organic compound, about the same, that, with the purpose of increasing the hydrophobic properties of the skin and formtorescence of the skin from it, the composition contains rosin as an organic compound. and additionally 1P5 zobutylene and an organic solvent trail; The ratio of coyayants, May. %: Polyterpenes or hydroxypoliterpenes, 14-18 Paraffin2-3. Rosin0,2-0,5 Polyisobutylene 0.5-2.0 Organic solventOstal South
Description
Мзооретенне относитс к пропичоч иьм составам дл нат-уральпой кожи, ii Тзчкес к состапам, обес11ечиваю г;им Hj.icoKHii г11дрофобный эффект и формеу (-той 1илссть изделий; работающих с на1рузкой в услови х повыше пой в.пажностИз папример футбольпых ( чой, мо;1сет быть - Спользовапо па ксжевеиных заводах и применено пред при ти ми -изготовител ми спорттоваров , 1увесте}{ состав дл гюкрыти нат радплюй коки5 зключаю ц-тй лолимерь; ерггепов (политерпепы или: оксиполитериепк ), парафин (окисленгпж) и ор1;а П1ческое соединение (например, ГгПр гсна соль жирной кислоты) , на - ), в с оотно иании (мае. %j; (80-90) : (7--12) : (3-8) ГЦ. О.тнако 1римене 1ие известного сое . ПС обеспечивает за,г(анпого комплекса не обход и;.ьгк свойств из-за не ;тс;етато:июй мехагигческой nponnocTPj ii. смазки, т.е. пе обеепечивает . достаточна гидрофобность и формоустойчивосчь кожи (изделий из нее) , 11е;и: изобретени - повышение гнд рофоб1{ых свойств кожи и формоустой ижпуги издетп-гй из нее. Поставленна цель достигаетс е:-, что состав дл покрыти патура .птн-юй кожИд включающий иолитерпе 1 ;ли оксиполимеры терпенов, парафин (; органи-ю.ское соедин.епие, содержит : -а -честве оргчитиггеското соединени канифоль и дспюлпительно - полиизоб THJTen и органический растворитель при ::Л;дyIOi ;e f соотношении компоненПо пттерпены или оксипопитерпены 14-18 Парафин2-3 КанифольО, 2-0 ,,5 По:н;изобутилен о ,5-2; О Орханический растверительОстальное При ен екые в композиции политер . .; .рл ютс продуктом нолимеризадии С1;ип,1дара-, а оксиполимеры терпе ной прод;1:;то; 1 автоокислени политеркоиов , Это }з зкне: светло-коричне хтле т;иги;:ост1; с плотиостьк) при 20° С /л;.; и д намичаскг)й в зкостью В качестве растворител использу т бапзиН; уайт--спирит, керосин, аг:то;.;ритель ff 646 и , с V о с о б о суще с т вл ют ел ед ующим Пра::/ОМ. В аппарат, енабженный мешалкой, люком дл завр5зки суких продуктов; термометром и системой обогрева, заливают pacTBopnTBJH-j (переменно), нагревают его до 60С и при перемешивании ввод т канифоль (переменно), полимеры или оксиполимеры терпенов (переменно) и полиизобутилен (переменно ) . Перемешивание продолжают до полного растворени компонентов. Обрабатываемую кожу выдерживают 13 течение 053-0,5 ч при комнатной температуре либо в этом аппарате, либо в аппарате, специально дл этой цели приспособленном. Обработанные кожи сушат в выт жном шкафу,. Определен и е в од о п р о м о к а е м о с т и образцов кожи до и после обработки провод т по ГОСТ 938.22-71 в динамических услови х на приборе П1-1Д-2. Водопромокаемость характеризуетс времепем промокани образца при многократном изгибе. Определение времеьн промокани основано на изменении электропроводности кожи, В табл. 1 приведены рецептуры предлагаемого и известного составов, а также величины в зкости и подопромокаемости кож, обработанных этими составами, и сухих образцов кожи. Из табл. 1 видно, что предлагаемые составы обеспечивают зпа гительно более высокий гидрофобный эффект по сравнению с известным. Полученные лабораторные данные подтверждены натурными испытани ми. В табл. 2 приведены средние значени р спытаний физико-механических свойств образцов кожи5 (разрул1а1ош,а пагрузка, абсолютное удлинение и относительное удл11пение) , обработанной Из пр1пзеденных в табл. 2 данньп ; ВИДНО; что образцы кожи, обработанные предлагаемым гидрофобньм составом и влажные, имеют одно и то же относительное удлинение, чего нет у образцов кожи:, обработанной 1- звестной смазкой. Отсутствие разницы в относите.пьном удлинении образцов при их испытании на разрыв говорит о том, что кожи, обработанные предлагаемым гидрофобHiiiM составом, не будут деформироватьс и их можно использовать в издели х, работающих в услови х повышенной влажности с ударной нагрузкой. Обес3 . 1Zooretentenne refers to the preparation of compositions for nat-uralpoy skin, ii Tzkkes to composites, I provide them; he has a hjflushy effect and form (the 1st part of the products; working with load in conditions of higher level;) my; 1set to be - Used by a pair of fabulous factories and used in the case of manufacturers of sports goods, a model, a picture} {composition for hyatry nat radpluy coca5 includes c-lymer; erggepov (polyterpeps or hydroxypolyperies), paraffin; and P1icheskaya compound (for example, GgPr gsa salt of fatty oh acid), on -), in recourse (May.