Abstract

FIELD: printing.

SUBSTANCE: in the invention, a method is described for the improvement of image adhesion to at least one substrate surface. The method includes the treatment of at least part of the surface by application to the part of the surface of a composition containing one or more polymers. The method additionally includes drying of the composition, carried out after the application of the composition to substrate, to obtain treated substrate. The method additionally includes printing of an image on treated substrate, using an electrophotographic printer, using a liquid toner technology. Substrate is treated and dried for less than about 5 min before printing on it.

EFFECT: obtaining a method for the improvement of image adhesion to substrate.

20 cl

Description

ПЕРЕКРЕСТНАЯ ССЫЛКА НА РОДСТВЕННУЮ ЗАЯВКУCROSS-REFERENCE TO RELATED APPLICATION

По настоящей заявке испрашивается приоритет по предварительной заявке U.S. №62/507741, поданной 17 мая 2017 г., которая во всей ее полноте включена в настоящее изобретение в качестве ссылки.This application claims priority over U.S. Provisional Application. No. 62/507741, filed May 17, 2017, which is incorporated herein by reference in its entirety.

ОБЛАСТЬ ТЕХНИКИ, К КОТОРОЙ ОТНОСИТСЯ ИЗОБРЕТЕНИЕFIELD OF TECHNOLOGY TO WHICH THE INVENTION RELATES

Настоящее изобретение в целом относится к способу улучшения адгезии жидкого тонера по меньшей мере к одной поверхности подложки, включающему: (i) проводимую непосредственно перед печатью обработку подложки для печати композицией, содержащей полимер; (ii) сушку обработанной подложки; и (iii) печать изображения на обработанной подложке с помощью жидкостной электрофотографии с использованием жидкого тонера. Кроме того, настоящее изобретение в целом относится к подложке с печатью, полученной таким способом.The present invention relates generally to a method for improving the adhesion of a liquid toner to at least one surface of a substrate, comprising: (i) immediately prior to printing, treating the substrate for printing with a composition containing a polymer; (ii) drying the treated substrate; and (iii) printing an image on the treated substrate by liquid electrophotography using a liquid toner. In addition, the present invention generally relates to a printed substrate obtained in this manner.

УРОВЕНЬ ТЕХНИКИBACKGROUND OF THE INVENTION

При печати с помощью жидкостной электрофотографии (ЖЭФ) для печати на подложках вместо сухого порошкообразного тонера используют жидкую краску. Типичными примерами печатных машин для ЖЭФ являются печатные машины HP® digital Indigo™. Частицы тонера, содержащиеся в жидкой краске, использующейся для печати с помощью ЖЭФ, являются достаточно небольшими, поэтому изображения, напечатанные с помощью ЖЭФ, не скрывают неровность/глянец поверхности, например, бумажных подложек. Жидкая краска (в настоящем изобретении также называющаяся "краской", "жидким тонером" или "краской для ЖЭФ"), использующаяся для печати с помощью ЖЭФ, представляет собой суспензию небольших частиц пигмента, обладающих размером, находящимся в диапазоне примерно от 1 до 2 мкм, в неводной жидкости. Для печати с помощью жидкостной электрофотографии обычно используют жидкую краску HP® Electrolnk®. Частицы пигмента могут означать пигмент, диспергированный в полимере. Считается, что при печати с помощью ЖЭФ посредством цифровой печати получают одни из лучших по качеству изображения при сравнительно высокой скорости печати.When printing using liquid electrophotography (LEP), liquid ink is used to print on substrates instead of dry powder toner. Typical examples of ZEF presses are HP® digital Indigo™ presses. The toner particles contained in the liquid ink used for VEF printing are small enough that VEF printed images do not hide surface roughness/gloss, such as paper substrates. The liquid ink (also referred to as "ink", "liquid toner" or "VET ink" in the present invention) used for VEP printing is a suspension of small pigment particles having a size ranging from about 1 to 2 µm. , in a non-aqueous liquid. Liquid electrophotography printing typically uses HP® Electrolnk® Liquid Ink. Pigment particles may mean a pigment dispersed in a polymer. It is believed that when printing with LEF through digital printing, some of the best image quality is obtained at a relatively high print speed.

Однако установлено, что напечатанные с помощью ЖЭФ изображения, а также изображения, полученные по методикам электрорепрографической печати с использованием сухого тонера, часто не прилипают к подложке. Поэтому необходимо улучшение адгезии краски для ЖЭФ к подложкам при печати с помощью ЖЭФ.However, it has been found that the images printed with the help of LEF, as well as images obtained by electroreprographic printing techniques using dry toner, often do not adhere to the substrate. Therefore, it is necessary to improve the adhesion of the LEF ink to the substrates when printing with the LEF.

КРАТКОЕ ИЗЛОЖЕНИЕ СУЩНОСТИ ИЗОБРЕТЕНИЯSUMMARY OF THE INVENTION

Настоящее изобретение относится к способу улучшения адгезии изображения по меньшей мере к одной поверхности подложки. Способ включает, но не ограничивается только этим, обработку по меньшей мере части поверхности путем нанесения композиции, содержащей один или большее количество полимеров, по меньшей мене на часть поверхности. Способ дополнительно включает, но не ограничивается только этим, сушку композиции, проводимую после нанесения композиции на подложку, с получением обработанной подложки. Способ дополнительно включает, но не ограничивается только этим, печать изображения на обработанной подложке с помощью электрофотографического принтера с использованием технологии жидкого тонера. Подложку обрабатывают и сушат менее, чем примерно за 5 мин до печати на ней. Настоящее изобретение также относится к печатному материалу. Печатный материал включает, но не ограничивается только ей, подложку с обработанной поверхностью, включающую запечатываемое покрытие. Запечатываемое покрытие нанесено по меньшей мере на часть по меньшей мере одной стороны подложки. Запечатываемое покрытие включает, но не ограничивается только ими, один или большее количество полимеров. Печатный материал дополнительно включает, но не ограничивается только им, изображение, находящееся по меньшей мере на части запечатываемого покрытия. Изображение напечатано на запечатываемом покрытии с помощью электрофотографического принтера с использованием технологии жидкого тонера. Покрытие наносят на подложку менее, чем примерно за 5 мин до печати изображения.The present invention relates to a method for improving the adhesion of an image to at least one surface of a substrate. The method includes, but is not limited to, treating at least a portion of the surface by applying a composition containing one or more polymers to at least a portion of the surface. The method further includes, but is not limited to, drying the composition after application of the composition to the substrate to obtain a treated substrate. The method further includes, but is not limited to, printing an image on the treated substrate with an electrophotographic printer using liquid toner technology. The substrate is treated and dried less than about 5 minutes before being printed on it. The present invention also relates to printed matter. The printed material includes, but is not limited to, a surface treated substrate including a printable coating. The sealable coating is applied to at least a portion of at least one side of the substrate. The sealable coating includes, but is not limited to, one or more polymers. The printed material further includes, but is not limited to, an image located on at least a portion of the printed coating. The image is printed on the overprint with an electrophotographic printer using liquid toner technology. The coating is applied to the substrate less than about 5 minutes before the image is printed.

