RU2810967C2 - Explosive emulsion composition - Google Patents
Explosive emulsion composition Download PDFInfo
- Publication number
- RU2810967C2 RU2810967C2 RU2019124762A RU2019124762A RU2810967C2 RU 2810967 C2 RU2810967 C2 RU 2810967C2 RU 2019124762 A RU2019124762 A RU 2019124762A RU 2019124762 A RU2019124762 A RU 2019124762A RU 2810967 C2 RU2810967 C2 RU 2810967C2
- Authority
- RU
- Russia
- Prior art keywords
- emulsion
- explosive
- hydrogen peroxide
- aqueous solution
- ammonium nitrate
- Prior art date
Abstract
Description
Изобретение относится к промышленным взрывчатым веществам, а именно к эмульсионным взрывчатым составам.The invention relates to industrial explosives, namely emulsion explosive compositions.
Известно эмульсионное водоустойчивое взрывчатое вещество (патент РФ №2544680, опубл. 20.03.2015, бюл. №8). Состав содержит, в мас. %: водомасляную эмульсию 80,00-30,00, аммиачную селитру 18,60-65,70, газогенерирующую добавку в виде раствора для газификации 0,20-0,10 и нефтепродукты 1,20-4,20. В качестве нефтепродуктов использовано дизельное топливо, водомасляная эмульсия выполнена на основе водного раствора аммиачной и натриевой селитр и включает кислоту уксусную 70%-ную, тиомочевину в качестве катализатора и натр едкий 40%-ный. Эмульсионное взрывчатое вещество включает гранулированную аммиачную селитру, которую механически смешивают с указанной эмульсией.An emulsion waterproof explosive is known (RF patent No. 2544680, published 03.20.2015, Bulletin No. 8). The composition contains, by weight. %: water-oil emulsion 80.00-30.00, ammonium nitrate 18.60-65.70, gas-generating additive in the form of a solution for gasification 0.20-0.10 and petroleum products 1.20-4.20. Diesel fuel was used as petroleum products; the water-oil emulsion was made on the basis of an aqueous solution of ammonium and sodium nitrate and included 70% acetic acid, thiourea as a catalyst and 40% sodium hydroxide. The emulsion explosive comprises granular ammonium nitrate, which is mechanically mixed with said emulsion.
Недостатком данного состава является большое количество ядовитых газов, образующихся при детонации зарядов взрывчатых веществ.The disadvantage of this composition is the large amount of toxic gases formed during the detonation of explosive charges.
Известен эмульсионный взрывчатый состав типа "вода в масле"(патент РФ №2155094, опубл. 27.08.2000, бюл. №24), включающий аммиачную селитру, минеральное (индустриальное) масло, воду и эмульгатор для производства эмульсионного взрывчатого состава, полученный путем смешения алкиленянтарного (в частности, полиизобутиленянтарного) ангидрида с продуктом его взаимодействия с органическим моно- или полиамином.A known emulsion explosive composition of the "water in oil" type (RF patent No. 2155094, published on August 27, 2000, Bulletin No. 24), including ammonium nitrate, mineral (industrial) oil, water and an emulsifier for the production of an emulsion explosive composition, obtained by mixing alkylenesuccinic (in particular, polyisobutylenesuccinic) anhydride with the product of its reaction with an organic mono- or polyamine.
Недостатком данного состава является большое количество ядовитых газов, образующихся при детонации зарядов взрывчатых веществ.The disadvantage of this composition is the large amount of toxic gases formed during the detonation of explosive charges.
Известен состав эмульсионного взрывчатого вещества (патент РФ №2252928, опубл. 27.05.2005, №15), содержащий гранулированную аммиачную селитру, нефтепродукты, эмульсию порэмита и порошкообразный ферросилиций. Во взрывчатом составе может применяться пористая гранулированная аммиачная селитра.The composition of an emulsion explosive is known (RF patent No. 2252928, published on May 27, 2005, No. 15), containing granulated ammonium nitrate, petroleum products, poremite emulsion and powdered ferrosilicon. Porous granular ammonium nitrate can be used in the explosive composition.
Недостатком данного состава является большое количество ядовитых газов, образующихся при детонации зарядов взрывчатых веществ.The disadvantage of this composition is the large amount of toxic gases formed during the detonation of explosive charges.
