RU2143462C1

RU2143462C1 - Lubricant for metal cold drawing

Info

Publication number: RU2143462C1
Application number: RU98111268A
Authority: RU
Inventors: Г.В. Васильева; В.Г. Демидов; Б.Ю. Мальков
Original assignee: Открытое акционерное общество "Чебоксарский завод кабельных изделий "Чувашкабель"
Priority date: 1998-06-11
Filing date: 1998-06-11
Publication date: 1999-12-27

Abstract

FIELD: drawing lubricants; applicable in plastic metal working, more precisely, drawing of copper wire. SUBSTANCE: lubricant contains soap and water and is distinguished by the fact that it additionally contains product of saponification of still bottoms after distillation and rectification of crude primary alcohols, with the following amounts of components, wt.%: soap 5-15; products of saponification of still bottoms after distillation and rectification of crude primary alcohols 1-50; the balance, water. EFFECT: extended assortment of lubricants with improved properties. 3 tbl

Description

Изобретение относится к технологическим смазкам и может быть использовано в производстве для холодной обработки металлов давлением, в частности при волочении меди. The invention relates to technological lubricants and can be used in the production of cold metal forming, in particular when drawing copper.

К смазкам, предназначенным для использования при волочении, предъявляется ряд общих требований. Смазки должны легко наноситься на заготовку перед волочением и легко удаляться с готового изделия по окончании процесса. Они должны быть химически пассивными к материалу инструмента, т.е. не вступать с ним в химические реакции, не вызывать его коррозии. A number of general requirements apply to greases intended for use in drawing. Lubricants should be easily applied to the workpiece before drawing and easily removed from the finished product at the end of the process. They must be chemically passive to the tool material, i.e. Do not enter into chemical reactions with it, do not cause its corrosion.

Помимо общих требований в зависимости от условий волочения к смазкам предъявляются специальные требования. Так, высокое значение имеет толщина обрабатываемого изделия (например, диаметр проволоки). Общей тенденцией является повышение консистентности смазки при увеличении прочности или толщины изделия. In addition to the general requirements, depending on the drawing conditions, special requirements are imposed on the lubricants. So, the thickness of the workpiece (for example, the diameter of the wire) is of high importance. A general trend is to increase the consistency of the lubricant while increasing the strength or thickness of the product.

Известны смазки, применяемые для волочения меди, включающие мыльно-масляные и масляные эмульсии (Грудев А.П., Зильберг Ю.В., Тилик В.Т. Трение и смазки при обработке металлов давлением. Справочник. - М.: Металлургия, 1982, с. 298-299). Known lubricants used for drawing copper, including soap-oil and oil emulsions (Grudev A.P., Zilberg Yu.V., Tilik V.T. Friction and lubricants in the processing of metals by pressure. Reference book. - Moscow: Metallurgy, 1982 , p. 298-299).

Известна "Смазка для холодной обработки металлов давлением", содержащая воду, соду и мыла щелочных металлов сульфатированной головной фракции ректификации талового масла (авторское свидетельство СССР N 1171516, кл. C 10 M 173/02, 1995). The well-known "Grease for cold metal forming" containing water, soda and alkali soaps of sulfated head fraction of distillation of tall oil (USSR author's certificate N 1171516, class C 10 M 173/02, 1995).

Известна "Смазка для сухого волочения металлов", содержащая медный купорос, мыльный порошок и порошкообразный наполнитель (авторское свидетельство СССР N 1625891, кл. C 10 M 105/24, 1985). The well-known "Grease for dry drawing of metals" containing copper sulfate, soap powder and powder filler (USSR copyright certificate N 1625891, class C 10 M 105/24, 1985).

Известен "Концентрат смазки "Синсопол" для холодной обработки металлов давлением", содержащий кубовый остаток синтетических жирных кислот, натриевые соли кубового остатка синтетических жирных кислот, соапсток растительных масел (авторское свидетельство N 154647, кл. C 10 M 173/02, 1990). The well-known "Lubricant Concentrate" Sinsopol "for cold metal forming" containing bottoms of synthetic fatty acids, sodium salts of bottoms of synthetic fatty acids, co-stock of vegetable oils (copyright certificate N 154647, class C 10 M 173/02, 1990).