ПОДРОБНОЕ ОПИСАНИЕ ИЗОБРЕТЕНИЯDETAILED DESCRIPTION OF THE INVENTION

Приведенное ниже подробное описание по существу является лишь иллюстративным и не предназначено для ограничения раскрытия или возможности применения и применения объектов, описанных в настоящем изобретении. Кроме того, не следует ограничиваться никакими теоретическими соображениями, приведенными в предшествующем уровне техники или последующем подробном описании.The following detailed description is essentially illustrative only and is not intended to limit the disclosure or the applicability and use of the objects described in the present invention. In addition, one should not be limited by any of the theoretical considerations given in the prior art or the following detailed description.

Кроме того, для обеспечения полного понимания настоящего изобретения в приведенном ниже описании указаны конкретные подробности, такие как материалы и размеры. Однако для специалиста в данной области техники должно быть очевидно, что настоящее изобретение можно практически осуществить без использования этих конкретных подробностей. В действительности, настоящее изобретение можно практически осуществить совместно с методиками обработки, производства или изготовления, обычно использующимися в полиграфической промышленности. Кроме того, в приведенных ниже способах описаны лишь стадии, а не полная схема способа получения подложки, включающей композицию, предназначенную для улучшения адгезии изображения, предлагаемого в настоящем изобретении.In addition, in order to provide a thorough understanding of the present invention, the following description provides specific details such as materials and dimensions. However, for a person skilled in the art it should be obvious that the present invention can be practiced without the use of these specific details. In fact, the present invention may be practiced in conjunction with processing, manufacturing, or fabrication techniques commonly used in the printing industry. In addition, the following methods describe only the steps, and not the complete scheme of the method for obtaining a substrate, including a composition designed to improve the adhesion of the image proposed in the present invention.

При использовании в настоящем изобретении термины в единственном числе или термины во множественном числе означают один или большее количество, если не указано иное. Термин "или" может являться объединяющим или разъединяющим. Открытые термины, такие как "включать", "включающий", "содержать", "содержащий" и т.п. означают "включающий". Термин "примерно" при использовании применительно к числовому значению в настоящем описании и формуле изобретения означает интервал точности, известный и приемлемый для специалиста в данной области техники. Обычно такой интервал точности составляет ±10%. Таким образом, "примерно 10" означает от 9 до 11. В настоящем описании все числовые значения, указывающие количества, отношения количеств материалов, физические характеристики материалов и/или применение, следует понимать, как модифицированные термином "примерно", если явно не указанное иное. При использовании в настоящем изобретении "%", описанные в настоящем изобретении, означают массовые проценты, если не указано иное. При использовании в настоящем изобретении выражение "в основном не содержит" означает, что композиция содержит небольшое количество указанного ингредиента/компонента, такое, как менее примерно 1 мас. %, 0,5 мас. % или 0,1 мас. %, или менее обнаруживаемого количества указанного ингредиента. Если не указано иное, молекулярная масса полимера означает среднемассовую молекулярную массу.When used in the present invention, terms in the singular or terms in the plural mean one or more, unless otherwise indicated. The term "or" can be inclusive or severing. Open terms such as "include", "comprising", "comprise", "comprising", etc. means "including". The term "about" when used in relation to the numerical value in the present description and the claims means the range of accuracy known and acceptable to a person skilled in the art. Typically, this accuracy interval is ±10%. Thus, "about 10" means from 9 to 11. In the present specification, all numerical values indicating amounts, ratios of materials, physical characteristics of materials, and/or application are to be understood as modified by the term "about", unless expressly stated otherwise. . When used in the present invention, the "%" described in the present invention means weight percent, unless otherwise indicated. When used in the present invention, the expression "essentially does not contain" means that the composition contains a small amount of the specified ingredient/component, such as less than about 1 wt. %, 0.5 wt. % or 0.1 wt. % or less of the detectable amount of the specified ingredient. Unless otherwise indicated, the molecular weight of the polymer means the weight average molecular weight.

При использовании в настоящем изобретении термины "печать с помощью жидкостной электрофотографии" "печать с помощью ЖЭФ", "электрорепрографическая печать с использованием частиц жидкого тонера" или "ксерографическая печать с использованием частиц жидкого тонера" можно использовать взаимозаменяемым образом; все они включают, например, использование печатных машин и методик HP® digital Indigo. Кроме того, при использовании в настоящем изобретении печать с помощью жидкостной электрофотографии не означает и не включает методику офсетной печати, известную, как литография и более подробно описанную в публикации Alex Glassman, Printing Fundamentals, TAPPI Press, 1985, которая во всей ее полноте включена в настоящее изобретение в качестве ссылки.When used in the present invention, the terms "liquid-based electrophotography printing", "PVD printing", "electroreprographic printing using liquid toner particles", or "xerographic printing using liquid toner particles" can be used interchangeably; all include, for example, the use of HP® digital Indigo presses and methodologies. Furthermore, as used herein, liquid electrophotography printing does not mean or include the offset printing technique known as lithography and described in more detail in Alex Glassman, Printing Fundamentals, TAPPI Press, 1985, which is incorporated in its entirety in the present invention as a reference.

Для специалистов с общей подготовкой в данной области техники должно быть очевидно, что в способах электрофотографической печати, раскрытых в настоящем изобретении, используют машины для печати с помощью жидкостной электрофотографии, также называющиеся, например, машинами для печати с помощью ЖЭФ и цифровыми принтерами для ЖЭФ. Хорошо известными примерами имеющихся в продаже машин для печати с помощью ЖЭФ являются печатные машины HP® digital Indigo, также называющиеся принтерами Indigo, или разновидности таких машин.It should be apparent to those of ordinary skill in the art that the electrophotographic printing methods disclosed in the present invention use liquid electrophotography printing machines, also referred to as, for example, VEF printing machines and digital VEF printers. Well-known examples of commercially available LEF printing presses are HP® digital Indigo presses, also referred to as Indigo printers, or variations thereof.

При использовании в настоящем изобретении термин "раствор полимера" означает, что полимер или некоторая часть полимера растворима в воде или в щелочных или кислых водных растворах.When used in the present invention, the term "polymer solution" means that the polymer or some part of the polymer is soluble in water or in alkaline or acidic aqueous solutions.

Термин "модификатор реологических характеристик" означает химическое соединение, которое изменяет вязкость раствора или зависимость вязкости раствора от сдвигового усилия.The term "rheology modifier" means a chemical compound that changes the viscosity of the solution or the dependence of the viscosity of the solution from the shear force.

Если в настоящем изобретении не указано иное, то при использовании в настоящем изобретении термин "полимер" означает полимер, содержащий мономерные звенья одного или большего количества типов, который может включать, например, сополимеры и тройные сополимеры. Один или большее количество полимеров, применяющихся в настоящем изобретении, представляют собой растворы полимеров.Unless otherwise indicated in the present invention, when used in the present invention, the term "polymer" means a polymer containing monomer units of one or more types, which may include, for example, copolymers and terpolymers. One or more of the polymers used in the present invention are polymer solutions.

