Abstract

FIELD: building engineering, particularly for living building interior finish. SUBSTANCE: saline coating including binding agent and filling agent, namely mineral sodium salt. Mineral sodium salt content exceeds solubility thereof in binding agent. Sodium chloride is used as mineral sodium salt. Coating includes 30-80 mass% of mineral salt, remainder is binding agent. EFFECT: possibility of application for living building interior finish, providing of preventive-therapeutic influence. 1 ex, 1 dwg

Description

Изобретение относится к области строительства и может быть использовано для внутренней отделки жилого помещения.The invention relates to the field of construction and can be used for interior decoration of a residential building.

Известна двухслойная облицовочная плитка и способ ее изготовления по патенту № 2036879, опубл. 09.06.1995. Данная плитка включает лицевой слой, состоящий из натриевой соли, и несущий слой (связующее), выполненный из смеси, содержащей такие компоненты, как цемент, песок речной, алебастр, вода. Недостаток данной плитки заключается в том, что она может быть использована только в солелечебницах, что обусловлено спецификой ее конструкции.Known two-layer facing tiles and the method of its manufacture according to patent No. 2036879, publ. 06/09/1995. This tile includes a front layer, consisting of sodium salt, and a carrier layer (binder) made of a mixture containing such components as cement, river sand, alabaster, water. The disadvantage of this tile is that it can only be used in salt schools, due to the specifics of its design.

В строительстве также используется двухслойная декоративная облицовочная плита и способ ее изготовления по патенту № 2132916, опубл. 10.07.1999. Облицовочная декоративная плита содержит лицевой слой, выполненный из смеси поливинилацетатной (ПВА) эмульсии, крошки природного камня и фракционированного вспученного перлитового песка, и несущий слой (связующее), включающий смесь цементного связующего и вспученного перлитового песка, эмульсии ПВА, в несущий слой может быть дополнительно введена крошка природного камня. Недостаток данного изобретения в том, что оно не обладает профилактически-терапевтическими свойствами и может быть использовано для изготовления строительных изделий - облицовочных плит, предназначенных для подвесных потолков и облицовки стен преимущественно промышленных зданий.In the construction also uses a two-layer decorative facing plate and the method of its manufacture according to patent No. 2132916, publ. 07/10/1999. The decorative facing plate contains a front layer made of a mixture of polyvinyl acetate (PVA) emulsion, natural stone chips and fractionated expanded perlite sand, and a carrier layer (binder), including a mixture of cement binder and expanded perlite sand, PVA emulsion, may additionally be in the carrier layer introduced crumb natural stone. The disadvantage of this invention is that it does not have prophylactic and therapeutic properties and can be used for the manufacture of building products - cladding plates intended for suspended ceilings and wall cladding mainly of industrial buildings.

Известен материал декоративный облицовочный по патенту № 2117122, опубл. 10.08.1998. Данный материал содержит хлопковую или древесную целлюлозу, натриевую соль карбоксиметилцеллюлозы или полиакриламид (связующее) и декоративные добавки (наполнитель), в качестве которых могут быть использованы опил хвойных деревьев, растительные волокна, текстильные волокна, слюда. Недостаток данного материала - отсутствие профилактически-терапевтического эффекта.Known decorative facing material according to patent No. 2117122, publ. 08/10/1998. This material contains cotton or wood pulp, sodium carboxymethyl cellulose or polyacrylamide (binder) and decorative additives (filler), which can be used sawdust of coniferous trees, plant fibers, textile fibers, mica. The disadvantage of this material is the lack of a preventive therapeutic effect.

Наиболее близким аналогом, принятым за прототип, является облицовочное покрытие по патенту № 2076674, опубл. 10.04.1997 года. Солевое покрытие, наносимое на стены и потолки, включающее связующее - магнезиальный цемент и калиево-натриево-магниевую соль при следующем соотношении компонентов, мас.%:The closest analogue adopted for the prototype is a facing coating according to patent No. 2076674, publ. 04/10/1997 Salt coating applied to walls and ceilings, including a binder - magnesia cement and potassium-sodium-magnesium salt in the following ratio of components, wt.%:

Калиево-натриево-магниевая соль 85 - 98Potassium-sodium-magnesium salt 85 - 98

Связующее 2 - 15Binder 2 - 15

Недостаток данного изобретения - отсутствие декоративных качеств.The disadvantage of this invention is the lack of decorative qualities.

Задача предлагаемого технического решения - возможность использования солевого покрытия для внутренней отделки жилого помещения и обеспечение профилактически-терапевтического эффекта.The objective of the proposed technical solution is the possibility of using salt coating for interior decoration of the living room and providing a preventive and therapeutic effect.

Сущность изобретения заключается в том, что в солевом покрытии, включающем связующее и наполнитель - минеральную соль натрия, содержание которой превышает ее растворимость в связующем, в качестве указанной соли используют хлористый натрий при следующем соотношении, вес.%:The essence of the invention lies in the fact that in a salt coating comprising a binder and a filler is a sodium mineral salt, the content of which exceeds its solubility in the binder, sodium chloride is used as the indicated salt in the following ratio, wt.%:

Хлористый натрий 30 - 80Sodium Chloride 30 - 80

Связующее ОстальноеBinder Else

Декоративные качества позволяют использовать солевое покрытие при отделке жилого помещения.Decorative qualities allow the use of salt coating in the decoration of the premises.

На чертеже изображено поперечное сечение солевого покрытия. Солевое покрытие включает связующее 1, наполнитель 2. Один из примеров применения солевого покрытия следующий. Цемент (ГОСТ 25328-82. Цемент для строительных растворов. Технические условия) перемешивается с водой, образуя цементное тесто, которое перемешивается с кристаллами хлористого натрия (ГОСТ 13830-97. Соль поваренная пищевая), составляющими 60% от общего веса солевого покрытия. Солевое покрытие наносится на стены жилого помещения.The drawing shows a cross section of a salt coating. The salt coating includes a binder 1, a filler 2. One example of the use of a salt coating is as follows. Cement (GOST 25328-82. Cement for mortars. Technical conditions) is mixed with water, forming a cement paste, which is mixed with sodium chloride crystals (GOST 13830-97. Edible salt), which make up 60% of the total weight of the salt coating. Salt coating is applied to the walls of the living room.

Таким образом, солевое покрытие, обладающее декоративными качествами, может быть использовано для внутренней отделки жилого помещения, при этом оно обеспечивает профилактически-терапевтический эффект.Thus, a salt coating with decorative qualities can be used for interior decoration of a living room, while it provides a preventive and therapeutic effect.

Claims

A salt coating comprising a binder and a filler is a sodium mineral salt, the content of which exceeds its solubility in the binder, characterized in that sodium chloride is used as the indicated salt in the following ratio, weight. %:

Sodium Chloride 30-80

Binder Else