% j; (80-90): (7--12): (3-8) HZ. O. but the first one is known soy. PS provides for, r (anpy complex does not bypass and;. hc properties due to not; ts; etato: yu mega-nagging nponnocTPj ii. lubricant, i.e., does not provide sufficient hydrophobicity and shape of the skin (its products), 11e; and - an increase in the skin properties of the skin and formulary skin from the object. The goal is achieved: - that the composition for covering the patura. Ph. skin includes Ioliterpe 1; whether terpenes oxypolymers, paraffin (; The organic compound contains, as follows: the organic compound rosin and, in particular, the polyisob THJTen and the organic solvent at: L; dIOIOi; ef the ratio of the components of the pterpenes or hydroxypoperpenes 14-18 Paraffin2-3 Rosin, 2-0 ,, 5 By: n; isobutylene o, 5-2; О Orhanic solventOther Phenix in the composition of a polyester. ; They are the product of nolimerizadia C1; un, 1dara-, and hydroxypolymers, thermo prod; 1:; 1 auto-oxidation of polytercoils, it is: zcne: light brown ht t; igi;: ost1; with a density) at 20 ° C / l;.; and dimchastic viscosity BazziN is used as a solvent; White - spirit, kerosene, ag: that;., the user ff 646 and, from V o s o b o c, are eaten by the unit Pra :: / OM. To the apparatus, which is agitated with a mixer, a hatch for loading dry products; With a thermometer and a heating system, pacTBopnTBJH-j (variable) is poured, heated to 60 ° C and rosin (variable), polymers or terpenes oxypolymers (variable) and polyisobutylene (variable) are added with stirring. Stirring is continued until complete dissolution of the components. The treated skin is kept for 13 053-0.5 hours at room temperature, either in this device or in an apparatus specially adapted for this purpose. Processed skins are dried in a hood. The determination of the skin specimen and skin samples before and after treatment is carried out according to GOST 938.22-71 under dynamic conditions on the device P1-1D-2. The water resistance is characterized by the time of wetting of the sample during repeated bending. The determination of the blotting time is based on the change in the electrical conductivity of the skin. 1 shows the formulations of the proposed and known compositions, as well as the values of the viscosity and sub-impregnability of the leather treated with these compositions, and dry skin samples. From tab. 1 that the proposed formulations provide a significantly higher hydrophobic effect compared to the known. The obtained laboratory data was confirmed by field tests. In tab. Table 2 shows the average values of the physicomechanical properties of skin samples 5 (disrupted, and load, absolute elongation, and relative elongation) processed from the preceding table. 2 dannp; IT IS SEEN; that the skin samples treated with the proposed hydrophobic composition and wet, have the same relative elongation, which the skin samples do not have: treated with 1-known lubricant. The absence of a difference in the relative elongation of the samples during their tensile testing indicates that the skin treated with the proposed hydrophobic IIIiM composition will not deform and can be used in products operating under conditions of high humidity with a shock load. About one
печение формоустойчивости кожаных изделий с помощью предлагаемого гидрофобного состава (футбольных м чей) по сравнению с известным подтверждено натурными испытани ми (после 10 ч под дождем и после 50 ч при сухой погоде кожа м ча по окрз ности не сдеформировалась) .The baking of the form-stability of leather products with the help of the proposed hydrophobic composition (football balls) as compared with the known one was confirmed by field tests (after 10 hours in the rain and after 50 hours in dry weather, the skin of the skin did not deform around).
Применение предлагаемого состава при изготовлении кожаных изделий, работающих в услови х повышенной влажности с ударной нагрузкой (фут120354The use of the proposed composition in the manufacture of leather products, working in conditions of high humidity with a shock load (ft120354
больные м чи) , позволит Звеличить их качество и снизить закупки по импорту .sick mi), will allow Zvelicit their quality and reduce purchases on imports.
г Технологи изготовлени предлагаемого гидрофобного состава дл натуральной кожи и предварительна обработка кож проста и не требует дополнительных капитальных затрат, может 10 проводитьс не только на кожевенных заводах, но и на предпри ти х-изготовител х спорттоваров.The technology of manufacturing the proposed hydrophobic composition for natural leather and the pretreatment of leather is simple and does not require additional capital expenditures; it can be carried out not only at tanneries, but also at enterprises of sporting goods.
Т а T a
Необработанна кожаRaw leather
Кожа, обработанна известной смазкой Кожа, обработанна предлагаемой смазко следующих составовLeather treated with a known lubricant Leather treated with the proposed lubricant of the following composition
Политерпены Polyterpenes
КанифольRosin
ПарафинParaffin
Полиизобутилен Polyisobutylene
ль eh
ОстальноеRest
14,0 0,2 3,0 2,014.0 0.2 3.0 2.0
нn
ОстальноеRest
18,0 0,5 2,018.0 0.5 2.0
210210
10221022
1414
7-97-9
21702170
3131
22052205
7-107-10
31,531.5
Полиизобутилен Polyisobutylene
РастворительSolvent
(керосин) (kerosene)
ОксиполимерыHydroxypolymers
терпеновterpenes
КанифольRosin
ПарафинParaffin
Полиизобутилен Polyisobutylene
Растворитель (сврй марки 646)Solvent (brand 646)
НеобработанныеUnprocessed
Обработанные известной гидрофобной смазкой Treated with known hydrophobic grease
Обработанные предлагаемой смазкойProcessed the proposed lubricant
Необработанные, влажные Raw, wet
Обработанные известной смазкой, влажные Treated with a well-known lubricant, wet
Обработанные предлагаемой смдзкой, влажные Processed proposed smdzkoy, wet
Продолжение табл,1Continued tabl, 1
1one
21602160
3-J3-j
2828
30thirty
21002100
5-85-8
Т T
28 3228 32
33 4533 45
42 3342 33
Claims (1)