При использовании в настоящем изобретении термин "покрытие" означает пленку или однородный слой материала, нанесенный по меньшей мере на часть по меньшей мере одной поверхности подложки, и он может включать один или большее количество компонентов, для специалиста с общей подготовкой в данной области техники очевидно, что нанесение покрытия на подложку (например, бумажную подложку и/или содержащую пластик подложку) благоприятно для улучшения качества подложки и/или печати напечатанного на ней изображения. Однако термин "покрытие" применительно к "бумаге с покрытием" означает бумагу, поверхность которой обработана комбинацией наполнителей и связующего, как это определено в публикации David Saltman, et al., Pulp & Paper Primer, 2nd Edition, TAPPI Press (1998), например, но без наложения ограничений, на стр. 24-25, которая во всей ее полноте включена в настоящее изобретение в качестве ссылки.As used in the present invention, the term "coating" means a film or uniform layer of material deposited on at least a portion of at least one surface of a substrate, and it may include one or more components, for a specialist with a general training in this field of technology it is obvious, that coating a substrate (eg, a paper substrate and/or a plastic-containing substrate) is beneficial in improving the quality of the substrate and/or printing the image printed on it. However, the term "coating" in relation to "coated paper" means paper that has been surface treated with a combination of fillers and binder as defined in David Saltman, et al., Pulp & Paper Primer, 2nd Edition, TAPPI Press (1998), e.g. , but without imposing restrictions, on pages 24-25, which in its entirety is incorporated into the present invention by reference.

Настоящее изобретение относится к обработке подложек, которые готовы для печати с использованием других методик, но затем их модифицируют после изготовления путем нанесения композиции на подложку и в вариантах осуществления непосредственно перед печатью с целью улучшения адгезии напечатанных с помощью жидкого тонера изображений. Так, например, если подложкой является бумага, то композицию наносят на бумажное изделие после того, как бумагу извлекают из бумагоделательной машины. Композиция содержит один или большее количество полимеров, где полное количество одного или большего количества полимеров составляет более примерно 50%, альтернативно более 70% в пересчете на сухое вещество, в пересчете на массу композиции. Обработка может являться частью способа печали с помощью печатной машины. Согласно изобретению неожиданно было установлено, что в композиции, использующейся для обработки, не требуется связующее, к которому добавляют один или большее количество полимеров, применяющихся в настоящем изобретении для обеспечения необходимой адгезии напечатанных изображений. Кроме того, неожиданно было установлено, что один или большее количество полимеров, применяющихся в настоящем изобретении, можно наносить на подложку непосредственно перед проведением способа печати или даже в виде части способа печати, где полное количество одного или большего количества полимеров составляет более примерно 50%, альтернативно более 70% в пересчете на сухое вещество, в пересчете на массу композиции, и по существу обеспечено удобное обращение и удобный способ, с помощью которого можно обработать готовые для печати подложки и обеспечить улучшенную адгезию изображений. Настоящее изобретение относится к способу улучшения адгезии жидкого тонера, с помощью которого печатают по меньшей мере на части по меньшей мере одной поверхности подложки с использованием цифрового принтера для ЖЭФ. Настоящее изобретение также относится к одному или большему количеству печатных продуктов, которые получены способом, предлагаемым в настоящем изобретении.The present invention relates to the treatment of substrates that are ready to be printed using other techniques but are then modified after manufacture by applying the composition to the substrate and in embodiments just prior to printing to improve adhesion of liquid toner printed images. Thus, for example, if the substrate is paper, the composition is applied to the paper product after the paper has been removed from the paper machine. The composition contains one or more polymers, where the total amount of one or more polymers is more than about 50%, alternatively more than 70% on a dry basis, based on the weight of the composition. Processing may be part of the method of sadness with a printing press. According to the invention, it has surprisingly been found that the composition used for processing does not require a binder to which one or more polymers used in the present invention are added to provide the necessary adhesion of the printed images. In addition, it has surprisingly been found that one or more of the polymers used in the present invention can be applied to the substrate immediately prior to the printing process, or even as part of the printing process, where the total amount of one or more polymers is more than about 50%, alternatively greater than 70% on a dry matter basis, based on the weight of the composition, and as such provides easy handling and a convenient process by which print-ready substrates can be processed and improved image adhesion is achieved. The present invention relates to a liquid toner adhesion improvement method that prints on at least a portion of at least one surface of a substrate using a digital LEF printer. The present invention also relates to one or more printed products, which are obtained by the method proposed in the present invention.

Настоящее изобретение относится к способу улучшения адгезии жидкого тонера по меньшей мере к одной поверхности подложки, включающему: (i) проводимую перед печатью обработку подложки для печати, в вариантах осуществления менее, чем примерно за 5 мин до печати, или менее, чем примерно за 1 мин до печати, или менее, чем примерно за 30 с до печати, путем нанесения композиции, содержащей один или большее количество полимеров и необязательно модификатор реологических характеристик, (ii) проводимую после нанесения композиции на подложку сушку композиции с получением обработанной подложки; и (iii) печать изображения на обработанной подложке с помощью жидкостной электрофотографии с использованием жидкой краски. Кроме того, настоящее изобретение в целом относится к подложке с печатью, полученной таким способом.The present invention relates to a method for improving the adhesion of a liquid toner to at least one surface of a substrate, comprising: (i) pre-printing treatment of the substrate for printing, in embodiments, less than about 5 minutes before printing, or less than about 1 minutes before printing, or less than about 30 seconds before printing, by applying a composition containing one or more polymers and optionally a rheology modifier, (ii) drying the composition after applying the composition to a substrate to form a treated substrate; and (iii) printing an image on the treated substrate by liquid electrophotography using liquid ink. In addition, the present invention generally relates to a printed substrate obtained in this manner.

Композиция содержит один или большее количество полимеров, один или большее количество полимеров содержат повторяющееся звено, где повторяющееся звено содержит локализованный сильный отрицательно заряженный диполь (такой как карбонильная группа) и не содержит сильный положительно заряженный диполь. При использовании в настоящем изобретении термин "локализованный сильный отрицательно заряженный диполь" означает, что в структуре повторяющегося звена содержится функциональная группа, такая как карбоксигруппа, и в настоящем изобретении термин "сильный" определен, как обладающий локальным дипольным моментом, равным более 2 дин, где известно, что карбонильная группа обладает дипольным моментом, равным примерно 2,4 дин, локальный дипольный момент возникает вследствие разной электроотрицательности соединенных вместе атомов. В настоящем изобретении термин "не содержит сильный положительно заряженный диполь" означает, что не содержится локализованный диполь (такой как гидроксигруппа), который обладает дипольным моментом, равным более 0,8 дин.The composition contains one or more polymers, one or more polymers contain a repeating unit, where the repeating unit contains a localized strong negatively charged dipole (such as a carbonyl group) and does not contain a strong positively charged dipole. When used in the present invention, the term "localized strong negatively charged dipole" means that the structure of the repeat unit contains a functional group such as a carboxy group, and in the present invention the term "strong" is defined as having a local dipole moment greater than 2 dynes, where the carbonyl group is known to have a dipole moment of about 2.4 dynes, a local dipole moment arising from the different electronegativity of the atoms joined together. In the present invention, the term "does not contain a strong positively charged dipole" means that it does not contain a localized dipole (such as a hydroxy group) that has a dipole moment greater than 0.8 dyne.

