RU2391423C1 - Sintered copper based alloy - Google Patents
Sintered copper based alloy Download PDFInfo
- Publication number
- RU2391423C1 RU2391423C1 RU2009123531/02A RU2009123531A RU2391423C1 RU 2391423 C1 RU2391423 C1 RU 2391423C1 RU 2009123531/02 A RU2009123531/02 A RU 2009123531/02A RU 2009123531 A RU2009123531 A RU 2009123531A RU 2391423 C1 RU2391423 C1 RU 2391423C1
- Authority
- RU
- Russia
- Prior art keywords
- copper
- alloy
- zinc
- nickel
- iron
- Prior art date
Abstract
Description
Изобретение относится к области металлургии и касается составов спеченных сплавов на основе меди, используемых в машиностроении.The invention relates to the field of metallurgy and relates to compositions of sintered copper-based alloys used in mechanical engineering.
Известен сплав на основе меди, содержащий, мас.%: олово 3,0-6,0; цинк 3,5-8,5; свинец 3,5-7,5; никель 0,1-1,5; железо 0,1-1,0; медь - остальное [1]. Предел прочности сплава составляет 318-330 МПа.Known copper based alloy containing, wt.%: Tin 3.0-6.0; zinc 3.5-8.5; lead 3.5-7.5; nickel 0.1-1.5; iron 0.1-1.0; copper - the rest [1]. The tensile strength of the alloy is 318-330 MPa.
Задачей изобретения является повышение прочности сплава.The objective of the invention is to increase the strength of the alloy.
Технический результат достигается тем, что спеченный сплав на основе меди, содержащий олово, цинк, свинец, никель, железо, дополнительно включает ванадий и церий при следующем соотношении компонентов, мас.%: олово 4,0-6,0; цинк 2,0-3,0; свинец 1,0-2,0; никель 2,0-3,0; железо 0,03-0,05; ванадий 0,2-0,3; церий 0,1-0,2; медь - остальное.The technical result is achieved in that the sintered alloy based on copper, containing tin, zinc, lead, nickel, iron, additionally includes vanadium and cerium in the following ratio of components, wt.%: Tin 4.0-6.0; zinc 2.0-3.0; lead 1.0-2.0; nickel 2.0-3.0; iron 0.03-0.05; vanadium 0.2-0.3; cerium 0.1-0.2; copper is the rest.
В таблице приведены составы спеченного сплава на основе меди.The table shows the compositions of the sintered alloy based on copper.
Повышение прочности сплава на основе меди достигается за счет комплексного влияния компонентов, входящих в его состав. Олово и цинк способствуют улучшению металлической основы сплава. Свинец повышает антифрикционные свойства сплава. Никель повышает плотность сплава, благоприятно влияет на выравнивание механических свойств изделий. Железо и ванадий способствуют измельчению зерна. Церий нейтрализует влияние вредных примесей сурьмы и мышьяка.An increase in the strength of a copper-based alloy is achieved due to the complex effect of the components included in its composition. Tin and zinc contribute to the improvement of the metal base of the alloy. Lead increases the antifriction properties of the alloy. Nickel increases the density of the alloy, favorably affects the alignment of the mechanical properties of products. Iron and vanadium contribute to the grinding of grain. Cerium neutralizes the influence of harmful impurities of antimony and arsenic.
Сплав получают методом порошковой металлургии путем прессования под давлением 2 т/см2 смеси порошков компонентов в изделия необходимой формы и последующего спекания при температуре 950°С в течение 3-4 ч в атмосфере инертного газа или в вакууме.The alloy is obtained by powder metallurgy by pressing under pressure 2 t / cm 2 a mixture of the powders of the components into products of the desired shape and subsequent sintering at a temperature of 950 ° C for 3-4 hours in an inert gas atmosphere or in vacuum.
Источники информацииInformation sources
1. SU 1601169, С22С 9/08, 1990.1. SU 1601169, C22C 9/08, 1990.
Claims (1)