RU2348534C1

RU2348534C1 - Method for application of image on pvc material

Info

Publication number: RU2348534C1
Application number: RU2007118596/12A
Authority: RU
Inventors: Владимир Михайлович Зевахин (RU); Владимир Михайлович Зевахин
Original assignee: Владимир Михайлович Зевахин
Priority date: 2007-05-15
Filing date: 2007-05-15
Publication date: 2009-03-10
Also published as: RU2007118596A

Abstract

FIELD: technological processes.

SUBSTANCE: invention is related to methods for jet printing with the help of printer on polyvinylchloride (PVC) material, mostly on film PVC material used for manufacture of casement ceilings. Method includes stepwise introduction of material sections into printing area located in the area of jet printing head location. Application of dye with the help of jet printing head on material surface in compliance with information received by printer for reproduction of previously formed image. Treatment of material with applied dye for its fixation on material surface is carried out. Image is applied by method of cold printing without previous heating of material supplied to printing area and without heating of environment in specified area. Dye used is solvent or ecosolvent ink for jet printers. Treatment of material with applied dye is realised after material exit from printing area by blowing of material surface with applied dye by air with temperature of 14-25°C.

EFFECT: possibility to apply image on non-modified film PVC materials with the help of jet printer.

3 cl

Description

Изобретение относится к области печати, а именно к способам струйной печати на поливинилхлоридном (ПВХ) материале.The invention relates to the field of printing, and in particular to methods of inkjet printing on polyvinyl chloride (PVC) material.

В настоящее время все более широкое применение находят материалы с нанесенным на его поверхность изображением для художественно-оформительских работ, в частности для изготовления натяжных потолков и декорирования стен.At present, materials with an image applied to its surface for art and design work, in particular for the manufacture of stretch ceilings and wall decoration, are increasingly used.

Известно использование для указанных целей бумажных и тканевых материалов, нанесение изображения на поверхность которых осуществляют по традиционной технологии струйной печати с использованием цветных широкоформатных сольвентных и экосольвентных струйных принтеров.It is known to use paper and fabric materials for these purposes, the application of the image on the surface of which is carried out according to the traditional technology of inkjet printing using color wide format solvent and eco-solvent inkjet printers.

Однако в последнее время для изготовления натяжных потолков и декорирования стен стали применять пленочные ПВХ материалы, для нанесения изображения на которые методом струйной печати требуется разрабатывать специальные приемы или технологии, с помощью которых обеспечивается закрепление красителя на поверхности материала.Recently, however, PVC film materials have begun to be used for the manufacture of stretch ceilings and wall decoration, for applying the image onto which the inkjet printing method requires the development of special techniques or technologies that can be used to fix the dye on the surface of the material.

Так, в частности, известны технические решения, согласно которым модифицируют поверхностные свойства ПВХ материала, например, путем нанесения на основу из ПВХ материала специального покрытия [KR 20020082661, KR 20020085607], в результате чего при печати изображения на данном материале достигается достаточно прочное закрепление красителя на нем.So, in particular, technical solutions are known according to which they modify the surface properties of a PVC material, for example, by applying a special coating to a PVC base material [KR 20020082661, KR 20020085607], as a result of which sufficiently strong fixing of the dye is achieved when printing an image on this material On him.

Известны технические решения, согласно которым для струйной печати на ПВХ материалах предлагается использовать чернила специального разработанного состава, обеспечивающие закрепление на данном материале изображения, напечатанного указанными чернилами [см., например, US 6602334, GB 2410705].Known technical solutions, according to which it is proposed to use ink of a specially developed composition for inkjet printing on PVC materials, which ensures fixing on this material an image printed with the indicated ink [see, for example, US 6602334, GB 2410705].

Однако весьма привлекательным является разработка способа, позволяющего наносить изображение по технологии струйной печати с помощью струйных принтеров, использующих сольвентные или экосольвентные чернила, на немодифицированный (не обработанный специальным образом или составом с целью закрепления красителя) ПВХ материал.However, it is very attractive to develop a method that allows you to apply an image using inkjet technology using inkjet printers using solvent or eco-solvent inks onto unmodified (not specially treated or with a composition to fix the dye) PVC material.

