SK277682B6

SK277682B6 - Waxed dental thread

Info

Publication number: SK277682B6
Application number: SK284892A
Authority: SK
Inventors: Olga Durcova; Pavel Stefanik; Ondrej Alexaj; Dusan Zitnansky
Original assignee: Olga Durcova; Dusan Zitnansky
Priority date: 1992-09-17
Filing date: 1992-09-17
Publication date: 1993-12-08
Also published as: CZ284892A3; CZ277802B6; SK284892A3

Abstract

A waxed dental thread consisting of a bunde of polypropylene fine fibril whereby individual smooth fibrils from polypropylene have a noncircular cross rust, unit length mass from 5 to 8 dtex, total length mass from 400 to 1200 dtex and a surface of thread is treated by 15-35 wt. per cent of paraffin wax, e.g. with a content 5-20 wt. per cent of beeswax and 0.5-5.0 wt. per cent of methol, respectively other medicinal and/or aromatized substance, with softening temperature 55-60 degree Celsius.

Description

Vynález sa týka voskovanej zubnej nite z polypropylénu, pozostávajúcej z jemných profilovaných fibríl, ktoré sú držané v kompaktnom zväzku vrstvou upraveného parafínového vosku. Spadá do oblasti zdravotníctva pre zubolekárske alebo hygienické účely.The invention relates to a waxed dental floss of polypropylene consisting of fine profiled fibrils which are held in a compact bundle by a layer of treated paraffin wax. It falls within the health sector for dental or hygiene purposes.

Doterajší stav technikyBACKGROUND OF THE INVENTION

Zubná niť je určená špeciálne na čistenie medzizubných priestorov, okrajov zubných koruniek a môstikov. Čistením zubov v medzizubných priestoroch a pod okrajom ďasna (tam, kde nie je prístup zubnou kefkou) zubná niť pomáha predchádzať usadzovaniu a rozmnožovaniu substancií, ktoré tvoria zubné bakteriálne povlaky. Tieto sú mimoriadne nebezpečné a v skutočnosti sú hlavnou príčinou vzniku zubného kazu, krvácania a zápalov ďasien. Počase infekcia poškodí aj kostné lôžko, v ktorom je zub uložený a dochádza ku kývaniu, až vypadávaniu zubov. Zubná niť sa používa najmenej 1-krát denne. Bakteriálny povlak sa vytvára za 24-36 hodín. Použitie zubnej nite s dôkladným vyčistením zubov kefkou a pastou sa doporučuje najmä večer pred spaním, pretože bakteriálny povlak je najaktívnejší práve počas spánku.Dental floss is specially designed for cleaning interdental spaces, edges of dental crowns and bridges. By brushing the teeth in the interdental spaces and below the edge of the gum (where there is no toothbrush access), the dental floss helps prevent sedimentation and reproduction of the substances that form dental bacterial coatings. These are extremely dangerous and are in fact the main cause of tooth decay, bleeding and gum inflammation. In the course of the infection, the bone bed in which the tooth is deposited and the rocking, or even the tooth loss, will also be damaged. Dental floss is used at least once a day. Bacterial coating is formed in 24-36 hours. The use of dental floss with thorough brushing with toothbrush and paste is recommended especially in the evening before bed as the bacterial coating is most active during sleep.

