RU2156786C2 - Composition for antiicing coating - Google Patents
Composition for antiicing coating Download PDFInfo
- Publication number
- RU2156786C2 RU2156786C2 RU98124088A RU98124088A RU2156786C2 RU 2156786 C2 RU2156786 C2 RU 2156786C2 RU 98124088 A RU98124088 A RU 98124088A RU 98124088 A RU98124088 A RU 98124088A RU 2156786 C2 RU2156786 C2 RU 2156786C2
- Authority
- RU
- Russia
- Prior art keywords
- composition
- coating
- icing
- talc
- toluene
- Prior art date
Abstract
Description
Изобретение относится к композициям для покрытий, обеспечивающих снижение сил сцепления между льдом и различными поверхностями и защищающих от воздействия атмосферных факторов. Изобретение может быть использовано для борьбы с обледенением металлических конструкций, радиолокационных установок (антенн и куполов укрытий), холодильной техники и прочее. The invention relates to compositions for coatings, providing a reduction in adhesion between ice and various surfaces and protecting against atmospheric factors. The invention can be used to combat icing of metal structures, radar installations (antennas and domes of shelters), refrigeration equipment and more.
Известно двухслойное антиобледенительное покрытие (авторское свидетельство N 739080) на основе тетраэтоксисилана, содержащее в первом слое тетраэтоксисилан в количестве 1-30 об.%, комплексный катализатор - 0,18-5,2 об. % и органический растворитель, а во втором - полиэтилгидросилоксановую жидкость в количестве 5-20 вес.%, адгезионноактивный катализатор - 0,3-1,2 вес. % и органический растворитель. Состав для первого слоя покрытия приготавливают смешиванием органического растворителя с комплексным катализатором, в полученный раствор добавляют тетраэтоксисилан, перемешивают в течение 24 - 48 часов. Длительность перемешивания определяется необходимостью "вызревания" раствора. Срок хранения такого состава невысок и поэтому приготавливают его перед применением. Состав для второго слоя покрытия готовят путем растворения полиэтилгидросилоксана в органическом растворителе с последующим добавлением в полученный раствор адгезионноактивного катализатора. Для полученного таким образом покрытия усилие отрыва льда от защищенной поверхности составляет 0,04 - 0,08 кгс/см2 (методика определения адгезионной прочности не приводится, поэтому приведенные здесь и далее данные не могут быть признаны абсолютными), при этом количество циклов намораживания, характеризующее долговечность покрытия, равно 15 - 17. Для создания первого и второго слоев описываемого покрытия используют составы с очень высоким содержанием летучих органических растворителей (в первом слое -65-80 мас.%).Known two-layer anti-icing coating (copyright certificate N 739080) based on tetraethoxysilane containing in the first layer tetraethoxysilane in an amount of 1-30 vol.%, The complex catalyst is 0.18-5.2 vol. % and an organic solvent, and in the second - a polyhydrosiloxane liquid in an amount of 5-20 wt.%, an adhesive active catalyst - 0.3-1.2 wt. % and organic solvent. The composition for the first coating layer is prepared by mixing an organic solvent with a complex catalyst, tetraethoxysilane is added to the resulting solution, and stirred for 24 to 48 hours. The duration of mixing is determined by the need for "aging" of the solution. The shelf life of such a composition is low and therefore it is prepared before use. The composition for the second coating layer is prepared by dissolving polyethylsiloxane in an organic solvent, followed by adding an adhesive catalyst to the resulting solution. For the coating obtained in this way, the force of separation of ice from the protected surface is 0.04-0.08 kgf / cm 2 (the method for determining the adhesive strength is not given, therefore, the data presented hereinafter cannot be considered absolute), while the number of freezing cycles, characterizing the durability of the coating, equal to 15 - 17. To create the first and second layers of the described coating using compositions with a very high content of volatile organic solvents (in the first layer -65-80 wt.%).
