SE467159B - SET FOR PREPARATION OF A BITUMINOUS BINDING, INCLUDING POLYMERS - Google Patents

SET FOR PREPARATION OF A BITUMINOUS BINDING, INCLUDING POLYMERS

Info

Publication number
SE467159B
SE467159B SE8802026A SE8802026A SE467159B SE 467159 B SE467159 B SE 467159B SE 8802026 A SE8802026 A SE 8802026A SE 8802026 A SE8802026 A SE 8802026A SE 467159 B SE467159 B SE 467159B
Authority
SE
Sweden
Prior art keywords
vinyl acetate
composition
ethylene
polyisobutylene
acetate copolymer
Prior art date
Application number
SE8802026A
Other languages
Swedish (sv)
Other versions
SE8802026L (en
SE8802026D0 (en
Inventor
J Lesage
Original Assignee
British Petroleum Co Plc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by British Petroleum Co Plc filed Critical British Petroleum Co Plc
Publication of SE8802026D0 publication Critical patent/SE8802026D0/en
Publication of SE8802026L publication Critical patent/SE8802026L/en
Publication of SE467159B publication Critical patent/SE467159B/en

Description

15 20 25 30 35 467 159 Uppfinningen omfattar även framställning av gatubeläggningar eller tätningar med användning av den enligt ovan erhållna produkten. övriga syften med uppfinningen kommer att klart framgå av följande beskrivning och utföringsexempel. The invention also comprises the preparation of street coatings or seals using the product obtained as above. Other objects of the invention will become apparent from the following description and embodiments.

Sättet enligt uppfinningen består huvudsakligen i att man till en bitumen sätter en blandning, framställd på förhand och omfattande en eten/vinylacetat-sampolymer och en polyísobuten med en molekylvikt av mellan 400 och 1000.The process according to the invention consists essentially in adding to a bitumen a mixture, prepared in advance and comprising an ethylene / vinyl acetate copolymer and a polyisobutylene having a molecular weight of between 400 and 1000.

Kompositionen. omfattande blandningen av etenlvinylacetat- -sampolymeren och polyisobuten, faller likaledes inom upp- finningens ram. Den framställes företrädevis genom gradvis tillsats av granuler av eten/vinylacetat-sampolymer till en vätskeformig polyisobuten vid en temperatur något över upp- lösningstemperaturen för eten/vinylacetat-sampolymeren, genom blandning i en långsam skovelomrörare (malaxator) eller in- sprutning medelst en pump och omrörning.The composition. comprising the mixture of the ethylene / vinyl acetate copolymer and polyisobutylene, likewise falls within the scope of the invention. It is preferably prepared by gradually adding granules of ethylene / vinyl acetate copolymer to a liquid polyisobutylene at a temperature slightly above the dissolution temperature of the ethylene / vinyl acetate copolymer, by mixing in a slow paddle stirrer (malaxator) or injecting by means of a pump and stirring.

Eten/vinylacetat-sampolymeren är företrädesvis en sampolymer, innehållande 5-45 viktprocent vinylacetatenheter och företrä- desvis mindre än 20 %, och med smältflödesindex mellan 0,1 och 600, företrädesvis mellan 100 och 200. Polyisobutenen har företrädesvis en molekylvikt av under 1000 och över 400.The ethylene / vinyl acetate copolymer is preferably a copolymer, containing 5-45% by weight of vinyl acetate units and preferably less than 20%, and having a melt flow index between 0.1 and 600, preferably between 100 and 200. The polyisobutylene preferably has a molecular weight of less than 1000 and over 400.

Sammanblandningen av polymerer utföres i förhållanden mellan polyísobuten och eten/vinylacetat av mellan 90:10 och 50:50, företrädesvis av storleksordningen 80:20.The blending of polymers is carried out in polyisobutene to ethylene / vinyl acetate ratios of between 90:10 and 50:50, preferably of the order of 80:20.

Bitumen är företrädesvis en blåst eller direkt vägbitumen av inom tekniken i och för sig väl känt slag.Bitumen is preferably a blown or direct road bitumen of a type well known in the art per se.