Na výrobu zubných nití sa používajú prírodné i syntetické materiály (US č. 4,033.365) a tieto sa ďalej líšia druhom použitého povlaku. EP č. 172.671 chráni zubnú niť, pozostávajúcu z fibríl nylonu 6, nylonu 66, viskózy, acetátového polyméru, polyesteru, polyetylénu alebo polypropylénu. Ochranu tu predstavuje stavba zubnej nite v počte od 25 do 1 000 fibríl v zväzku priadze, ktoré obsahujú buď voskový povlak alebo nevoskový povlak. Tento nevoskovaný povlak je vybraný zo skupiny obsahujúcej alkylmonoestery, polyvinyléter maleinovej kyseliny, polyvinylpyrolidóny a mnohé ďalšie. Zubná niť má tiež chránený počet zákrutov priadze.Both natural and synthetic materials are used in the manufacture of dental floss (US No. 4,033,365) and these further differ in the type of coating used. EP no. 172.671 protects dental floss consisting of fibrils of nylon 6, nylon 66, viscose, acetate polymer, polyester, polyethylene or polypropylene. The protection here is the construction of a dental floss of between 25 and 1000 fibrils in a yarn bundle containing either a wax coating or a non-wax coating. This non-waxed coating is selected from the group consisting of alkyl monoesters, polyvinyl ether maleic acid, polyvinylpyrrolidones and many others. The floss also has a protected number of yarn twists.

Konvenčné zubné nite pozostávajú z nylonového multifibrilámeho zväzku. Ich výhodou býva nízka jemnosť v ťahu alebo nízka pevnosť, v dôsledku čoho sa pri použití trhajú a nie sú vhodné pre čistenie medzizubných priestorov. Samomazné vlastnosti nití sú slabé, čím sú náchylné uviaznuť medzi zubami a vyvolávať nepríjemný pocit pri použití. Komfort použitia ďalej znižujú vlákna s vysokým koeficientom trenia, lebo užívateľ musí použiť značnú silu na pretiahnutie nite do medzizubných priestorov.Conventional dental floss consists of a nylon multifibrillar bundle. Their advantage is low tensile fineness or low strength, which tears in use and is not suitable for cleaning the interdental spaces. The self-lubricating properties of the yarns are weak, making them prone to stick between the teeth and cause discomfort in use. Fibers with a high coefficient of friction further reduce the comfort of use because the user has to use considerable force to pull the thread into the interdental spaces.

CS AO č. 270.866 chráni niť o dĺžkovej hmotnosti jednotlivých fibríl od 5 do 8 dtex z nematovaného polyamidu na báze polykaproamidu s obsahom 0,01 až 0,95 % hm. aromatických a/alebo liečivých látok. Polyamidový hodváb má priemer 12 oblúčikov a/alebo slučiek na 1 cm dĺžky. CS AO č. 267.480 chráni fyzikálne a/alebo chemicky modifikovanú niť, ktorá je na svojom povrchu a medzi elementárnymi vláknami za účelom zvýšenia zmáčavosti napustená dezinfekčnými, adstringentnými alebo antikariesnými látkami.CS AO no. 270.866 protects the yarn of individual fibrils from 5 to 8 dtex of unpainted polyamide based on polycaproamide containing 0.01 to 0.95 wt. aromatic and / or medicinal substances. The polyamide silk has a diameter of 12 arches and / or loops per 1 cm of length. CS AO no. 267.480 protects physically and / or chemically modified yarn impregnated with disinfectant, astringent or anticaries agents on its surface and between the elementary fibers to increase wettability.

Polyolefínové polyméry využité pre výrobu zubných nití chránia ďalšie patenty. EP č. 335.466 chráni zubnú niť z modifikovaného polyetylénu a to polytetrafluoretylénu, pokrytú priľnavým mikrokryštalickým voskom s teplotou tavenia 76 až 80 ’C. Naviac niť spája v jedno aspoň jeden aktívny materiál, vybraný zo skupiny látok proti zubnému kameňu, kostižeru a plaketovaniu a prítomné je tiež koagulačné činidlo.The polyolefin polymers used in dental floss manufacture protect other patents. EP no. 335.466 protects dental floss of modified polyethylene, namely polytetrafluoroethylene, covered with adhesive microcrystalline wax with a melting point of 76 to 80 80 C. In addition, the yarn combines into at least one active material selected from the group of anti-tartar, bone and plaque substances, and a coagulant is also present.