Повторяющееся звено может содержать, но не ограничиваться только ей, например, карбонильную группу.The repeating unit may contain, but is not limited to, for example, a carbonyl group.

Композиция может содержать один или большее количество полимеров, включающих по меньшей мере одно повторяющееся звено, содержащее третичную амидную группу, где (i) по меньшей мере один из атомов углерода, связанных с атомом азота третичной амидной группы, содержит связанные с ним два или три атома водорода, и (ii) карбонильная группа, содержащаяся в третичной амидной группе, связана с группой -СН, -СН₂ или -СН₃.The composition may contain one or more polymers comprising at least one repeating unit containing a tertiary amide group, where (i) at least one of the carbon atoms associated with the nitrogen atom of the tertiary amide group contains two or three atoms associated with it hydrogen, and (ii) the carbonyl group contained in the tertiary amide group is linked to a -CH, -CH ₂ or -CH ₃ group.

Один или большее количество полимеров, применяющихся для обработки, включают один или большее количество полимеров, полученных из одного или большего количества мономеров, где по меньшей мере один из одного или большего количества мономеров, использующихся для получения каждого из одного или большего количества полимеров, выбран из группы, состоящей из следующих: винилпирролидон, мономер, содержащий оксазолин, N-винилпиперидинон (также известный, как N-винилпиперидон), N-винилкапролактам, N,N-диметилакриламид и их комбинации. Один или большее количество полимеров могут представлять собой гомополимеры, сополимеры или их комбинации. Так, например, один или большее количество полимеров, применяющихся для обработки, могут представлять собой один или большее количество гомополимеров и включать один или большее количество полимеров, полученных из одного или большего количества мономеров, где мономер, использующийся для получения каждого из одного или большего количества полимеров, выбран из группы, состоящей из следующих: винилпирролидон, мономер, содержащий оксазолин, N-винилпиперидинон (также известный, как N-винилпиперидон), N-винилкапролактам и N,N-диметилакриламид.The one or more polymers used for processing include one or more polymers derived from one or more monomers, where at least one of the one or more monomers used to obtain each of the one or more polymers is selected from a group consisting of the following: vinylpyrrolidone, an oxazoline-containing monomer, N-vinylpiperidinone (also known as N-vinylpiperidone), N-vinylcaprolactam, N,N-dimethylacrylamide, and combinations thereof. One or more polymers may be homopolymers, copolymers, or combinations thereof. For example, one or more polymers used for processing may be one or more homopolymers and include one or more polymers derived from one or more monomers, where the monomer used to obtain each of the one or more polymers selected from the group consisting of the following: vinylpyrrolidone, an oxazoline containing monomer, N-vinylpiperidinone (also known as N-vinylpiperidone), N-vinylcaprolactam and N,N-dimethylacrylamide.

Один или большее количество полимеров дополнительно включают один или большее количество неионогенных мономерных звеньев. Так, например, они могут включать один или большее количество полимеров, полученных с использованием (i) по меньшей мере одного или большего количества полимеров, выбранных из группы, состоящей из следующих: винилпирролидон, мономер, содержащий оксазолин, N-винилпиперидинон, N-винилкапролактам, N,N-диметилакриламид и их комбинации, для получения каждого из одного или большего количества полимеров; и (ii) одного или большего количества неионогенных мономеров. Неограничивающими примерами мономера, содержащего оксазолин, являются 2-этил-2-оксазолин и/или 2-метилоксазолин. И в этом случае один или большее количество полимеров могут представлять собой гомополимеры и каждый из одного или большего количества полимеров можно получить из одного мономера, выбранного из группы, состоящей из следующих: 2-этил-2-оксазолин и 2-метилоксазолин. При использовании в настоящем изобретении неионогенным мономером является мономер, который не содержит анионогенную или катионогенную функциональную группу при условиях применения, такой как акриловая кислота, метакриловая кислота или мономеры, содержащие четвертичный амин. Один или большее количество полимеров могут дополнительно включать один или большее количество мономерных звеньев, наличие которых не приводит к образованию водородной связи с первичным полимером, применяющимся для обработки, для задач настоящего изобретения их наличие не приводит к существенной степени сомоассоциации внутри полимера. Для задач настоящего изобретения существенная степень сомоассоциации означает образование существенного количества водородных связей внутри полимера или высокой степени диполь-дипольного взаимодействия внутри полимера. Описание взаимодействия мономерных звеньев в полимере и одного полимера с другим полимером или с растворителем приведено в главе 12 классической публикации Пола Флори "Principles of Polymer Chemistry", впервые опубликованной в 1953 г. издательством Cornell Press. Он определил параметр взаимодействия, который выражен, как "свободная энергия взаимодействия с ближайшим соседом". После выхода работы Флори другие исследователи значительно расширили эту концепцию. Для специалистов, знакомых с этой концепцией, должно быть очевидно, что в настоящем изобретении приведено положение о том, полимеры, предлагаемые в настоящем изобретении, по сравнению с другими полимерами обладают такой характеристикой, как незначительная степень сомоассоциации и, что является более важным (хотя не следует ограничиваться теоретическими соображениями), они являются полимерами, которые на молекулярном уровне взаимодействуют с полимером, содержащимся в жидком тонере, сильнее, чем друг с другом. Поэтому следует понимать, что небольшие количества других сомономеров, такие как составляющие менее 5%, можно включить в один или большее количество полимеров без изменения основных характеристик, придаваемых подложке одним или большим количеством полимеров.One or more polymers further include one or more nonionic monomeric units. Thus, for example, they may include one or more polymers obtained using (i) at least one or more polymers selected from the group consisting of the following: vinylpyrrolidone, oxazoline-containing monomer, N-vinylpiperidinone, N-vinylcaprolactam , N,N-dimethylacrylamide and combinations thereof, each to obtain one or more polymers; and (ii) one or more nonionic monomers. Non-limiting examples of an oxazoline containing monomer are 2-ethyl-2-oxazoline and/or 2-methyloxazoline. Again, one or more of the polymers may be homopolymers, and each of the one or more polymers may be derived from a single monomer selected from the group consisting of the following: 2-ethyl-2-oxazoline and 2-methyloxazoline. As used in the present invention, a nonionic monomer is a monomer that does not contain an anionic or cationic functional group under the conditions of use, such as acrylic acid, methacrylic acid, or monomers containing a quaternary amine. One or more polymers may further include one or more monomeric units, the presence of which does not lead to the formation of a hydrogen bond with the primary polymer used for processing, for the purposes of the present invention, their presence does not lead to a significant degree of self-association within the polymer. For the purposes of the present invention, a significant degree of self-association means the formation of a significant amount of hydrogen bonds within the polymer or a high degree of dipole-dipole interaction within the polymer. For a description of the interaction of monomeric units in a polymer and one polymer with another polymer or with a solvent, see Chapter 12 of Paul Flory's classic "Principles of Polymer Chemistry", first published in 1953 by Cornell Press. He defined the interaction parameter, which is expressed as "free energy of interaction with the nearest neighbor". After the publication of Flory's work, other researchers have significantly expanded this concept. For those familiar with this concept, it should be obvious that in the present invention the provision is made that the polymers of the present invention, compared with other polymers, have such a characteristic as a low degree of self-association and, more importantly (although not should be limited to theoretical considerations), they are polymers that, at the molecular level, interact with the polymer contained in the liquid toner more strongly than with each other. Therefore, it should be understood that small amounts of other comonomers, such as less than 5%, can be included in one or more polymers without changing the basic characteristics imparted to the support by one or more polymers.