Известна "Смазка для холодного волочения металлов", содержащая жидкое мыло, полученное омылением соапстоков растительных масел едким натром, и тальк (патент N 2052494, кл. C 10 M 169/04, C 10 N 40/24, 1992). Known "Grease for cold drawing of metals" containing liquid soap obtained by saponification of soap stocks of vegetable oils with sodium hydroxide, and talc (patent N 2052494, class C 10 M 169/04, C 10 N 40/24, 1992).

К наиболее близкой по технической сущности относится "Смазка для холодного волочения медной проволоки", представляющая собой водную эмульсию, содержащую мыло, растительное масло, воду (Груднев А.П., Зильберг Ю.В., Тилик В. Т. Трение и смазки при обработке металлов давлением. - М.: Металлургия, 1982, с. 208, табл. 56). К недостаткам следует отнести образование медных мыл в процессе волочения, достаточно высокий остаток эмульсии на поверхности проволоки. The closest in technical essence is “Lubricant for cold drawing of copper wire”, which is an aqueous emulsion containing soap, vegetable oil, water (Grudnev A.P., Zilberg Yu.V., Tilik V.T. Friction and lubricants for metal forming. - M.: Metallurgy, 1982, p. 208, table 56). The disadvantages include the formation of copper soaps in the process of drawing, a sufficiently high emulsion residue on the surface of the wire.

Изобретение направлено на создание состава смазки для холодного волочения металлов, расширяющего ассортимент смазок для обработки металлов давлением, с улучшенными свойствами. The invention is aimed at creating a lubricant composition for cold drawing of metals, expanding the range of lubricants for metal forming, with improved properties.

Это достигается тем, что смазка для холодного волочения металлов, содержащая мыло и воду, дополнительно содержит продукт омыления кубового остатка после дистилляции и ректификации сырых первичных спиртов при следующем соотношении компонентов, мас.%:
Мыло - 5 - 15
Продукт омыления кубового остатка после дистилляции и ректификации сырых первичных спиртов - 1 - 50
Вода - Остальное
Смазку готовят по следующей технологии: в обогреваемый бак с мешалкой помещают воду и нарезанное на куски мыло. После перемешивания и кипячения смеси в течение 30 минут в этот же бак загружают расчетное количество расплавленного продукта омыления кубового остатка после дистилляции и ректификации сырых первичных спиртов и интенсивно перемешивают. Окончание процесса определяют измеряя pH полученного концентрата, который должен быть не ниже 7 и не выше 8. Концентрат может применяться как в исходном, так и в разбавленном состоянии. Разбавление производят обычной водой до концентрации, предусмотренной в процессе волочения.This is achieved by the fact that the lubricant for cold drawing of metals, containing soap and water, additionally contains a product of saponification of the bottom residue after distillation and rectification of crude primary alcohols in the following ratio of components, wt.%:
Soap - 5 - 15
Saponification product of bottom residue after distillation and rectification of crude primary alcohols - 1 - 50
Water - Else
Lubrication is prepared according to the following technology: water and soap cut into pieces are placed in a heated tank with a stirrer. After mixing and boiling the mixture for 30 minutes, the calculated amount of the molten saponification product of the bottom residue after distillation and rectification of the crude primary alcohols is loaded into the same tank and mixed vigorously. The end of the process is determined by measuring the pH of the resulting concentrate, which should be no lower than 7 and no higher than 8. The concentrate can be used both in the initial and diluted state. Dilution is carried out with ordinary water to the concentration provided in the drawing process.

Составы смазок приводятся в табл. 1. The lubricant compositions are given in table. 1.

Для получения смазки использовали следующие материалы:
Мыло хозяйственное 60% - По ОСТ-18-36-8-80
Мыло детское - РТУ РСФСР-214-64
Вода питьевая - По ГОСТ 2874-82
Продукт омыления кубового остатка после дистилляции и ректификации сырых первичных спиртов - ТУ 38.107.115-80
Продукт омыления представляет собой однородное вещество от светло-серого до коричневого цвета с массовой долей мыла не менее 15%; молекулярный вес 310-330; удельный вес 0,85-0,88 г/см³; температура кипения выше 200^oC; точка плавления 55-65^oC; температура застывания 45-50^oC; температура вспышки выше 140^oC; температура деструкции выше 300^oC. Продукт частично растворяется в воде, растворим в маслах и органических растворителях, pH 8-10.To obtain the lubricant used the following materials:
Laundry soap 60% - According to OST-18-36-8-80
Soap for children - RTU RSFSR-214-64
Drinking water - According to GOST 2874-82
Saponification product of bottom residue after distillation and rectification of crude primary alcohols - TU 38.107.115-80
The saponification product is a homogeneous substance from light gray to brown in color with a mass fraction of soap of at least 15%; molecular weight 310-330; specific gravity 0.85-0.88 g / cm ³ ; boiling point above 200 ^o C; melting point 55-65 ^o C; pour point 45-50 ^o C; flash point above 140 ^o C; the temperature of destruction is above 300 ^o C. The product is partially soluble in water, soluble in oils and organic solvents, pH 8-10.