EP C. 339.935 chráni zubnú niť zloženú z predĺženého multifibrilámeho ultravysokomolekulového polyolefínu s vnútornou viskozitou aspoň 5 dl/g a spôsob jej výroby. Polyolefín je ultravysokomolekulový hmôt, polyetylén, definovaný etylén/alfaoleflnový kopolymér, 5 kde α-olefín je aspoň 1 propylén, butén-1, 4-metylpentén-1, hexén-1, oktén-1 a decen-1.EP C. 339.935 protects a dental floss composed of an elongated multifibrillar ultra-high molecular weight polyolefin with an intrinsic viscosity of at least 5 dl / g and a process for its manufacture. Polyolefin is an ultra-high molecular weight, polyethylene, defined ethylene / alpha-olefin copolymer, 5 wherein the α-olefin is at least 1 propylene, butene-1,4-methylpentene-1, hexene-1, octene-1 and decene-1.

Bolo zistené, že požiadavky kladené na zubné nite spĺňajú aj syntetické vlákna z polypropylénu. K tomuto účelu môžu byť použité rôzne typy polyméru izotak10 tického polypropylénu, ktoré spĺňajú platné hygienické normy. Podobne hygienickým normám musia vyhovovať všetky ďašie prísady použité v technológii prípravy zubných nití. Dobrý čistiaci účinok majú hladké vlákna s kruhovým profilom v skanej forme, pričom počet zá15 krutov je rôzny aniejeroz-hodujúci.Synthetic polypropylene fibers have also been found to meet the requirements for dental floss. For this purpose, various types of isotactic polypropylene polymer can be used which meet the applicable hygiene standards. Similarly, all other ingredients used in dental floss technology must meet hygiene standards. Smooth fibers with a circular profile in a twisted form have a good cleaning effect, the number of twists being different and irrelevant.

Podstata vynálezuSUMMARY OF THE INVENTION

Podstatou vynálezu je voskovaná zubná niť, pozostávajúca zo zväzku polypropylénových jemných fibríl, pričom jednotlivé hladké fibrily z polypropylénu majú nekruhový priečny rez, jednotkovú dĺžkovú hmotnosť od 5 do 8 dtex, celkovú dĺžkovú jemnosť od 400 do 25 1200 dtex a povrch nite je upravený 15 až 35 % hm.The present invention is based on a waxed dental floss consisting of a bundle of polypropylene fine fibrils, wherein the single smooth polypropylene fibrils have a non-circular cross-section, a unit length of from 5 to 8 dtex, a total length fineness of 400 to 25 1200 dtex and a thread surface of 15 to 35% wt.

parafínového vosku s obsahom 5 až 20 % včelieho vosku a 0,5 až 5,0 % hm. mentolu, resp. inej liečivej a/alebo aromatizujúcej látky a jeho teplota mäknutia je 55 až 65 “C.% paraffin wax containing 5 to 20% beeswax and 0.5 to 5.0% wt. menthol, respectively. other medicinal and / or flavoring and its softening temperature is 55 to 65 ° C.

Podstata tohto vynálezu spočíva v tom, že hladké vlákna sú priečne profilované a k čistiacemu efektu na povrchu zubov prispieva väčšia využiteľná plocha povrchu vlákien. Samotná príprava zubných nití pozostáva z dvoch operácií: príprava profilovaného hladkého 35 skaného multifibrilámeho vlákna a voskovanie vlákna.The essence of the present invention is that the smooth fibers are transversely profiled and a greater usable fiber surface area contributes to the cleaning effect on the tooth surface. The preparation of dental floss itself consists of two operations: the preparation of a profiled smooth twisted multifibrillar fiber and the waxing of the fiber.