Известна композиция для получения противообледенительного покрытия "Крезан" (авторское свидетельство N 1386630) на основе полиорганосилоксана в количестве 42 - 49 мас.% в органическом растворителе, содержащая гидрофобизованный органсилоксанами или парафином, или стеариновой кислотой наполнитель в количестве 2-15 мас.%, выбранный из группы: диоксид кремния, диоксид титана, оксид цинка, графит расширенный, базальтовое волокно и их смеси. Сила сцепления льда с покрытием не превышает 0,09 кг/см2 (методика оценки адгезионной прочности не приводится). Твердость покрытия по прибору М-3 составляет 0,4 усл. ед. Критический угол скатывания капли воды с покрытия составляет 25 - 30 град. Срок службы покрытия, предотвращающего обледенение, например, холодильников, взлетных площадок, летательных аппаратов, составляет всего 2 года. Кроме того, предварительная стадия гидрофобизации наполнителя, позволяющая получить покрытие с высокими эксплуатационными характеристиками, требует просушки компонентов композиции и длительного вакуумирования при повышенной температуре в интервале 290 - 420oC.Known composition for anti-icing coatings "Crozan" (copyright certificate N 1386630) based on polyorganosiloxane in an amount of 42 - 49 wt.% In an organic solvent containing hydrophobized organansiloxanes or paraffin, or stearic acid filler in an amount of 2-15 wt.%, Selected from the group: silicon dioxide, titanium dioxide, zinc oxide, expanded graphite, basalt fiber and mixtures thereof. The adhesion force of ice with the coating does not exceed 0.09 kg / cm 2 (the method for assessing the adhesive strength is not given). The hardness of the coating on the M-3 device is 0.4 srvc. units The critical angle of rolling a drop of water from the coating is 25-30 degrees. The service life of the anti-icing coating, for example, refrigerators, take-off areas, aircraft, is only 2 years. In addition, the preliminary stage of hydrophobization of the filler, allowing to obtain a coating with high performance characteristics, requires drying of the components of the composition and prolonged evacuation at elevated temperatures in the range of 290 - 420 o C.
Известна композиция для противооблединительного покрытия (авторское свидетельство N 1712388). Указанная композиция содержит в качестве полимерного связующего кремнийорганическую смолу в количестве 25 - 45 мас.%, выбранный из группы: оксид цинка, оксид магния, диоксид титана или расширенный графит, наполнитель, гидрофобизированный органическими модификаторами в виде метилхлороформа, или смолки производства этилсиликатов, или полиорганогидридсилоксановой жидкости в количестве 16-30 мас.%, и растворитель. При приготовлении названной композиции в качестве растворителя используется малотоксичный, пожаробезопасный метилхлороформ в количестве 25 - 60%, а в качестве разбавителей- хладоны 11; 12; 113. По сущесвующим в настоящее время представлениям фторированные углеводороды участвуют в процессе образования "озоновой дыры", поэтому по экологическим требованиям их применение нежелательно. Антиобледенительное свойство покрытия обусловлено главным образом наличием в составе композиции для его получения гидрофобизированного наполнителя, а гидрофобизация является сложной энергоемкой технологической операцией. Адгезия такого покрытия к субстрату удовлетворительная. При этом срок службы покрытия составляет всего 3 года. Known composition for anti-icing coat (copyright certificate N 1712388). The specified composition contains as a polymeric binder, an organosilicon resin in an amount of 25 - 45 wt.%, Selected from the group: zinc oxide, magnesium oxide, titanium dioxide or expanded graphite, a filler that is hydrophobized with organic modifiers in the form of methyl chloroform, or a resin for the production of ethyl silicates, or polyorganosiloxane liquids in an amount of 16-30 wt.%, and a solvent. In preparing the aforementioned composition, low-toxic, fireproof methyl chloroform in an amount of 25-60% is used as a solvent, and
