RU2430025C1 - Charge for glass production - Google Patents
Charge for glass production Download PDFInfo
- Publication number
- RU2430025C1 RU2430025C1 RU2010117914/03A RU2010117914A RU2430025C1 RU 2430025 C1 RU2430025 C1 RU 2430025C1 RU 2010117914/03 A RU2010117914/03 A RU 2010117914/03A RU 2010117914 A RU2010117914 A RU 2010117914A RU 2430025 C1 RU2430025 C1 RU 2430025C1
- Authority
- RU
- Russia
- Prior art keywords
- glass
- charge
- soda
- glass production
- fluorspar
- Prior art date
Abstract
Description
Изобретение относится к области технологии силикатов и касается производства стекла, используемого для изготовления смальты.The invention relates to the field of technology of silicates and for the production of glass used for the manufacture of smalt.
Известна шихта для получения стекла, включающая соду, кварцевый песок, диопсидовую породу 25,9-85,0 мас.% (с содержанием примесей не более 15,0 мас.%.A known mixture for producing glass, including soda, quartz sand, diopside rock of 25.9-85.0 wt.% (With an impurity content of not more than 15.0 wt.%.
Задачей изобретения является снижение температуры варки стекла.The objective of the invention is to reduce the temperature of glass melting.
Технический результат достигается тем, что шихта для получения стекла, включающая соду и кварцевый песок, дополнительно содержит бой тарного стекла, предварительно прокаленный медный купорос и плавиковый шпат при следующем соотношении компонентов, мас.%: сода 20,0-24,0; кварцевый песок 20,0-24,0; бой тарного стекла 45,5-53,5; предварительно прокаленный медный купорос 0,5-2,5; плавиковый шпат 4,0-6,0.The technical result is achieved in that the mixture for producing glass, including soda and quartz sand, further comprises a container glass break, previously calcined copper sulfate and fluorspar in the following ratio of components, wt.%: Soda 20.0-24.0; silica sand 20.0-24.0; container glass battle 45.5-53.5; pre-calcined copper sulfate 0.5-2.5; fluorspar 4.0-6.0.
В таблице приведены составы шихты.The table shows the composition of the charge.
Стекло может быть получено в стекловаренных печах любой конструкции при температуре 1250-1290°С.Glass can be obtained in glass melting furnaces of any design at a temperature of 1250-1290 ° C.
Источники информацииInformation sources
1. SU 1530588, С03С 6/00, 1990.1. SU 1530588, C03C 6/00, 1990.
Claims (1)