SE463673B - Bolt cement for securing bolts in boreholes in rock and concrete and anchoring prefabricated concrete elements, method for producing the bolt cement, and the use thereof - Google Patents
Bolt cement for securing bolts in boreholes in rock and concrete and anchoring prefabricated concrete elements, method for producing the bolt cement, and the use thereofInfo
- Publication number
- SE463673B SE463673B SE8702891A SE8702891A SE463673B SE 463673 B SE463673 B SE 463673B SE 8702891 A SE8702891 A SE 8702891A SE 8702891 A SE8702891 A SE 8702891A SE 463673 B SE463673 B SE 463673B
- Authority
- SE
- Sweden
- Prior art keywords
- cement
- weight
- sulphonated
- bolt
- specific surface
- Prior art date
Abstract
Description
463 673 2 10 15 20 25 30 35 Likaså måste vid montage av byggnader utförda med prefabrice- rade betongelement vissa element. såsom exempelvis pelare. förankras i omgivande konstruktionsdelar, i första hand till dess hela stommen monterats och byggnaden som helhet kan bära beräknade laster. Denna förankring utförs normalt genom in- gjutning av gängade bultar. För att få en rationell produktion krävs att det använda ingjutningsbruket ger en tillräckligt snabb hâllfasthetstillväxt. Detta har medfört att man normalt använder olika typer av polymerbaserade bindemedel såsom epoxi o dyl. Av arbetarskyddsskäl finns dock starka önskemål om att kunna använda andra, mer hälsosamma typer av bindemdel. 463 673 2 10 15 20 25 30 35 Similarly, when assembling buildings made with prefabricated concrete elements some elements. such as pillars, for example. anchored in surrounding structural parts, primarily to its entire frame assembled and the building as a whole can carry calculated loads. This anchoring is normally performed by casting of threaded bolts. To get a rational production it is required that the casting mill used provides a sufficient rapid strength growth. This has meant that one normally uses various types of polymer-based binders such as epoxy o dyl. For occupational safety reasons, however, there is a strong desire to be able to use other, healthier types of binders.
Fordringarna på ett sådant bindemedel överensstämmer i stort med punkterna l och 2 enligt ovan. En cementpasta med lämplig sammanställning borde därför kunna användas för båda dessa ovan nämnda bultförankringsfall. 0 Prov gjorda med ett cement med en C3A-halt av 2 viktt och ett vattencementtal (vct) av ca 0.28 gav en bultcementpasta med lämplig konsistens. Med retarderande och accelererande tillsatsmedel erhölls dessutom önskad bindetid och snabb häll- fasthet.The requirements for such a binder are broadly consistent with points 1 and 2 as above. A cement paste with suitable compilation should therefore be able to be used for both of these above mentioned bolt anchoring case. 0 Samples made with a cement with a C3A content of 2 weights and a water cement number (vct) of about 0.28 gave a bolt cement paste with appropriate consistency. With decelerating and accelerating additives also obtained the desired binding time and fast pouring firmness.
Resultaten visade sig emellertid inte vara reproducerbara från gång till annan och från ett cementparti till ett annat.However, the results did not appear to be reproducible from time to another and from one cement lot to another.
Undersökningar visade att kristallvattenhalten i cementets gipsinnehâll varierade i olika partier. Vid tillverkning av portlandcement tillsätts gips i samband med malningen av klinker till cement, detta för att inte cementets trikalcium- ~ aluminatinnehâll skall reagera direkt med vatten och därmed orsaka en omedelbar bindning av cementpastan. Då gips finns närvarande reagerar istället trikalciumaluminatet med gipsen och bildar mineralet ettringit, varvid den snabba C3A- -hydratationen förhindras. Den bildade ettringiten omvandlas senare till andra sulfatföreningar och cementmineral, som trikalciumsilikat, C33, dikalciumsilikat. C2 kalciumaluminatferrit, C4AF. hydratiseras varigenom cementets hållfasthet börjar öka.Studies have shown that the crystal water content of the cement gypsum contents varied in different batches. In the manufacture of portland cement is added gypsum in connection with the grinding of clinker to cement, this so that the cement's tricalcium- ~ aluminate content must react directly with water and thus cause an immediate bonding of the cement paste. Then plaster is available present, the tricalcium aluminate instead reacts with the gypsum and forms the mineral etringingite, the rapid C3A hydration is prevented. The formed ettringite is converted later to other sulphate compounds and cement minerals, which tricalcium silicate, C33, dicalcium silicate. C2 calcium aluminate ferrite, C4AF. thereby hydrated the strength of the cement begins to increase.