Наиболее близким по технической сущности к заявляемому изобретению является способ нанесения изображения на текстильный материал, описанный в [RU 2203994], который выбран авторами в качестве ближайшего аналога.Closest to the technical nature of the claimed invention is a method of applying an image to a textile material described in [RU 2203994], which is selected by the authors as the closest analogue.

Согласно рассматриваемому способу наносят изображение на поверхность воздухопроницаемого текстильного материала, транспортируемого через струйный принтер, содержащий по меньшей мере одну струйную печатающую головку. При этом способ включает шаговое введение участков материала в область печати, находящуюся в зоне расположения струйной печатающей головки, нанесение красителя с помощью струйной печатающей головки на поверхность материала в соответствии с получаемой принтером информацией для воспроизведения предварительного определенного рисунка, а также обработку материала с нанесенным красителем для его закрепления на поверхности материала. Указанную обработку осуществляют путем просасывания сквозь материал в области печати предварительно нагретого воздуха, причем в рассматриваемом способе предусмотрен предварительный нагрев материала перед поступлением его в область печати.According to the method under consideration, an image is applied to the surface of a breathable textile material transported through an inkjet printer containing at least one inkjet printhead. The method includes the step-by-step introduction of sections of material into the print area located in the area of the inkjet printhead, applying dye with an inkjet printhead on the surface of the material in accordance with the information received by the printer to reproduce a predetermined pattern, and also processing the material with the dye applied fixing it to the surface of the material. The specified processing is carried out by sucking through the material in the print area of the preheated air, and in the present method provides for the preliminary heating of the material before it enters the print area.

Данный способ обеспечивает нанесение изображения на поверхность текстильного материала методом струйной печати. Однако рассматриваемый способ не может быть применен для нанесения изображения на немодифицированный ПВХ материал.This method provides the application of the image on the surface of the textile material by inkjet printing. However, the considered method cannot be applied for applying an image to unmodified PVC material.

Задачей заявляемого изобретения является разработка способа нанесения изображения на немодиицированный ПВХ материал методом струйной печати с помощью струйного принтера, в котором используются сольвентные или экосольвентные чернила.The objective of the invention is the development of a method of applying an image on unmodified PVC material by inkjet printing using an inkjet printer that uses solvent or eco-solvent ink.

Сущность заявляемого изобретения заключается в том, что в способе нанесения изображения на поверхность рулонного материала, транспортируемого через струйный принтер, содержащий по меньшей мере одну струйную печатающую головку, включающем шаговое введение участков материала в область печати, находящуюся в зоне расположения струйной печатающей головки, нанесение красителя с помощью струйной печатающей головки на поверхность материала в соответствии с получаемой принтером информацией для воспроизведения предварительного сформированного рисунка, а также обработку материала с нанесенным красителем для его закрепления на поверхности материала, согласно изобретению изображение наносят методом холодной печати без предварительного нагрева поступающего в область печати материала и без нагрева окружающей среды в указанной области, в качестве материала используют пленочный поливинилхлоридный материал, в качестве красителя используют сольвентные или экосольвентные чернила для струйных принтеров, обработку материала с нанесенным красителем осуществляют после выхода материала из области печати путем обдува поверхности материала с нанесенным красителем воздухом с температурой 14-25°С.The essence of the claimed invention lies in the fact that in the method of applying an image to the surface of a roll of material transported through an inkjet printer containing at least one inkjet printhead, comprising the stepwise introduction of sections of material in the print area located in the area of the inkjet printhead, applying dye using an inkjet printhead on the surface of the material in accordance with the information received by the printer to reproduce the preformed according to the invention, the image is applied by cold printing without preheating the material entering the print area and without heating the environment in the specified area, using polyvinyl chloride film material as solvent or eco-solvent ink for inkjet printers is used as a dye; processing of the material with the applied dye is carried out after exit material from the print area by blowing the surface of the material coated with dye air with a temperature of 14-25 ° C.

В частном случае выполнения изобретения формирование рисунка осуществляется на персональном компьютере, при этом наносят краситель в соответствии с информацией для воспроизведения рисунка, получаемой от персонального компьютера.In the particular case of the invention, the formation of the pattern is carried out on a personal computer, while dye is applied in accordance with the information for reproducing the pattern received from the personal computer.