Известна также полимерная композиция для антиобледенительного покрытия (Н.П. Харитонов, Л.Н. Красильникова, Т.И.Войнова, - Сб. трудов "Исследования в области физики и химии каучуков и резин", Л. 1975, с. 205). Указанная композиция содержит в качестве связующего полимерную систему, состоящую из полиметилфенилсилоксана и полидиметилсилоксана, и в качестве растворителя - толуол. Механизм формирования антиобледенительного покрытия основан на миграции в поверхностный слой низкомолекулярного полидиметилсилоксана. Самопроизвольное расслаивание, происходящее в полимерной системе, приводит к образованию в покрытии двух слоев, каждый из которых выполняет свою функцию: внутренний слой обеспечивает адгезию покрытия к поверхности, а наружный - уменьшает силу сцепления со льдом. Адгезия покрытия к подложке на основе рассматриваемой композиции составляет 1 - 2 балла. Сила сцепления льда с пленками из этой композиции составляет 0,3 - 0,4 кгс/см2.Also known is a polymer composition for anti-icing coatings (NP Kharitonov, LN Krasilnikova, T.I. . The specified composition contains as a binder a polymer system consisting of polymethylphenylsiloxane and polydimethylsiloxane, and toluene as a solvent. The mechanism of formation of the anti-icing coating is based on the migration of low molecular weight polydimethylsiloxane into the surface layer. The spontaneous delamination that occurs in the polymer system leads to the formation of two layers in the coating, each of which performs its function: the inner layer ensures adhesion of the coating to the surface, and the outer one reduces the adhesion to ice. The adhesion of the coating to the substrate based on the composition in question is 1–2 points. The force of adhesion of ice with the films of this composition is 0.3 - 0.4 kgf / cm 2 .
Несмотря на большое количество предлагаемых композиций проблема борьбы с обледенением путем использования покрытий до cих пор не решена удовлетворительно по одному или нескольким аспектам. Рассмотренные антиобледенительные покрытия обладают низким сцеплением со льдом, снегом и иными кристаллическими формами воды. Однако, обеспечивая сравнительно хорошую защиту от обледенения в течение относительно короткого периода времени, 2 - 3 года, известные покрытия не сохраняют антиобледенительных свойств в течение более длительного срока. Despite the large number of proposed compositions, the problem of anti-icing by using coatings has not yet been satisfactorily solved in one or more aspects. The considered anti-icing coatings have low adhesion to ice, snow and other crystalline forms of water. However, while providing relatively good icing protection for a relatively short period of time, 2 to 3 years, known coatings do not retain anti-icing properties for a longer period.
Известны защитные покрытия на основе органосиликатных материалов, которые являются атмосферостойкими и гидрофобными, угол смачивания которых составляет 90 - 95 град., но такая степень гидрофобности недостаточна для обеспечения хороших антиобледенительных свойств. Например, органосиликатная композиция для защитного покрытия ОС-12-03 (Н. П. Харитонов, В. А. Кротиков, В.В.Островский "Органосиликатные композиции", Каталог- справочник, Л. Наука. 1980 г., с. 20), включающая кинетически устойчивую смесь кремнийорганических полимеров, наполнитель (слюда, тальк), пигмент (оксиды и соли переходных металлов) и растворитель (толуол). Покрытие, сформированное на основе указанной композиции, является атмосферостойким и может применяться для защиты металлических, железобетонных и других конструкций, а также различного оборудования на открытом воздухе. Однако оно не обладает антиобледенительным свойством. Protective coatings based on organosilicate materials are known, which are weatherproof and hydrophobic, the wetting angle of which is 90 - 95 degrees, but this degree of hydrophobicity is insufficient to provide good anti-icing properties. For example, an organosilicate composition for a protective coating OS-12-03 (N.P. Kharitonov, V.A. Krotikov, V.V. Ostrovsky "Organosilicate compositions", Directory, L. Nauka. 1980, p. 20 ), including a kinetically stable mixture of organosilicon polymers, a filler (mica, talc), a pigment (oxides and salts of transition metals) and a solvent (toluene). The coating formed on the basis of this composition is weatherproof and can be used to protect metal, reinforced concrete and other structures, as well as various equipment in the open air. However, it does not have an anti-icing property.