В одном варианте осуществления по меньшей мере один из одного или большего количества полимеров включает по меньшей мере один из следующих: поли(2-этил-2-оксазолин) и поли(2-метилоксазолин). В другом варианте осуществления по меньшей мере один или большее количество полимеров содержат первичное повторяющееся звено на основе винилпирролидона.In one embodiment, at least one of the one or more polymers includes at least one of the following: poly(2-ethyl-2-oxazoline) and poly(2-methyloxazoline). In another embodiment, at least one or more polymers contain a vinylpyrrolidone-based primary repeating unit.

Каждый из одного или большего количества полимеров может обладать среднечисловой молекулярной массой, равной более примерно 40000 Да или более примерно 80000 Да, или более примерно 190000 Да, или более примерно 450000 Да, где верхнее предельное значение молекулярной массы означает молекулярную массу, которая препятствует образованию раствора, содержащего один или большее количество полимеров, как это должно быть очевидно для специалиста с общей подготовкой в данной области техники. В некоторых вариантах осуществления верхнее предельное значение составляет менее примерно 2000000 Да.Each of the one or more polymers may have a number average molecular weight greater than about 40,000 Da, or greater than about 80,000 Da, or greater than about 190,000 Da, or greater than about 450,000 Da, where the upper molecular weight limit is the molecular weight that prevents solution from forming. containing one or more polymers, as would be apparent to those of ordinary skill in the art. In some embodiments, the upper limit is less than about 2,000,000 Da.

Модификаторы реологических характеристик можно добавить к композиции, содержащей один или большее количество полимеров, для регулирования вязкости композиции и обеспечения эффективной вязкости, при которой ее можно нанести на подложку по методикам, известным специалистам в данной области техники.Rheology modifiers can be added to a composition containing one or more polymers to control the viscosity of the composition and provide an effective viscosity at which it can be applied to a substrate by techniques known to those skilled in the art.

Подложка может быть выбрана из группы, состоящей из следующих: бумажные изделия, тканые и/или нетканые волокнистые материалы, материалы на основе пластика (в настоящем изобретении также называющиеся просто "пластиками") и их комбинации. Подложка должна быть подходящей для печати по какой-либо методике до обработки и подходящей для обработки в соответствии с настоящим изобретением, включая сушку, проводимую до печати с помощью электрорепрографического принтера на основе жидкого тонера.The substrate may be selected from the group consisting of the following: paper products, woven and/or nonwoven fibrous materials, plastic-based materials (also referred to simply as "plastics" in the present invention), and combinations thereof. The substrate must be suitable for printing by any method before processing and suitable for processing in accordance with the present invention, including drying, carried out before printing with a liquid toner-based electroreprographic printer.

В одном варианте осуществления подложкой является бумажное изделие, которое может обладать любой формой, известной специалисту с общей подготовкой в данной области техники, такое как один или большее количество рулонов, нарезанных листов, и/или может обладать разными формами и конфигурациями и подходить для печати с помощью цифрового принтера для ЖЭФ. Подложкой также может являться любая другая подложка, совместимая с методикой печати с помощью ЖЭФ, известная специалисту с общей подготовкой в данной области техники.In one embodiment, the substrate is a paper product that may be in any shape known to one of ordinary skill in the art, such as one or more rolls, cut sheets, and/or may be in a variety of shapes and configurations and suitable for printing with using a digital printer for JEF. The substrate may also be any other substrate compatible with the VEF printing technique known to one of ordinary skill in the art.

Количество полимера, нанесенного на подложку, зависит от характеристик подложки. Так, например, если подложкой является не содержащая покрытия бумага, то композиция, содержащая один или большее количество полимеров, может впитываться в подложку или может оставаться на поверхности.The amount of polymer deposited on the substrate depends on the characteristics of the substrate. For example, if the substrate is uncoated paper, then the composition containing one or more polymers may be absorbed into the substrate or may remain on the surface.

Методика, с помощью которой композицию, содержащую один или большее количество полимеров, наносят на поверхность для печати, может влиять на количество композиции, нанесенной на подложку. В таких случаях количество полимера указанно в настоящем изобретении, как количество, добавленное к подложке, выраженное в массовых процентах в пересчете на массу подложки. Однако в случаях, когда композиция не впитывается в подложку, полное количество одного или большего количества полимеров выражено, как количество, нанесенное на поверхность, и добавляемое количество выражено, как масса в пересчете на площадь обработанной поверхности. Количества соответствуют полному количеству одного или большего количества полимеров, нанесенных на подложку, а не всей нанесенной композиции.The technique by which a composition containing one or more polymers is applied to a printable surface can affect the amount of composition applied to the substrate. In such cases, the amount of polymer is referred to in the present invention as the amount added to the substrate, expressed as a weight percent based on the weight of the substrate. However, in cases where the composition does not soak into the substrate, the total amount of one or more polymers is expressed as the amount applied to the surface, and the amount added is expressed as weight based on the surface area treated. The amounts correspond to the total amount of one or more polymers deposited on the substrate, and not to the entire applied composition.

Обычно, если обработанной подложкой является бумажное изделие или пористая или полупористая подложка, то количество одного или большего количества полимеров, добавленных к обработанному бумажному изделию, может находиться в диапазоне от примерно 0,02 до примерно 1 мас. % или от примерно 0,03 до примерно 0,5%, или от примерно 0,04 до примерно 0,25%, или от примерно 0,04 до примерно 0,1% в пересчете на массу сухой подложки. Количества соответствуют полному количеству одного или большего количества полимеров, нанесенных на подложку, а не всей нанесенной композиции.Typically, if the treated substrate is a paper product or a porous or semi-porous substrate, then the amount of one or more polymers added to the treated paper product may range from about 0.02 to about 1 wt. %, or from about 0.03 to about 0.5%, or from about 0.04 to about 0.25%, or from about 0.04 to about 0.1%, based on the weight of the dry substrate. The amounts correspond to the total amount of one or more polymers deposited on the substrate, and not to the entire applied composition.