Известен состав эмульсионного взрывчатого вещества (патент РФ №2446134, опубл. 27.03.2012, бюл. №9). Состав содержит аммиачную селитру (10-45 мас. %) в газифицированной обратной эмульсии (остальное до 100), при этом газифицированная обратная эмульсия содержит, в мас. %: масло индустриальное 3,0-9,5; эмульгатор 1,0-3,5; воду 13,0-18,0; аммиачную селитру - остальное до 100; газогенерирующую добавку 0,4-2,5 сверх 100, причем обратная эмульсия содержит 0,09-6,0 мас. % дополнительного компонента, образующего ионы металлов, например хлорид натрия, соли щелочных металлов жирных кислот животного происхождения, например стеарата натрия, или растительного происхождения, например талового мыла. Эмульсия может содержать карбамид 0,5-2,5 мас. %, а частицы аммиачной селитры имеют среднюю удельную поверхность не менее 11900 мм2/г.The composition of the emulsion explosive is known (RF patent No. 2446134, published March 27, 2012, Bulletin No. 9). The composition contains ammonium nitrate (10-45 wt. %) in a gasified inverse emulsion (the rest up to 100), while the gasified inverse emulsion contains, by weight. %: industrial oil 3.0-9.5; emulsifier 1.0-3.5; water 13.0-18.0; ammonium nitrate - the rest up to 100; gas-generating additive 0.4-2.5 over 100, and the reverse emulsion contains 0.09-6.0 wt. % of an additional component forming metal ions, for example sodium chloride, alkali metal salts of fatty acids of animal origin, for example sodium stearate, or vegetable origin, for example tallow soap. The emulsion may contain urea 0.5-2.5 wt. %, and ammonium nitrate particles have an average specific surface area of at least 11900 mm 2 /g.
Недостатком данного состава является большое количество ядовитых газов, образующихся при детонации зарядов взрывчатых веществ.The disadvantage of this composition is the large amount of toxic gases formed during the detonation of explosive charges.
Известно эмульсионное взрывчатое вещество (патент UA №41672, опубл. 25.05.2009), содержащее эмульсионную матрицу, включающую в себя водные растворы нитратов аммония и кальция, оксид кальция и эмульгатор, и газогенерирующую добавку, в качестве которой используют 3-10%-ный водный раствор неорганических пероксидов (преимущественно перекиси водорода H2O2).An emulsion explosive is known (patent UA No. 41672, published on May 25, 2009), containing an emulsion matrix that includes aqueous solutions of ammonium and calcium nitrates, calcium oxide and an emulsifier, and a gas-generating additive, which uses 3-10% an aqueous solution of inorganic peroxides (mainly hydrogen peroxide H 2 O 2 ).
Недостатком данного состава является большое количество ядовитых газов, образующихся при детонации зарядов взрывчатых веществ.The disadvantage of this composition is the large amount of toxic gases formed during the detonation of explosive charges.
Известен эмульсионный взрывчатый состав типа «вода в масле», принятый за прототип (патент РФ №2622305, опубл. 14.06.2017 г., бюл. №17). Эмульсионное взрывчатое вещество содержит эмульсионную матрицу, включающую в себя водные растворы нитратов аммония и кальция, оксид кальция и эмульгатор, и газогенерирующую добавку, полученную растворением в воде перекиси водорода с добавлением линейной алкилбензолсульфоновой кислоты. В качестве эмульгатора используют эмульгатор «Аргунит РХ», представляющий собой 35%-ный раствор неионогенного поверхностно-активного вещества «Амолин-Ф» в дизельном топливе и/или индустриальном масле.An emulsion explosive composition of the “water in oil” type is known, adopted as a prototype (RF patent No. 2622305, published June 14, 2017, Bulletin No. 17). An emulsion explosive contains an emulsion matrix, including aqueous solutions of ammonium and calcium nitrates, calcium oxide and an emulsifier, and a gas-generating additive obtained by dissolving hydrogen peroxide in water with the addition of linear alkylbenzenesulfonic acid. The emulsifier “Argunit RKh” is used as an emulsifier, which is a 35% solution of the nonionic surfactant “Amolin-F” in diesel fuel and/or industrial oil.
Недостатком данного состава является достаточно большое количество ядовитых газов, образующихся при детонации зарядов взрывчатых веществ.The disadvantage of this composition is the fairly large amount of toxic gases formed during the detonation of explosive charges.
Техническим результатом изобретения является снижение количества ядовитых газов, образующихся при детонации зарядов взрывчатых веществ.The technical result of the invention is to reduce the amount of toxic gases formed during the detonation of explosive charges.