В частном случае выполнения изобретения, когда формирование рисунка осуществляется на персональном компьютере, наносят краситель с использованием предварительно полученной экспериментальным путем для конкретного принтера и конкретного вида пленочного ПВХ материала базы данных, полученной с учетом спектральных характеристик отображенных на рассматриваемом конкретном материале цветов печати, используемой для программного выбора рецептуры красителя из набора применяемых в принтере чернил, требуемого для воспроизведения нужного цвета и его интенсивности.In the particular case of the invention, when the drawing is carried out on a personal computer, a dye is applied using a database previously obtained experimentally for a specific printer and a specific type of PVC film material, obtained taking into account the spectral characteristics of the printing colors displayed on the particular material used for the software the choice of dye formulation from the set of ink used in the printer, required to reproduce the desired color eta and its intensity.

В результате проведенных экспериментальных исследований автору заявляемого изобретения удалось подобрать совокупность приемов, обеспечивающих нанесение изображения с помощью струйных принтеров, использующих сольвентные или экосольвентные чернила, на поверхность немодифицированных пленочных ПВХ материалов.As a result of experimental studies, the author of the claimed invention was able to select a set of techniques for applying images using inkjet printers using solvent or eco-solvent ink on the surface of unmodified PVC film materials.

А именно, предлагается процесс печатания осуществлять методом холодной печати, то есть без предварительного нагрева поступающего в область печати материала и без нагрева окружающей среды в указанной области, поскольку при повышенных температурах указанные материалы деформируются, что приводит к искажению изображения. Также предлагается для закрепления красителя на поверхности ПВХ материала после выхода его из области печати обдувать его поверхность воздухом с температурой от 14 до 25°С. При обдуве воздухом с температурой, выбранной из указанного диапазона, из чернил достаточно быстро удаляются летучие компоненты, при этом за счет кислорода воздуха происходит процесс полимеризации молекул входящих в состав чернил соединений с молекулами ПВХ материала. В результате чернила прочно закрепляются на ПВХ материале, не растекаясь по его поверхности. При обдуве поверхности ПВХ материала воздухом с температурой менее 14°С замедляются выше указанные процессы и чернила хуже закрепляются на ПВХ материале. При обдуве поверхности ПВХ материала воздухом с температурой выше 25°С существует опасность его деформации. Выбор конкретной температуры воздуха из указанного диапазона зависит от толщины пленочного ПВХ материалаNamely, it is proposed that the printing process be carried out by cold printing, that is, without preheating the material entering the print region and without heating the environment in the specified region, since these materials are deformed at elevated temperatures, which leads to image distortion. It is also proposed to fix the dye on the surface of the PVC material after it leaves the print area to blow its surface with air with a temperature of from 14 to 25 ° C. When air is blown at a temperature selected from the indicated range, volatile components are quickly removed from the ink, while the process of polymerization of the molecules of the ink compounds with the molecules of the PVC material occurs due to oxygen in the air. As a result, the ink is firmly fixed on the PVC material, not spreading over its surface. When blowing the surface of the PVC material with air with a temperature of less than 14 ° C, the above processes slow down and the ink is worse attached to the PVC material. When blowing the surface of the PVC material with air with a temperature above 25 ° C, there is a danger of its deformation. The choice of a specific air temperature from the specified range depends on the thickness of the PVC film material

Таким образом, техническим результатом, достигаемым при использовании заявляемого изобретения, является обеспечение возможности нанесения изображения на немодифицированные пленочные ПВХ материалы с помощью струйных принтеров, использующих сольвентные или экосольвентные чернила.Thus, the technical result achieved by using the claimed invention is the ability to apply images to unmodified film PVC materials using inkjet printers using solvent or eco-solvent ink.