Наиболее близким к изобретению по совокупности существенных признаков является композиция для антиобледенительного покрытия (Л.Н. Красильникова, Т.И.Войнова, Н.А.Никитина, Н.П.Харитонов - "Кремнийорганические соединения и материалы на их основе", Л. , Наука, 1984, с. 155). Указанная композиция включает в качестве связующего (в количестве 40 - 60 мас.%) полидиметилфенилсилоксан и полидиметилсилоксан, образующие термодинамически несовместимую, быстро расслаивающуюся систему, а в качестве растворителя - толуол. The closest to the invention in terms of essential features is a composition for anti-icing coatings (L.N. Krasilnikova, T.I. Voinova, N.A. Nikitina, N.P. Kharitonov - "Organosilicon compounds and materials based on them", L. , Science, 1984, p. 155). The specified composition includes as a binder (in an amount of 40-60 wt.%) Polydimethylphenylsiloxane and polydimethylsiloxane forming a thermodynamically incompatible, rapidly delaminating system, and toluene as a solvent.
Заявленное изобретение направлено на решение проблемы борьбы с обледенением поверхностей различных материалов путем создания на российском сырье антиобледенительной композиции с простой технологией приготовления, нанесения и формирования, сохранения и улучшения защитных свойств покрытия, снижения адгезии льда к покрытию при сохранении или увеличении адгезии покрытия к подложке, увеличения срока службы антиобледенительного защитного покрытия. The claimed invention is aimed at solving the problem of combating icing of surfaces of various materials by creating an anti-icing composition on Russian raw materials with a simple technology for preparing, applying and forming, maintaining and improving the protective properties of the coating, reducing ice adhesion to the coating while maintaining or increasing the adhesion of the coating to the substrate, increasing service life of the anti-icing protective coating.
Поставленная задача может быть решена следующим образом. The problem can be solved as follows.
Композиция для антиобледенительного покрытия, включающая кремнийорганическое полимерное связующее, состоящее из полидиметилфенилсилоксана и полидиметилсилоксана, и растворитель в виде толуола, в качестве наполнителя содержит тальк или смесь талька с белитом, и (или) баритом, а в качестве пигмента - оксиды и (или) соли переходных металлов, при следующем соотношении компонентов, мас.%:
Кремнийорганическое полимерное связующее - 30-40
Наполнитель - 9-18
Пигмент - 6-15,
Растворитель - Остальные
Композиция для антиобледенительного покрытия может быть приготовлена путем диспергирования наполнителей и пигментов в толуольном растворе кремнийорганических полимеров. Процесс проводится в шаровых или бисерных мельницах в течение 24 - 48 часов. Для нанесения композиции на защищаемую поверхность применяются методы лакокрасочной технологии: кисть, валик, краскораспылитель, окунание и другие. Сушка покрытия может проводиться по двум режимам: либо отверждение происходит при температуре 180oC в течение 3 часов, либо отверждение происходит при температуре окружающей среды с предварительно внесенным в композицию отвердителем.An anti-icing composition comprising an organosilicon polymer binder consisting of polydimethylphenylsiloxane and polydimethylsiloxane, and a solvent in the form of toluene, contains talc or a mixture of talc with belite and (or) barite as the filler, and oxides and (or) salts as the pigment transition metals, in the following ratio of components, wt.%:
Silicone polymer binder - 30-40
Filler - 9-18
Pigment - 6-15,
Solvent - Other
The anti-icing composition can be prepared by dispersing fillers and pigments in a toluene solution of organosilicon polymers. The process is carried out in ball or bead mills for 24 to 48 hours. To apply the composition to the surface to be protected, the methods of paint and varnish technology are used: brush, roller, paint sprayer, dipping and others. Drying of the coating can be carried out in two modes: either curing occurs at a temperature of 180 o C for 3 hours, or curing occurs at ambient temperature with a hardener previously added to the composition.