Технический результат достигается тем, что в эмульсионном взрывчатом составе, содержащем матричную эмульсию взрывчатого вещества на основе водного раствора нитрата аммония, включающую жидкое горючее, эмульгатор, газогенерирующую добавку и воду согласно изобретению раствор нитрата аммония для приготовления матричной эмульсии взрывчатого вещества делают на основе водного раствора перекиси водорода в следующем соотношении, мас. %:The technical result is achieved by the fact that in an emulsion explosive composition containing a matrix emulsion of an explosive based on an aqueous solution of ammonium nitrate, including liquid fuel, an emulsifier, a gas-generating additive and water according to the invention, the ammonium nitrate solution for preparing the matrix emulsion of an explosive is made on the basis of an aqueous solution of peroxide hydrogen in the following ratio, wt. %:
Технический результат достигается также тем, что водный раствор перекиси водорода стабилизируют фосфатом натрия.The technical result is also achieved by the fact that an aqueous solution of hydrogen peroxide is stabilized with sodium phosphate.
Технический результат достигается также тем, что водный раствор перекиси водорода стабилизируют салициловой кислотой.The technical result is also achieved by the fact that an aqueous solution of hydrogen peroxide is stabilized with salicylic acid.
Технический результат достигается также тем, что водный раствор перекиси водорода стабилизируют пирофосфорнокислым натрием.The technical result is also achieved by the fact that an aqueous solution of hydrogen peroxide is stabilized with sodium pyrophosphate.
Известные эмульсионные взрывчатые составы с использованием перекиси водорода в качестве газогенерирующей добавки (например - прототип) частично позволяют снизить объемы выделения ядовитых газов при детонации зарядов взрывчатых веществ на их основе, так как объем фактической добавки перекиси водорода мал относительно объема матричной эмульсии. Для более полной нейтрализации ядовитых газов предлагается использовать вместо водного раствора нитрата аммония готовить раствор нитрата аммония на водном растворе перекиси водорода в концентрациях от 3% до 98%. Перекись водорода выпускается в виде водных растворов, стандартная концентрация 1-6%, 30, 38, 50, 60, 85, 90 и 98%. 30% водный раствор пероксида водорода, стабилизированный добавлением фосфатов натрия, называется пергидролем. Концентрацию перекиси водорода определяют аналитическим, экспериментально-аналитическим или опытным путями в зависимости от требований по выделению ядовитых газов, доступности перекиси водорода и т.д.Known emulsion explosive compositions using hydrogen peroxide as a gas-generating additive (for example, a prototype) partially make it possible to reduce the volume of toxic gases released during the detonation of explosive charges based on them, since the volume of the actual addition of hydrogen peroxide is small relative to the volume of the matrix emulsion. To more completely neutralize toxic gases, it is proposed to use instead of an aqueous solution of ammonium nitrate to prepare a solution of ammonium nitrate in an aqueous solution of hydrogen peroxide in concentrations from 3% to 98%. Hydrogen peroxide is available in the form of aqueous solutions, standard concentrations are 1-6%, 30, 38, 50, 60, 85, 90 and 98%. A 30% aqueous solution of hydrogen peroxide stabilized by the addition of sodium phosphates is called perhydrol. The concentration of hydrogen peroxide is determined analytically, experimentally-analytically or experimentally, depending on the requirements for the release of toxic gases, the availability of hydrogen peroxide, etc.
Эмульсионный взрывчатый состав приготавливают следующим способом. В промышленную емкость заливают раствор перекиси водорода и начинают перемешивание и одновременный подогрев раствора с добавлением нитрата аммония для получения раствора окислителя. После приготовления раствора окислителя в него добавляют эмульгатор и жидкое горючее с одновременным проведением процесса эмульгирования. Полученную матричную эмульсию перекачивают в смесительно-зарядную машину и при производстве работ по формированию скважинных зарядов на взрываемом блоке добавляют газогенерирующую добавку, например нитрит натрия или стекленные или полистирольные микросферы. После проведения взрыва предложенного эмульсионного взрывчатого состава выделение ядовитых газов будет минимальным. Это было доказано в лабораторных условиях.The emulsion explosive composition is prepared in the following way. A hydrogen peroxide solution is poured into an industrial container and mixing and simultaneous heating of the solution with the addition of ammonium nitrate begin to obtain an oxidizing solution. After preparing the oxidizing solution, an emulsifier and liquid fuel are added to it while simultaneously carrying out the emulsification process. The resulting matrix emulsion is pumped into a mixing-charging machine, and during the formation of borehole charges on the blasted block, a gas-generating additive, for example sodium nitrite or glass or polystyrene microspheres, is added. After the explosion of the proposed emulsion explosive composition, the release of toxic gases will be minimal. This has been proven in laboratory conditions.