Pre rôzne typy hygienicky nezávadných polypropylénov musia byť zvolené rôzne technologické režimy prípravy orientovaných vlákien. Výsledné profilované hladké skané vlákna vhodné pre prípravu zubných nití 40 musia mať pevnosť nad 3 cN/dtex. Na povrch zväzku vlákien sa nanáša upravený parafínový vosk. Popri základnom komponente, parafínovom vosku, je prítomný aj včelí vosk a rôzne liečivá, resp. aromatizujúce prísady. Voskovaná zubná niť dobre kĺže po povrchu zu45 bov v medzizubných priestoroch.For the different types of hygienically harmless polypropylenes, different technological regimes for the preparation of oriented fibers must be chosen. The resulting profiled plain twisted fibers suitable for the preparation of dental floss 40 must have a strength above 3 cN / dtex. Treated paraffin wax is applied to the surface of the fiber bundle. In addition to the basic component, paraffin wax, beeswax and various drugs, respectively. flavoring additives. The waxed dental floss glides well over the surface of zu45 bov in the interdental spaces.

Výhodou voskovanej zubnej nite z polypropylénu je, že v styku s vodným prostredím-slinami nedochádza k uvoľňovaniu žiadnych látok na rozdiel napr. polyami-du 6, z ktorého sa uvoľňujú monoméry a 50 oligoméry horkej chuti.An advantage of waxed polypropylene dental floss is that no contact with the aqueous environment-saliva occurs, as opposed to e.g. polyamide 6 from which monomers and 50 oligomers of bitter taste are released.

Príklady vynálezuExamples of the invention

Príklad 1:Example 1:

Z polyméru TATREN Ή 902/P s indexom toku od 25 do 31 g/10 min. sa zvlákňovaním pripravili nedĺžené polypropylénové vlákna s trojuholníkovým profilom za použitia zdravotne nezávadnej zvlákňovacej prepa60 rácie BK 2083. Nedĺžené vlákna sa vydĺžili, pričom sa dosiahla jednotková dĺžková hmotnosť 6,2 dtex. Vlákna boli združené do zväzku s výslednou dĺžkovou hmotnosťou 620 dtex. Vláknam bol daný zákrut, a to 70 na 1 meter. Skané vlákna boli zafixované. Celková ⁶⁵ pevnosť zväzku vláken bola 3,5 cN/dtex a ťažnosť 45 %. V jednom zväzku sa nachádzalo 100 profilovaných elementárnych fibríl. Takto pripravené dĺžené vlákna boli voskované. K tomuto účelu sa pripravil parafínovýFrom TATREN® 902 / P polymer with flow index from 25 to 31 g / 10 min. Non-stretched polypropylene fibers with a triangular profile were prepared by spinning using a non-toxic spinning preparation BK 2083. The non-stretched fibers were elongated to a unit density of 6.2 dtex. The fibers were bundled to a final density of 620 dtex. The fibers were given a twist of 70 per meter. The twisted fibers were fixed. The total ⁶⁵ fiber bundle strength was 3.5 cN / dtex and the ductility was 45%. There were 100 profiled elemental fibrils in one bundle. The elongated fibers thus prepared were waxed. Paraffin was prepared for this purpose

SK 277682 Β6 vosk s obsahom 10 % hm. včelieho vosku a 5 % hm. mentolu. Metódou diferenciálnej termickej analýzy bola stanovená teplota mäknutia upraveného vosku 57’C. Na povrch vláken sa nanieslo 21 % hm. upraveného parafínového vosku na špeciálnom laboratórnom zariadení.Tým bola získaná voskovaná niť určená k používaniu. Pre účely expedovania voskovaná zubná niť sa prevíja na malé námotky, ktoré potepelnej fixácii v sušiarni sa vkladajú do vhodných hygienických obalov.2776 wax containing 10% wt. beeswax and 5 wt. menthol. The softening temperature of the treated wax was determined to be 57'C by differential thermal analysis. 21% wt. treated paraffin wax on a special laboratory equipment. This waxed yarn for use was obtained. For dispatch purposes, the waxed dental floss is rewound onto small wristbands which are placed in a suitable sanitary wrapping by a heat-fixation in an oven.