S, och tetra- 10 15 20 25 30 35 3 465 673 Den tillsatta gipsen är i form av dihydrat eller halvhydrat. dvs innehåller olika mängder kristallvatten. Vid cementmal- ningen stiger temperaturen i kvarnen. Detta kan medföra att gipsens kristallvatten förångas helt eller delvis, beroende på omgivningens temperatur och kyleffekt. Om sådant cement senare blandas med vatten kan ibland en falsk snabbindning uppstå, då gipsen åter tar upp vatten som kristallvatten. Bindnings- kraften blir då relativt svag, men kan vara besvärande vid sådana cementrika sammansättningar som bultcement. Den bristande reproducerbarheten hos vårt bultcement orsakades förmodligen till största delen av sådan gipsreaktion. och problemet gav anledning till försök att finna ett annat material än gips att reglera cementets bindetid med.S, and tetra- 10 15 20 25 30 35 3 465 673 The added gypsum is in the form of dihydrate or semi-hydrate. ie contains different amounts of crystal water. In the case of cement the temperature in the mill rises. This can lead to the crystal water of the gypsum evaporates completely or partially, depending on ambient temperature and cooling effect. About such cement later mixed with water, a false fast binding can sometimes occur, then the plaster again absorbs water as crystal water. Binding the force then becomes relatively weak, but can be troublesome such cement-rich compositions as bolt cement. The the lack of reproducibility of our bolt cement was caused probably for the most part of such plaster reaction. and the problem gave rise to attempts to find another materials other than gypsum to regulate the bonding time of the cement.
En tidigare känd gipsersättning är en kombination av produkter baserade på sulfonerad polyelektrolyt och olika typer av alkalikarbonater. Sådana tillsatser medför att cementets C3A inkapslas av ett diffusionsskikt som fördröjer vattnets penetrering och därmed förhindrar den omedelbara bindningen genom hydratation av C3A. Dylika tillsatser, som maximalt tillsätts med 2 viktt. förändrar också dramatiskt cement- pastans flytegenskaper i förhållande till en pasta baserad på vanlig gipshaltig cement. Från att reologiskt sett ha s.k.A previously known plaster replacement is a combination of products based on sulfonated polyelectrolyte and various types of alkali carbonates. Such additives cause the cement C3A encapsulated by a diffusion layer which retards the water penetration and thus prevents the immediate binding by hydration of C3A. Such additives, as a maximum added with 2 weights. also dramatically changes cement the flow properties of the pasta in relation to a pasta based on ordinary gypsum-containing cement. From rheologically speaking, have so-called
Bingham-egenskaper med utpräglad flytgräns fås ett material med Newton-egenskaper, dvs. utan någon flytgräns. Cement- pastans vattenhalt kan därmed minskas väsentligt vid oföränd- rad konsistens, vilket möjliggör höga hållfastheter, lämpliga för bultcement. där man vill ha både en styrd snabb bindning och en snabb hållfasthetstillväxt.Bingham properties with a pronounced yield strength are obtained from one material with Newton properties, i.e. without any yield strength. Cement- the water content of the paste can thus be significantly reduced at unchanged range of consistency, enabling high strengths, suitable for bolt cement. where you want both a controlled fast binding and rapid strength growth.
På de åtföljande ritningarna visar fig. l hâllfastheten för gipsfritt cement jämfört med standard Portland cement. Det streckade området anger gränserna för de principiella möjligheterna att reglera hållfasthetsprofilen, och fig. 2 den principiella inverkan av tillsatsmedel på binde- tiden. 463 673 10 15 20 25 30 35 Med utgångspunkt från detta har vi undersökt olika medel för att utveckla ett snabbindande bultcement.In the accompanying drawings Fig. 1 the strength of gypsum-free cement compared to standard Portland cement. The dashed area indicates the boundaries of the the fundamental possibilities of regulating the strength profile, and Fig. 2 shows the principal effect of additives on the binder the time. 463 673 10 15 20 25 30 35 Based on this, we have investigated various means to develop a fast-binding bolt cement.