Пропорции эмульсионного взрывчатого состава для приготовления в лабораторных условиях принимали следующие, мас. %:The proportions of the emulsion explosive composition for preparation in laboratory conditions were as follows, wt. %:
Пример получения состава эмульсионного взрывчатого состава в лабораторных условиях. Матричную эмульсию взрывчатого вещества изготавливают известным способом: приготовленный при температуре 80-90°С водный раствор окислителя перекиси водорода с нитратом аммония в течение 1 минуты приливают при интенсивном перемешивании к смеси из жидкого горючего (например, масла И-20) и эмульгатора, далее продолжают эмульгирование в пределах 3 минут.В полученную матричную эмульсию взрывчатого вещества добавляют газогенерирующую добавку - 0,5% водного раствора нитрита натрия концентрацией 5÷15% и перемешивают в течение 10÷15 минут. После перемешивания полученный эмульсионный взрывчатый состав использовали для исследования. Результаты исследований эмульсионного взрывчатого состава приведены в таблице. Основные характеристики эмульсионного взрывчатого состава определяли по известным методикам.An example of obtaining the composition of an emulsion explosive composition in laboratory conditions. The matrix emulsion of the explosive is prepared in a known manner: an aqueous solution of the oxidizing agent hydrogen peroxide with ammonium nitrate prepared at a temperature of 80-90°C is poured for 1 minute with vigorous stirring into a mixture of liquid fuel (for example, I-20 oil) and emulsifier, then continue emulsification within 3 minutes. A gas-generating additive is added to the resulting explosive matrix emulsion - a 0.5% aqueous solution of sodium nitrite with a concentration of 5÷15% and stirred for 10÷15 minutes. After mixing, the resulting emulsion explosive composition was used for research. The results of studies of the emulsion explosive composition are given in the table. The main characteristics of the emulsion explosive composition were determined using known methods.
Примеры 1, 2, 3, 4, 5 приготовления эмульсионного взрывчатого состава (ЭВС) приведены в таблице. В таблице приведены данные о объеме выделения ядовитых газов, динамической вязкости при t=+60°C, измеренной на ротационном вискозиметре Брукфилда при частоте оборотов шпинделя 20-30 об/мин, насадкой RV6.Examples 1, 2, 3, 4, 5 of the preparation of an emulsion explosive composition (EVS) are given in the table. The table shows data on the volume of toxic gases released, dynamic viscosity at t=+60°C, measured on a Brookfield rotational viscometer at a spindle speed of 20-30 rpm, with an RV6 attachment.
Как видно из данных таблицы, применение эмульсионного взрывчатого состава без перекиси водорода (пример 1) имеет наибольшее количество выделения ядовитых газов - оксидов азота. Добавление перекиси водорода в количестве 6 процентов и более (перекись водорода неограниченно растворима в воде) позволяет снизить количество оксидов азота, вплоть до полной нейтрализации с соблюдением требуемой вязкости продукта для прокачки насосами. Отметим, что использование недостаточно чистой перекиси водорода, а также водного раствора высокой концентрации требует особо осторожного, например со стабилизацией фосфатом натрия, салициловой кислотой, пирофосфорнокислым натрием.As can be seen from the table data, the use of an emulsion explosive composition without hydrogen peroxide (example 1) has the greatest amount of release of toxic gases - nitrogen oxides. Adding hydrogen peroxide in an amount of 6 percent or more (hydrogen peroxide is unlimitedly soluble in water) allows you to reduce the amount of nitrogen oxides, up to complete neutralization, while maintaining the required viscosity of the product for pumping. Note that the use of insufficiently pure hydrogen peroxide, as well as a high concentration aqueous solution, requires special care, for example with stabilization with sodium phosphate, salicylic acid, sodium pyrophosphate.
Применение данного эмульсионного взрывчатого состава обеспечивает следующие преимущества:The use of this emulsion explosive composition provides the following advantages:
- снижение количества ядовитых газов, образующихся при детонации зарядов взрывчатых веществ;- reducing the amount of toxic gases formed during the detonation of explosive charges;
- повышение безопасности проведения работ.- increasing the safety of work.
Claims (5)