Изобретение так же как и описанная выше композиция для защитного покрытия ОС - 12-03 включает в качестве наполнителя тальк и в качестве пигмента - оксиды и соли переходных металлов. The invention, as well as the above-described composition for the protective coating OS - 12-03, includes talc as a filler and transition metal oxides and salts as a pigment.
Известно, что введение наполнителя в виде талька приводит к увеличению геометрического пути агрессивных компонентов к подложке, т.е. затрудняет воздействие внешних факторов на защищаемую поверхность. Барит также проявляет высокую экранирующую способность и, кроме этого, придает покрытию высокую плотность и повышает сопротивление к истиранию. Последнее свойство оказывается важным при эксплуатации некоторых видов радиотехнических установок в полевых условиях. It is known that the introduction of a filler in the form of talc leads to an increase in the geometric path of aggressive components to the substrate, i.e. complicates the impact of external factors on the protected surface. Barite also exhibits high shielding ability and, in addition, gives the coating a high density and increases abrasion resistance. The latter property is important when operating certain types of radio installations in the field.
Белит представляет интерес как дешевый продукт, получаемый при двойной сепарации шлаков от производства силикотермического феррохрома, силикокальция, ферросплавов и т.д. По своим свойствам он близок к бариту. Belite is of interest as a cheap product obtained by double slag separation from the production of silicothermic ferrochrome, silicocalcium, ferroalloys, etc. By its properties, it is close to barite.
В качестве пигментов в заявленной композиции могут быть использованы оксиды и соли переходных металлов, например оксиды хрома, железа, титана, цинка. Ряд пигментов наряду с приданием покрытию определенного цвета в той или иной степени оказывают влияние на защитные свойства покрытия. Например, оксиды железа и хрома являются противокоррозионными. As pigments in the claimed composition can be used oxides and salts of transition metals, for example oxides of chromium, iron, titanium, zinc. A number of pigments, along with giving the coating a certain color, to one degree or another, affect the protective properties of the coating. For example, iron and chromium oxides are anticorrosive.
Для подтверждения заявляемых интервалов, входящих в заявляемую композицию ингредиентов, проведены испытания. Результаты испытаний иллюстрируются приведенными в таблицах примерами, содержащими составы заявляемой композиции в пределах, указанных в формуле изобретения интервалов значений каждого ингредиента (таблица 1), и данные по техническим характеристикам покрытия на основе заявляемой композиции (таблица 2). To confirm the claimed intervals included in the claimed composition of the ingredients, tests were performed. The test results are illustrated by the examples in the tables containing the compositions of the claimed composition within the ranges indicated in the claims of the ranges of values of each ingredient (table 1), and data on the technical characteristics of the coating based on the claimed composition (table 2).
Применение в заявленной композиции известного наполнителя и пигмента позволяет использовать их свойства, проявляемые в композициях для защитных покрытий. При этом их использование в композиции для антиобледенительного покрытия на основе двухкомпонентной полимерной системы не влияет на кинетику расслаивания, обуславливающую антиобледенительные свойства этого покрытия. Таким образом, заявленная композиция для антиобледенительного покрытия позволяет получить покрытие, сочетающее более высокие антиобледенительные свойства покрытия на основе самопроизвольно расслаивающейся полимерной системы со свойствами защитного покрытия. The use in the claimed composition of a known filler and pigment allows you to use their properties that are shown in compositions for protective coatings. Moreover, their use in the composition for de-icing coatings based on a two-component polymer system does not affect the kinetics of delamination, causing the de-icing properties of this coating. Thus, the claimed composition for de-icing coatings allows you to get a coating that combines higher de-icing properties of the coating based on spontaneously exfoliating polymer system with the properties of a protective coating.