Príklad 2:Example 2:

Z polyméru TATREN HPF 321 s indexom toku llg/10 min. sa zvlákňovaním pripravili predorientované polypropylénové vlákna s trilobalovým profilom za použitia zdravotne nezávadnej zvlákňovacej preparácie BK 2083. Predorientované vlákna boli ďalej dodížené na výslednú dĺžkovú hmotnosť 750 dtex/96 fibríl. Vláknam boli dané zákruty, a to 100 zákrutov na jeden meter. Vlákna boh zafixované pri teplote 120 ’C. Výsledné mechanické vlastnosti vlákien sú: pevnosť 3,40 cN/dtex a ťažnosť 36 %.From TATREN HPF 321 polymer with a flow index of 11 g / 10 min. Pre-oriented polypropylene fibers with a trilobal profile were prepared by spinning using a non-toxic spinning preparation BK 2083. The pre-oriented fibers were further fed to a final density of 750 dtex / 96 fibrils. Twists were given to the fibers at 100 twists per meter. Fibers god fixed at 120 120 C. The resulting mechanical properties of the fibers are: strength 3.40 cN / dtex and elongation 36%.

K voskovaniu vlákien sa pripravil upravený parafínový vosk s obsahom 20 % hm. včelieho vosku s 5 % hm. mentolu. Teplota mäknutia upraveného vosku stanovená metódou diferenciálnej termickej analýzy bola 62 C. Na špeciálnom laboratórnom zariadení bolo na povrch profilovaných vlákien nanesené 35 % hm. vosku. Takto bola pripravená voskovaná zubná niť k ďalšiemu použitiu. Pre účely expedovania bola vhodne hygienicky zabalená ako v príklade 1.For waxing of the fibers, treated paraffin wax containing 20 wt. beeswax with 5 wt. menthol. The softening temperature of the treated wax, determined by the differential thermal analysis method, was 62 C. On a special laboratory apparatus, 35 wt. wax. Thus, waxed dental floss was prepared for further use. It was suitably hygienically packaged for dispatch as in Example 1.

Príklad 3:Example 3:

Z polyméru TATREN HPF 321 s indexom toku llg/10 min. sa zvlákňovaním pripravili predorientované vlákna s priečnym štvorcovým profilom za použitia zdravotne nezávadnej zvlákňovacej preparácie BK 2083 za podmienok prípravy a úpravy vlákna podľa príkladu 2. Výsledné mechanické vlastnosti vlákna sú: pevnosť 3,2 cN/dtex, ťažnosť 42 %.From TATREN HPF 321 polymer with a flow index of 11 g / 10 min. Pre-oriented cross-sectional fibers were prepared by spinning using a non-toxic spinning preparation BK 2083 under the conditions of fiber preparation and conditioning according to Example 2. The resulting mechanical properties of the fiber are: strength 3.2 cN / dtex, elongation 42%.

Príklad 4:Example 4:

Z polyméru TATREN Ή 902/P s indexom toku od 25 do 31 g/10 min. sa zvlákňovaním pripravili nedĺžené polypropylénové vlákna s trojuholníkovým profilom za použitia zdravotne nezávadnej zvlákňovacej preparácie BK 2083. Nedĺžené vlákna sa za tepla vydĺžili, ich jednotková dĺžková hmotnosť bola 5,8 dtex.From TATREN® 902 / P polymer with flow index from 25 to 31 g / 10 min. Non-stretched polypropylene fibers with a triangular profile were prepared by spinning using a non-toxic spinning preparation BK 2083. The non-stretched fibers were hot elongated, their unit weight was 5.8 dtex.

Vlákna boli združené do zväzku s celkovou dĺžkovou hmotnosťou 580 dtex. Vláknam bol daný zákrut, a to 70 na 1 meter. Zväzok skaných vláken sa vyznačoval celkovou pevnosťou 3,5 cN/dtex a ťažnosťou 65 %.The fibers were bundled together with a total length of 580 dtex. The fibers were given a twist of 70 per meter. The twisted bundle was characterized by an overall strength of 3.5 cN / dtex and an elongation of 65%.