Komositionen på basis av blandningen av polymerer sättes till denna bitumen i proportioner av företrädesvis l-35 %. räknat på kompositionens totala vikt. företrädesvis i proportioner av 5-30 %. 10 15 20 25 30 35 467 159 Vi har funnit att det är möjligt att framställa ett bituminöst bindemedel direkt på stället genom blandning av kompositionen på basis av polymerer enligt ovanstående definition och bitu- men under en tid av mindre än 15 minuter med t.ex. en skovel- omrörare (malaxator) eller nästan omedelbart med en statisk blandare.The composition based on the mixture of polymers is added to this bitumen in proportions of preferably 1-35%. calculated on the total weight of the composition. preferably in proportions of 5-30%. We have found that it is possible to prepare a bituminous binder directly on site by mixing the composition on the basis of polymers as defined above and the bitumen for a time of less than 15 minutes with e.g. . a paddle stirrer (malaxator) or almost immediately with a static mixer.

Vi har funnit att tillsats av kompositionen. innehållande blandningen av polymerer enligt ovanstående definition, gör det möjligt att uppnå en synergistisk effekt som ett resultat av en höjning av mjukningspunkten och en samtidig minskning av lågtemperatur-brottpunkten. Som ett resultat av kombinationen är det således möjligt att förbättra det plastiska området och. genomträngningsindex. Detta är speciellt överraskande mot bakgrund av egenskaperna för de enskilda polymererna.We have found that the addition of the composition. containing the mixture of polymers as defined above, makes it possible to achieve a synergistic effect as a result of an increase in the softening point and a simultaneous decrease in the low-temperature breaking point. As a result of the combination, it is thus possible to improve the plastic area and. penetration index. This is particularly surprising given the properties of the individual polymers.

En annan fördel med uppfinningen är att kompositionen på basis av polymerblandningen. avsedd att sättas till bitumen. kan lagras utan några problem under lång tid utan nedbrytning och med bibehållande av den ursprungliga viskositeten.Another advantage of the invention is that the composition is based on the polymer blend. intended to be added to bitumen. can be stored without any problems for a long time without degradation and while maintaining the original viscosity.

De således framställda gatubeläggningarna förhåller sig speciellt väl i stark värme. Vi har i själva verket funnit att bindemedlet bibehåller tillräcklig fasthet och viskositet för att förebygga varje eventuell irreversibel deformation på grund av flytning hos ytbeläggningen, speciellt under inverkan av tung trafik.The street coatings thus prepared behave particularly well in strong heat. In fact, we have found that the adhesive maintains sufficient firmness and viscosity to prevent any possible irreversible deformation due to flow of the coating, especially under the influence of heavy traffic.

Det således applicerade bindemedlet uppvisar dessutom i kallt väder beständighet mot köldsprickor, vilket möjliggör för vägbeläggningen att motstå vinterpåfrestningar. härrörande exempelvis från dubbdäck. De på detta sätt framställda bitu- minösa bindemedlen uppvisar dessutom extraordinära egenskaper beträffande elasticitet. seghet och vidhäftningsförmåga till aqgfêqöten.The adhesive thus applied also exhibits resistance to cold cracks in cold weather, which enables the pavement to withstand winter stresses. originating, for example, from studded tires. The bituminous binders produced in this way also show extraordinary properties in terms of elasticity. toughness and adhesion to the aqgfêqöten.

Nedan följande exempel avser att belysa uppfinningen utan att därvid begränsa densamma. 4e7 159 10 15 20 25 30 35 EXGIIIQQ l l 23 delar av en eten/vinylacetat-sampolymer med en vinylacetat- halt av 18 % och smältflödesindex 140 och 77 delar av en poly- isobuten med molekylvikt 900 blandas vid en temperatur av l40°C i en skovelomrörare (malaxator), varvid etenlvinylace- tat-sampolymeren införes i form av granulat. Med 3 kg polyme- rer och ett varvtal av 300 varv per minut uppnås insmältning av eten/vinylacetat-granulerna i polyisobutenen under mindre än 15 minuter.The following examples are intended to illustrate the invention without thereby limiting it. 23 parts of an ethylene / vinyl acetate copolymer having a vinyl acetate content of 18% and a melt flow index of 140 and 77 parts of a polyisobutylene having a molecular weight of 900 are mixed at a temperature of 140 ° C in a paddle stirrer (malaxator), the ethylene / vinyl acetate copolymer being introduced in the form of granules. With 3 kg of polymers and a speed of 300 rpm, melting of the ethylene / vinyl acetate granules in the polyisobutylene is achieved in less than 15 minutes.

Förvaring av denna polymerblandning under 15 dagar vid en temperatur av l35°C visar att blandningen är fullständigt stabil och bibehåller sin ursprungliga viskositet. Ingen avsättning kan observeras.Storage of this polymer mixture for 15 days at a temperature of 135 ° C shows that the mixture is completely stable and retains its original viscosity. No deposition can be observed.