Bultcementpastan enligt uppfinningen kännetecknas av att det be- står av ett cement av klinker med en halt av trikalciumaluminat mindre än 5 vikt% malda till en specifik yta motsvarande 500-700 m2/kg med tillsats av 0,1-0,5 vikt% sulfonerat lignin som mal- hjälpmedel, innehållande 0,1-l,0% räknat på cementvikten av ett första bindetids- och hållfasthetsreglerande tillsatsmedel av sulfonerade polyelektrolyter såsom lignosulfonat, sulfonerat lignin, sulfonerade kondensat av naftalen, melamin eller fenol eller motsvarande kondensat med formaldehyd, 0,2-2,0% räknat på cementvikten av ett andra bindetids- och hâllfasthetsreglerande tillsatsmedel av ett eller flera alkali- karbonat, såsom K2C03, Na2CO3, KHCO3, NaHCO3 samt 0,1-l,0% räknat på cementvikten av ett konsistensreglerande tillsatsmedel bestående av amorf kiselsyra med en specifik yta större än 100 ooo m2/kg.The bolt cement paste according to the invention is characterized in that it is consists of a cement of clinker with a content of tricalcium aluminate less than 5% by weight ground to a specific surface area corresponding to 500-700 m2 / kg with the addition of 0.1-0.5% by weight of sulfonated lignin as malt aids, containing 0.1-1,0% calculated on the cement weight of a first binding and strength-regulating additive of sulfonated polyelectrolytes such as lignosulfonate, sulfonated lignin, sulfonated condensates of naphthalene, melamine or phenol or equivalent condensate with formaldehyde, 0.2-2.0% based on the cement weight of a second bonding time and strength-regulating additives of one or more alkali carbonate such as K 2 CO 3, Na 2 CO 3, KHCO 3, NaHCO 3 and 0.1-0.0% calculated on the cement weight of a consistency regulator additives consisting of amorphous silicic acid with a specific surface area greater than 100 ooo m2 / kg.
Cementet utgörs av klinker med C3A-halt 55 vikt% som malts till en spec. yta motsvarande 500-700 m2/kg (Blaine). Vid malningen tillsätts ett malhjälpmedel bestående av sulfonerat lignin som doseras i en mängd av 0,l~0,5 vikt%.The cement consists of clinker with a C3A content of 55% by weight which has been ground to a spec. area corresponding to 500-700 m2 / kg (Blaine). When grinding add a grinding aid consisting of sulfonated lignin which dosed in an amount of 0.1 ~ 0.5% by weight.
De bindetidsreglerande tillsatsmedlen utgörs av två komponenter.The binding time-regulating additives consist of two components.
Komponent A kan bestå av sulfonerade polyelektrolyter såsom ligë nosulfonat, sulfonerat lignin, sulfonerade koncentrat av nafta- len, melamin eller fenol, liksom även kondensat med formaldehyd.Component A may consist of sulfonated polyelectrolytes such as ligë nosulfonate, sulfonated lignin, sulfonated concentrates of naphtha- melamine or phenol, as well as condensate with formaldehyde.
Komponent A tillsätts med en mängd om 0,1-l,0% av cementvikten.Component A is added in an amount of 0.1-0.0% of the cement weight.
Komponent B utgörs av olika typer av alkalikarbonater såsom KZCO3, Na2CO3, KHCO3, NaHCO3, som doseras i en mängd av 0,2-2% av cementvikten.Component B consists of various types of alkali carbonates such as KZCO3, Na2CO3, KHCO3, NaHCO3, which are dosed in an amount of 0.2-2% of cement weight.
Bultcementpastans konsistens regleras genom tillsats av amorf kiselsyra med spec. yta >100 000 m?/kg (BET). Tillsatsmedlet tillsätts med en dosering av 0,1-1,0% av cementvikten.The consistency of the bolt cement paste is regulated by the addition of amorphous silicic acid with spec. area> 100,000 m? / kg (BET). The additive is added at a dosage of 0.1-1.0% of the cement weight.
Bultcementpastan tillverkas genom att tillsatsmedlen enligt ovan 'x 10 15 20 25 30 35 5 4650673 tillförs cementet i form av vattenlösning eller genom torrin- blandning. Till blandningen sätts vatten så att total vatten- halt, inklusive eventuellt vatten i vattenupplösta tillsatsme- del, är 20-25% av cementvikten. I Följande prov har utförts som belyser bultcementpastans egenska- per.The bolt cement paste is manufactured by adding the additives as above 'x 10 15 20 25 30 35 5 4650673 the cement is added in the form of an aqueous solution or by drying mixture. To the mixture is added water so that the total water content, including any water in water-dissolved additives part, is 20-25% of the cement weight. IN The following tests have been performed which illustrate the properties of the bolt cement paste. per.
Exempel 1: För att prova bultcementpastans tryckhàllfasthetsutveckling göts prismor, 40x40xl6O mm, vilka provades med avseende på tryckhàll- fastheten vid olika tidpunkter. Jämförelse gjordes med en bult- cementpasta som normalt används, bestående av vanligt portland- cement. Resultaten framgàr av nedanstående tabell.Example 1: To test the pressure strength development of the bolt cement paste was cast prisms, 40x40x16 mm, which were tested for pressure holding the firmness at different times. Comparison was made with a bolt- cement paste normally used, consisting of ordinary Portland cement. The results are shown in the table below.