Обработанной подложкой может являться относительно непористая подложка и даже бумага со сплошной поверхностью, и количество одного или большего количества полимеров, находящихся на каждой стороне обработанной подложки, может находиться в диапазоне от примерно 0,0075 до примерно 0,375 г/м² или от 0,0115 примерно до 0,165 г/м², или от примерно 0,015 до примерно 0,095 г/м², или от примерно 0,015 до примерно 0,04 г/м² в пересчете на массу сухой подложки. Количества соответствуют полному количеству одного или большего количества полимеров, нанесенных на подложку, а не всей нанесенной композиции.The treated substrate may be a relatively non-porous substrate and even a continuous surface paper, and the amount of one or more polymers present on each side of the treated substrate may range from about 0.0075 to about 0.375 g/m ² , or from 0.0115 up to about 0.165 g/m ² , or from about 0.015 to about 0.095 g/m ² , or from about 0.015 to about 0.04 g/m ² , based on the dry weight of the substrate. The amounts correspond to the total amount of one or more polymers applied to the substrate, and not to the entire applied composition.

Композиция, содержащая один или большее количество полимеров, может дополнительно содержать дополнительные добавки, предназначенные для улучшения адгезии жидкого тонера при печати на подложке. Такими добавками могут являться полиэтиленимин или сополимер этилена с акриловой кислотой.The composition containing one or more polymers may additionally contain additional additives designed to improve the adhesion of liquid toner when printed on a substrate. Such additives may be polyethyleneimine or an ethylene-acrylic acid copolymer.

Композиция, содержащая один или большее количество полимеров, может дополнительно содержать дополнительные добавки, известные в данной области техники, включая, например, наполнители, противовспениватели, воска, пигменты, красители, биоциды, модификаторы реологических характеристик, производные канифоли, поверхностно-активные вещества и/или их комбинации. В настоящем изобретении нет необходимости использования связующего для обеспечения необходимой функции, заключающейся в обеспечении адгезии изображений к обработанной подложке, а также нет необходимости использования связующего для нанесения, как в случае обработки бумаги в бумагоделательной машине, такой как пресс для проклеивания. Массовое количество одного или большего количества полимеров, применяющихся для обработки подложки, в пересчете на массу сухого вещества составляет не менее примерно 50%, не менее примерно 75%, не менее примерно 80%, не менее примерно 90%, не менее примерно 95% и не менее 98% в пересчете на полную массу сухой композиции.The composition containing one or more polymers may additionally contain additional additives known in the art, including, for example, fillers, antifoams, waxes, pigments, dyes, biocides, rheology modifiers, rosin derivatives, surfactants and/ or their combinations. In the present invention, it is not necessary to use a binder to provide the necessary function of adhesion of the images to the treated substrate, nor is it necessary to use a binder for application, as is the case for paper processing in a paper machine, such as a size press. The weight of one or more of the polymers used to treat the substrate, on a dry weight basis, is at least about 50%, at least about 75%, at least about 80%, at least about 90%, at least about 95%, and not less than 98% in terms of the total weight of the dry composition.

Способ может дополнительно включать отверждение подложек с обработанной поверхностью, проводимое по любой методике, известной в данной области техники, включая, например, добавление в композицию, содержащую полимер, отверждаемых УФ-излучением или термически отверждаемых мономеров и/или отверждение УФ-излучением или термическое отверждение подложек с обработанной поверхностью.The method may further include curing the surface treated substrates by any technique known in the art, including, for example, adding UV curable or thermally curable monomers to the polymer-containing composition and/or UV curing or thermal curing. surface-treated substrates.

В способе, предлагаемом в настоящем изобретении, можно использовать любую известную специалисту с общей подготовкой в данной области техники методику, подходящую для нанесения композиции, содержащей полимер, на подложку, с помощью которой обеспечена в основном однородная обработка поверхности подложки или областей, необходимых для печати. Такие методики включают, но не ограничиваются только ими, например, нанесение покрытия распылением, нанесение покрытия в пенной фазе, нанесение покрытия поливом, нанесение покрытия валиком, нанесение покрытия путем переноса из формы, печатание и/или их комбинации.The method of the present invention may use any technique known to those of ordinary skill in the art that is suitable for applying a polymer-containing composition to a substrate that provides a substantially uniform surface finish on the substrate or areas to be printed. Such techniques include, but are not limited to, for example, spray coating, foam phase coating, curtain coating, roller coating, transfer coating, printing, and/or combinations thereof.

Одним объектом настоящего изобретения является подложка с печатью, полученная любым из указанных выше способов.One object of the present invention is a printed substrate obtained by any of the above methods.

Другим объектом настоящего изобретения является подложка с печатью, полученная любым из способов, предлагаемых в настоящем изобретении, которая может дополнительно содержать одно или большее количество изображений, напечатанных на подложке до и/или после проведения способов, предлагаемых в настоящем изобретении. Одно или большее количество дополнительных изображений, напечатанных на подложке, могут быть напечатаны с использованием любой методики/процедуры печати, известной специалисту с общей подготовкой в данной области техники, включая, например, но не ограничиваясь только ей, струйную печать.Another object of the present invention is a printed substrate obtained by any of the methods proposed in the present invention, which may additionally contain one or more images printed on the substrate before and/or after the methods proposed in the present invention. The one or more additional images printed on the substrate may be printed using any printing technique/procedure known to one of ordinary skill in the art, including, for example, but not limited to, inkjet printing.

В вариантах осуществления изображение, напечатанное на подложке с помощью способа, предлагаемого в настоящем изобретении, может обладать адгезией к подложке, определенной с помощью теста на отслаивание с использованием клейкой ленты 3М 230, составляющей более примерно 80% или более примерно 85%, или более примерно 90%, или более примерно 95%.In embodiments, an image printed on a substrate using the method of the present invention may have adhesion to the substrate, as determined by a peel test using 3M 230 adhesive tape, of greater than about 80%, or greater than about 85%, or greater than about 90%, or more than about 95%.