Для использования возможностей цифровой печати целесообразным является осуществлять формирование рисунка на персональном компьютере, который при этом используется для программного управления работой совместимого с персональным компьютером струйного принтера. Печатающие головки указанного принтера наносят краситель в соответствии с получаемой от персонального компьютера информацией для воспроизведения рисунка.To use the capabilities of digital printing, it is advisable to create a drawing on a personal computer, which is used for program control of the operation of an inkjet printer compatible with a personal computer. The printheads of the indicated printer apply dye in accordance with the information received from the personal computer for reproducing the pattern.

Для более качественного воспроизведения цветовой гаммы наносимого на ПВХ материал изображения по технологии цифровой печати следует наносить краситель с использованием предварительно полученной экспериментальным путем для конкретного принтера и конкретного вида пленочного ПВХ материала базы данных, полученной с учетом спектральных характеристик отображенных на рассматриваемом конкретном материале цветов печати, используемой для программного выбора рецептуры красителя из набора применяемых в принтере чернил, требуемого для воспроизведения нужного цвета и его интенсивности.For better reproduction of the color gamut applied to PVC, the image material using digital printing technology should be applied with a dye using experimentally previously obtained data for a specific printer and a specific type of PVC film material of the database obtained taking into account the spectral characteristics of the print colors used on the particular material used for programmatically selecting a dye formulation from the set of inks used in the printer required for reproducing products of the desired color and its intensity.

Способ осуществляют следующим образом.The method is as follows.

Для нанесения изображения используют выпускаемые промышленностью немодифицированные пленочные ПВХ материалы, в частности, пленочные ПВХ материалы, предназначенные для изготовления натяжных потолков или стеновых панелей, имеющие свойство растяжения - сжатия до 20% площади полотна соответственно при его нагревании и остывании, толщиной 0,15-0,40 мм с матовой, глянцевой, лаковой, гладкой или каландрированной поверхностью.Unmodified PVC film materials manufactured by the industry, in particular, PVC film materials intended for the manufacture of stretch ceilings or wall panels, having the property of stretching-compressing up to 20% of the canvas area, respectively, when it is heated and cooled, with a thickness of 0.15-0, are used for applying the image , 40 mm with a matte, glossy, lacquered, smooth or calendered surface.

Для печати изображения используют совместимый с персональным компьютером струйный принтер, использующий сольвентные или экосольвентные чернила, например, стандартный многоцветный широкоформатный плоттер марки SJ-1000EX, выпускаемый фирмой Roland DG, с шестью подвижными струйными печатными головками, в котором используются экосольвентные чернила марки ECO-SOL Max.An inkjet printer compatible with a personal computer using solvent or eco-solvent inks, for example, the standard multi-color SJ-1000EX wide-format plotter manufactured by Roland DG, with six movable inkjet printheads using ECO-SOL Max eco-solvent inks, is used for printing images. .

Предварительно экспериментальным путем для конкретного принтера и конкретного вида пленочного ПВХ материала формируют базу данных для программного выбора рецептуры красителя, которую получают на основе измерения спектральных характеристик множества цветовых проб, наносимых на рассматриваемый конкретный материал (строят так называемые цветовые профили). В соответствии с указанными цветовыми профилями по программе персонального компьютера при печати изображения задается рецептура красителя, то есть на принтер передается команда, каких чернил и в каком количестве из набора чернил, применяемых в принтере, следует наносить для воспроизведения в конкретной точке изображения нужного цвета и его интенсивности.Preliminarily experimentally, for a particular printer and a specific type of PVC film material, a database is formed for the software selection of the dye formulation, which is obtained by measuring the spectral characteristics of many color samples applied to the specific material in question (so-called color profiles are built). In accordance with the specified color profiles, the dye formulation is set when printing the image when the image is printed, that is, the command is sent to the printer, which ink and in what quantity from the set of ink used in the printer should be applied to reproduce at a specific point in the image the desired color and its intensity.

В персональном компьютере, совместимом со струйным принтером, программным путем формируют изображение, которое требуется нанести на ПВХ материал, и вводят его в память компьютера.In a personal computer compatible with an inkjet printer, an image is formed by software that needs to be applied to PVC material, and it is entered into the computer's memory.

Подают рулонный ПВХ материал в струйный принтер с помощью системы загрузки-выгрузки.PVC roll material is fed into an inkjet printer using a loading and unloading system.

