SE437345B

SE437345B - Method for facilitating and rationalising sawing

Info

Publication number: SE437345B
Application number: SE8001840A
Authority: SE
Inventors: Bror Olof Heger
Original assignee: Bror Olof Heger
Priority date: 1980-03-10
Filing date: 1980-03-10
Publication date: 1985-02-25
Also published as: SE8001840L

Abstract

The invention concerns a method of sawing timber. Before sawing, the timber is heated through, dielectrically, to a temperature of up to 150 degrees C, preferably to around 100 degrees C, whereby sawing resistance is reduced. During the heating process, the timber comes to offer less sawing resistance and there is a less affect on the sawing unit from the timber and any irregularities in same. This means a more stable sawing cut. A thinner saw implement can be used, leading to increased performance and a reduction in the amount of shavings.

Description

8001840-1 virke fördröjer eller omöjliggör den varma_gasens intrång- ning i virket och därmed den snabba värmningen. En'ojämn: fuktfördelning medför därför också ojämn uppvärmning. 8001840-1 timber delays or makes it impossible for the hot_gas to penetrate the timber and thus the rapid heating. Uneven: moisture distribution therefore also results in uneven heating.

Vidare kompliceras värmningen av virket genom att den måste ske i tryckcylinder.Furthermore, the heating of the wood is complicated by the fact that it must take place in a pressure cylinder.

En snabb genomvärmning kan uppnås dielektriskt.A fast heating can be achieved dielectrically.

Värme av detta slag appliceras direkt inuti virket varför inga problem med värmeenergiens konvektion eller ledning _ föreligger. Värmningen insättes i samband med sågningen.Heat of this kind is applied directly inside the wood, so there are no problems with the convection or conduction of the heat energy. The heating is used in connection with the sawing.

Den kan få taga viss tid - exempelvis ett antal minuter -_ om den insättes på inmatat lager av stockar eller virke från vilket de enskilda enheterna hämtas för sågning. Bäst torde emellertid vara att värmningen helt eller delvis insättes pâ den virkesenhet som skall sågas. Denna värmning kan då om den omfattar en längd motsvarande hela enheten ske på den tid som det tager för enhetens sågning. Ju kortare avsnitt som värmes ju snabbare måste genomvärmningen j*ske. Värmningstiden måste härvid successivt kortas ned mot den tid som åtgår att såga det värmda avsnittet. Några principiella uppvärmningsproblem föreligger egentligen icke då det är en apparaturfråga att tillse att tillräcklig» gmängd energi tillföres virket.It may take some time - for example a number of minutes - if it is deposited on a loaded layer of logs or timber from which the individual units are retrieved for sawing. It is best, however, that the heating is applied in whole or in part to the wood unit to be sawn. This heating can then, if it covers a length corresponding to the entire unit, take place in the time it takes for the unit to be sawn. The shorter the section that is heated, the faster the through-heating must take place. The heating time must be gradually shortened to the time required to saw the heated section. There are not really any fundamental heating problems as it is a matter of equipment to ensure that a sufficient amount of energy is supplied to the wood.

Genom uppvärmningen komer virket att bjuda mindre sågmotstånd och lägre påverkan på sågorganet från oregel- bundenheter i virket._Qetta betyder stabilare sågsnitt varvid tunnare sågorgan kan användas medförande ökat utbyte och minskning av spânmängden: Tour 80018-40-1 För att få påtaglig effekt bör virkets temperatur höjas till minst 50 grader. Normalt bör uppvärmning ske till 80 ä 100 grader företrädesvis till omkring 100 grader.Through the heating, the wood will offer less sawing resistance and lower impact on the saw member from irregularities in the wood. This means more stable saw cuts where thinner saw means can be used leading to increased yield and reduction of the amount of chip: Tour 80018-40-1 To get a noticeable effect, the wood should temperature is raised to at least 50 degrees. Normally, heating should take place to 80 to 100 degrees, preferably to about 100 degrees.

Om virket värmes till 100 grader synes sågmotståndet minska till virka 40 procent eller mindre av motståndet vid 20 grader.If the wood is heated to 100 degrees, the saw resistance seems to decrease to wood 40 percent or less of the resistance at 20 degrees.

Sågmotstàndet minskas i allt högre grad ju högre virket värmes. Även om gränsen av vissa praktiska skäl företrädesvis ligger omkring 100 grader kan högre tempera- turer mycket väl användas för att uppnå ökad effekt. Gränsen uppåt begränsas 1 huvudsak av tvâ skäl. Virket kan ej utan skada värmas viss tid över viss temperatur. Vidare är det svårt åstadkomma en hög uppvärmning av virket beroende på att i virket bildad mättad vattenånga får så högt tryck att den med sitt värmeinnehâll rusar ut ur virket. Båda dessa omständigheter gör att temperaturer på över 150 grader knappast kan ifrågakomma. Virket tål för en kort stund i fuktigt tillstånd 150 graders Vid 150 grader har mättad vattenånga ett tryck på 5 kg och högre temperaturer ger ännu högre tryck. En temperatur på 150 grader kan hållas blott ett ögonblick i virket r dvs strax före sâgningen. Högre temperaturer torde icke kunna åstadkommas då ånga motsvarande sådana temperaturer på grund av sitt tryck icke kvarstannar i virket. ~ En annan fördel med virkets uppvärmning är att inbyggda spänningar i detsamma utjämnas. Den färdiga såg- produkten kommer därför att uppvisa mindre böjning och \É¶¶ Q UÅUTY snn1ß4n-1 vridning. På grund av att uppvärmningstiden som _regel är kort är denna effekt begränsad.Saw resistance decreases more and more the higher the wood is heated. Although the limit for some practical reasons is preferably around 100 degrees, higher temperatures can very well be used to achieve increased effect. The upward limit is limited 1 mainly for two reasons. The wood can not be heated without a certain time over a certain temperature without damage. Furthermore, it is difficult to achieve a high heating of the wood due to the fact that saturated water vapor formed in the wood has such a high pressure that it rushes out of the wood with its heat content. Both of these circumstances mean that temperatures above 150 degrees can hardly be questioned. The wood can withstand for a short time in a humid condition 150 degrees At 150 degrees, saturated water vapor has a pressure of 5 kg and higher temperatures give even higher pressure. A temperature of 150 degrees can be maintained for only a moment in the wood, ie just before sawing. Higher temperatures should not be achieved as steam corresponding to such temperatures does not remain in the wood due to its pressure. ~ Another advantage of heating the wood is that the built-in stresses in it are equalized. The finished saw product will therefore show less bending and \ É¶¶ Q UÅUTY snn1ß4n-1 rotation. Due to the fact that the heating time is usually short, this effect is limited.