Продукт малотоксичен ДЛ 50 > 15 г/кг. Местным кожно-раздражающим и кожно-резорбтивным, кумулятивным, сенсибилизирующим свойствами не обладает. The product has low toxicity. DL 50> 15 g / kg. It does not have local skin-irritating and skin-resorptive, cumulative, sensitizing properties.

У составов смазок 1-7 определяли стабильность, корродирующее действие и pH разбавленных растворов. In lubricant formulations 1-7, stability, corrosion, and pH of dilute solutions were determined.

Стабильность определяли по ГОСТ 6243-75. Stability was determined according to GOST 6243-75.

Корродирующее действие определяли по ГОСТ 97080-77. The corrosive effect was determined according to GOST 97080-77.

Результаты испытаний приведены в табл. 2. The test results are given in table. 2.

Составы смазок 1-6 испытывали в сравнении с известной смазкой (состав 7) при волочении медной круглой проволоки марки МТЭ, ММЭ на машинах типа MP-9; M-30; MS-250; C-213; M-15; DHCF21; фирмы "ДИГЕП" и "СКЕТ". Compositions of lubricants 1-6 were tested in comparison with the known lubricant (composition 7) when drawing copper round wire of the MTE, MME grade on machines of the MP-9 type; M-30; MS-250; C-213; M-15; DHCF21; firms "DIGEP" and "SKET".

Волочение проводилось:
по маршруту с диаметром 2,00 мм на размер 1,20 мм при скорости волочения 25,00-15,00 м/с;
по маршруту с диаметром 2,00 мм на размер 0,35 мм при скорости 40,00-20,00 м/с;
по маршруту с диаметром 0,50 мм на размер 0,1 мм при скорости 50,00-20,00 м/с;
по маршруту с диаметром 0,25 на размер 0,05 мм при скорости 20-30 м/с.Drawing was carried out:
along a route with a diameter of 2.00 mm to a size of 1.20 mm at a drawing speed of 25.00-15.00 m / s;
along a route with a diameter of 2.00 mm to a size of 0.35 mm at a speed of 40.00-20.00 m / s;
along a route with a diameter of 0.50 mm to a size of 0.1 mm at a speed of 50.00-20.00 m / s;
along a route with a diameter of 0.25 to a size of 0.05 mm at a speed of 20-30 m / s.

Результаты волочения медной проволоки приведены в табл. 3. The results of the drawing of copper wire are given in table. 3.

Как видно из представленных данных (табл. 3) применение предлагаемой смазки в процессе волочения медной проволоки обеспечивает содержание чистой меди в шламе на 15% больше; уменьшение остатка эмульсии на поверхности проволоки в 2 раза по сравнению с известной смазкой. As can be seen from the data presented (table. 3), the use of the proposed lubricant in the process of drawing copper wire provides a pure copper content in the sludge of 15% more; a decrease in the emulsion residue on the surface of the wire by 2 times compared with the known lubricant.

При применении предлагаемой смазки отсутствует образование медных мыл в процессе волочения, отработанная смазка хорошо фильтруется и может многократно использоваться в дальнейшем в отличие от известной смазки. When using the proposed grease, there is no formation of copper soaps during the drawing process, the used grease is well filtered and can be reused later in contrast to the known grease.

Предлагаемая смазка не расслаивается со временем и не обладает корродирующим действием (табл. 2), что также позволяет расширить пределы применения данных смазок. The proposed lubricant does not stratify over time and does not have a corrosive effect (table. 2), which also allows you to expand the application of these lubricants.

Claims

A lubricant for cold drawing of metals containing soap and water, characterized in that it additionally contains a saponification product of the bottom residue after distillation and rectification of crude primary alcohols in the following ratio, wt.%:
Soap - 5 - 15
Saponification products of bottom residue after distillation and rectification of crude primary alcohols - 1 - 50
Water - Else