Транспортируют указанный материал через струйный принтер с пошаговым введением участков материала в область печати, находящуюся в зоне расположения струйных печатающих головок, и наносят краситель на поверхность материала в соответствии с получаемой принтером от персонального компьютера информацией для воспроизведения сформированного изображения. Процесс печатания осуществляют методом холодной печати, то есть без предварительного нагрева поступающего в область печати материала и без нагрева окружающей среды в указанной области. В частности, при использовании вышеуказанного плоттера процесс печатания ведут при отключенной встроенной в плоттер системе нагрева.The specified material is transported through an inkjet printer with the step-by-step introduction of sections of material into the print area located in the area of the inkjet printheads, and dye is applied to the surface of the material in accordance with the information received by the printer from the personal computer for reproducing the generated image. The printing process is carried out by cold printing, that is, without pre-heating the material entering the print area and without heating the environment in the specified area. In particular, when using the above plotter, the printing process is carried out with the heating system built into the plotter turned off.

После выхода из области печати транспортируемого через струйный принтер ПВХ материала его поверхность обдувают воздухом с температурой от 14 до 25°С. Указанный обдув может быть осуществлен с помощью сопел или с помощью вентилятора, расположенных таким образом, чтобы поток воздуха обдувал поверхность ПВХ материала с нанесенным изображением без разбрызгивания чернил. Требуемая температура воздуха может быть достигнута путем пропускания воздуха через термостат или путем поддерживания требуемой температуры в помещении, где размещен струйный принтер.After leaving the printing area of the material transported through the inkjet printer, its surface is blown with air at a temperature of 14 to 25 ° C. The specified airflow can be carried out using nozzles or using a fan located so that an air stream blows around the surface of the PVC material with the printed image without splashing ink. The required air temperature can be achieved by passing air through a thermostat or by maintaining the desired temperature in the room where the inkjet printer is located.

Выбор конкретной температуры воздуха из указанного диапазона зависит от толщины пленочного ПВХ материала. Чем тоньше пленка, тем температура воздуха должна быть ниже.The choice of a specific air temperature from the specified range depends on the thickness of the PVC film material. The thinner the film, the lower the air temperature.

Принимают рулонный ПВХ материал с нанесенным изображением, наматывая материал на приемный вал системы загрузки-выгрузки.They accept rolled PVC material with a printed image, winding the material onto the receiving shaft of the loading and unloading system.

Таким образом, заявляемый способ позволяет адаптировать стандартное оборудование струйной печати, в частности, многоцветный широкоформатный струйный принтер, использующий стандартные сольвентные или экосольвентные чернила, для нанесения изображения на немодифицированный пленочный ПВХ материал за счет разработанной автором описанной выше нестандартной технологии струйной печати.Thus, the inventive method allows you to adapt standard inkjet printing equipment, in particular, a multi-color wide format inkjet printer using standard solvent or eco-solvent inks, for applying images to unmodified PVC film material due to the non-standard inkjet technology developed above by the author.

Claims

1. The method of applying the image to the surface of the roll of material transported through an inkjet printer containing at least one inkjet printhead, comprising the stepwise introduction of sections of material into the print area located in the area of the inkjet printhead, applying dye using an inkjet printhead to the surface material in accordance with the information received by the printer for reproducing a pre-formed pattern, as well as processing material with a printed pattern a carrier for fixing it on the surface of the material, characterized in that the image is applied by cold printing without preheating the material entering the print area and without heating the environment in the specified area, film polyvinyl chloride material is used as a dye, solvent or eco-solvent ink is used as a dye for inkjet printers, dye-coated material is processed after the material leaves the print area by blowing the mat surface rial coated with dye air with a temperature of 14-25 ° C.

2. The method according to claim 1, characterized in that the formation of the pattern is carried out on a personal computer, while dye is applied in accordance with the information for reproducing the pattern obtained from the personal computer.

3. The method according to claim 2, characterized in that the dye is applied using a previously obtained experimentally for a specific printer and a specific type of film polyvinyl chloride database material, obtained taking into account the spectral characteristics of the printing colors displayed on the particular material used for the program formulation selection dye from the set of ink used in the printer, required to reproduce the desired color and its intensity.