Det virke som värmebehandlas enligt före- liggande uppfinning - temperaturer'över 80 grader - uppvisar här en särskild fördel genom att hettan medför en sterilisering av virket. Särskilt in- ö tresserant är att de svampar som orsakar den så _ kallade justerverkssjukan bekämpas. Dessa orsakar allvarliga bekymmer i konventionella torkar. För övrigt kan torkningen med fördel ske_enligt det *förfarande som beskrives i patentet 393.676 då virket behandlas i varm olja under vaouum. Vid detta förfarande är risken för utveckling av be- ' svärande svampar helt utesluten.The wood which is heat-treated according to the present invention - temperatures above 80 degrees - has a special advantage here in that the heat entails a sterilization of the wood. It is particularly interesting that the fungi that cause the so-called adjustment disease are controlled. These cause serious problems in conventional droughts. Incidentally, the drying can advantageously take place according to the procedure described in patent 393,676 when the wood is treated in hot oil during vacuum. In this procedure, the risk of developing troublesome fungi is completely excluded.

En sterilisering kan också åstadkommas genom att värma virket efter ságningen men före torkningen. Det är naturligtvis lättare att värma det sågade virket som har mindre volym ooh klenare dimensioner än den osägade stocken men i detta fall bortfaller vinsten med den förbättrade sågningen, lvilket är avsikten med föreliggande uppfinning.A sterilization can also be achieved by heating the wood after sawing but before drying. It is, of course, easier to heat the sawn timber which has a smaller volume and smaller dimensions than the unsaid log, but in this case the benefit of the improved sawing is lost, which is the object of the present invention.

Då det är förhållandevis enkelt att insätta denna 7 dielektriska värmning, som då nyttiggöres för sterilisering och för följande torkning, kan det. ofta vara en fördel att använda sig av densamma.Since it is relatively easy to use this dielectric heater, which is then utilized for sterilization and for subsequent drying, it can. often be an advantage to use the same.

Efter sågningen går det värmda virket lämp- ligen till en tork där den i virket befintliga värmen tillvaratages för torkändamál.After sawing, the heated wood is suitably sent to a dryer where the heat contained in the wood is utilized for drying purposes.

En viktig omständighet år följande. Den er- forderliga snabba genomvârmningen kräver högvärdig energi. Den kan emellertid till stor del ersättas' av mer làgvärdig energi för uppvärmning av större ieeserrﬁiﬁﬁö 8001840-1 delen av virket som skall sågas. Genom konvektion och ledning kan virkets yttre delar värmas. Dessa yttre delar representerar en större del av virkesmassan och därmed också en större del av erforderlig en@I9imäU9d- En sådan tillförsel av värme till virkets yttre delar sker lämpligast genom att virket behandlas med varmluft, basas eller förvaras viss tid i varmvatten. Den åter- stående inre värmningen sker därefter dielektriskt.An important circumstance is the following. The required rapid heating requires high-quality energy. However, it can be largely replaced by lower energy for heating larger parts of the timber to be sawn. By convection and conduction, the outer parts of the wood can be heated. These outer parts represent a larger part of the timber mass and thus also a larger part of the required one. The remaining internal heating then takes place dielectrically.

Uppfinningen kan kombineras med användningen av den såg som beskrives i svenska patentansökan nr. 7905412-8. Den är .dub'be11<1ingad_<>ch så konstruerad att tunna sàgsnitt uppnås. Den kan också kombineras med en eluppvärmning av sågsnittet och har i så motto viss lik- het med föreliggande uppfinning. Fördelarna hos före- liggande uppfinning och den dubbelklingade sågen kan samordnas.The invention can be combined with the use of the saw described in Swedish patent application no. 7905412-8. It is .dub'be11 <1inged _ <> ch so designed that thin saw cuts are achieved. It can also be combined with an electric heating of the saw cut and in that motto has some resemblance to the present invention. The advantages of the present invention and the double-blade saw can be coordinated.

QUALITYQUALITY

Claims

* 8001840-1 PATENTKRBV

1. l. Methods of facilitating and rationalizing sawing as well as any subsequent drying of materials, preferably wood, characterized in that the material is rapidly heated to a temperature up to 150 ° C immediately before sawing by dielectric heating.

2. ~ 2. A method according to claim 1, characterized in that the heating takes place to a temperature in the range 80-100 ° C, preferably to a temperature around 100 ° C;

3. A method according to claim 1, characterized in that the heating takes place to a temperature above -50 ° C. IN

4. A method according to claim 1, characterized in that the sawn products are transferred to the dryer as soon as possible so that the amount of heat stored in the products is utilized to the greatest possible extent for the drying of the products. PÛOH i QUALLU; .. - .. sm \