Ďížené skané vlákna boli podrobené voskovaniu. K tomuto účelu sa pripravil parafínový vosk s obsahom 5 % hm. včelieho vosku a 5 % hm. mentolu. Metódou diferenciálnej termickej analýzy bola stanovená teplota mäknutia upraveného vosku 57 ’C.The woven twisted fibers were waxed. For this purpose, a paraffin wax containing 5 wt. beeswax and 5 wt. menthol. The softening temperature of the treated wax was determined to be 57 ° C by differential thermal analysis.

Na vlákno sa nanieslo 15 % hm. upraveného parafínového vosku na špeciálnom poloprevádzkovom zariadení. Tým bola pripravená voskovaná zubná niť určená k používaniu. Pre účely expedovania sa voskovaná zubná niť napr. prevíja na malé námotky, ktoré po tepelnej fixácii v sušiarni sa vkladajú do vhodných hygienických obalov.15% wt. treated paraffin wax on a special pilot plant. A waxed dental floss was prepared for use. For shipping purposes, waxed dental floss e.g. rewinds into small wraps, which after heat fixing in the oven are put into suitable hygienic packaging.

Príklad 5:Example 5:

Z polyméru TATREN HPF 321 s indexom toku 11 g/10 min sa zvlákňovaním pripravili predorientované polypropylénové vlákna s trilobalovým profilom za použitia zdravotne nezávadnej zvlákňovacej preparácie BK 2083. Predorientované vlákna boli ďalej dodížené a celková dĺžková hmotnosť bola 616 dtex/100 fibríl. Vláknam boli dané zákruty, a to 87 zákrutov na 1 meter. Vlákna boli zafixované pri teplote 120 ’C. Výsledné mechanické vlastnosti vlákien sú pevnosť 3,01 cN/dtex a 49,4 % ťažnosti.Pre-oriented polypropylene fibers with a trilobal profile were prepared by spinning from TATREN HPF 321 polymer with a flow index of 11 g / 10 min using a health-friendly spinning preparation BK 2083. The pre-oriented fibers were further fed and the total density was 616 dtex / 100 fibrils. Twists were given to the fibers, namely 87 twists per meter. The fibers were fixed at 120 ° C. The resulting mechanical properties of the fibers are a strength of 3.01 cN / dtex and 49.4% ductility.

K voskovaniu vlákien sa pripravil upravený parafínový vosk s obsahom 20 % hm. včelieho vosku a 2 % hm. mentolu. Teplota mäknutia upraveného vosku stanovená metódou diferenciálnej termickej analýzy bola 57 ’C. Na špeciálnom poloprevádzkovom zariadení bolo nanesených 26% hm. vosku na povrch zväzku skaných fixovaných vlákien. Takto bola pripravená voskovaná zubná niť k ďalšiemu používaniu. Pre účely expedovania bola vhodne hygienicky zabalená ako v príklade 1.For waxing of the fibers, treated paraffin wax containing 20 wt. beeswax and 2 wt. menthol. The softening temperature of the treated wax determined by the differential thermal analysis method was 57 C. C. On a special pilot plant, 26 wt. wax on the surface of the bundle of twisted fixed fibers. Thus, waxed dental floss was prepared for further use. It was suitably hygienically packaged for dispatch as in Example 1.

Priemyselná využiteľnosťIndustrial usability

Voskovaná zubná niť podľa vynálezu je použiteľná ako vhodná pomôcka na čistenie medzizubných priestorov pri prevencii ochorenia ústnej dutiny.The waxed dental floss of the invention is useful as a suitable aid for cleaning the interdental spaces in preventing oral cavity disease.

Claims

Waxed dental floss consisting of a bundle of polypropylene fine fibrils, characterized in that the individual smooth polypropylene fibrils have a non-circular cross-section, a unit length of from 5 to 8 dtex and a total length of from 400 to 1200 dtex, the thread surface being treated with 15 to 35% wt. % paraffin wax containing 5 to 20 wt. beeswax and 0.5 to 5.0 wt. menthol, respectively. other medicinal and / or flavoring, with a softening point of 55 to 65 ’C.