Альтернативно, любое изображение, 100% черное изображение или 290% составное черное изображение (использующееся для исследований HP), напечатанное на подложке, обладает сохранением адгезии к обработанной подложке, определенным с помощью теста на отслаивание с использованием клейкой ленты 3М 230, который более подробно описан ниже, составляющим более примерно 80%, альтернативно, более примерно 85%, альтернативно, более примерно 90% или, альтернативно, более 95%. В одном варианте осуществления изображение, полученное с помощью 100% черного жидкого тонера, обладает сохранением адгезии к обработанной подложке, определенным с помощью теста на отслаивание с использованием клейкой ленты, проведенным в Rochester Institute of Technology (RIT) с использованием стандартной процедуры фирмы HP для печатной машины HP Indigo 5500, составляющим более 90%. В настоящее время в тестах требуется использование клейкой ленты 3М 234. Ее используют вместо клейкой ленты 3М 230 и в процедуру вносят изменения вследствие изменения типа клейкой ленты. В другом варианте осуществления адгезия, определенная в RIT, составляет более 95%. В другом варианте осуществления изображение, полученное с помощью 290% черного жидкого тонера, обладает сохранением адгезии к обработанной подложке, определенным в RIT с помощью такого же теста HP с использованием клейкой ленты, составляющим более 80% или более 90%, или более 95%.Alternatively, any image, 100% black image or 290% composite black image (used for HP research) printed on a substrate has retention of adhesion to the treated substrate as determined by the 3M 230 Adhesive Tape Peel Test, which is described in more detail. lower than about 80%, alternatively, more than about 85%, alternatively, more than about 90%, or alternatively, more than 95%. In one embodiment, an image produced with 100% black liquid toner has retention of adhesion to a treated substrate as determined by a tape peel test conducted at the Rochester Institute of Technology (RIT) using HP's standard printing procedure. machines HP Indigo 5500, accounting for more than 90%. Tests currently require the use of 3M 234 adhesive tape. This is used in place of 3M 230 adhesive tape and the procedure is being modified due to a change in the type of adhesive tape. In another embodiment, the adhesion determined by the RIT is greater than 95%. In another embodiment, an image produced with 290% black liquid toner has retention of adhesion to a treated substrate as determined by the RIT using the same HP tape test of greater than 80%, or greater than 90%, or greater than 95%.

Настоящее изобретение относится к печатному материалу, включающему: (i) подложку, обработанную композицией, содержащей полимер, обработку проводят способом, предлагаемым в настоящем изобретении, с получением обработанной подложки; и (ii) изображение, находящееся по меньшей мере на части одной поверхности обработанной подложки, где изображение напечатано на обработанной подложке с помощью электрофотографического принтера и жидкого тонера.The present invention relates to a printed material, including: (i) a substrate treated with a composition containing a polymer, the processing is carried out by the method proposed in the present invention, to obtain a treated substrate; and (ii) an image located on at least a portion of one surface of the treated substrate, where the image is printed on the treated substrate using an electrophotographic printer and liquid toner.

ПРИМЕРЫEXAMPLES

В приведенных ниже примерах проиллюстрировано улучшение адгезии жидкого тонера для ЖЭФ к подложке, раскрытой в настоящем изобретении, по сравнению с адгезией краски для ЖЭФ к подложкам, известным из предшествующего уровня техники. Эти примеры предназначены лишь для иллюстрации настоящего изобретения и не предназначены для ограничения настоящего изобретения конкретными соединениями, методиками, условиями или случаями применения, раскрытыми в настоящем изобретении.The following examples illustrate the improvement in the adhesion of liquid VEF toner to the substrate disclosed in the present invention compared to the adhesion of VEF ink to prior art substrates. These examples are only intended to illustrate the present invention and are not intended to limit the present invention to the particular compounds, methods, conditions or uses disclosed in the present invention.

МЕТОДИКА ИССЛЕДОВАНИЯ ДЛЯ ОПРЕДЕЛЕНИЯ АДГЕЗИИRESEARCH TECHNIQUE FOR DETERMINING ADHESION

Использующейся методикой исследования являлась стандартная методика определения адгезии напечатанных с помощью HP® digital Indigo™ изображений к подложкам, определенная фирмой HP для исследования пригодности бумаги для печати с помощью их печатных машин Indigo. Точнее, с помощью 100% черного жидкого тонера печатали черные прямоугольные изображения с использованием принтера HP® Indigo 5500 в режиме 4 циклов с использованием условий стандартной температуры и получали исследуемый образец. Черные прямоугольные изображения также печатали с использованием такого же принтера и условий, но черный тонер состоял из 52 частей желтого, 66 частей пурпурного, 72 частей голубого и 100 частей черного тонера, такие изображения обычно называются 290% фотоизображениями. Последнее исследование обычно является более строгим.The test method used was the standard HP® digital Indigo™ printed image to substrate adhesion test method defined by HP to test paper suitability for printing on their Indigo presses. More specifically, 100% black liquid toner was used to print black rectangular images using an HP® Indigo 5500 printer in 4 cycle mode using standard temperature conditions, and a test sample was obtained. Black rectangular images were also printed using the same printer and conditions, but the black toner consisted of 52 parts yellow, 66 parts magenta, 72 parts cyan, and 100 parts black toner, such images are commonly referred to as 290% photo images. The latter study is usually more rigorous.

Через 10 мин после печати описанных выше изображений исследовали адгезию изображений к подложке с помощью теста на отслаивание с использованием клейкой ленты ЗМ™ 230 и валика с грузом для обеспечения равномерного и постоянного приложенного усилия. Определяли выраженную в процентах часть изображения, не удаленную при отслаивании клейкой ленты.Ten minutes after the printing of the above images, the adhesion of the images to the substrate was examined using a peel test using 3M™ 230 adhesive tape and a weighted roller to ensure uniform and constant applied force. The percentage of the image not removed by peeling off the adhesive tape was determined.

Исследования проводили в Rochester Institute of Technology (находящееся в Северной Америке место проведения испытаний для определения пригодности обработки бумаги для печати с помощью печатных машин Indigo) в соответствии со стандартными процедурами исследования, описанными фирмой HP, для испытания адгезии краски, нанесенной с помощью одной из их печатных машин Indigo. Для этих исследований использовали печатную машину HP® Indigo 5500. Настоящее изобретение применимо для любых печатных машин/принтеров HP Indigo на основе жидкого тонера и их можно использовать для исследования адгезии по методикам, известным специалистам в данной области техники.Studies were conducted at the Rochester Institute of Technology (North American-based test site for paper processing suitability for printing with Indigo presses) in accordance with HP's standard test procedures to test ink adhesion applied with one of their Indigo printing machines. An HP® Indigo 5500 press was used for these studies. The present invention is applicable to any HP Indigo presses/printers based on liquid toner and can be used to test adhesion according to methods known to those skilled in the art.