Denna blandning sättes till vägbitumen (40/50) i proportioner av 30 % av polymerblandningen, räknat på kompositionens totala vikt. Polymer/bitumen-blandningen framställes under mindre än 15 minuter medelst en skovelomrörare (malaxator).This mixture is added to the road bitumen (40/50) in proportions of 30% of the polymer mixture, based on the total weight of the composition. The polymer / bitumen mixture is prepared in less than 15 minutes by means of a paddle stirrer (malaxator).

E§2m2§l_ë (jämförelse) 2 % eten/vinylacetat-sampolymer. innehållande 18 % vinylacetat och med smältflödesindex 140 sättes till en 40/50-kvalitet bitumen (penetration 41, mjukningspunkt 56, Fraass-punkt -9°C, inträngningsindex +0,46). Mjukningspunkten bringas till 60.S°C och inträngníngsindex till 0,85 utan att Fraass-punkten modi- fieras. Det plastiska området har stigit från 65 till 69,S°C.(§) 2% ethylene / vinyl acetate copolymer. containing 18% vinyl acetate and with a melt flow index 140 is added to a 40/50 grade bitumen (penetration 41, softening point 56, Fraass point -9 ° C, penetration index +0.46). The softening point is brought to 60 ° C and the penetration index to 0.85 without the Fraass point being modified. The plastic range has risen from 65 to 69 ° C.

Tillsats av 5 % polyisobuten med molekylvikt 900 till samma bitumen ändrar inte mjukningspunkten, sänker Fraass-punkten till -16°C och bringar genomträngningsindex till +O,5 och det plastiska området till C.Addition of 5% polyisobutylene with molecular weight 900 to the same bitumen does not change the softening point, lowers the Fraass point to -16 ° C and brings the penetration index to + 0.5 and the plastic range to C.

Tillsats till samma bitumen av en komposition såsom definieras i exempel 1 på basis av eten/vinylacetat-sampolymer och poly- 10 15 20 25 30 35 467 159 isobuten och innehållande 28 % eten/vinylacetat-sampolymer samt 72 % polyisobuten. vilken komposition tillsättes i en proportion av 7 % räknat på bitumen-kompositionen, bringar mjukningspunkten till 58°C, Fraass-punkten till -l7°C, genom- trängningsindex till +l.2 och det plastiska omrâdet till 75°C.Addition to the same bitumen of a composition as defined in Example 1 based on ethylene / vinyl acetate copolymer and polyisobutylene and containing 28% ethylene / vinyl acetate copolymer and 72% polyisobutylene. which composition is added in a proportion of 7% based on the bitumen composition, brings the softening point to 58 ° C, the Fraass point to -17 ° C, the penetration index to + 1.2 and the plastic range to 75 ° C.

Tillsats av kompositionen gör det således möjligt att för- bättra det bituminösa bindemedlet med avseende pâ alla dessa egenskaper utan att öka dess driftspäfrestningar.Addition of the composition thus makes it possible to improve the bituminous binder with respect to all these properties without increasing its operating stresses.

Exempel 3 Man framställer en beredning, innehållande 10 delar polyisobu-_ ten med molekylvikt 900 och tre delar eten/vinylacetat-sam- polymer med en vinylacetathalt av 18 % och smältflödesindex 140 och denna beredning införes i 87 delar av en 40/50-bitumen enligt ovanstående definition.Example 3 A preparation is prepared containing 10 parts of 900 molecular weight polyisobutylene and three parts of ethylene / vinyl acetate copolymer having a vinyl acetate content of 18% and a melt flow index of 140 and this preparation is introduced into 87 parts of a 40/50 bitumen as defined above.

Följande viskositeter observeras: Vid l40°C: 722 mPa.s; vid l60°C: 297 mPa.s; vid l80°C: 142 mPa.s medan basbitumenen har följande viskositeter: Vid l40°C: 600 mPa.S; vid l60°C: 263 mPa.S; vid l80°C: 142 mPa.s.The following viscosities are observed: At 140 ° C: 722 mPa.s; at 160 ° C: 297 mPa.s; at 180 ° C: 142 mPa.s while the base bitumen has the following viscosities: At 140 ° C: 600 mPa.s; at 160 ° C: 263 mPa.S; at 180 ° C: 142 mPa.s.

