Abstract
Description
Изобретение относится к области металлургии, а именно к составам сплавов, которые могут быть использованы для изготовления корпусов часов, монет, ювелирных изделий.The invention relates to the field of metallurgy, and in particular to alloy compositions that can be used for the manufacture of watch cases, coins, jewelry.
Известен сплав, содержащий, мас.%: бериллий 0,1-0,5; серебро 10,0-35,0; цинк 6,0-10,0; медь 40,0-60,0; золото - остальное [1].Known alloy containing, wt.%: Beryllium 0.1-0.5; silver 10.0-35.0; zinc 6.0-10.0; copper 40.0-60.0; gold is the rest [1].
Задачей изобретения является снижение твердости сплава.The objective of the invention is to reduce the hardness of the alloy.
Технический результат достигается тем, что сплав, содержащий бериллий, серебро, золото, медь, дополнительно содержит кадмий при следующем соотношении компонентов, мас.%: бериллий 0,2-0,3; серебро 40,0-45,0; золото 34,8-40,8; медь 15,0-17,0; кадмий 3,0-4,0.The technical result is achieved in that the alloy containing beryllium, silver, gold, copper, additionally contains cadmium in the following ratio of components, wt.%: Beryllium 0.2-0.3; silver 40.0-45.0; gold 34.8-40.8; copper 15.0-17.0; cadmium 3.0-4.0.
В таблице приведены составы сплава.The table shows the alloy compositions.
В составе сплава компоненты проявляют себя следующим образом. Серебро придает сплаву ковкость, снижает его твердость. Медь, золото и бериллий увеличивают прочность и упругость сплава. Кадмий обеспечивает сохранение ковкости и пластичности сплава. Твердость сплава снижается на 7-10% в сравнении со сплавом [1].In the composition of the alloy, the components manifest themselves as follows. Silver gives the alloy ductility, reduces its hardness. Copper, gold and beryllium increase the strength and elasticity of the alloy. Cadmium preserves the ductility and ductility of the alloy. The hardness of the alloy is reduced by 7-10% in comparison with the alloy [1].
Выплавка сплава может быть проведена в электропечах.Smelting of the alloy can be carried out in electric furnaces.
Источник информацииThe source of information
1. JP 57-152437, C22C 9/00, 1982.1. JP 57-152437, C22C 9/00, 1982.
Claims (1)
Priority Applications (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
RU2012108789/02A RU2479654C1 (en) | 2012-03-07 | 2012-03-07 | Alloy |
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
RU2012108789/02A RU2479654C1 (en) | 2012-03-07 | 2012-03-07 | Alloy |
Publications (1)
Publication Number | Publication Date |
---|---|
RU2479654C1 true RU2479654C1 (en) | 2013-04-20 |
Family
ID=49152725
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
RU2012108789/02A RU2479654C1 (en) | 2012-03-07 | 2012-03-07 | Alloy |
Country Status (1)
Country | Link |
---|---|
RU (1) | RU2479654C1 (en) |
Citations (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4804517A (en) * | 1986-03-06 | 1989-02-14 | Williams Dental Company, Inc. | Gold colored palladium - indium alloys |
US5240172A (en) * | 1989-10-27 | 1993-08-31 | Degussa Aktiengesellschaft | Solder alloy for dental and jewelry parts |
DE4423646C1 (en) * | 1994-07-06 | 1995-08-17 | Wieland Edelmetalle | Nickel@-free white gold jewelry alloy |
DE19958800A1 (en) * | 1999-06-30 | 2001-01-04 | Wieland Edelmetalle | White gold jewelry alloy for all jewelry purposes contains alloying additions of silver and iron |
RU2335557C1 (en) * | 2007-03-05 | 2008-10-10 | Юлия Алексеевна Щепочкина | Alloy on base of gold |
-
2012
- 2012-03-07 RU RU2012108789/02A patent/RU2479654C1/en active
Patent Citations (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4804517A (en) * | 1986-03-06 | 1989-02-14 | Williams Dental Company, Inc. | Gold colored palladium - indium alloys |
US5240172A (en) * | 1989-10-27 | 1993-08-31 | Degussa Aktiengesellschaft | Solder alloy for dental and jewelry parts |
DE4423646C1 (en) * | 1994-07-06 | 1995-08-17 | Wieland Edelmetalle | Nickel@-free white gold jewelry alloy |
DE19958800A1 (en) * | 1999-06-30 | 2001-01-04 | Wieland Edelmetalle | White gold jewelry alloy for all jewelry purposes contains alloying additions of silver and iron |
RU2335557C1 (en) * | 2007-03-05 | 2008-10-10 | Юлия Алексеевна Щепочкина | Alloy on base of gold |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
IN2012DN04940A (en) | ||
MY166908A (en) | HIGH PURITY Cu BONDING WIRE | |
RU2501875C1 (en) | Gold-based alloy | |
RU2479654C1 (en) | Alloy | |
RU2507287C1 (en) | Copper-based alloy | |
RU2457269C1 (en) | Copper-based alloy | |
RU2446220C1 (en) | Copper-based alloy | |
RU2562560C1 (en) | Copper-based alloy | |
RU2437947C1 (en) | Alloy for mintage | |
RU2399689C1 (en) | Alloy on gold base | |
RU2418875C1 (en) | Alloy on base of silver | |
RU2496900C1 (en) | Copper-base alloy | |
RU2335557C1 (en) | Alloy on base of gold | |
RU2445385C1 (en) | Copper-based alloy | |
RU2405053C1 (en) | Alloy | |
RU2326955C1 (en) | Copper based alloy with yellow gold colour | |
RU2537688C1 (en) | Copper-based alloy | |
RU2508414C1 (en) | Copper-based alloy | |
RU2363750C1 (en) | Alloy | |
RU2356970C1 (en) | Alloy on basis of gold | |
RU2502816C1 (en) | Silver-base alloy | |
RU2318889C1 (en) | Gold-base alloy | |
RU2500825C1 (en) | Gold-base alloy | |
RU2356974C1 (en) | Alloy on basis of gilt copper | |
RU2528924C1 (en) | Jewellery alloy |