Важно отметить следующее: в настоящее время широко применяются атмосферостойкие перхлорвиниловые эмали группы ХВ, предназначенные для защиты металлических конструкций от атмосферных агрессивных факторов (например, эмаль ХВ-518 - "Лакокрасочные материалы. Технические требования и контроль качества". Москва, Химия, 1988 г., с. 239 и эмаль ХВ-124 - журнал "Лакокрасочные материалы их применение.", N 3, 1992 г., с. 20). It is important to note the following: at present, weather-resistant perchlorovinyl enamels of the ХВ group are widely used, designed to protect metal structures from atmospheric aggressive factors (for example, enamel ХВ-518 - “Paints and varnishes. Technical requirements and quality control.” Moscow, Chemistry, 1988. , p. 239 and enamel ХВ-124 - journal "Paintwork materials and their use.",
В таблице 3 приведены сравнительные свойства покрытий на основе заявленной композиции, прототипа, ОС - 12-03 и эмали группы ХВ. Table 3 shows the comparative properties of coatings based on the claimed composition, prototype, OS - 12-03 and enamel of the group XB.
Обобщая данные таблицы 3, можно сделать вывод, что заявленная композиция по таким важным характеристикам антиобледенительного покрытия как твердость, краевой угол смачивания и адгезионная прочность льда превосходит прототип. По защитным свойствам превосходит атмосферостойкое органосиликатное покрытий ОС-12-03 и противокоррозионные хлорвиниловые эмали. Таким образом, изобретение обеспечивает синергетический эффект, проявляющийся в повышении количественных показателей антиобледенительных свойств по сравнению с известными антиобледенительными покрытиями и повышение количественных показателей защитных свойств в сравнении с показателями известных защитных покрытий. Вследствие этого срок службы антиобледенительного покрытия на основе заявленной композиции в условиях обледенения в 1,5 раза превышает срок службы защитного покрытия марки ХВ, рекомендованного для использования в условиях холодного климата; адгезионная прочность льда в 3-10 раз меньше, чем у ОС-12-03, и в 4-10 раз меньше, чем у эмалей группы ХВ; способы приготовления и нанесения композиции очень просты и технологичны; в состав композиции входит только отечественное и недефицитное сырье, причем белит является отходом металлургического производства. Summarizing the data of table 3, we can conclude that the claimed composition on such important characteristics of the anti-icing coating as hardness, wetting angle and adhesive strength of ice exceeds the prototype. Its protective properties are superior to weather-resistant organosilicate coatings OS-12-03 and anticorrosive vinyl chloride enamels. Thus, the invention provides a synergistic effect, which is manifested in an increase in the quantitative indicators of anti-icing properties in comparison with the known anti-icing coatings and an increase in the quantitative indicators of the protective properties in comparison with the indicators of the known protective coatings. As a result, the service life of the anti-icing coating based on the claimed composition under icing conditions is 1.5 times longer than the service life of the XB grade protective coating recommended for use in cold climates; adhesive strength of ice is 3-10 times less than that of OS-12-03, and 4-10 times less than that of enamels of group XB; methods for preparing and applying the composition are very simple and technologically advanced; the composition includes only domestic and non-deficient raw materials, and whitewash is a waste of metallurgical production.
Claims (1)
Кремнийорганическое полимерное связующее - 30 - 40
Тальк или смесь талька с белитом и/или баритом - 9 - 18
Оксиды и/или соли переходных металлов - 6 - 15
Толуол - ОстальноеA composition for anti-icing coatings comprising an organosilicon polymer binder consisting of polydimethylphenylsiloxane and polydimethylsiloxane and toluene, characterized in that the composition further comprises talc or a mixture of talc with belite and / or barite and oxides and / or salts of transition metals in the following ratio of components, wt. %:
Organosilicon polymer binder - 30 - 40
Talc or a mixture of talc with belite and / or barite - 9 - 18
Oxides and / or salts of transition metals - 6 - 15
Toluene - Else