Man har funnit att kombinationen enligt uppfinningen gör det möjligt att något öka viskositeten i värme och även att för- bättra handskandet med blandningen. Detta har observerats vid rotationsskjuvpresstest i Laboratoire des Ponts de Chaussées med en diskontinuerlig O/14-blandning med sammansättningen: 10/14 porfyr: 26 % 6/10 porfyr: 31 % 0/2 porfyr: 39 % kalkhaltiga finmaterial: 4 % bindemedelshalt: 7.7 pph (viktdelar per 100 viktdelar aggregat). 3467 159 10 15 20 25 30 35 0/14-blandningen med polymer-bindemedlet enligt uppfinningen uppnår 89,5 packning (sammanträngdhet) vid 10 rotationer 92,0 packning vid 20 rotationer 95,0 packning vid 50 rotationer.It has been found that the combination according to the invention makes it possible to slightly increase the viscosity in heat and also to improve the handling of the mixture. This has been observed in rotary shear press tests in the Laboratoire des Ponts de Chaussées with a discontinuous U / 14 mixture with the composition: 10/14 porphyry: 26% 6/10 porphyry: 31% 0/2 porphyry: 39% calcareous fines: 4% binder content: 7.7 pph (parts by weight per 100 parts by weight of aggregate). The 0/14 mixture with the polymeric binder according to the invention achieves 89.5 packing (compressibility) at 10 rotations 92.0 packing at 20 rotations 95.0 packing at 50 rotations.

Det på detta sätt framställda bindemedlet uppvisar dessutom klart förbättrade egenskaper beträffande utmattningsbeständig- het och beständighet mot vattenavfläkning eller adhesions- egenskaper. vilka även klart förbättras.The adhesive prepared in this way also has clearly improved properties in terms of fatigue resistance and resistance to water peeling or adhesion properties. which are also clearly improving.

Ett utmattningstest utföres enligt LCPC (Laboratoire Central des Ponts et Chaussées)-metoden med sinusformad böjning till konstant deformation av trapetsformade testbitar. varvid testet utföres med användning av skivor av blandningar, till- verkade och kompakterade enligt Laboratoire des Ponts et Chaussées-förfarandena på blandningar enligt följande receptur: 6/10 La Noubleau 33 % 2/6,3 La Noubleau 24 % 0/2 La Noubleau 40,7 % kalkhaltiga fyllmedelz 2.3 % bindemedel 5.75 pph.A fatigue test is performed according to the LCPC (Laboratoire Central des Ponts et Chaussées) method with sinusoidal bending to constant deformation of trapezoidal test pieces. the test being carried out using slices of mixtures, manufactured and compacted according to the Laboratoire des Ponts et Chaussées procedures on mixtures according to the following recipe: 6/10 La Noubleau 33% 2 / 6.3 La Noubleau 24% 0/2 La Noubleau 40.7% calcareous fillers 2.3% binder 5.75 pph.

Följande värden erhålles vid en frekvens av 25 herz och vid 10°C: med 106 cykler är den relativa deformationen: 1,40 X 10-4 för referensblandningen (40/50 bindemedel) men 2,20 x 10-4 för ovan definierade blandning med bitumen/polymer-bindemedel.The following values are obtained at a frequency of 25 Hz and at 10 ° C: with 106 cycles the relative deformation is: 1.40 X 10-4 for the reference mixture (40/50 binder) but 2.20 x 10-4 for the mixture defined above with bitumen / polymer binder.

Vid 105 cykler är den relativa deformationen: 2 x 10-4 för referensblandningen och 3 x 10-4 för blandningen med bitumen/polymer-bindemedel_ fr' Man finner således att det föreligger en större tillåten de- formation för samma utmattningstesttid för blandningen, inne- hållande polymerbindemedlet enligt uppfinningen. Vid vatten- strippningstestet framgår denna egenskap av förhållandet 10 15 467 159 mellan beständigheterna vid l8°C vid DURIEZ- (eller LCPC)-en- axligt tryckförsök, med bibehållande av neddoppning i vatten under 7 dagar och å andra sidan koncentrationen i torrt till- stånd. likaledes för 7 dagar.At 105 cycles the relative deformation is: 2 x 10-4 for the reference mixture and 3 x 10-4 for the mixture with bitumen / polymer binder_fr 'It is thus found that there is a larger allowable deformation for the same fatigue test time for the mixture, inside - holding the polymer binder according to the invention. In the water stripping test, this property is shown by the ratio of the resistances at 18 ° C in the DURIEZ (or LCPC) one-axis pressure test, while maintaining immersion in water for 7 days and on the other hand the concentration in dry conditions. stand. likewise for 7 days.