Tryckhållfasthet, MPa Bultcementpasta Vanlig bultcement- Ålder enligt uppfinningen pasta 2 tim 7,8 0 4 tim 16,9 O 8 tim 56,8 l dygn 67,1 0,9 7 dygn 90,1 86,5 28 dygn 104,5 96,3 Exempel 2: För att prova den förankringskraft som uppnàs med bultcement- pasta enligt uppfinningen göts bultar av armeringsstàl, ß'25 mm KS40, in dels i form av 300 mm bultar i stålrör, dels i form av 1000 mm bultar i berg.Compressive strength, MPa Bolt cement paste Ordinary bolt cement Age according to the invention pasta 2 tim 7.8 0 4 h 16.9 O 8 tim 56.8 l day 67.1 0.9 7 days 90.1 86.5 28 days 104.5 96.3 Example 2: To test the anchoring force achieved with bolt cement paste according to the invention cast bolts of reinforcing steel, ß'25 mm KS40, partly in the form of 300 mm bolts in steel pipes, partly in the form of 1000 mm bolts in rock.
Brukstiden för bultcementpastan uppmättes till 45-70 min.The service life of the bolt cement paste was measured at 45-70 min.
Bultcementpastans förankringsegenskaper provades genom provdrag- ning av bultarna vid olika tidpunkter. Vid ingjutning i rör gjordes jämförelse med normal bultcementpasta. Resultat av prov- ningen framgár av nedanstående tabell. 463 673 6 10 15 20 25 30 35 - Prov i rör Brottlast, ton Bultcementpasta Vanlig bultcement- Ålder enligt uppfinningen pasta 2 tim >9,7 0 6 tim >l6*) 12 tim >l6*) , 24 tim >l6 3,7 *) Full förankringskraft. Brottlasten bestäms av stålets håll- fasthet.The anchoring properties of the bolt cement paste were tested by bolts at different times. When pouring into pipes comparison was made with normal bolt cement paste. Results of test The table is shown below. 463 673 6 10 15 20 25 30 35 Samples in tubes Break load, ton Bolt cement paste Ordinary bolt cement Age according to the invention pasta 2 hrs> 9.7 0 6 tim> l6 *) 12 tim> l6 *), 24 tim> l6 3.7 *) Full anchoring force. The breaking load is determined by the firmness.
- Prov 1 berg (enbart bultcementpasta enligt uppfinningen) Ålder Brottlast ton 2 tim 12,6-16,0 8 tim 12,6-16,0 Exempel 3: Hed avsikt att prova bultcementpastans förmåga att förankra bultar för tillfällig infästning av betongelement (exempelvis pelare) under montagetiden göts bultar, typ H27, in 300 mm i betong. Förankringen provades genom dragprov vid olika tid- punkter. Resultaten framgår av nedanstående tabell. Ålder Brottlast ton 2.5 tim 6,5 8 tim 9,8 24 um 19,9 i 3,71) 1) Brott erhölls i samtliga fall genom brott i kringliggande betong.Sample 1 rock (only bolt cement paste according to the invention) Age Breakage load ton 2 h 12.6-16.0 8 h 12.6-16.0 Example 3: Intended to test the bolt cement paste's ability to anchor bolts for temporary attachment of concrete elements (for example pillars) during assembly, bolts, type H27, were cast in 300 mm in concrete. The anchorage was tested by tensile tests at different times. points. The results are shown in the table below. Age Breakage load ton 2.5 and 6.5 8 tim 9.8 24 (19.9 and 3.71) 1) Crimes were obtained in all cases through crimes in the surrounding area concrete.
Kravet på denna typ av bultförankring var att klara ca 10 ton dragkraft efter 24 timmar. -4 10 i7 463 673 Pastan enligt uppfinningen har en sådan egenskapsprofil att den ger att att och är pumpbar under ca 1 timme och därefter binder snabbt och en snabb hâllfasthetstillväxt. Den kan också modifieras så den får en förlängd brukstid på upp till ca 2-3 timmar så större blandningar kan göras utan risk för stopp i pump slangar genom variationer av tillsatsmängderna inom de angivna gränserna. För att få en snabb bindning kan då en snabbindande tillsats tillsättas direkt i borrhâlet i samband med injekteringen, t.ex. vid förspända bultar där en snabb uppspänning är önskvärd.The requirement for this type of bolt anchoring was to handle about 10 tons traction after 24 hours. -4 10 i7 463 673 The paste according to the invention has such a property profile that the ger to to and is pumpable for about 1 hour and then binds quickly and a rapid strength growth. It can also be modified that way it gets an extended service life of up to about 2-3 hours so larger mixtures can be made without the risk of stopping the pump hoses through variations of the additive amounts within the specified limits. To get a quick binding then one can fast-binding additive is added directly to the borehole in connection with the grouting, e.g. at prestressed bolts where a fast clamping is desirable.
Claims (4)