ПРИМЕР 1EXAMPLE 1

Исследовали адгезию изображений, полученных с помощью принтера HP 5500 Indigo (тест проводили в Rochester Institute of Technology), к имеющейся в продаже бумаги для офсетной печати, обладающей плотностью 112 г/м², содержанием золы, равным 19%, степенью проклеивания, определенной с помощью теста проклеивания фирмы Hercules (HST), равной 8 с, и содержащей сульфированный оптически отбеливающий реагент. Образцы также обрабатывали раствором поли-2-этил-2-оксазолина (PEtOx), обладающего средней ММ (молекулярная масса), равной 500000 Да, при количестве использующегося для обработки полимера, составляющем 0,3% и 0,6% в пересчете на массу сухой бумаги. Обработку проводили путем нанесения 15% раствора и последующей сушки в барабанной сушилке. Выраженная в % адгезия оттиска 100% черной краской к контрольной бумаге составляла 84%. При обработке с помощью 0,3% PEtOx адгезия улучшалась до 91% и при обработке с помощью 0,6% адгезия составляла 92%. Поэтому добавление PEtOx улучшает адгезию. Вместе с PEtOx не добавляли другой полимер или модификатор реологических характеристик.The adhesion of images obtained with an HP 5500 Indigo printer (test conducted at the Rochester Institute of Technology) to a commercially available offset printing paper having a density of 112 g/m ² , an ash content of 19%, a sizing ratio determined with using a Hercules Sizing Test (HST) of 8 seconds and containing a sulfonated optical brightening agent. The samples were also treated with a solution of poly-2-ethyl-2-oxazoline (PEtOx) having an average MW (molecular weight) of 500,000 Da, with a polymer treatment of 0.3% and 0.6% by weight. dry paper. The treatment was carried out by applying a 15% solution and subsequent drying in a drum dryer. Expressed in % adhesion print 100% black ink to the control paper was 84%. When treated with 0.3% PEtOx adhesion improved to 91% and when treated with 0.6% adhesion was 92%. Therefore, the addition of PEtOx improves adhesion. No other polymer or rheology modifier was added along with PEtOx.

Хотя в приведенном выше подробном описании представлен по меньшей мере один типичный вариант осуществления, следует понимать, что существует большое количество модификаций. Следует понимать, что типичный вариант осуществления или типичные варианты осуществления являются лишь примерами и они не предназначены для какого-либо ограничения объема, применимости или конфигурации разных вариантов осуществления. С помощью приведенного выше подробного описания специалистам в данной области техники скорее предоставлена подходящая схема выполнения типичного варианта осуществления, входящего в объем настоящего изобретения. Следует понимать, что в функции и расположение элементов, описанных в типичном варианте осуществления, можно внести различные изменения без отклонения от объема разных вариантов осуществления, приведенных в прилагаемой формуле изобретения.While at least one exemplary embodiment has been presented in the above detailed description, it should be understood that a large number of modifications exist. It should be understood that the exemplary embodiment or exemplary embodiments are merely examples and are not intended to limit in any way the scope, applicability, or configuration of the various embodiments. With the above detailed description, those skilled in the art are rather provided with a suitable embodiment of an exemplary embodiment within the scope of the present invention. It should be understood that various changes can be made to the function and arrangement of the elements described in the exemplary embodiment without departing from the scope of the various embodiments recited in the appended claims.

Claims

1. The method of obtaining an image to at least one surface of the substrate, the method includes:

treating at least a portion of the surface by applying a composition containing one or more water-soluble polymers to at least a portion of the surface, in which each of the one or more polymers contains a repeating unit, and where the repeating unit contains a negatively charged dipole moment , equal to more than 2 debyes, and where the repeating link does not contain a positively charged dipole moment, equal to more than 0.8 debyes;

drying the composition after application of the composition to the substrate to obtain a treated substrate; and

printing an image on a processed substrate using an electrophotographic printer using liquid toner technology,

where the substrate is processed and dried less than 5 minutes before printing on it;

wherein the composition is free of ethylene-acrylic acid polymer and ethylene-methacrylic acid polymer, and wherein the composition is free of binder.

2. Process according to claim 1, wherein one or more polymers are derived from 2-ethyl-2-oxazoline and/or 2-methyloxazoline.

3. The method of claim. 1, in which each of the one or more polymers includes at least one repeating unit containing a tertiary amide group, where (i) at least one of the carbon atoms associated with the nitrogen atom of the tertiary amide group, contains two or three hydrogen atoms associated with it, and (ii) the nitrogen atom of the tertiary amide group is bonded to a carbonyl group associated with a CH, CH ₂ or CH ₃ group.

4. The method of claim 1, wherein one or more of the polymers are homopolymers derived from 2-ethyl-2-oxazoline.

5. The method of claim 1 wherein one or more of the polymers are homopolymers derived from 2-methyloxazoline.

6. The method of claim 1, wherein each of the one or more polymers is a homopolymer and has a number average molecular weight of 500,000 to 2,000,000 Da.

7. The method according to any one of paragraphs. 1-6, in which the composition contains one or more polymers in an amount of at least 95%, based on the dry weight of the composition.

8. Printed substrate obtained by the method according to any one of paragraphs. 1-7.

9. The printed substrate according to claim 8, wherein at least one of all treated sides of the substrate contains one or more polymers in an amount of 0.0075 to 0.375 g/m ² based on the dry weight of the substrate.

10. A printed substrate as claimed in claim 8 or 9, wherein the image has greater than about 90% adhesion to the substrate, as determined by a peel test using 3M 230 adhesive tape.

11. Printed material, including:

a surface-treated substrate comprising a printable coating, where the printable coating is applied to at least a portion of at least one side of the substrate, where the printable coating includes one or more water-soluble polymers, in which one or more polymers contain one or more the number of repeating links having a negatively charged dipole greater than 2 debyes and not having a positively charged dipole greater than 0.8 debyes; and

an image located on at least a portion of the printable cover, where the image is printed on the printable cover by an electrophotographic printer using liquid toner technology;

wherein the coating is applied to the substrate less than about 5 minutes before the image is printed;

in which the composition is free from a polymer of ethylene and acrylic acid and a polymer of ethylene and methacrylic acid; and

in which the composition is free from a binder.

12. Printed material according to claim 11, wherein one or more polymers are derived from 2-ethyl-2-oxazoline and/or 2-methyloxazoline.

13. The printed matter of claim. 11, in which each of the one or more polymers includes at least one repeat unit containing a tertiary amide group, where (i) at least one of the carbon atoms associated with the nitrogen atom of the tertiary amide group , has two or three hydrogen atoms associated with it, and (ii) the nitrogen atom of the tertiary amide group is bonded to a carbonyl group associated with a CH, CH ₂ or CH ₃ group.

14. The printed matter of claim 11 wherein one or more of the polymers are homopolymers derived from 2-ethyl-2-oxazoline.

15. The printed matter of claim 13, wherein one or more of the polymers are homopolymers derived from 2-methyloxazoline.

16. The method of obtaining an image to at least one surface of the substrate includes:

treating at least a portion of the surface by applying a composition containing one or more water-soluble homopolymers to at least a portion of the surface, wherein each of the one or more water-soluble homopolymers is derived from 2-ethyl-2- oxazoline or 2-methyloxazoline and has a number average molecular weight of 500,000 to 2,000,000 Da;

printing an image on a processed substrate using an electrophotographic printer using liquid toner technology;

where the substrate is processed and dried less than 5 minutes before printing on it; in which the composition is free from a polymer of ethylene and acrylic acid and a polymer of ethylene and methacrylic acid; and

in which the composition is free from a binder.

17. The method of claim 16 wherein the composition contains one homopolymer.

18. The process of claim 16 wherein one homopolymer is derived from 2-ethyl-2-oxazoline.

19. The method of claim 18, wherein one homopolymer has a number average molecular weight of 500,000 Da.

20. The method of claim 16 wherein the homopolymer has a number average molecular weight of 500,000 Da.