Med följande blandningsberedning: 10/14 La Noubleau 69 % 0/2 La Noubleau 27,5 % kalkhaltigt fyllmedelz 3,5 % bindemedelshalt: 5,5 pph är förhållandet mellan beständigheterna 0.88 för 40/50 refe- rensblandningen. jämfört med 0,96 för blandningen med bitu- men/polymerbindemedel enligt ovanstående definition.With the following mixture preparation: 10/14 La Noubleau 69% 0/2 La Noubleau 27.5% calcareous fillerz 3.5% binder content: 5.5 pph, the ratio of the constituents is 0.88 for the 40/50 reference mixture. compared to 0.96 for the bitumen / polymer binder mixture as defined above.

Claims (1)

5467 159 10 15 20 25 30 Patentkrav l. Sätt för framställning av ett bituminöst bindemedel, inne- hållande polymerer. k ä n n e t e c k n a t av att en bitu- men försättes med en på förhand framställd komposition av en eten/vinylacetat-sampolymer och en polyisobuten med molekyl- vikt 400-1000 i ett molärt förhållande mellan polyisobuten och eten/vínylacetat av från 90:10 till 50:50. 2. Sätt enligt krav l, k ä n n e t e c k n a t av att eten/vinylacetat-sampolymeren är en sådan, som innehåller 5-45 viktprocent vinylacetatenheter och med smältflödesindex 0.1-600. 3. Sätt enligt krav l, av att k ä n n e t e c k n a_t kompositionen utgör l-35 viktprocent av hela blandningens vikt. 4. Sätt enligt något av kraven l-3 k ä n n e t e c k n a t av att det genomföres på användningsstället. varvid bland- ningstiden ej överstiger 15 minuter. 5. Sätt enligt krav 4, k ä n n e t e c k n a t av att den resulterande blandningen efter fullständig sammanblandning appliceras som vägbeläggning. 6. Sätt att framställa en komposition enligt definitionen i något av kraven l-2. k ä n n e t e c k n a t av att man gradvis sätter granuler av eten/vinylacetat-sampolymer till polyisobutenen vid en temperatur, som ligger något över upp- lösningstemperaturen för eten/vinylacetat-sampolymeren i den flytande polyisobutenen under sammanblandning. 10 467 159 7. Sätt enligt något av kraven 1-5, k ä n n e t e c k n a t av att kompositionen framställes medelst ett förfarande en- ligt krav 6. 8. Komposítion, k ä n n e t e c k n a d av att den fram- ställts i enlighet med sättet enligt krav 6. 9. Bitumínöst bindemedel, k ä n n e t e c k n a t av att det framställts medelst förfarandet enligt något av kraven5467 159 10 15 20 25 30 Claim 1. A process for the preparation of a bituminous binder containing polymers. characterized in that a bitumen is added to a preformed composition of an ethylene / vinyl acetate copolymer and a polyisobutylene having a molecular weight of 400-1000 in a molar ratio of polyisobutylene to ethylene / vinyl acetate of from 90:10 to 50 : 50. 2. A method according to claim 1, characterized in that the ethylene / vinyl acetate copolymer is one which contains 5-45% by weight of vinyl acetate units and with a melt flow index of 0.1-600. 3. A method according to claim 1, in that the composition constitutes 1 to 35% by weight of the weight of the whole mixture. 4. A method according to any one of claims 1-3, characterized in that it is carried out at the place of use. the mixing time not exceeding 15 minutes. 5. A method according to claim 4, characterized in that the resulting mixture after complete mixing is applied as a road surface. A method of preparing a composition as defined in any one of claims 1-2. characterized in that granules of ethylene / vinyl acetate copolymer are gradually added to the polyisobutylene at a temperature slightly above the dissolution temperature of the ethylene / vinyl acetate copolymer in the liquid polyisobutylene during mixing. A composition according to any one of claims 1-5, characterized in that the composition is prepared by a process according to claim 6. A composition, characterized in that it is prepared in accordance with the method according to claim 6. Bituminous binder, characterized in that it is prepared by the process according to any one of the claims 1. -5 eller 7.1. -5 or 7.
SE8802026A 1987-04-02 1988-05-31 SET FOR PREPARATION OF A BITUMINOUS BINDING, INCLUDING POLYMERS SE467159B (en)